The structure characteristics of a2/γinterfaces and the features of deformation twins in a quasi-isothermal forged Ti-45Al-10Nb alloy were studied by highresolution transmission electron microscopy. Three types of st...The structure characteristics of a2/γinterfaces and the features of deformation twins in a quasi-isothermal forged Ti-45Al-10Nb alloy were studied by highresolution transmission electron microscopy. Three types of strain induced a2/γinterfaces and two types of strain induced twin boundaries were identified The most,important features are high density of ledges and the existence of I/3[111] Frank partial dislocation. Mechanisms for the formation these interfaces were proposed Two types of deformation twins were observed These deformation twins always start from the ledges it seems that ledges at interfaces are important features of interfacial structure for the mechanical behavior of alloys.展开更多
A series of Ti_(56.25-x)Zr_(x)Ni_(25)Cu1_(8.75)(x=0–25,at.%) filler metals were designed based on a cluster-plus-glue-atom model to vacuum braze TiAl intermetallic to K4169 alloy. The impact of Zr content on the inte...A series of Ti_(56.25-x)Zr_(x)Ni_(25)Cu1_(8.75)(x=0–25,at.%) filler metals were designed based on a cluster-plus-glue-atom model to vacuum braze TiAl intermetallic to K4169 alloy. The impact of Zr content on the interfacial microstructure and shear strength of joints was examined. And the relationship between the interfacial lattice structure and the fracture behavior of the joint was investigated. The findings reveal a sectionalized characteristic with three reaction zones (Zone I, Zone II and Zone III) in the microstructure of the TiAl intermetallic to K4169 alloy joint. As the Zr content in filler metals increased, the diffusion of Ti transitioned from long-distance to short-distance in Zone I, changing the initial composition from TiNi_(3) /TiNi/NiNb/(Cr, Fe, Ni)SS to NiCrFe/(Cr, Fe, Ni)SS /TiNi. In Zone II, the initial composition altered from TiNi_(3) /TiNi to TiNi/Ti_(2) Ni/TiNi_(3) /TiCu/TiNi. The interface between Zones II and III altered from a non-coherent and semi-coherent interface of TiNi/TiAl/Ti_(3) Al with significant residual stress to a semi-coherent interface of TiNi/TiNi_(3) /TiAl_(2) /Ti_(3) Al with a gradient distribution. The shear strength of the joint initially decreased and then increased. When the Zr content of filler metal was 25 at.%, the shear strength of the joint reached 288 MPa. The crack initiation position changed from non-coherent TiNi/TiAl interface with high angle grain boundaries (HAGBs) and lattice mismatch of 65.86 at.% to a semi-coherent Ti3 Al/TiAl2 interface with a lattice mismatch of 20.07 at.% when the Zr content increased. The brittle fracture was present on the fracture surfaces of all brazed joints.展开更多
文摘The structure characteristics of a2/γinterfaces and the features of deformation twins in a quasi-isothermal forged Ti-45Al-10Nb alloy were studied by highresolution transmission electron microscopy. Three types of strain induced a2/γinterfaces and two types of strain induced twin boundaries were identified The most,important features are high density of ledges and the existence of I/3[111] Frank partial dislocation. Mechanisms for the formation these interfaces were proposed Two types of deformation twins were observed These deformation twins always start from the ledges it seems that ledges at interfaces are important features of interfacial structure for the mechanical behavior of alloys.
基金supported by the National Natural Science Foun-dation of China(Nos.52275314 and 52075074)the Collaborative Innovation Center of Major Machine Manufacturing in Liaoning.
文摘A series of Ti_(56.25-x)Zr_(x)Ni_(25)Cu1_(8.75)(x=0–25,at.%) filler metals were designed based on a cluster-plus-glue-atom model to vacuum braze TiAl intermetallic to K4169 alloy. The impact of Zr content on the interfacial microstructure and shear strength of joints was examined. And the relationship between the interfacial lattice structure and the fracture behavior of the joint was investigated. The findings reveal a sectionalized characteristic with three reaction zones (Zone I, Zone II and Zone III) in the microstructure of the TiAl intermetallic to K4169 alloy joint. As the Zr content in filler metals increased, the diffusion of Ti transitioned from long-distance to short-distance in Zone I, changing the initial composition from TiNi_(3) /TiNi/NiNb/(Cr, Fe, Ni)SS to NiCrFe/(Cr, Fe, Ni)SS /TiNi. In Zone II, the initial composition altered from TiNi_(3) /TiNi to TiNi/Ti_(2) Ni/TiNi_(3) /TiCu/TiNi. The interface between Zones II and III altered from a non-coherent and semi-coherent interface of TiNi/TiAl/Ti_(3) Al with significant residual stress to a semi-coherent interface of TiNi/TiNi_(3) /TiAl_(2) /Ti_(3) Al with a gradient distribution. The shear strength of the joint initially decreased and then increased. When the Zr content of filler metal was 25 at.%, the shear strength of the joint reached 288 MPa. The crack initiation position changed from non-coherent TiNi/TiAl interface with high angle grain boundaries (HAGBs) and lattice mismatch of 65.86 at.% to a semi-coherent Ti3 Al/TiAl2 interface with a lattice mismatch of 20.07 at.% when the Zr content increased. The brittle fracture was present on the fracture surfaces of all brazed joints.