In this study,the Mg-3Zn-0.5Zr-χNd(χ=0,0.6)alloys were subjected to final rolling treatment with large deformation of 50%.The impact of annealing temperatures on the microstructure and mechanical properties was inve...In this study,the Mg-3Zn-0.5Zr-χNd(χ=0,0.6)alloys were subjected to final rolling treatment with large deformation of 50%.The impact of annealing temperatures on the microstructure and mechanical properties was investigated.The rolled Mg-3Zn-0.5Zr-0.6Nd alloy exhibited an ultimate tensile strength of 386 MPa,a yield strength of 361 MPa,and an elongation of 7.1%.Annealing at different temperatures resulted in reduced strength and obviously increased elongation for both alloys.Optimal mechanical properties for the Mg-3Zn-0.5Zr-0.6Nd alloy were achieved after annealing at 200℃,with an ultimate tensile strength of 287 MPa,a yield strength of 235 MPa,and an elongation of 26.1%.The numerous deformed microstructures,twins,and precipitated phases in the rolled alloy could impede the deformation at room temperature and increase the work hardening rate.After annealing,a decrease in the work hardening effect and an increase in the dynamic recovery effect were obtained due to the formation of fine equiaxed grains,and the increased volume fraction of precipitated phases,which significantly improved the elongation of the alloy.Additionally,the addition of Nd element could enhance the annealing recrystallization rate,reduce the Schmid factor difference between basal and prismatic slip systems,facilitate multi-system slip initiation and improve the alloy plasticity.展开更多
As the traditional forging process has many problems such as low efficiency, high consumption of material and energy, large cylindrical shell rolling is introduced. Large cylindrical shell rolling is a typical rotary ...As the traditional forging process has many problems such as low efficiency, high consumption of material and energy, large cylindrical shell rolling is introduced. Large cylindrical shell rolling is a typical rotary forming technology, and the upper and lower rolls have different radii and speeds. To quickly predict the three-dimensional stresses and eliminate fishtail defect, an improved strip layer method is developed, in which the asymmetry of the upper and lower rolls, non-uniform deformation and stress, as well as the asymmetrical spread on the end surface are considered. The deformation zone is divided into a certain number of layers and strips along the thickness and width, respectively. The transverse displacement model is constructed by polynomial function, in order to increase the computation speed greatly. From the metal plastic mechanics principle, the three-dimensional stress models are established. The genetic algorithm is used for optimization calculation in an industrial experiment example. The results show that the rolling pressure, the normal stresses, the upper and lower friction stress distributions are not similar with those of a general plate rolling. There are two relative maximum values in rolling pressure distribution. The upper and lower longitudinal friction stresses change direction nearby the upper and lower neutral points, respectively. The fishtail profile of spread on the end surface is predicted satisfactorily. The reduction could be helpful to eliminate fishtail defect. The large cylindrical shell rolling example illustrates the calculation results acquired rapidly are good agreements with the finite element simulation and experimental values of previous study. A highly effective and reliable three-dimensional simulation method is proposed for large cylindrical shell rolling and other asymmetrical rolling.展开更多
A gyro-stabilizer is the interesting system that it can apply to marine vessels for diminishes roll motion.Today it has potentially light weight with no hydrodynamics drag and effective at zero forward speed.The...A gyro-stabilizer is the interesting system that it can apply to marine vessels for diminishes roll motion.Today it has potentially light weight with no hydrodynamics drag and effective at zero forward speed.The twin-gyroscope was chosen.Almost,the modelling for designing the system use linear model that it might not comprehensive mission requirement such as high sea condition.The non-linearity analysis was proved by comparison the results between linear and non-linear model of gyro-stabilizer throughout frequency domain also same wave input,constrains and limitations.Moreover,they were cross checked by simulating in time domain.The comparison of interested of linear and non-linear close loop model in frequency domain has demonstrated the similar characteristics but gave different values at same frequency obviously.The results were confirmed again by simulation in irregular beam sea on time domain and they demonstrate the difference of behavior of both systems while the gyro-stabilizers are switching on and off.From the resulting analysis,the non-linear gyro-stabilizer model gives more real results that correspond to more accuracy in a designing gyro-stabilizer control system for various amplitudes and frequencies operating condition especially high sea condition.展开更多
Considering the characteristics of large cylindrical shell rolling, such as double driving rolls, asymmetrical rolling and huge workpiece, a slab method was developed to establish the rolling force model. In this mode...Considering the characteristics of large cylindrical shell rolling, such as double driving rolls, asymmetrical rolling and huge workpiece, a slab method was developed to establish the rolling force model. In this model, the non- uniform normal and shear stresses and the upper and lower surface temperatures of the workpiece were taken into ac- count. Moreover, the flow stress model, considering the dynamic recovery and dynamic recrystallization behaviors of the material, was established. The rolling pressure distribution, the rolling force, the rolling torque and the neutral points could be calculated quickly and easily by the roiling force model. The predicted results were shown to be in good agreement with the measured values, which indicated that the model can satisfy the requirement of industrial application.展开更多
基金Project(202203021221088)supported by the Fundamental Research Program of Shanxi Province,ChinaProject(20230010)supported by the Fund Program for the Scientific Activities of Selected Returned Overseas Professionals in Shanxi Province,China+5 种基金Project(202201050201012)supported by the Shanxi Provincial Science and Technology Major Special Project Plan of Taking the Lead in Unveiling the List,ChinaProject(2023-063)supported by the Research Project Supported by Shanxi Scholarship Council of ChinaProjects(51771129,52271109)supported by the National Natural Science Foundation of ChinaProject(2021YFB3703300)supported by the National Key Research and Development Program for Young Scientists,ChinaProject(YDZJSX2021B019)supported by the Special Fund Project for Guiding Local Science and Technology Development by the Central Government,ChinaProject(SKL-YSJ202103)supported by the Open Foundation of State Key Laboratory of High-end Compressor and System Technology,China。
文摘In this study,the Mg-3Zn-0.5Zr-χNd(χ=0,0.6)alloys were subjected to final rolling treatment with large deformation of 50%.The impact of annealing temperatures on the microstructure and mechanical properties was investigated.The rolled Mg-3Zn-0.5Zr-0.6Nd alloy exhibited an ultimate tensile strength of 386 MPa,a yield strength of 361 MPa,and an elongation of 7.1%.Annealing at different temperatures resulted in reduced strength and obviously increased elongation for both alloys.Optimal mechanical properties for the Mg-3Zn-0.5Zr-0.6Nd alloy were achieved after annealing at 200℃,with an ultimate tensile strength of 287 MPa,a yield strength of 235 MPa,and an elongation of 26.1%.The numerous deformed microstructures,twins,and precipitated phases in the rolled alloy could impede the deformation at room temperature and increase the work hardening rate.After annealing,a decrease in the work hardening effect and an increase in the dynamic recovery effect were obtained due to the formation of fine equiaxed grains,and the increased volume fraction of precipitated phases,which significantly improved the elongation of the alloy.Additionally,the addition of Nd element could enhance the annealing recrystallization rate,reduce the Schmid factor difference between basal and prismatic slip systems,facilitate multi-system slip initiation and improve the alloy plasticity.
基金Supported by National Science and Technology Major Project of China(Grant No.2011ZX04002-101)National Science and Technology Support Plan of China(Grant No.2011BAF15B02)National Natural Science Foundation of China(Grant No.51305388)
文摘As the traditional forging process has many problems such as low efficiency, high consumption of material and energy, large cylindrical shell rolling is introduced. Large cylindrical shell rolling is a typical rotary forming technology, and the upper and lower rolls have different radii and speeds. To quickly predict the three-dimensional stresses and eliminate fishtail defect, an improved strip layer method is developed, in which the asymmetry of the upper and lower rolls, non-uniform deformation and stress, as well as the asymmetrical spread on the end surface are considered. The deformation zone is divided into a certain number of layers and strips along the thickness and width, respectively. The transverse displacement model is constructed by polynomial function, in order to increase the computation speed greatly. From the metal plastic mechanics principle, the three-dimensional stress models are established. The genetic algorithm is used for optimization calculation in an industrial experiment example. The results show that the rolling pressure, the normal stresses, the upper and lower friction stress distributions are not similar with those of a general plate rolling. There are two relative maximum values in rolling pressure distribution. The upper and lower longitudinal friction stresses change direction nearby the upper and lower neutral points, respectively. The fishtail profile of spread on the end surface is predicted satisfactorily. The reduction could be helpful to eliminate fishtail defect. The large cylindrical shell rolling example illustrates the calculation results acquired rapidly are good agreements with the finite element simulation and experimental values of previous study. A highly effective and reliable three-dimensional simulation method is proposed for large cylindrical shell rolling and other asymmetrical rolling.
文摘A gyro-stabilizer is the interesting system that it can apply to marine vessels for diminishes roll motion.Today it has potentially light weight with no hydrodynamics drag and effective at zero forward speed.The twin-gyroscope was chosen.Almost,the modelling for designing the system use linear model that it might not comprehensive mission requirement such as high sea condition.The non-linearity analysis was proved by comparison the results between linear and non-linear model of gyro-stabilizer throughout frequency domain also same wave input,constrains and limitations.Moreover,they were cross checked by simulating in time domain.The comparison of interested of linear and non-linear close loop model in frequency domain has demonstrated the similar characteristics but gave different values at same frequency obviously.The results were confirmed again by simulation in irregular beam sea on time domain and they demonstrate the difference of behavior of both systems while the gyro-stabilizers are switching on and off.From the resulting analysis,the non-linear gyro-stabilizer model gives more real results that correspond to more accuracy in a designing gyro-stabilizer control system for various amplitudes and frequencies operating condition especially high sea condition.
基金Item Sponsored by National Science and Technology Major Project of China(2011ZX04002-101)National Science and Technology Support Plan of China(2011BAF15B02)National Natural Science Foundation of China(51305388)
文摘Considering the characteristics of large cylindrical shell rolling, such as double driving rolls, asymmetrical rolling and huge workpiece, a slab method was developed to establish the rolling force model. In this model, the non- uniform normal and shear stresses and the upper and lower surface temperatures of the workpiece were taken into ac- count. Moreover, the flow stress model, considering the dynamic recovery and dynamic recrystallization behaviors of the material, was established. The rolling pressure distribution, the rolling force, the rolling torque and the neutral points could be calculated quickly and easily by the roiling force model. The predicted results were shown to be in good agreement with the measured values, which indicated that the model can satisfy the requirement of industrial application.