The phenolic resin-chloroprene nthher was used for sandwich in manufueturing the vibra-tion damping laminated steel sheet (also calied laminated sheet), Il is a metal matrix com-posite. The tensie-shear tests have bee...The phenolic resin-chloroprene nthher was used for sandwich in manufueturing the vibra-tion damping laminated steel sheet (also calied laminated sheet), Il is a metal matrix com-posite. The tensie-shear tests have been conducted over a range of temperatures from 20C to 150C and at the strain rates from 1.67× 10 ^(5) to 1.67× 10^(-2)s^(-1). The results show that test temperature will significaiilly affect the tensile shear strength of laminated sheet. and a minimal strength and a minimal activation energy occur near 80C . The tensile-shear breaking morphology of laminated sheet varies with strain rate and test temjteralurc.展开更多
The tensile-shear failure zone of the laminated damping steel sheet was investigated by scanning electron microscopy and X-ray photoelectron spectroscopy. It is found that there exists cohesive failure in polymer sand...The tensile-shear failure zone of the laminated damping steel sheet was investigated by scanning electron microscopy and X-ray photoelectron spectroscopy. It is found that there exists cohesive failure in polymer sandwich and sub-boundary failure between the steel sheet and the polymer. The sub-boundary layer is dominantly polymer material. The tensile-shear failure of the laminated damping steel sheet is a process during which the crazes form, grow up and merge into cracks.展开更多
The ANSYS simulation software was used to analyze the bending formability of laminate steel/resin/steel lightweight composite sheet. The skin steel at external side produces relative slipping-off change during the ben...The ANSYS simulation software was used to analyze the bending formability of laminate steel/resin/steel lightweight composite sheet. The skin steel at external side produces relative slipping-off change during the bending due to its composite structure. The internal stress strain states, materials effect tools parameters and intermediate layer resin of lightweight sheet on slipping-off change were analyzed. The spring back and shear stress state after bending have also been discussed.展开更多
文摘The phenolic resin-chloroprene nthher was used for sandwich in manufueturing the vibra-tion damping laminated steel sheet (also calied laminated sheet), Il is a metal matrix com-posite. The tensie-shear tests have been conducted over a range of temperatures from 20C to 150C and at the strain rates from 1.67× 10 ^(5) to 1.67× 10^(-2)s^(-1). The results show that test temperature will significaiilly affect the tensile shear strength of laminated sheet. and a minimal strength and a minimal activation energy occur near 80C . The tensile-shear breaking morphology of laminated sheet varies with strain rate and test temjteralurc.
文摘The tensile-shear failure zone of the laminated damping steel sheet was investigated by scanning electron microscopy and X-ray photoelectron spectroscopy. It is found that there exists cohesive failure in polymer sandwich and sub-boundary failure between the steel sheet and the polymer. The sub-boundary layer is dominantly polymer material. The tensile-shear failure of the laminated damping steel sheet is a process during which the crazes form, grow up and merge into cracks.
文摘The ANSYS simulation software was used to analyze the bending formability of laminate steel/resin/steel lightweight composite sheet. The skin steel at external side produces relative slipping-off change during the bending due to its composite structure. The internal stress strain states, materials effect tools parameters and intermediate layer resin of lightweight sheet on slipping-off change were analyzed. The spring back and shear stress state after bending have also been discussed.