Postsynthesis of hierarchical core/shell ZSM-5 as an efficient catalyst in ketalation and acetalization reactions

Hierarchical core/shell Zeolite Socony Mobil-five(ZSM-5)zeolite was hydrothermally postsythesized in the solution of NaOH and diammonium surfactant via a dissolution-reassembly strategy.The silica and alumina species were firstly dissolved partially from the bulky ZSM-5 crystals and then were reassembled into the MFI-type nanosheets with the structure-directing effect of diammonium surfactant,attaching to the out-surface of ZSM-5 core crystals.The mesopores thus were generated in both the core and shell part,giving rise to a micropore/mesopore composite material.The micropore volume and the acidity of the resultant hybrid were well-preserved during this recrystallization process.Possessing the multiple mesopores and enlarged external surface area,the core/shell ZSM-5 zeolite exhibited higher activity in the ketalation and acetalization reactions involving bulky molecules in comparison to the pristine ZSM-5.

Catalytic synthesis of cyclohexanone 1,2-propanediol ketal with H_4SiW_(12)O_(40)/PAn

A new environmental friendly catalyst, H_4SiW_(12)O_(40)/PAn was prepared andidentified by means of FT-IR, XRD and TG/DTA. Cyclohexanone 1,2-propanediol ketal was synthesizedfrom cyclohexanone and 1,2-propanediol in the presence of H_4SiW_(12)O_(40)/PAn The factorsinfluencing tlie synthesis were discussed and the best conditions were found out. The optimumconditions are: molar ratio of cyclohexanone to 1,2-propanediol is 1:1.4, the quantity of catalystis equal to 1.0 percent of feed stocks, and the reaction time is 40 min. H_4SiW_(12)O_(40)/PAn is anexcellent catalyst for synthesizing cyclohexanone 1,2-propanediol ketal and its yield can reachover 96.5 percent.

Eco-friendly one-pot synthesis of acetals and ketals by heterogeneously catalyzed liquid-solid phase reaction

Twelve classes of acetals and ketals were synthesized from aldehyde/ketone and glycol using ZiSiW12O40/TiO2 as a novel eco-friendly catalyst. The physical characterizations were carried out by TG/DTA, FT-IR, XRD, and ^1H NMR spectra. The results indicated that the catalyst showed excellent catalytic activity for the condensation reactions. The yield of 12 classes of acetals and ketals reached 56.3%-96.3% under the typical reaction conditions （the molar ratio of aldehyde/ketone and glycol was 1：1.5, the quantity of catalyst was 0.5% of feed stock, the reaction time was 1.0 h, and the reaction temperature was 80-116℃）. The catalyst was easily recovered and reused to give almost the same yield of the product as that given by fresh TiSiW12O10/TiO2.

H4SiW6Mo6O40-Doped Polyaniline-Synthesis, characterization and catalytic properties of acetals and ketals

A new environmental friendly catalyst, HaSiWrMo6O40/PAn was prepared and identified by means of FT-IR, XRD and TG/DTA. The optimum conditions have been found, that was, mass ratio of m（PAn）： m（HaSiW6Mo6On.） was 1：1.25, volume of methanol was 20 mL, and the reflux reaction time was 2h. The structural identity of Keggin units was preserved after the incorporation into polyaniline matrix. H4SiW6Mo6040/PAn was used as catalyst in catalytic synthesis of acetals and ketals. Effects of n（aldehyde（ketone ））： n（glycol）, catalyst dosage and reaction time on yield were investingated. Optimal conditions were： n（aldehyde（ketone））： n（glycol）=1.0： 1.5; mass fraction of catalyst to reactants, 0.5%; reaction time, 1.0 h and cyclohexane as water-stripped reagent, 15 mL. Under these conditions, yields of actels and ketals were 31.9%-91.6%.

Catalytic synthesis of acetals and ketals with H3PW6Mo6O40/TiO2

A new environmental friendly catalyst, H3PW6Mo6O40/TiO2 was prepared. The optimum conditions have been found, that is, mass ratio of m （TiO2）： m （H3PW6Mo6O40） is 1：2.0, volume of water is 30 mL, the reflux reaction time is 2 h, and activated temperature is 150 ℃. H3PW6Mo6O40/TiO2 was used as catalyst in catalytic synthesis ofacetals and ketals. Effects ofn （aldehyde（ketone））： n （glycol）, catalyst dosage and reaction time on yield were investigated. Optimal conditions were： n（aldehyde （ketone））： n （glycol）=1.0 ： 1.4; mass fraction of catalyst to reactants, 0.8%; reaction time, 1.0 h and cyclohexane as water-stripped reagent, 10 mL. Under these conditions, yields of acetals and ketals can reach 53.0% -86.9 0%

杂多酸(HPA)催化制取环缩酮和缩醛

本文在文[1—4]的基础上,报导以杂多酸为催化剂制取环缩酮和缩醛。杂多酸是一种固体酸,是近年来国内外学者广泛关注的多功能催化剂,可作为固体酸催化剂进行酯化、醇脱水、烯烃水合制醇、烯烃加醇制醚以及付克烷基化反应等;

Catalytic synthesis of acetals and ketals with H3PW12O40/PAn

A new environmental friendly catalyst H3PW12O40/PAn was prepared and identified by means of FT-IR,XRD,and TG/DTA.The optimum conditions have been found;that is,the mass ratio of PAn to H3PW12O40 is 1：1.5,the volume of methanol is 20 mL,and the reflux reaction time is 3 h.The structural identity of Keggin units is preserved after the incorporation into polyaniline matrix.Catalytic activities of H3PW12O40/PAn in synthesizing 2-methyl-2-ethoxycarbonylmethyl-1,3-dioxolane,2,4-dimethyl-2-ethoxycarbonylmethyl-1,3-dioxolane,cyclohexanone ethylene ketal,cyclohexanone 1,2-propanediol ketal,butanone ethylene ketal,butanone 1,2-propanediol ketal,2-phenyl-1,3-dioxolane,4-methyl-2-phenyl-1,3-dioxolane,2-propyl-1,3-dioxolane,and 4-methyl-2-propyl-1,3-dioxolane were reported.It has been demon-strated that H3PW12O40/PAn is an excellent catalyst.Various factors concerned in these reactions were investigated.The optimum conditions are as follows：the molar ratio of aldehyde/ketone to glycol（r） is 1：1.5,the mass ratio of the catalyst used to the reactants is 0.6%,and the reaction time is 1.0 h.Under these conditions,the yield is as follows：2-methyl-2-ethoxycarbonylmethyl-1,3-dioxolane,69.0%;2,4-dimethyl-2-ethoxycarbonylmethyl-1,3-dioxolane,79.5%;cyclohexanone ethylene ketal,78.9%;cyclohexanone 1,2-propanediol ketal,85.3%;butanone ethylene ketal,56.9%;butanone 1,2-propanediol ketal,78.1%;2-phenyl-1,3-dioxolane,76.3%;4-methyl-2-phenyl-1,3-dioxolane,94.2%;2-propyl-1,3-dioxolane,70.7%;and 4-methyl-2-propyl-1,3-dioxolane,79.2%.

Synthesis of acetals and ketals catalyzed by tungstosilicic acid supported on active carbon

Catalytic activity of activated carbon supported tungstosilicic acidin synthesizing 2-methyl-2-ethoxycarbonylmethyl- 1,3-dioxolane, 2,4-dimethyl-2-ethoxycarbonylmethyl-1,3-dioxolane, cyclohexanone ethylene ketal, cyclohexanone 1,2-propa- nediol ketal, butanone ethylene ketal, butanone 1,2-propanediol ketal, 2-phenyl-1,3-dioxolane, 4-methyl-2-phenyl-1,3-dioxolane, 2-propyl-1,3-dioxolane, 4-methyl-2-propyl-1,3-dioxolane was reported. It has been demonstrated that activated carbon supported tungstosilicic acid is an excellent catalyst. Various factors involved in these reactions were investigated. The optimum conditions found were: molar ratio of aldehyde/ketone to glycol is 1/1.5, mass ratio of the catalyst used to the reactants is 1.0%, and reaction time is 1.0 h. Under these conditions, the yield of 2-methyl-2-ethoxycarbonylmethyl-1,3-dioxolane is 61.5%, of 2,4-dimethyl- 2-ethoxycarbonylmethyl-1,3-dioxolane is 69.1%, of cyclohexanone ethylene ketal is 74.6%, of cyclohexanone 1,2-propanediol ketal is 80.1%, of butanone ethylene ketal is 69.5%, of butanone 1,2-propanediol ketal is 78.5%, of 2-phenyl-1,3-dioxolane is 56.7%, of 4-methyl-2-phenyl-1,3-dioxolane is 86.2%, of 2-propyl-1,3-dioxolane is 87.5%, of 4-methyl-2-propyl-1,3-dioxolane is 87.9%.

Tungstophosphoric heteropolyacid supported onto neutral alumina: characterization and synthesis of acetals and ketals

Tungstophosphoric acid （HPW） catalyst supported on the neural alumina was studied. It was prepared by means of an equilibrium and incipient wetness impregnation technique. Solution of HPW in 50% V/V ethanol-water was used to impregnate Al2O3 at 25℃. It was found that the catalyst containing 30% PW by calcination at 500℃ showed a higher catalytic activity in the synthesis of acetals and/or ketals. In the following condition, that is, the molar ratio of aldehyde/ketone to glycol being 1：1.5, the mass fraction of the catalyst used was 0.5%, and the reaction time was 1.0 h; the yields of ketals and acetals could reach up to 60.5%-86.7%. Moreover, it could be easily recovered and reused.

Polyaniline Supported 12-Tungstosilicic Acid as the Catalyst for Acetals and Ketals Synthesis

A novel environmental friendly catalyst, H4SiW12O40/PAn was prepared and identified by FT-IR, XRD and TG/DTA. The optimal synthetic protocol was a PAn to H4SiW12O40 mass ratio of 1 ： 1, a 20 mL of methanol and a reaction time of 2 h at reflux. It was used in catalytic synthesis of ten important ketals and acetals with a high catalytic activity. With an aldehyde/ketone to glycol molar ratio of 1 ： 1.5 and a 1 wt% catalyst loading, the yields of ketals and acetals could reach 60.0%- 93.8 % after 1 h.

PHOTOINITIATED CROSSLINKING OF EPDM/INORGANIC FILLER BLENDS AND CHARACTERIZATION OF RELATED PROPERTIES

Photoinitiated crosslinking of ethylene-propylene-diene terpolymer （EPDM） blends filled with calcium carbonate, talc and calcined kaolin （CK） in the presence of benzil dimethyl ketal as photoinitiator and trimethylolpropane triacrylate as crosslinker and their related properties have been studied by different analytical methods, The results from gel content and heat extension determination show that the efficiency ofphotocrosslinking of EPDM increases with increasing the content of diene and its molecular weight. The EPDM blends with 100 phr different inorganic fillers can be photocrosslinked to gel content of above 60% by 5 s UV-irradiation under optimum conditions. Under the same conditions of irradiation, the orders of photocrosslinking rate and final gel content are EPDM/CaCO3 〉 EPDM/talc 〉 EPDM/CK. The data from thermogravimetric analysis, dynamic mechanical thermal analysis, electrical properties, mechanical tests and scanning electron microscopy show that UV irradiation crosslinking apparently enhances the thermal stability, mechanical properties and electrical properties of the photocrosslinked EPDM/inorganic filler samples. Although the attenuated total-reflection FTIR data show that inorganic fillers can promote the surface photo-oxidation of EPDM/inorganic filler samples with increasing the irradiation time, the above related properties of the photocrosslinked EPDM blends irradiated within 5 s are enough to satisfy many applications in the cable industry.

Vapor-Phase Transport Synthesis of MnSAPO-34 and Its Catalytic Properties

MnSAPO-34 molecular sieves were synthesized by vapor-phase transport （VPT） method using triethylamine （Et3N） as a structure directing agent （SDA）, and were characterized by XRD, BET, SEM, UV-Vis, FT-IR, and TG analy- ses. The influence of the zeolite crystallization conditions and the dry-gel composition were investigated. The results showed that the synthesis conditions had an effect on the crystalline phase. Pure MnSAPO-34 had been obtained when it was crystallized at 140 C for 18 hours. The ratio of MnO/A1203 in the starting gel ranging from 0.1 to 0.2 resulted in pure MnSAPO-34 with a CHA topology. Beyond this scope, MnSAPO-5 with an AFI topology structure was obtained as an impurity substance. UV-Vis spectroscopy and FT-IR spectroscopy study indicated that manganese was incorporated into the framework of the molecular sieve. The catalytic performance of MnSAPO-34 molecular sieve was tested by ketalization reaction of l, 2-propanediol with cyclohexanone. High yield of cyclohexanone-1, 2-propanediol ketal was obtained.

Zeolite-Catalyzed Acetalization Ⅰ. Synthesis of Some Acetals and Ketals through Reaction of Carbonyl Compounds with Ethanediol

The acetalization of a series of carbonyl compounds with ethanediolwas performed over two self-steaxned HY zeolle catalpsts' The acetal and ketaiproducts were obtained with high ytelds Espectw, the HY zeollte with highfraxnework Si/A1 ratio was proven to be suitable cataipst for the acetabotion ofunsaturated carbonyl compounds, during which the C =C double bond was notperturbed

Solventless ketalization of glycerol to solketal with acetone over the ionic liquid[P(C4H9)3C14H29][TsO]

The ketalization of glycerol with acetone was conducted over an ionic liquid[P(C4H9)3C14H29][TsO](TTPT)in a batch reactor.A scheme to obtain the purified product using TTPT as a homogeneous catalyst is proposed and a maximum solketal yield of 86%is achieved at acetone/glycerol molar ratio of 6/1,reaction time of 0.5 h,reaction temperature of 303 K,catalyst amount of 5 wt%of glycerol.TTPT was recycled and reused for ten times without obvious losses in terms of quantity and activity.Furthermore,effects of various experimental parameters(stirring speed,catalyst loadings,temperature and reactant composition)on the reaction kinetics are investigated.In terms of kinetics modeling,Kγis fitted by reactant composition at the temperature range 298 K–323 K,which was a concise strategy that showed good precision in the kinetics fitting.The activation energy for this ketalization reaction was evaluated to be 28.2 kJ·mol^-1.In addition,the kinetics of the reaction at a temperature exceeding the boiling point of acetone were also studied.We believe that all the results are important for further development of a technology for the continuous synthesis of solketal.

An Efficient Cleavage of 1,3-Dioxolane Using ZnCl_2/THF/H_2O

A new. mild and efficient method for the cleavage of 1,3-dioxolane is reported.

A Novel Synthesis of 3-O-Allyl-4,5,6-tri-O-benzyl-1-O-(p-methoxybenzyl)-D-myo-inositol

Highly efficient synthesis of the entitled compound was achieved from a readily availablemyo-inositol derivative. The key step involved a desymmetrization with (+)-camphor dimethylketal to give two diastereomers. The two diastereomers could be used to synthesize the samecompound by changing the orders to introduce the protective groups.

A NEW METHOD FOR AROMATIZAT ION OF Δ^(5(10))-STEROIDAL C_(3)-DIMETHYL KETALS

A new method for aromatization of Δ^(5(10))-steroidal C_3-dimethyl ketals with pyridinium hydrobromide perbromide (PHP.Py·HBr·Br_2) to aromatic A ring steroids in high yield (90-95%) is described.

DEPROTECTION OF ACETALS AND KETALS WITH CpTiCl_3-KI

When the mixture of CpTiCl_3-KI is used, many acetals and ketals, which are difficuitly deprotected with CpTiCl_3 alone, can be easily converted to the corresponding carbonyl compounds in high yield at 30℃ in Et_2O.