Different effect of NiMnCo or FeNiCo on the growth of type-Ⅱa large diamonds with Ti/Cu as nitrogen getter

In order to synthesize high-quality type-Ⅱa large diamond, the selection of catalyst is very important, in addition to the nitrogen getter. In this paper, type-IIa large diamonds are grown under high pressure and high temperature（HPHT） by using the temperature gradient method（TGM）, with adopting Ti/Cu as the nitrogen getter in Ni70Mn25Co5（abbreviated as NiMnCo） or Fe（55）Ni（29）Co（16）（abbreviated FeNiCo） catalyst. The values of nitrogen concentration（Nc） in both synthesized high-quality diamonds are less than 1 ppm, when Ti/Cu（1.6 wt%） is added in the FeNiCo or Ti/Cu（1.8 wt%） is added in the NiMnCo. The difference in solubility of nitrogen between both catalysts at HPHT is the basic reason for the different effect of Ti/Cu on eliminating nitrogen. The nitrogen-removal efficiency of Ti/Cu in the NiMnCo catalyst is less than in the FeNiCo catalyst. Additionally, a high-quality type-Ⅱa large diamond size of 5.0 mm is obtained by reducing the growth rate and keeping the nitrogen concentration of the diamond to be less than 1 ppm, when Ti/Cu（1.6 wt%） is added in the FeNiCo catalyst.

Effect of FeS doping on large diamond synthesis in FeNi-C system

The large single-crystal diamond with FeS doping along the （111） face is synthesized from the FeNi-C system by the temperature gradient method （TGM） under high-pressure and high-temperature （HPHT）. the effects of different FeS additive content on the shape, color, and quality of diamond are investigated. It is found that the （111） face of diamond is dominated and the （100） face of diamond disappears gradually with the increase of the FeS content. At the same time, the color of the diamond crystal changes from light yellow to gray-green and even gray-yellow. The stripes and pits corrosion on the diamond surface are observed to turn worse. The effects of FeS doping on the shape and surface morphology of diamond crystal are explained by the number of hang bonds in different surfaces of diamond. It can be shown from the test results of the Fourier transform infrared （FTIR） spectrum that there exists an S element in the obtained diamond. The N element content values in different additive amounts of diamond are calculated. The XPS spectrum results demonstrate that our obtained diamond contains S elements that exist in S-C and S-C-O forms in a diamond lattice. This work contributes to the further understanding and research of FeS-doped large single-crystal diamond characterization.

Effects of additive NaN_3 on the HPHT synthesis of large single crystal diamond grown by TGM

In this paper,large single crystal diamond with perfect shape and high nitrogen concentration approximately 1671-1742 ppm was successfully synthesized by temperature gradient method (TGM) under high pressure and high temperature (HPHT).The HPHT synthesis conditions were about 5.5 GPa and 1500-1550 K.Sodium azide (NaN3) with different amount was added as the source of nitrogen into the synthesis system of high pure graphite and kovar alloy.The effects of additive NaN3 on crystal growth habit were investigated in detail.The crystal morphology,nitrogen concentration and existing form in synthetic diamond were characterized by means of scanning electron microscope (SEM) and infrared (IR) absorption spectra,respectively.The results show that with an increase of the content of NaN3 added in the synthesis system,the region of synthesis temperature for high-quality diamond becomes narrow,and crystal growth rate is restricted,whereas the nitrogen concentration in synthetic diamond increases.Nitrogen exists in diamond mainly in dispersed form (C-centers) and partially aggregated form (A-centers).The defects occur more frequently on crystal surface when excessive NaN3 is added in the synthesis system.