Bulging Distortion of Austenitic Stainless Steel Sheet on the Partially Penetrated Side of Non-Penetration Lap Laser Welding Joint

Non-penetration laser welding of lap joints in austenitic stainless steel sheets is commonly preferred in fields where the surface quality is of utmost importance.However,the application of non-penetration welded austenitic stainless steel parts is limited owing to the micro bulging distortion that occurs on the back surface of the partial penetration side.In this paper,non-penetration lap laser welding experiments,were conducted on galvanized and SUS304 austenitic stainless steel plates using a fiber laser,to investigate the mechanism of bulging distortion.A comparative experiment of DC01 galvanized steel-Q235 carbon steel lap laser welding was carried out,and the deflection and distortion profile of partially penetrated side of the sheets were measured using a noncontact laser interferometer.In addition,the cold-rolled SUS304 was subjected to heat holding at different temperatures and water quenching after bending to characterize its microstructure under tensile and compressive stress.The results show that,during the heating stage of the thermal cycle of laser lap welding,the partial penetration side of the SUS304 steel sheet generates compressive stress,which extrudes the material in the heat-affected zone to the outside of the back of the SUS304 steel sheet,thereby forming a bulge.The findings of these experiments can be of great value for controlling the distortion of the partial penetrated side of austenitic stainless steel sheet during laser non-penetration lap welding.

Effect of process parameters on the morphology of aluminum/copper alloy lap joints by red and blue hybrid laser welding

In order to overcome the problems of many pores,large deformation and unstable weld quality of traditional laser welded aluminumcopper alloy joints,a red-blue dual-beam laser source and a swinging laser were introduced for welding.T2 copper and 6063 aluminum thin plates were lap welded by coaxial dual-beam laser welding.The morphology of weld cross section was compared to explore the influence of process parameters on the formation of lap joints.The microstructure characteristics of the weld zone were observed and compared by optical microscope.The results show that the addition of laser beam swing can eliminate the internal pores of the weld.With the increase of the swing width,the weld depth decreases,and the weld width increases first and then decreases.The influence of welding speed on the weld cross section morphology is similar to that of swing width.With the increase of welding speed,the weld width increases first and then decreases,while the weld depth decreases all the time.This is because that the red laser is used as the main heat source to melt the base metals,with the increase of red laser power,the weld depth increases.As an auxiliary laser source,blue laser reduces the total energy consumption,consequently,the effective heat input increases and the spatter is restrained effectively.As a result,the increase of red laser power has an enhancement effect on the weld width and weld depth.When the swing width is 1.2 mm,the red laser power is 550 W,the blue laser power is 500 W,and the welding speed is 35 mm/s,the weld forming is the best.The lap joint of T2 copper and 6063 aluminum alloy thin plate can be connected stably with the hybrid of blue laser.The effect rules of laser beam swing on the weld formation were obtained,which improved the quality of the joints.

Study on the Effects of Helium-Argon Gas Mixture on the Laser Welding Performance of High Temperature Alloys

In order to solve the problem of porosity in laser deep penetration welding of GH3625 high-temperature alloy plates,five different ratios of high-purity helium gas and high-purity argon gas mixed gases were compared in welding experiments after various process parameter improvements and adjustments failed to achieve Class I welds.The experimental results show that using high-purity helium gas or a mixture of 50%high-purity helium gas and 50%high-purity argon gas can both achieve Class I welds.This indicates that using high-purity helium gas or an appropriate mixed gas instead of pure argon is one of the effective ways to solve the problem of porosity in laser deep penetration welding of high-temperature alloys.The mixture of 50%high-purity argon gas and 50%high-purity helium gas can reduce the consumption of high-purity helium gas,lower production costs,and is more suitable.

Research on microstructure and properties of boron/Q235 steel laser welded dissimilar joints under synchronous thermal field

The mechanical mismatch effect frequently occurs in the dissimilar materials welded joints, thus leading to plastic gradient at the interface between the weld and heat-affected zone(HAZ). In this work, the boron steel and Q235 steel were selected for laser tailor welding,which obtained boron/Q235 steel tailor-welded blanks(TWBs). The method of welding with synchronous thermal field(WSTF) was utilized to eliminate the mismatch effects in TWBs. The WSTF was employed to adjust cooling rates of welded joints, thereby intervening in the solidification behaviors and phase transition of the molten pool. Boron/Q235 steel was welded by laser under conventional and WSTF(300-600 ℃) conditions, respectively. The results show that the microstructure of weld and HAZ(boron) was adequately transitioned to ferrites and pearlites instead of abundant martensite by WSTF. Meanwhile, the discrepancy of microhardness and yield strength between various regions of welded joints was greatly reduced, and the overall plasticity of welded joints was enhanced by WSTF. It is indicated that WSTF can effectively contribute to reducing plastic gradient and achieving mechanical congruity in welded joints by restraining the generation of hardbrittle phase, which could significantly improve the formability of TWBs in subsequent hot stamping.

Microstructures and Toughness of Weld Metal of Ultrafine Grained Ferritic Steel by Laser Welding

3 mm thick 400 MPa grade ultrafine grained ferritic steel plates were bead-on-plate welded by CO2 laser with heat input of 120-480 J/mm. The microstructures of the weld metal mainly consist of bainite, which form is lower bainite plates or polygonal ferrite containing quantities of dispersed cementite particles, mixed with a few of low carbon martensite laths or ferrite, depending on the heat input. The hardness and the tensile strength of the weld metal are higher than those of the base metal, and monotonously increase as the heat input decreases. No softened zone exists in heat affected zone (HAZ). Compared with the base metal, although the grains of laser weld are much larger, the toughness of the weld metal is higher within a large range of heat input. Furthermore, as the heat input increases, the toughness of the weld metal rises to a maximum value, at which point the percentage of lower bainite is the highest, and then drops.

Effects of Laser Shock Processing on Mechanical Properties of Laser Welded ANSI 304 Stainless Steel Joint

With the rapid development of engineering component with integration,high-speed and multi-parameter,traditional techniques haven＇t met practical needs in extreme service environment.Laser welding,a new welding technology,has been widely used.However,it would generate the drop of mechanical properties for laser welded joint due to its thermal effect.Laser shock processing（LSP） is one of the most effective methods to improve the mechanical properties of laser welded ANSI 304 stainless steel joint.In this paper,the effects of LSP on the mechanical properties of laser welded ANSI 304 stainless steel joint have been investigated.The welded joint on the front of the tensile samples is treated by LSP impacts,and the overlapping rate of the laser spot is 50%.The tensile test of the laser welded joint with and without LSP impacts is carried out,and the fracture morphology of the tensile samples is analyzed by scanning electron microscope（SEM）.Compared with the yield strength of 11.70 kN,the tensile strength of 37.66 kN,the yield-to-tensile strength ratio of 0.310 7,the elongation of 25.20%,the area reduction of 32.68% and the elastic modulus of 13 063.876 MPa,the corresponding values after LSP impacts are 14.25 kN,38.74 kN,0.367 8,26.58%,42.29% and 14 754.394 MPa,respectively.Through LSP impacts,the increasing ratio of the yield strength and tensile strength are 121.79% and 102.87%,respectively;the elongation and area reduction are improved by 5.48% and 29.38%,respectively.By comparing with coarse fracture surface of the welded joint,the delamination splitting with some cracks in the sharp corner of the welded joint and asymmetric dimples,LSP can cause brighter fracture surface,and finer and more uniform dimples.Finally,the schematic illustration of dimple formation with LSP is clearly described.The proposed research ensures that the LSP technology can clearly improve the yield strength,tensile strength,yield-to-tensile strength ratio,elongation,area reduction and elastic modulus of the welded joint.The enhancement mechanism of LSP on laser welded ANSI 304 stainless steel joint is mainly due to the fact that the refined and uniform dimples effectively delay the fracture of laser welded joints.

Effect of filler wire on the joint properties of AZ31 magnesium alloys using CO_2 laser welding

Laser welding with filler wire of AZ31 magnesium alloys is investigated using a CO2 laser experimental system. The effect of three different filler wires on the joint properties is researched. The results show that the weld appearance can be effectively improved when using laser welding with filler wire. The microhardness and tensile strength of joints are almost the same us those of the base metal when ER AZ31 or ER AZ61 wire is adopted. However, when the filler wire of ER 5356 aluminum alloy is used, the mechanical properties of flints become worse. For ER AZ31 and ER AZ61 filler wires, the microstructure of weld zone slws small dendrite grains. In comparison, for ER 5356 filler wire, the weld shows a structure of snowy dendrites and many intermetallic compounds and eutectic phases distribute in the dendrites. These intermetallic constituents with low melting point increase the tendency of hot crack and result in fiagile joint properties. Therefore, ER AZ31 and ER AZ61 wire are more suitable filler material than ER 5356 for CO2 laser welding of AZ31 magnesium alloys.

Study of Dynamic Features of Surface Plasma in High-Power Disk Laser Welding

High-speed photography was used to obtain the dynamic changes in the surface plasma during a high-power disk laser welding process. A color space clustering algorithm to extract the edge information of the surface plasma region was developed in order to improve the accuracy of image processing. With a comparative analysis of the plasma features, i.e., area and height, and the characteristics of the welded seam, the relationship between the surface plasma and the stability of the laser welding process was characterized, which provides a basic understanding for the real-time monitoring of laser welding.

YAG laser welding with surface activating flux

YAG laser welding with surface activating flux has been investigated, and the influencing factors and mechanism are discussed. The results show that both surface activating flux and surface active element S have fantastic effects on the YAG laser weld shape, that is to obviously increase the weld penetration and D/W ratio in various welding conditions. The mechanism is thought to be the change of weld pool surface tension temperature coefficient, thus, the change of fluid flow pattern in weld pool due to the flux.

Structure Character of M-A Constituent in CGHAZ of New Ultra-Low Carbon Bainitic Steel under Laser Welding Conditions

800 MPa grade new ultra-low carbon bainitic （NULCB） steel is the recently developed new generation steel. The microstructure in the coarse-grained heat affected zone （CGHAZ） of NULCB steel under laser welding conditions was investigated by thermal simulation. The influence of the cooling time from 800℃ to 500℃.t8/5 （0.3-30 s）, on the microstructure of the CGHAZ was discussed. The experimental results indicate that the microstructnre of the CGHAZ is only the granular bainite which consists of bainitic ferrite （BF） lath and M-A constituent while t8/5 is 0.3-30 s. The M-A constituent consists of twinned martensite and residual austenite, and the change of the volume fraction of the residual austenite in the M-A constituent is very small when t8/5 is between 0.3 and 30 s. The morphology of the M-A constituent obviously changes with the variation of t8/5.As t8/5 increases, tile average width, gross and shape parameter of the M-A constituent increase, while the line density of the M-A constituent decreases.

Underwater Laser Welding/Cladding for High-performance Repair of Marine Metal Materials:A Review

With the rapid developments of marine resource exploitation,mounts of marine engineering equipment are settled on the ocean.When it is not possible to move the damaged equipment into a dry dock,welding operations must be performed in underwater environments.The underwater laser welding/cladding technique is a promising and advanced technique which could be widely applied to the maintenance of the damaged equipment.The present review paper aims to present a critical analysis and engineering overview of the underwater laser welding/cladding technique.First,we elaborated recent advances and key issues of drainage nozzles all over the world.Next,we presented the underwater laser processing and microstructural-mechanical behavior of repaired marine materials.Then,the newly developed powder-feeding based and wire-feeding based underwater laser direct metal deposition techniques were reviewed.The differences between the convection,conduction,and the metallurgical kinetics in the melt pools during underwater laser direct metal deposition and in-air laser direct metal deposition were illustrated.After that,several challenges that need to be overcame to achieve the full potential of the underwater laser welding/cladding technique are proposed.Finally,suggestions for future directions to aid the development of underwater laser welding/cladding technology and underwater metallurgical theory are provided.The present review will not only enrich the knowledge in the underwater repair technology,but also provide important guidance for the potential applications of the technology on the marine engineering.

Effect of laser characteristics on the weld shape and properties of penetration laser weld of BT20 titanium alloy

The laser beam welding of BT20 titanium alloy was conducted to investigate the weld shape, microstructures and properties. The full penetration weld characteristics produced by CO_2 laser and by YAG laser were compared. The results show that the full penetration weld of YAG laser welding closes to “X” shape, and weld of CO_2 laser welding is “nail-head” shape. Those result from special heating mode of laser deep penetration welding. The tension strength of CO_2 laser and YAG laser joints equal to that of the base metal, but the former has better ductility. All welds consist mainly of the acicular α phase and a few β phase in microstructure. The dendritic crystal of CO_2 laser weld is a little finer than YAG laser weld. According the research CO_2 laser is better than YAG laser for welding of BT20 titanium alloy.

Microstructure and Mechanical Properties of Aer Met 100 Ultra-high Strength Steel Joints by Laser Welding

AerMet100 ultra-high strength steel plates with a thickness of 2 mm were welded using a COz laser welding system. The influences of the welding process parameters on the morphology and microstructure of the welding joints were investigated, and the mechanical property of the welding joints was analyzed. The experimental results showed that the fusion zone of welding joint mainly consisted of columnar grains and a fine dendrite substructure grew epitaxially from the matrix. With the other conditions remaining unchanged, a finer weld microstructure was along with the scanning speed increase. The solidification microstructure gradually transformed from cellular crystal into dendrite crystal and the spaces of dendrite secondary arms rose from the fusion line to the center of the fusion zone. In the fusion zone of the weld, the rapid cooling caused the formation of martensite, which led the microhardness of the fusion zone higher than that of the matrix and the heat affected zone. The tensile strength of the welding joints was tested as 1 700 MPa, which was about 87% of the matrix. However, the tensile strength of the welding joints without defects existed was tested as 1832 MPa, which was about 94% of the matrix.

Thermal cycle and its influence on the microstructure of laser welded butt joint of 8 mm thick Ti-6Al-4V alloy

Ti-6Al-4V alloy is extensively used in the manufacture of components in aviation.In the current study,the laser welding process is adopted to joint the Ti-6Al-4V alloy plate which has the thick of 8 mm.A three-dimensional finite element model is established to simulate the temperature distribution of laser welding process.The thermal cycle curves are produced on the strength of the simulation results.Meanwhile,the microstructure characteristics of the welded joint are investigated combined with simulation results.The results show that weld zone,heat affected zone and based metal experience similar thermal cycles process and the cooling rate has an important influence on the formation of microstructure.Moreover,the simulation results are well matched with experiment results.

HAZ Characterization and Mechanical Properties of QP980-DP980 Laser Welded Joints

The QP980-DP980 dissimilar steel joints were fabricated by fiber laser welding.The weld zone(WZ)was fully martensitic structure,and heat-affected zone(HAZ)contained newly-formed martensite and partially tempered martensite(TM)in both steels.The supercritical HAZ of the QP980 side had higher microhardness(~549.5 Hv)than that of the WZ due to the finer martensite.A softened zone was present in HAZ of QP980 and DP980,the dropped microhardness of softened zone of the QP980 and DP980 wasΔ21.8 Hv andΔ40.9 Hv,respectively.Dislocation walls and slip bands were likely formed at the grain boundaries with the increase of strain,leading to the formation of low angle grain boundaries(LAGBs).Dislocation accumulation more easily occurred in the LAGBs than that of the HAGBs,which led to significant dislocation interaction and formation of cracks.The electron back-scattered diffraction(EBSD)results showed the fraction of LAGBs in sub-critical HAZ of DP980 side was the highest under different deformation conditions during tensile testing,resulting in the failure of joints located at the sub-critical HAZ of DP980 side.The QP980-DP980 dissimilar steel joints presented higher elongation(~11.21%)and ultimate tensile strength(~1011.53 MPa)than that of DP980-DP980 similar steel joints,because during the tensile process of the QP980-DP980 dissimilar steel joint(~8.2%and 991.38 MPa),the strain concentration firstly occurred on the excellent QP980 BM.Moreover,Erichsen cupping tests showed that the dissimilar welded joints had the lowest Erichsen value(~5.92 mm)and the peak punch force(~28.4 kN)due to the presence of large amount of brittle martensite in WZ and inhomogeneous deformation.

Influence of welding parameters on temperature field characteristics during laser welding of TA15 by infrared thermography

Using an infrared thermographic technique, the temperature field during laser welding of TA15 is quantitatively measured and investigated. The ilffluenee of two welding parameters on the weld temperature distribution is analyzed and the meehanisnl is discussed. New conclusions are drawn that are different from conventional weld temperature distributions. For the face of the weld, changes in welding speed induce changes in the temperature distribution because of different heat inputs and the cooling effect. Sinfilar temperature features in the welds are observed for all speeds, which exhibit a relatively low temperature area below 1 500 ℃ between the high temperature area in the position of laser incidence and the sub-high temperature area at the end of the molten pool. For the ilffluenee of laser power on the face of the weld, the temperature on the weld is higher for P = 2.8 kW compared to P = 2.0 kW, especially the temperature in the sub-high temperature area. However, for the temperature field of the back of the weld, the ilffluenee of welding speeds is quite different compared to the results for the face of the weld. The highest temperature does not locate in the keyhole area, but instead in the middle of the molten pool. And there are different temperature features at different speeds. When v = 6 m/min, the temperature field is like a uniform color belt and the temperature along the center of the weld fluctuates between 300 and 450 ℃. When v = 4 m/rain, the transient temperature distribution is not uniform and is unstable at different times. However, for v = 2.4 m/rain and lower speeds, the temperature field becomes stable. The ilffluenee of laser power on the back of the weld temperature field is more complex. The measured temperature does not increase with increasing laser power, which seems to eolffliet with the conventional thermal conduction theory-. This may be related with the characteristics of the keyhole area.

Study on behavior of reinforcement in molten pool for submicron composite Al_2O_3p/6061 Al during laser welding

The behavior of the reinforcement of submicron composite Al_ 2 O_ 3 p/6061Al in molten pool during laser welding was studied. It was indicated that because there were the remarkable differences in thermal physical properties between matrix and reinforcement particulate, the reinforced particulate was pushed forward during molten pool solidification by the liquid-solid interface in matrix and the reinforced particulate segregated in the weld. It resulted in noticeable degradation in properties of the welded joint. The technology methods to improve the behavior of reinforcement were also investigated. It was pointed out that the laser pulse frequency is the main welding parameter affecting the distributive state of reinforcement, and the theory basis was established for welding the material by laser beam.

Effect of W/Cu composite filler metals on the microstructure and mechanical properties of laser welded pure niobium/304 stainless steel joint

Cracking in a laser weld of niobium to stainless steel occurred due to the formation of brittle,continuously distributed Nb-Fe intermetallic compounds.A crack-free joint,which had a tensile strength of 147 MPa,was obtained by using the W/Cu composite filler metals.To determine the reasons for cracking in the Nb/SS joint and the function of the W/Cu composite filler metals on the improvement of the cracking resistance of the Nb/W/Cu/SS joint,the microstructures of the joints were studied by optical microscopy,scanning electron microscopy and X-ray diffraction.The cracking susceptibilities of the joints were evaluated with microhardness test on the cross section of the Nb/W/Cu/SS joint.The results showed that the Nb/W/Cu/SS joint was characterized by various solid solution.The formation of solid solution reduced the cracking susceptibility of the joint.

The microstructures investigation in laser weld bonding AZ31B Mg alloy to 6061A1 alloy joint

Adhesive is used in the laser weld bonding Mg to A1 alloys process, in order to improve the property of laser welding joint. The effect of adhesive on the microstrnctures in laser weld bonding AZ31B Mg alloy to 6061Al alloy are observed by scanning electron microscopy and transmission electron microscope. The results show that the decomposition of the adhesive makes influence on the crystal structure of the Mg fusion zone, which forms the C-Mn precipitates. The morphology of Mg-Al intermetallics is changed, when the adhesive decomposition gas bubble floats out of the fusion zone. Dislocations are formed at the bottom of Al fusion zone with the effect of adhesive decomposition and pulse laser power.

Research on laser weld penetration monitoring with laser induced plasma signals

In this paper, laser induced plasma signals were analyzed during keyhole welding through three methods. According to the results, the relativity between optical and acoustic signals of plasma is shown when welds are in full-penetration, or partial-penetration and non-penetration.