The magnetic properties and the phase transformation of the partial substitution of Pr for La in LaFe11.4Si1.6 have been investigated by the means of X-ray diffraction (XRD) and vibrating sample magnetic (VSM). The re...The magnetic properties and the phase transformation of the partial substitution of Pr for La in LaFe11.4Si1.6 have been investigated by the means of X-ray diffraction (XRD) and vibrating sample magnetic (VSM). The results indicated that the single phase NaZn13-type cubic structure is stabilized for the compound La0.8Pr0.2Fe11.4Si1.6 and large values of the isothermal magnetic entropy change SM around the curie temperature TC～194 K in relative low magnetic fields. The maximum value︱SM︱max～37.07 J/kg·K-1 under a field of 1.5 T. Such large MCEs are attributed to the sharp change of the magnetization at the Curie temperature, the field-induced IEM transition and a strong temperature dependence of the critical field BC.展开更多
Magnetic properties and magnetic entropy changes in LaFe11.5Si1.5 have been investigated by partially substituting Pr by La. It is found that La1-xPrxFe11.5Si1.5 compounds remain cubic NaZn13-type structures even when...Magnetic properties and magnetic entropy changes in LaFe11.5Si1.5 have been investigated by partially substituting Pr by La. It is found that La1-xPrxFe11.5Si1.5 compounds remain cubic NaZn13-type structures even when the Pr content is increased to 0.5, i.e. x = 0.5. Substitution of Pr for La leads to a reduction in both the crystal constant and the Curie temperature. A stepwise magnetic behaviour in the isothermal magnetization curves is observed, indicating that the characteristic of the itinerant electron metamagnetic （IEM） transition above Tc becomes more prominent with the Pr content increasing. As a result, the magnetic entropy change is remarkably enhanced from 23.0 to 29.4 J/kg·K as the field changes from 0 to 5T, with the value of x increasing from 0 to 0.5. It is more attractive that the magnetic entropy changes for all samples are shaped into high plateaus in a wide range of temperature, which is highly favourable for Ericsson-type magnetic refrigeration.展开更多
The crystal structure, itinerant-electron metamagnetic transition (IEMT) and magnetocaloric effect (MCE) in the iron-based rare-earth intermetallic compound La0.8Ce0.2Fe11.4Si1.6 have been investi- gated. The powder X...The crystal structure, itinerant-electron metamagnetic transition (IEMT) and magnetocaloric effect (MCE) in the iron-based rare-earth intermetallic compound La0.8Ce0.2Fe11.4Si1.6 have been investi- gated. The powder X-ray diffraction revealed that the ingot of La0.8Ce0.2Fe11.4Si1.6 annealed at 1373 K in vacuum for only 5 days could be crystallized in the cubic NaZn13-type structure. The La0.8Ce0.2Fe11.4Si1.6 compound exhibited giant values of the isothermal entropy change ?SM around the Curie temperature TC (about 186 K). And the maximum value ΔS M max is about 78.29 J/(kg·K) under a field change of 0—3 T, which can be calculated by the magnetization iso- therms around TC. Such a large MCE is attributed to the sharp change of magnetization and susceptibility around TC and the first-order magnetic transition of field-induced IEMT above TC.展开更多
The FeNi coated LaFe_(11.6)Si_(1.4)/Sn composites were prepared by hot pressing(HP). The microstructure,corrosion behavior and magnetocaloric effect(MCE) of FeNi coated LaFe_(11.6)Si_(1.4)/Sn composites were investiga...The FeNi coated LaFe_(11.6)Si_(1.4)/Sn composites were prepared by hot pressing(HP). The microstructure,corrosion behavior and magnetocaloric effect(MCE) of FeNi coated LaFe_(11.6)Si_(1.4)/Sn composites were investigated systematically. The results show that the corrosion resistance of FeNi coated LaFe_(11.6)Si_(1.4)Sn composites is better than that of LaFe_(11.6)Si_(1.4)/Sn composites in deionized water. The maximum magnetic entropy change((-△S_M)^(max)) and relative cooling power(RCP) of FeNi coated LaFe_(11.6)Si_(1.4)/Sn composites are 13.30 J/(kg-K) and 146.25 J/kg, respectively, which are larger than that((-△S_M)^(max), 10.65 J/(kg·K) and RCP, 106.53 J/kg) of LaFe_(11.6)Si_(1.4)/Sn composites in a low magnetic field change of 2 T. FeNi coated LaFe_(11.6)Si_(1.4)/Sn composites possess a more negative slope. The improvement of magnetic properties is due to high permeability FeNi permalloy(1 J85) which improves the itinerant-electron metamagnetic(IEM) transition. So, the method of coating FeNi can provide a new idea for enhancing the corrosion resistance and magnetocaloric effect of La(Fe_xSi_(1-x))_(13)-based materials.展开更多
基金Project supported by The National Natural Science Foundation of China (50164003)
文摘The magnetic properties and the phase transformation of the partial substitution of Pr for La in LaFe11.4Si1.6 have been investigated by the means of X-ray diffraction (XRD) and vibrating sample magnetic (VSM). The results indicated that the single phase NaZn13-type cubic structure is stabilized for the compound La0.8Pr0.2Fe11.4Si1.6 and large values of the isothermal magnetic entropy change SM around the curie temperature TC～194 K in relative low magnetic fields. The maximum value︱SM︱max～37.07 J/kg·K-1 under a field of 1.5 T. Such large MCEs are attributed to the sharp change of the magnetization at the Curie temperature, the field-induced IEM transition and a strong temperature dependence of the critical field BC.
基金Project supported by the National Natural Science Foundation of China （Grant No 50571112）, the National Basic Reseaxch Program of China （Grant No 2006CB601101） and the Program of Chinese Academy of Sciences （Grant No KJCX2-YW-W02）.
文摘Magnetic properties and magnetic entropy changes in LaFe11.5Si1.5 have been investigated by partially substituting Pr by La. It is found that La1-xPrxFe11.5Si1.5 compounds remain cubic NaZn13-type structures even when the Pr content is increased to 0.5, i.e. x = 0.5. Substitution of Pr for La leads to a reduction in both the crystal constant and the Curie temperature. A stepwise magnetic behaviour in the isothermal magnetization curves is observed, indicating that the characteristic of the itinerant electron metamagnetic （IEM） transition above Tc becomes more prominent with the Pr content increasing. As a result, the magnetic entropy change is remarkably enhanced from 23.0 to 29.4 J/kg·K as the field changes from 0 to 5T, with the value of x increasing from 0 to 0.5. It is more attractive that the magnetic entropy changes for all samples are shaped into high plateaus in a wide range of temperature, which is highly favourable for Ericsson-type magnetic refrigeration.
基金This work was supported by the National Natural Science Foundation of China （Grant No. 50164003）.
文摘The crystal structure, itinerant-electron metamagnetic transition (IEMT) and magnetocaloric effect (MCE) in the iron-based rare-earth intermetallic compound La0.8Ce0.2Fe11.4Si1.6 have been investi- gated. The powder X-ray diffraction revealed that the ingot of La0.8Ce0.2Fe11.4Si1.6 annealed at 1373 K in vacuum for only 5 days could be crystallized in the cubic NaZn13-type structure. The La0.8Ce0.2Fe11.4Si1.6 compound exhibited giant values of the isothermal entropy change ?SM around the Curie temperature TC (about 186 K). And the maximum value ΔS M max is about 78.29 J/(kg·K) under a field change of 0—3 T, which can be calculated by the magnetization iso- therms around TC. Such a large MCE is attributed to the sharp change of magnetization and susceptibility around TC and the first-order magnetic transition of field-induced IEMT above TC.
基金Project supported by the Key Project of National Natural Science Foundation of China(51176065)
文摘The FeNi coated LaFe_(11.6)Si_(1.4)/Sn composites were prepared by hot pressing(HP). The microstructure,corrosion behavior and magnetocaloric effect(MCE) of FeNi coated LaFe_(11.6)Si_(1.4)/Sn composites were investigated systematically. The results show that the corrosion resistance of FeNi coated LaFe_(11.6)Si_(1.4)Sn composites is better than that of LaFe_(11.6)Si_(1.4)/Sn composites in deionized water. The maximum magnetic entropy change((-△S_M)^(max)) and relative cooling power(RCP) of FeNi coated LaFe_(11.6)Si_(1.4)/Sn composites are 13.30 J/(kg-K) and 146.25 J/kg, respectively, which are larger than that((-△S_M)^(max), 10.65 J/(kg·K) and RCP, 106.53 J/kg) of LaFe_(11.6)Si_(1.4)/Sn composites in a low magnetic field change of 2 T. FeNi coated LaFe_(11.6)Si_(1.4)/Sn composites possess a more negative slope. The improvement of magnetic properties is due to high permeability FeNi permalloy(1 J85) which improves the itinerant-electron metamagnetic(IEM) transition. So, the method of coating FeNi can provide a new idea for enhancing the corrosion resistance and magnetocaloric effect of La(Fe_xSi_(1-x))_(13)-based materials.