A phase inversion based sponge-like polysulfonamide/SiO_2 composite separator for high performance lithium-ion batteries

In this work,a sponge-like polysulfonamide(PSA)/SiO_2 composite membrane is unprecedentedly prepared by the phase inversion method,and successfully demonstrated as a novel separator of lithium-ion batteries(LIBs).Compared to the commercial polypropylene(PP) separator,the sponge-like PSA/SiO_2 composite possesses better physical and electrochemical properties,such as higher porosity,ionic conductivity,thermal stability and flame retarding ability.The LiCoO_2/Li half-cells using the sponge-like composite separator demonstrate superior rate capability and cyclability over those using the commercial PP separator.Moreover,the sponge-like composite separator can ensure the normal operation of LiCoO_2/Li half-cell at an extremely high temperature of 90 °C,while the commercial PP separator cannot.All these encouraging results suggest that this phase inversion based sponge-like PSA/SiO_2 composite separator is really a promising separator for high performance LIBs.

Four-channel catalytic micro-reactor based on alumina hollow fiber membrane for efficient catalytic oxidation of CO

The traditional automotive catalytic converter using commercial ceramic honeycomb carriers has many problems such as high back pressure,low engine efficiency,and high usage of precious metals.This study proposes a four-channel catalytic micro-reactor based on alumina hollow fiber membrane,which uses phase inversion method for structural molding and regulation.Due to the advantages of its carrier,it can achieve lower ignition temperature under low noble metal loading.With Pd/CeO_(2) at a loading rate of 2.3%(mass),the result showed that the reaction ignition temperature is even less than 160℃,which is more than 90℃ lower than the data of commercial ceramic substrates under similar catalyst loading and airspeed conditions.The technology in turn significantly reduces the energy consumption of the reaction.And stability tests were conducted under constant conditions for 1000 h,which proved that this catalytic converter has high catalytic efficiency and stability,providing prospects for the design of innovative catalytic converters in the future.

Preparation of Nano-MnFe2O4 and Its Catalytic Performance of Thermal Decomposition of Ammonium Perchlorate

Nano-MnFe2O4 particles were synthesized by co-precipitation phase inversion method and low-temperature combustion method respectively, using MnCl2, FeCl3, Mn（NO3）2, Fe（NO3）3, NaOH and C6H8O7. X-ray diffraction （XRD）, transmission electron microscope （TEM）, Fourier transform infrared spectroscopy （FT-IR）, thermogravim-etry-differential thermal analysis （TG-DTA） and differential scanning calorimetry （DSC） were used to characterize the structure, morphology, thermal stability of MnFe2O4 and its catalytic performance to ammonium perchlorate. Results showed that single-phased and uniform spinel MnFe2O4 was obtained. The average particle size was about 30 and 20 nm. The infrared absorption peaks appeared at about 420 and 574 cm-1, and the particles were stable below 524 ℃. Using the two prepared catalysts, the higher thermal decomposition temperature of ammonium perchlorate was decreased by 77.3 and 84.9 ℃ respectively, while the apparent decomposition heat was increased by 482.5 and 574.3 J？g？1. The catalytic mechanism could be explained by the favorable electron transfer space provided by outer d orbit of transition metal ions and the high specific surface absorption effect of MnFe2O4 particles.

Performance Improvement of Polyvinyl Formal Based Gel Polymer Electrolyte for Lithium-Ion Batteries by Coating Al2O3

Al2O3/PVFM/Al2O3 trilayer membranes are prepared by means of simple coating of PVA-Al2O3 solution onto both sides of PVFM thin membranes, which is prepared via phase inversion method. The characteristics of the trilayer membranes and gel polymer electrolytes are investigated using FESEM, tensile testing apparatus, thermal shrinkage test, EIS and charge-discharge test. When inorganic Al2O3 particles are used to coat the PVFM membrane, drawbacks associated with gel-type membranes, namely, poor mechanical strength and thermal stability are greatly improved. Lithium ion cell with the Al2O3/PVFM/Al2O3 based GPE matched with LiFePO4 shows excellent electrochemical performance.