Addressing the Fuel Resistance of Hot Mix Asphalt by an Enhanced Test Method

In areas where hot mix asphalt(HMA)is likely to be exposed by any form of mineral oil the layer has to withstand the attack of these substances in order not to damage the construction.The European Standard EN 12697-43 provides a test procedure to determine the resistance of HMA to fuel.The paper reviews this method thoroughly.A completely revised and simplified test device for the brush test was developed meeting the requirements of the standard and creating results with a high repeatability at the same time.The test conditions given by the standard such as the exposure to fuel,cleaning of the specimen after exposure or the contact pressure of the brush were varied to isolate those test conditions with a substantial influence on the result.The research revealed that in the standard some conditions with a rather small influence are set quite strictly while other conditions with a distinct influence on the result are not defined with the required accuracy to obtain comparable and repeatable results.The paper presents suggestions for the improvement of the test method and the standard itself in respect to the layout of the test device and the definition of important test conditions to enhance the outcome of the EN 12697-43.

Construction Technology of Warm Mix Asphalt Pavement in Cold High-Altitude Areas

With the continuous development of domestic highway construction,highway civil engineering and service level quality have attracted much attention.Good pavement quality and high-quality service make people feel comfortable and smooth when traveling.High-quality pavement can significantly reduce the probability of traffic accidents.At present,there is a direct relationship between pavement quality and pavement construction operations.Carrying out pavement construction operations in cold high-altitude areas requires a reasonable selection of construction equipment and methods.The application of warm-mix asphalt pavement construction technology can ensure pavement quality.Therefore,this paper analyzes the advantages of warm-mix technology,the environmental characteristics of cold high-altitude areas,and construction preparations,and discusses the construction technology of warm-mix asphalt pavement in cold high-altitude areas in detail,to improve the overall road quality of cold high-altitude areas.

Rheological properties of warm mix asphalt binder by DSR test at medium temperature

The rheological properties including the complex modulus G＊ and the phase angle δof matrix and warm mix asphalt （WMA）binders were measured by using the dynamic shear rheometer （DSR ） test at the medium temperature ranging from 16 to 40 ℃,and the relationships between the fatigue factor G＊ sinδand the matrix binder property,WMA additive and test temperature were established.It is found that G＊ decreases with the increasing temperature while δincreases inversely,and G＊ of the asphalt binder with high WMA additive dosage is large,and δis small.G＊sinδexponentially decreases with the increasing temperature and linearly increases with the increase in additive dosage,and the amplitudes of variation are large at low temperatures and high additive dosages.The effect of WMA additive on the rheological property is more remarkable for the matrix asphalt binder with low G＊.Besides,aging has a great effect on the property of matrix asphalt binder,and a slight effect on the interaction between asphalt and additive.The high additive dosage can increase the fatigue cracking potential of the asphalt binder.

Application of nano silica to improve self-healing of asphalt mixes

Nano silica due to its spherical shape, tiny size and higher density compared to bitumen, may have an inherent potential to improve hot mix asphalt(HMA) self-healing. In this research scanning electron microscopy(SEM) images were used to investigate size, morphology and dispersion of nano silica particles. Additionally, HMA self-healing mechanism was also examined by SEM. Furthermore, dynamic indirect tensile test(IDT) was used to evaluate HMA self-healing index. The SEM results indicated that bitumen mortar flowing into micro cracks may be one of the most important mechanisms of HMA self-healing. The experiment results also showed that modification of bitumen by nano silica promotes the ability of the HMA self-healing.

Long term performance of warm mix asphalt versus hot mix asphalt

The fatigue behavior, indirect tensile strength （ITS） and resilient modulus test results for warm mix asphalt （WMA） as well as hot mix asphalt （HMA） at different ageing levels were evaluated. Laboratory-prepared samples were aged artificially in the oven to simulate short-term and long term ageing in accordance with AASHTO R30 and then compared with unaged specimens. Beam fatigue testing was performed using beam specimens at 25 ℃ based on AASHTO T321 standard. Fatigue life, bending stiffness and dissipated energy for both unaged and aged mixtures were calculated using four-point beam fatigue test results. Three-point bending tests were performed using semi-circular bend （SCB） specimens at -10 ℃ and the critical mode I stress intensity factor K1 was then calculated using the peak load obtained from the load-displacement curve. It is observed that Sasobit and Rheofalt warm mix asphalt additives have a significant effect on indirect tensile strength, resilient modulus, fatigue behavior and stress intensity factor of aged and unaged mixtures.

Reducing the Compaction Segregation of Hot Mix Asphalt

This paper presented the methods of reducing the compaction segregation of asphalt layer by improving the operating characteristics of roller and paver. The fit formula, which expresses the compaction rule of the paving layer after passing different rolling passes of the steel wheel roller, was also put forward. The measured results of test road show that when some technical methods are adopted, the compaction segregation can be controlled.

The Compaction Characteristics of Hot Mixed Asphalt Mixtures

The quality of compaction is important to the performance of hot mixed asphalt （HMA） pavement. Most premature failures of asphalt pavement are concerned with poor compaction. Compaction characteristic of lIMA mixtures were studied. Compaction tests were done with typical widely used HMA mixtures, including dense gradation asphalt mixtures with different nominal maximum aggregate size （AC13,AC20,AC25）, and mixtures with different gradation （AC13, SMA13,Supl3 and OGFC13）. HMA mixtures were sampled at different compaction temperature and Marshall blow numbers, varying between 60 and 175 ~C and between 15 and 75 lows, respectively. The compaction characteristics of these mixtures were evaluated. The results showed that the Marshall stability and volumetric properties were significantly affected by the compaction temperature. Mixtures with the same NMAS but different type of gradation need different compaction energy to get the designed density.

The Influence of Material Related Parameters on the Mechanical Properties of Foamed Asphalt Mix

By indirect tensile strength （ITS） test and unconfined compressive strength （UCS） test, the influence of various material related parameters, including asphalt foamability, aggregate temperature, mixing moisture content （MMC） and foamed asphalt （FA） content, on the mechanical properties of FA mixes was studied. The results indicated that both asphalt foamability and aggregate temperature greatly affected ITS of FA mixes. Too low aggregate temperature was unfavorable for mechanical properties of FA mixes. Foamed index alone was unfit for the evaluation of asphalt foamability. Compared with half-life, expansion ratio had more prominent influence on ITS of FA mixes. MMC had significant impact on the mechanical properties of FA mixes and should be optimized by trial and test in FA mix design. The mechanical properties of FA mix were sensitive to the change of FA content. Compared with the ITS determined with standard Marshall specimens, both the ITS and UCS determined with static compressed specimens by 15 cm diameter were more effective in terms of choosing the optimal asphalt content for FA mixes.

Evaluation of environmental factors to fatigue performance of asphalt mixes

This paper studies the effect of different environmental factors, including the axle load weight, environmental temperature, vehicle speed, and the aging level of asphalt, on the fatigue performance of asphalt mixes based on four-point bending beam fatigue tests. A fractional factorial design method named ＂uniform design＂ was applied in experimental design. The relations of the environmental factors to initial stiffness, fatigue life, phase angle and cumulative dissipated energy were established with the general linear modeling method. It is found that there exists very good correlativity between the environmental factors and the fatigue performance indices of asphalt mixes. The coefficients of total correlation are mainly beyond 0. 95. The results indicate that the consideration of the effect of environmental factors is necessary in the fatigue performance evaluation on real asphalt pavement.

Experimental Study on Fatigue Performance of Gussasphalt Mixture

Four-point flexural fatigue test for Gussasphalt mixture specimen was carried out at a straincontrolled mode system. The results showed that the development of the tested stiffness modulus and phase angle of the mixtures with increasing load cycles exhibited three periods, initial generation, slow development and failure period. The fatigue crack generation zone formed in the third period, in which the macro mechanical properties were signifi cantly decreased. Moreover, we also analyzed the effects of asphalt content and mixing temperature on the fatigue life of the mixture. The results showed that the fi rst period when the specimen＇s initial stiffness modulus was reduced to 80% accounted for 5%-10% of the total fatigue life; the second period in which the reduction became slow and demonstrated a liner relationship with load cycles occupied 70%-85% of the fatigue life; and the third period was about 5%-10%. The results indicated that the lower the mixing temperature, the longer the fatigue life of Gussasphalt mixture. Besides, the increasing of asphalt content has a minor effect on the fatigue life of Gussasphalt mixture

Experimental Alternative to the Determination of the Thermal Dependence of the Complex Modulus of Asphalt Mixes in Dry Tropical Areas

Current pavement design methods do not allow for the reduction of early deformation of the surface layers of bituminous pavements in the city of Ouagadougou. Weather conditions combined with traffic, particularly during heat waves, are factors. The temperature at the surface of the bituminous pavement can reach 62˚C but the complex modulus associated with this temperature is not taken into account in the design, hence the interest in proposing laws of dependence of the complex moduli is taken into account in the maximum temperatures of the pavement surface. The objective of this paper is to propose an experimental method to determine the temperature dependence of the complex moduli of asphalt mixes for temperatures between 40˚C and 70˚C. This experimental method consists of performing axial compression tests on cylindrical asphalt specimens. It was applied to three different formulas of bituminous mixes, intended for the wearing course, obtained from mixes of crushed granites, granular classes 6/10, 4/6 and 0/4, pure bitumens of grade 50/70, 35/50 and modified bitumen of grade 10/65. The comparative study of the experimental results obtained with the results of a semi-empirical methodology revealed a root mean square deviation from the mean of between 6.58% and 14.8% of the norms of the complex moduli (modulus of rigidity) of the asphalt mixes for a fixed frequency of solicitations of 10 Hz. The consistency of these results with data from the literature led to the initial conclusion that asphalt mixes formulated with 35/50 and 10/65 bitumen would have better compressive strength than those formulated with 50/70 bitumen, for exposure temperatures between 40˚C and 70˚C. This experimental approach could be an alternative to the complex modulus test for determining the modulus of rigidity for design purposes under real pavement exposure conditions in the city of Ouagadougou during heat waves.

Warm-Mix Asphalt and Pavement Sustainability: A Review

Within the past two decades or so, the asphalt paving industry has responded positively to increasing global concerns over shrinking natural resource reserves and worsening environmental conditions through the development and deployment of warm-mix asphalt technologies. Such technologies make it possible to produce and place asphalt concrete at reduced temperatures compared to conventional hot-mix methods. Several studies have reported on the potential of warm-mix asphalt with regard to improved pavement performance, efficiency and environmental stewardship. This paper reviews several of those studies in the context of pavement sustainability. Overall, warm-mix asphalt provides substantial sustainability benefits similar to or, in some cases, better than conventional hot-mix asphalt. Sustainability benefits include lower energy use, reduced emissions, and potential for increased reclaimed asphalt pavement usage. Growth in utilization of warm-mix asphalt worldwide may, in the not-too-distant future, make the material the standard for asphalt paving. Regardless, there are concerns over some aspects of warm-mix asphalt such as lower resistance to fatigue cracking, rutting and potential water-susceptibility problems, particularly with mixes prepared with water-based technologies, which require further research to address.

不同钢渣掺量AC-16沥青混合料性能研究

研究将钢渣应用于道路建设中的可行性和钢渣沥青混合料性能特点,揭示混合料性能随钢渣掺量不同的变化规律。将钢渣0%、25%、50%、75%掺量代替石灰岩集料制备钢渣沥青混合料,采用高温单轴贯入试验、低温劈裂强度试验、冻融劈裂强度试验、间接拉伸疲劳试验,分别针对不同钢渣掺量下沥青混合料的高温性能、低温性能、水稳定性与疲劳性能展开相应研究。试验结果表明,钢渣各项性能指标均满足规范要求,可以作为集料制备沥青混合料,掺加钢渣后沥青混合料各项性能均有不同程度提高。随着钢渣掺量的提高沥青混合料各项性能变化规律不同,建议钢渣掺量控制在50%左右,以达到沥青混合料综合性能最优。

沥青温拌技术分类及温拌效果的试验评价方法

沥青温拌技术日益广泛应用于路面工程,为了定量评价温拌沥青混合料在拌和生产过程中的温拌效果,提供试验评价方法,本研究自主开发了一种沥青混合料变速拌和试验装置,采用70^(#)基质和SBS改性两种沥青、自主研发的一种表面活性剂型沥青温拌剂(取名为Alube)和一种有机降黏型沥青温拌剂(取名为ACMP),以市场成熟产品Evotherm为参照,分别制备了温拌沥青及其AC-13C型混合料,测试了不同沥青和温拌沥青的三大指标、布氏黏度和动态剪切流变指标,分析了沥青的黏温曲线特性,通过混合料的变温击实试验和变速拌和试验,研究了沥青混合料的压实特性和拌和流动特性,提出了沥青混合料的拌和流动模型。研究结果表明,有机降黏型温拌剂减小了沥青的黏度,增大了沥青的流动性,改变了沥青的技术性能,如针入度、延度、相位角等增大,软化点、布氏黏度等减小,而表面活性剂型温拌剂不改变沥青的基本技术性能;黏温曲线法仅可表征有机降黏型温拌沥青的温度变化,等黏温度降低约9℃,变温击实法和变速拌和法则可以同时表征两大类温拌剂的温拌效果;沥青混合料的拌和流动性服从宾汉黏塑性模型,从流变理论上解答了混合料的拌和流动性及和易性,推荐采用变速拌和试验来评价温拌沥青混合料的温拌效果;综合考察现有沥青温拌技术可知,在常用温拌剂掺量下,温拌沥青的生产拌和温度可比热拌沥青混合料低20~30℃,符合常规认识。

温拌SBS改性再生沥青混合料的路用性能研究

为研究再生SBS改性沥青混合料(RAP)掺量和温拌剂种类对温拌SBS改性再生沥青混合料的路用性能的影响,通过车辙试验、小梁弯曲试验和冻融劈裂试验分析了在RAP掺量为0,10%,30%,50%,Sasobit温拌剂掺量为3.0%和Evotherm温拌剂掺量为2.0%的温拌SBS改性再生沥青混合料的高温稳定性能、低温抗裂性能和水稳性能,并通过灰色关联度分析RAP掺量对两种温拌再生沥青混合料路用性能的影响。结果表明,RAP的掺入可以极大地改善温拌再生沥青混合料的高温性能,但不利于其低温抗裂性能和水稳定性能。不同RAP掺量的沥青混合料对各项路用性能影响程度大小排序均为:水稳定性能<低温抗裂性能<高温稳定性能。在RAP掺量为30%时,掺入Evotherm温拌剂的再生沥青混合料的高温性能、低温抗裂性能、水稳定性能优于掺入Sasobit温拌剂的再生沥青混合料。

再生沥青混合料拌和均匀性识别与机理分析

为探究再生沥青混合料(RAP)拌和过程中的均匀性特征变化规律,考虑拌和时间和RAP料老化程度因素,选择二氧化钛粉末作为RAP料示踪剂,在实验室内制备掺有质量分数40%RAP料的再生沥青混合料,并建立均匀性指标评价再生沥青混合料均匀性特征.通过计算机断层扫描技术(CT)获取沥青混合料数字图像,并对图像进行基于Mimics软件的组分识别,最终建立关于组分和结团的均匀性评价体系.结果表明:粗集料分布情况对混合料拌和均匀性的影响最大,其次是沥青和孔隙分布情况;延长搅拌时间有利于提高再生沥青混合料的拌和均匀性,然而拌和过程中形成的新结团又会阻碍拌和均匀性的改善.考虑组分和结团的均匀性评价体系可以有效揭示再生沥青混合料拌和均匀性特征变化规律,为建设高质量再生沥青路面提供参考.

SMC再生SBS沥青的流变性能和微观特性研究

【目的】探究新型温拌再生剂甲基苯乙烯共聚物(styreneic methyl copolymer,SMC)对老化苯乙烯系热塑性弹性体(styrene butadiene styrene,SBS)改性沥青的再生效果和再生机理。【方法】首先,在室内制备不同老化程度的沥青。然后,采用SMC再生剂对不同老化程度的SBS改性沥青进行再生。接着,对再生后的SBS改性沥青进行动态剪切流变和低温弯曲蠕变试验,以评价其流变性能。最后,开展红外光谱试验以揭示其作用机理,进行电镜扫描试验以验证SMC再生剂的再生效果。【结果】SMC再生剂会降低老化SBS改性沥青的车辙因子,降低老化SBS改性沥青的恢复率,同时会使老化SBS改性沥青的低温性能得到极大提升。SMC再生剂未与SBS改性沥青发生化学反应,两者仅为物理共混。同时,SMC再生剂能够弥补沥青因老化产生的裂缝。【结论】SMC再生剂对老化SBS改性沥青具有较好的修复效果,能够为沥青的再生提供一种新的途径。

聚乙烯蜡温拌再生沥青性能研究

聚乙烯蜡可提升沥青路用性能,同时具有良好的经济效益而受到研究人员的广泛关注。选取新聚乙烯蜡(NPEW)与回收聚乙烯蜡(RPEW)按照等比混掺的方式作为温拌剂(PEW),将PEW与再生剂(LBS)加入新旧共混沥青中制备了聚乙烯蜡温拌再生沥青,其中新旧共混沥青中分别含20%、30%、40%的老化SBS改性沥青(AAM),用于模拟实际路面再生过程中旧沥青比例。通过沥青三大指标、布氏黏度对不同PEW及AAM掺量下温拌再生沥青的感温性能、高低温性能及降黏效果进行分析。结果表明,AAM和PEW的添加可减少温拌再生沥青的温度敏感性;当温拌再生沥青中AAM掺量一定时,随着PEW掺量的增加,高温抗变形能力,低温抗裂性能均有显著提升;当温拌再生沥青中AAM掺量较低时,PEW的掺入可有效降低黏度;当AAM掺量30%,PEW掺量2%时,温拌再生沥青兼具最佳的路用性能及经济效益。

不同RAP掺量下热再生沥青混合料性能衰变规律

本文采用自主研发的全寿命分析仪对沥青混合料分别进行0、4、8、12个月的模拟老化,采用冻融劈裂试验、动态蠕变试验和半圆弯曲试验,研究不同RAP掺量下热再生沥青混合料长期老化后各项性能的衰变规律.结果表明:在12个月模拟老化后,RAP掺量为30%时沥青混合料的流变次数达到最大,RAP掺量的提高使得TSR衰减幅度变大且断裂能下降.50%RAP掺量时再生料TSR衰减幅度比新拌料大7.9%,流变次数和断裂能较新拌料分别减少38.6%和61.7%.长期老化作用下RAP掺量对沥青混合料疲劳寿命衰减的影响不明显,但会降低其应力敏感性.

赤泥填料对排水沥青混合料路用性能的影响

为探究赤泥填料对排水沥青混合料路用性能的影响,首先选择两种国产高黏改性剂PT-HVA和AR-HVA制备得到高黏改性沥青,并将成品苯乙烯-丁二烯-苯乙烯(styrene-butadiene-styrene,SBS)改性沥青作为对照组,对三种改性沥青进行各项沥青性能试验。结果表明:两种改性剂的最佳掺量均为15%。接着以三种改性沥青为胶结料配制三种排水性沥青混合料(填料为赤泥和矿粉),并进行各项路用性能试验。结果表明:由赤泥制备的混合料的路用性能良好,其中AR-HVA高黏改性沥青+赤泥制备的混合料性能最优,动稳定度达11053次/mm,残留稳定度为91.46%,冻融劈裂比为89.60%,飞散损失为5.20%,老化系数为24.60%。同时,由赤泥制备而成的混合料的弯拉强度和弯拉应变比由矿粉制备的混合料的小,这表明赤泥虽能有效地提高混合料的高温性能、水稳性能、抗松散性能和抗老化性能,但会降低混合料的低温性能。