Many staircases in reinforced concrete （RC） frame structures suffered severe damage during the Wenchuan earthquake. Elastic analyses for 18 RC structure models with and without staircases are conducted and compared ...Many staircases in reinforced concrete （RC） frame structures suffered severe damage during the Wenchuan earthquake. Elastic analyses for 18 RC structure models with and without staircases are conducted and compared to study the influence of the staircase on the stiffness, displacements and internal forces of the structures. To capture the yielding development and damage mechanism of frame structures, elasto-plastic analysis is carried out for one of the 18 models. Based on the features observed in the analyses, a new type of staircase design i.e., isolating them from the master structure to eliminate the effect of K-type struts, is proposed and discussed. It is concluded that the proposed method of staircase isolation is effective and feasible for engineering design, and does not significantly increase the construction cost.展开更多
Crack initiation, propagation and microfracture processes of austempered high silicon cast steel have been investigated by using an in-situ tensile stage installed inside a scanning electron microscope chamber. It is ...Crack initiation, propagation and microfracture processes of austempered high silicon cast steel have been investigated by using an in-situ tensile stage installed inside a scanning electron microscope chamber. It is revealed that micro cracks always nucleate at the yielding near imperfections and the boundary of matrix-inclusions due to the stress concentration. There are four types of crack propagations in the matrix: crack propagates along the boundary of two clusters of bainitic ferrite; crack propagates along the boundary of ferrite-austenite in bainitic ferrite laths; crack propagates into bainitic ferrite laths; crack nucleates and propagates in the high carbon brittle plate shape martensite which is transformed from some blocky retained austenite due to plastic deformation. Based on the observation and analysis of microfracture processes, a schematic diagram of the crack nucleation and propagation process of high silicon cast steel is proposed.展开更多
The tensile equipment of the advanced confocal scanning laser microscope （CSLM） was used to research the high temperature mechanical properties of low carbon silicon-bearing steel by twin-roll strip casting. The res...The tensile equipment of the advanced confocal scanning laser microscope （CSLM） was used to research the high temperature mechanical properties of low carbon silicon-bearing steel by twin-roll strip casting. The results show that, at the strain rate of 0. 000 5 s ^-1, the strip clearly shows signs of brittleness at around 600 ℃ and its plasticity falls considerably between 750 ℃ and 600 ℃. This is because during the transformation from austenite to ferrite, the low strength ferrite at the austenite grain boundaries greatly reduces the steel＇ s high temperature plasticity. The subsequent strip coiling process should be controlled at less than the brittle temperature of approximately 600 ℃, so cracks at the coiling stage can be prevented.展开更多
The mechanism of damage evolution and fracture in A357 casting alloys was investigated by in-situ scanning electron microscopy （SEM） tensile testing. Different microstructures of A357 casting alloys were produced by...The mechanism of damage evolution and fracture in A357 casting alloys was investigated by in-situ scanning electron microscopy （SEM） tensile testing. Different microstructures of A357 casting alloys were produced by eutectic Si modification and T6 heat treatment. It is shown that microcracks in these alloys are predominantly formed in eutectic Si particles. Large and elongated eutectic Si particles in unmodified alloy show the greater tendency to cracking, whereas cracking of small and round eutectic Si particles in Sr modified and T6 heat treated alloys is relatively lag. The crack mainly propagates along the broken eutectic Si particles in unmodified and Sr modified alloys or along the deepened shear bands in T6 heat treated alloy with accumulating the applied strain. The results were discussed in terms of Weibull statistics and the fracture models were established.展开更多
基金The National Key Technologies R&D Program under Grant No. 2009BAJ28B01The Technologies R&D Program of China State Construction Engineering Co., Ltd under Grant No. CSCEC-2009-Z-15
文摘Many staircases in reinforced concrete （RC） frame structures suffered severe damage during the Wenchuan earthquake. Elastic analyses for 18 RC structure models with and without staircases are conducted and compared to study the influence of the staircase on the stiffness, displacements and internal forces of the structures. To capture the yielding development and damage mechanism of frame structures, elasto-plastic analysis is carried out for one of the 18 models. Based on the features observed in the analyses, a new type of staircase design i.e., isolating them from the master structure to eliminate the effect of K-type struts, is proposed and discussed. It is concluded that the proposed method of staircase isolation is effective and feasible for engineering design, and does not significantly increase the construction cost.
基金supported by Swedish Institute of Sweden (No. 200/01954/2007/China Bilateral programme)
文摘Crack initiation, propagation and microfracture processes of austempered high silicon cast steel have been investigated by using an in-situ tensile stage installed inside a scanning electron microscope chamber. It is revealed that micro cracks always nucleate at the yielding near imperfections and the boundary of matrix-inclusions due to the stress concentration. There are four types of crack propagations in the matrix: crack propagates along the boundary of two clusters of bainitic ferrite; crack propagates along the boundary of ferrite-austenite in bainitic ferrite laths; crack propagates into bainitic ferrite laths; crack nucleates and propagates in the high carbon brittle plate shape martensite which is transformed from some blocky retained austenite due to plastic deformation. Based on the observation and analysis of microfracture processes, a schematic diagram of the crack nucleation and propagation process of high silicon cast steel is proposed.
文摘The tensile equipment of the advanced confocal scanning laser microscope （CSLM） was used to research the high temperature mechanical properties of low carbon silicon-bearing steel by twin-roll strip casting. The results show that, at the strain rate of 0. 000 5 s ^-1, the strip clearly shows signs of brittleness at around 600 ℃ and its plasticity falls considerably between 750 ℃ and 600 ℃. This is because during the transformation from austenite to ferrite, the low strength ferrite at the austenite grain boundaries greatly reduces the steel＇ s high temperature plasticity. The subsequent strip coiling process should be controlled at less than the brittle temperature of approximately 600 ℃, so cracks at the coiling stage can be prevented.
基金financial support from Innovation Fund of China Aerospace Science and Technology Corporation(2011)Research Fund of the State Key Laboratory of Solidification Processing(No.42-QP-009)the 111 Project of China(No.B08040)
文摘The mechanism of damage evolution and fracture in A357 casting alloys was investigated by in-situ scanning electron microscopy （SEM） tensile testing. Different microstructures of A357 casting alloys were produced by eutectic Si modification and T6 heat treatment. It is shown that microcracks in these alloys are predominantly formed in eutectic Si particles. Large and elongated eutectic Si particles in unmodified alloy show the greater tendency to cracking, whereas cracking of small and round eutectic Si particles in Sr modified and T6 heat treated alloys is relatively lag. The crack mainly propagates along the broken eutectic Si particles in unmodified and Sr modified alloys or along the deepened shear bands in T6 heat treated alloy with accumulating the applied strain. The results were discussed in terms of Weibull statistics and the fracture models were established.