The aim of this research work was to evaluate the potential of using renewable natural feedstock,i.e.,Jatropha curcas oil(JCO)for the synthesis of non-isocyanate polyurethane(NIPU)resin for wood composite applications...The aim of this research work was to evaluate the potential of using renewable natural feedstock,i.e.,Jatropha curcas oil(JCO)for the synthesis of non-isocyanate polyurethane(NIPU)resin for wood composite applications.Commercial polyurethane(PU)is synthesized through a polycondensation reaction between isocyanate and poly-ol.However,utilizing toxic and unsustainable isocyanates for obtaining PU could contribute to negative impacts on the environment and human health.Therefore,the development of PU from eco-friendly and sustainable resources without the isocyanate route is required.In this work,tetra-n-butyl ammonium bromide was used as the activator to open the epoxy ring with 3-Aminopropyltriethoxisylane as a catalyst to yield urethane of JCO(UJCO).The UJCO were characterized by Fourier Transform Infra-Red spectroscopy(FTIR)and their oxirane,and hydroxyl values were measured.The result showed that a decrease in oxirane value was found while the hydroxyl value was increased during the time,confirming that the urethane group was formed.The presence of functional groups in FTIR spectra at wave numbers 1732.08,1562.34,and 3348.42 cm^(−1) indicates the functional groups of C=O(urethane carbonyl),–NH,and–OH,respectively confirmed this finding.The potential applications of NIPU in the wood composite were also outlined.展开更多
The preparation and regeneration conditions of the identified catalyst X/Y/MgO/?-Al2O3 with high catalytic activity were studied and optimized. The biodiesel was prepared by transesterification of Jatropha curcas see...The preparation and regeneration conditions of the identified catalyst X/Y/MgO/?-Al2O3 with high catalytic activity were studied and optimized. The biodiesel was prepared by transesterification of Jatropha curcas seed oil produced in Guizhou with methanol at its reflux temoerature in the presence of X/Y/MgO/?-Al2O3 . The pilot plant tests were carried out in a 100 L reaction vessel. Both average yield and fatty acid methyl esters (FAME) content reached more than 96.50% under the optimum reaction conditions of the pilot plant tests designed with an oil/methanol molar ratio of 1 : 10, catalyst concentration of 1.00%, and reaction time of 3 h at reflux temperature. In addition, analysis shows that the quality of biodiesel meets the standard EN 14214.展开更多
A central composite rotatable design and response surface methodology were used in order to investigate the individual and combined effects of the ethanol-to-oil ratio, H2SO4 concentration, temperature and time of rea...A central composite rotatable design and response surface methodology were used in order to investigate the individual and combined effects of the ethanol-to-oil ratio, H2SO4 concentration, temperature and time of reaction on the reduction of free fatty acid （FFA） in jatropha oil. A quadratic polynomial model relating the reaction variables with FFA reduction was developed, presenting a good coefficient of determination （R2= 0.893）. For reducing FFA to less than 1%, the optimal combination was found to be 0.62 v.v^-1 ethanol-to-oil ratio （14.9 v.v^-1 ethanol-to-FFA ratio）, 1.7% v.vI H2SO4 concentration, and 79 rain reaction time at a reaction temperature of 54℃. These results are of great relevance to maximize methyl esters formation by transesterification using an alkaline catalyst.展开更多
文摘The aim of this research work was to evaluate the potential of using renewable natural feedstock,i.e.,Jatropha curcas oil(JCO)for the synthesis of non-isocyanate polyurethane(NIPU)resin for wood composite applications.Commercial polyurethane(PU)is synthesized through a polycondensation reaction between isocyanate and poly-ol.However,utilizing toxic and unsustainable isocyanates for obtaining PU could contribute to negative impacts on the environment and human health.Therefore,the development of PU from eco-friendly and sustainable resources without the isocyanate route is required.In this work,tetra-n-butyl ammonium bromide was used as the activator to open the epoxy ring with 3-Aminopropyltriethoxisylane as a catalyst to yield urethane of JCO(UJCO).The UJCO were characterized by Fourier Transform Infra-Red spectroscopy(FTIR)and their oxirane,and hydroxyl values were measured.The result showed that a decrease in oxirane value was found while the hydroxyl value was increased during the time,confirming that the urethane group was formed.The presence of functional groups in FTIR spectra at wave numbers 1732.08,1562.34,and 3348.42 cm^(−1) indicates the functional groups of C=O(urethane carbonyl),–NH,and–OH,respectively confirmed this finding.The potential applications of NIPU in the wood composite were also outlined.
基金supported by the Key Science and Technology Project of Guizhou(No.20076004).
文摘The preparation and regeneration conditions of the identified catalyst X/Y/MgO/?-Al2O3 with high catalytic activity were studied and optimized. The biodiesel was prepared by transesterification of Jatropha curcas seed oil produced in Guizhou with methanol at its reflux temoerature in the presence of X/Y/MgO/?-Al2O3 . The pilot plant tests were carried out in a 100 L reaction vessel. Both average yield and fatty acid methyl esters (FAME) content reached more than 96.50% under the optimum reaction conditions of the pilot plant tests designed with an oil/methanol molar ratio of 1 : 10, catalyst concentration of 1.00%, and reaction time of 3 h at reflux temperature. In addition, analysis shows that the quality of biodiesel meets the standard EN 14214.
文摘A central composite rotatable design and response surface methodology were used in order to investigate the individual and combined effects of the ethanol-to-oil ratio, H2SO4 concentration, temperature and time of reaction on the reduction of free fatty acid （FFA） in jatropha oil. A quadratic polynomial model relating the reaction variables with FFA reduction was developed, presenting a good coefficient of determination （R2= 0.893）. For reducing FFA to less than 1%, the optimal combination was found to be 0.62 v.v^-1 ethanol-to-oil ratio （14.9 v.v^-1 ethanol-to-FFA ratio）, 1.7% v.vI H2SO4 concentration, and 79 rain reaction time at a reaction temperature of 54℃. These results are of great relevance to maximize methyl esters formation by transesterification using an alkaline catalyst.