Fatigue Crack Growth Behavior of Different Zones in an Annealed Automatic Gas Tungsten Arc Weld Joint of TA16 and TC4 Titanium Alloys

Based on the investigated microstructure of different zones in the annealed automatic gas tungsten arc weld joint of TA16 and TC4 titanium alloys,the mechanical property of them was assessed under fatigue crack growth rate tests.For evaluation of fatigue crack growth rate,three points bending specimens were used.The correlation between the range of stress intensity factor and crack growth rate was determined in different zones of the annealed weld joint.Fatigue crack growth rates were obviously different in different zones of weld joint of dissimilar titanium alloys,due to their different microstructures.Scanning electron microscope examinations were conducted on the fracture surface in order to determine the relevant fracture mechanisms and crack growth mechanisms with respect to the details of microstructure.

铁素体──马氏体双相钢焊接接头的应力腐蚀

在慢应变速率条件下，研究了Ｆｅ－Ｓｉ－Ｃ系铁素体－马氏体双相钢焊接接头在人造海水中的应力腐蚀开裂（ＳＣＣ）行为。用单边预裂纹拉伸试样测定了焊接接头各部位的应力强度因子Ｋ１值。结果表明，焊接接头各部位在人造海水中的应力腐蚀开裂敏感性有很大差异，其中热影响区（ＨＡＺ）对ＳＣＣ最敏感，Ｋ１值最低；随着阴极电位朝负方向增加，ＳＣＣ敏感性增大；除氢处理可以改善焊接接头的ＳＣＣ抗力。

高压导管F11钢焊接裂纹分析及返修

通过对高压导管焊缝裂纹的情况核实,决定采用焊接挖补的方法进行修复。为此对母材金属F11钢的焊接性和焊补工艺特点进行详细分析,制定合理的焊接及热处理规范,以保证挖补焊接修复的效果;并针对根部间隙较宽的实际情况,探索F11钢厚壁管的宽间隙补焊方法,采用TIG焊的双层打底焊接,证明了在高合金钢的焊接中,在保证氩气保护措施严密的基础上,采用TIG焊双层打底焊的方法,更好的保证了焊接质量,减少了焊接缺陷的产生,获得了较好的效果。