In this study,Al–4Cu alloy specimens with spherical grains and liquid flms were obtained by isothermal reheating treatment.The hot cracking of the solidifcation process was determined using a modifed constrained rod ...In this study,Al–4Cu alloy specimens with spherical grains and liquid flms were obtained by isothermal reheating treatment.The hot cracking of the solidifcation process was determined using a modifed constrained rod casting experimental apparatus,and the efect of liquid flm characteristics at the end of solidifcation on hot cracking initiation of Al–4Cu alloys was systematically investigated by combining molecular dynamics simulations and other methods.With the extension of soaking time,the liquid fraction(liquid flm fraction at the end of solidifcation)and grain shape factor increased with higher isothermal reheating temperatures.Additionally,the widened flling channel decreased the hot cracking initiation temperature and the critical hot cracking shrinkage stress was found to increase,thus reducing the hot cracking severity in Al–4Cu alloys.Molecular dynamics simulations revealed that with the extension of soaking time,the composition of the liquid flm changed at diferent isothermal reheating temperatures,but the short-range structure and atomic ordering of the liquid flm remained the same.The activity of the liquid flm increased in equilibrium,leading to a decrease in viscosity and an increase in fuidity,which contributed to the flling behaviour.After isothermal reheating at 640℃for 60 min,the liquid fraction reached the maximum,and the viscosity of the liquid flm was the minimum.In addition,almost no hot cracks were found.展开更多
基金supported by the National Natural Science Foundation of China(No.51875365).
文摘In this study,Al–4Cu alloy specimens with spherical grains and liquid flms were obtained by isothermal reheating treatment.The hot cracking of the solidifcation process was determined using a modifed constrained rod casting experimental apparatus,and the efect of liquid flm characteristics at the end of solidifcation on hot cracking initiation of Al–4Cu alloys was systematically investigated by combining molecular dynamics simulations and other methods.With the extension of soaking time,the liquid fraction(liquid flm fraction at the end of solidifcation)and grain shape factor increased with higher isothermal reheating temperatures.Additionally,the widened flling channel decreased the hot cracking initiation temperature and the critical hot cracking shrinkage stress was found to increase,thus reducing the hot cracking severity in Al–4Cu alloys.Molecular dynamics simulations revealed that with the extension of soaking time,the composition of the liquid flm changed at diferent isothermal reheating temperatures,but the short-range structure and atomic ordering of the liquid flm remained the same.The activity of the liquid flm increased in equilibrium,leading to a decrease in viscosity and an increase in fuidity,which contributed to the flling behaviour.After isothermal reheating at 640℃for 60 min,the liquid fraction reached the maximum,and the viscosity of the liquid flm was the minimum.In addition,almost no hot cracks were found.