The ZrTiON gate-dielectric GaAs metal-oxide-semiconductor （MOS） capacitors with or without ZrAION as the interfacial passivation layer （IPL） are fabricated and their properties are investigated. The experimental r...The ZrTiON gate-dielectric GaAs metal-oxide-semiconductor （MOS） capacitors with or without ZrAION as the interfacial passivation layer （IPL） are fabricated and their properties are investigated. The experimental results show that the GaAs MOS capacitor with the ZrAION IPL exhibits better interracial and electrical properties, including lower interface-state density （1.14 × 10^12 cm^-2eV^-1）, smaller gate leakage current （6.82 × 10^-5 A//cm^2 at Vfb ＋1V）, smaller capacitance equivalent thickness （1.5 nm）, and larger k value （26）. The involved mechanisms lie in the fact that the ZrAION IPL can effectively block the diffusion of Ti and O towards the GaAs surface, thus suppressing the formation of interracial Ga-/As-oxides and As-As dimers, which leads to improved interracial and electrical properties for the devices.展开更多
基金Supported by the National Natural Science Foundation of China under Grant Nos 61176100,61274112 and 61404055
文摘The ZrTiON gate-dielectric GaAs metal-oxide-semiconductor （MOS） capacitors with or without ZrAION as the interfacial passivation layer （IPL） are fabricated and their properties are investigated. The experimental results show that the GaAs MOS capacitor with the ZrAION IPL exhibits better interracial and electrical properties, including lower interface-state density （1.14 × 10^12 cm^-2eV^-1）, smaller gate leakage current （6.82 × 10^-5 A//cm^2 at Vfb ＋1V）, smaller capacitance equivalent thickness （1.5 nm）, and larger k value （26）. The involved mechanisms lie in the fact that the ZrAION IPL can effectively block the diffusion of Ti and O towards the GaAs surface, thus suppressing the formation of interracial Ga-/As-oxides and As-As dimers, which leads to improved interracial and electrical properties for the devices.