Ultra-thin-body （UTB） In0.53Ga0.47As-on-insulator （In0.53Ga0.47As-OI） structures with thicknesses of 8 and 15nm are realized by transferring epitaxially grown In0.53Ga0.47As layers to silicon substrates with 15-nm...Ultra-thin-body （UTB） In0.53Ga0.47As-on-insulator （In0.53Ga0.47As-OI） structures with thicknesses of 8 and 15nm are realized by transferring epitaxially grown In0.53Ga0.47As layers to silicon substrates with 15-nmthick A12 03 as a buried oxide by using the direct wafer bonding method. Back gate n-channel metal-oxidesemiconductor field-effect transistors （nMOSFETs） are fabricated by using these In0.53Ga0.47As-OI structures with excellent electrical characteristics. Positive bias temperature instability （PBTI） and hot carrier injection （HCI） characterizations are performed for the In0.53Ga0.47As-OI nMOSFETs. It is confirmed that the In0.53Ga0.47 As-OI nMOSFETs with a thinner body thickness suffer from more severe degradations under both PBTI and HCr stresses. Moreover, the different evolutions of the threshold voltage and the saturation current of the UTB In0.53Ga0.47As-OI nMOSFETs may be due to the slow border traps.展开更多
基金Supported by the National Program on Key Basic Research Project of China under Grant No 2011CBA00607the National Natural Science Foundation of China under Grant Nos 61106089 and 61376097the Zhejiang Provincial Natural Science Foundation of China under Grant No LR14F040001
文摘Ultra-thin-body （UTB） In0.53Ga0.47As-on-insulator （In0.53Ga0.47As-OI） structures with thicknesses of 8 and 15nm are realized by transferring epitaxially grown In0.53Ga0.47As layers to silicon substrates with 15-nmthick A12 03 as a buried oxide by using the direct wafer bonding method. Back gate n-channel metal-oxidesemiconductor field-effect transistors （nMOSFETs） are fabricated by using these In0.53Ga0.47As-OI structures with excellent electrical characteristics. Positive bias temperature instability （PBTI） and hot carrier injection （HCI） characterizations are performed for the In0.53Ga0.47As-OI nMOSFETs. It is confirmed that the In0.53Ga0.47 As-OI nMOSFETs with a thinner body thickness suffer from more severe degradations under both PBTI and HCr stresses. Moreover, the different evolutions of the threshold voltage and the saturation current of the UTB In0.53Ga0.47As-OI nMOSFETs may be due to the slow border traps.