The Multi layer coating of Ni60 alloy was got by multi layer laser cladding. The height of the coating was about 12mm and the wall of the coating was perpendicular to the base. The microstructure of the coating was ...The Multi layer coating of Ni60 alloy was got by multi layer laser cladding. The height of the coating was about 12mm and the wall of the coating was perpendicular to the base. The microstructure of the coating was made up of fine dendrite. The conjunction between layers was good.展开更多
By laser multi-layer cladding using a pulsed Nd-YAG irradiation the thickness of the cladding zone Mg-based alloys(ZM2 and ZM5) can reach about 1.0 mm.The microstructure of the substrate and the cladding zone was stud...By laser multi-layer cladding using a pulsed Nd-YAG irradiation the thickness of the cladding zone Mg-based alloys(ZM2 and ZM5) can reach about 1.0 mm.The microstructure of the substrate and the cladding zone was studied using optical microscope, scanning electron microscopy(SEM), X-ray diffractometry(XRD) and micro hardness analysis. It is observed that constituent of ZM5 alloy is δ+Mg 17Al 12, that of ZM2 alloy is α+MgZn+Mg 9Ce. That of cladding layer ZM2 alloy(L-ZM2) is Mg+Mg 2Zn 11+MgCe; while that of the cladding layer ZM5 alloy(L-ZM5) is Mg+Mg 32(Al, Zn) 49. The hardness of the cladding area can be increased to values above HV127. Very fine uniform microstructure and the produced new phases of nanometer/sub-micrometer order were obtained. Now, many repaired Mg-based alloy components have been passed by flying test in outside field.展开更多
Straight plates, hollow columns, ear-like blade tips, twist plates withdirectional solidification microstructure made of Rene 95 superalloys were successfully fabricatedon Nickel-base superalloy and DD3 substrates, re...Straight plates, hollow columns, ear-like blade tips, twist plates withdirectional solidification microstructure made of Rene 95 superalloys were successfully fabricatedon Nickel-base superalloy and DD3 substrates, respectively. The processing conditions for productionof the parts with corresponding shapes were obtained. The fabrication precision was high and thecomponents were compact. The solidification microstructure of the parts was analyzed by opticalmicroscopy. The results show that the solidification microstructure is composed of columnardendrites, by epitaxial growth onto the directional solidification substrates. The crystallographyorientation of the parts was parallel to that of the substrates. The primary arm spacing was about10 mum, which is in the range of superfine dendrites, and the secondary arm was small or evendegenerated. It is concluded that the laser metal forming technique provides a method to manufacturedirectional solidification components.展开更多
文摘The Multi layer coating of Ni60 alloy was got by multi layer laser cladding. The height of the coating was about 12mm and the wall of the coating was perpendicular to the base. The microstructure of the coating was made up of fine dendrite. The conjunction between layers was good.
文摘By laser multi-layer cladding using a pulsed Nd-YAG irradiation the thickness of the cladding zone Mg-based alloys(ZM2 and ZM5) can reach about 1.0 mm.The microstructure of the substrate and the cladding zone was studied using optical microscope, scanning electron microscopy(SEM), X-ray diffractometry(XRD) and micro hardness analysis. It is observed that constituent of ZM5 alloy is δ+Mg 17Al 12, that of ZM2 alloy is α+MgZn+Mg 9Ce. That of cladding layer ZM2 alloy(L-ZM2) is Mg+Mg 2Zn 11+MgCe; while that of the cladding layer ZM5 alloy(L-ZM5) is Mg+Mg 32(Al, Zn) 49. The hardness of the cladding area can be increased to values above HV127. Very fine uniform microstructure and the produced new phases of nanometer/sub-micrometer order were obtained. Now, many repaired Mg-based alloy components have been passed by flying test in outside field.
基金This research was financially supported by the National High Technology Research and Development Program of China (No.2001AA337020)the Development Plan of State Key Fundamental Research of China (No. G2000067205-3)
文摘Straight plates, hollow columns, ear-like blade tips, twist plates withdirectional solidification microstructure made of Rene 95 superalloys were successfully fabricatedon Nickel-base superalloy and DD3 substrates, respectively. The processing conditions for productionof the parts with corresponding shapes were obtained. The fabrication precision was high and thecomponents were compact. The solidification microstructure of the parts was analyzed by opticalmicroscopy. The results show that the solidification microstructure is composed of columnardendrites, by epitaxial growth onto the directional solidification substrates. The crystallographyorientation of the parts was parallel to that of the substrates. The primary arm spacing was about10 mum, which is in the range of superfine dendrites, and the secondary arm was small or evendegenerated. It is concluded that the laser metal forming technique provides a method to manufacturedirectional solidification components.