Kinetic study on leaching of nickel from Turkish lateritic ore in nitric acid solution

Dissolution kinetics of nickel from lateritic ore in nitric acid solution was investigated. Experimental parameters used were stirring speed(100-600 r/min), temperature(40-96 °C), nitric acid concentration(0.1-2 mol/L) and particle size(<106 μm). The shrinking core model was applied to the results of experiments investigating the effects of leaching temperature in the range of 40-90 °C and nitric acid concentration in range of 0.1-2 mol/L on nickel dissolution rate. The kinetic analysis shows that the nickel dissolution from lateritic ore could be described by diffusion model. The activation energy(E_a) for the dissolution reaction is calculated as 79.52 kJ/mol.

Dissolution of lateritic nickel ore using ascorbic acid as synergistic reagent in sulphuric acid solution

The dissolution of nickel and cobalt from Caldag lateritic nickel ore using the combination of sulphuric and ascorbic acids was investigated. The use of other organic acids, namely citric, maleic and stearic acids, as synergistic reagents was studied for comparison. The results revealed that the use of ascorbic and citric acids markedly improved the dissolution of cobalt compared to the other two organic acids that only showed slight synergistic effect on the leaching rate. In terms of nickel dissolution, ascorbic acid is the most effective synergist, followed by citric, maleic and stearic acids in descending order. Under the most optimized conditions found in this study, i.e., using 1 mol/L of sulphuric acid with the presence of 4 g/L of ascorbic acid at 80 ℃and solid-to-liquid ratio of 1/10, more than 99% and 98% leaching rates of cobalt and nickel, respectively, can be achieved within 4 h of leaching. In addition, the leaching performance is relatively insensitive to the change of ascorbic acid concentration from 2 to 4 g/L which is highly desirable from operational perspective.

Dechromization and dealumination kinetics in process of Na_2CO_3-roasting pretreatment of laterite ores

A novel process was proposed for the activation pretreatment of limonitic laterite ores by Na2CO3 roasting. Dechromization and dealumination kinetics of the laterite ores and the effect of particle size, Na2CO3-ore mass ratio, and roasting temperature on Cr and Al extraction were studied. Experimental results indicate that the extraction rates of Cr and Al are up to 99%and 82%, respectively, under the optimal particle size of 44–74μm, Na2CO3-to-ore mass ratio of 0.6：1, and temperature of 1000 ℃. Dechromization within the range of 600–800 oC is controlled by the diffusion through the product layer with an apparent activation energy of 3.9 kJ/mol, and that it is controlled by the chemical reaction at the surface within the range of 900–1100 ℃ with an apparent activation energy of 54.3 kJ/mol. Besides, the Avrami diffusion controlled model with on apparent activation energy of 16.4 kJ/mol is most applicable for dealumination. Furthermore, 96.8%Ni and 95.6%Co could be extracted from the alkali-roasting residues in the subsequent pressure acid leaching process.

Coal-based reduction mechanism of low-grade laterite ore

A low-grade nickel laterite ore was reduced at different reduction temperatures. The morphology of metallic particles was investigated by scanning electron microscopy （SEM） and energy dispersive spectroscopy （EDS）. Experimental results indicate that the metallic nickel and iron gradually assemble and grow into larger spherical particles with increasing temperature and prolonging time. After reduction, the nickel laterite ore obviously changes into two parts of Fe-Ni metallic particles and slag matrix. An obvious relationship is found between the reduction of iron magnesium olivine and its crystal chemical properties. The nickel and iron oxides are reduced to metallic by reductant, and the lattice of olivine is destroyed. The entire reduction process is comprised of oxide reduction and metallic phase growth.

Thermodynamic of selective reduction of laterite ore by reducing gases

As the sulfide ore deposits become less economical and environmental viable as a source of nickel,increasing attention is being paid to the laterite ores.But in the pyrometallurgical process of laterite,more efforts should be paid to control the reduction of iron oxide in order to get high nickel-content nickeliferous product.For these reasons,equilibrium condition of iron oxide when laterite ore was selectively reduced by CO2/CO,H2O/H2 and CO2/H2 was studied from the perspective of iron activity with an assumption that the activities of Fe O and Fe3O4 equal 1 in this work,and it well accounts for the inescapability of Fe metallization.Activity coefficient of iron in Ni-Fe binary solid alloy was calculated by Miedema model based on the known thermodynamics datum filed.According to Raoult＇s law,the relationship among the Fe/Ni ratio,reduction temperature and reduction gas composition was calculated when laterite ore was selectively reduced by the three different reduction systems.The calculation result was discussed and also compared with the experimental result.The trend of metal iron content in the reduction product of laterite ore varying with temperature and gas composition was well predicted by the calculation result.

Efficient enrichment of nickel and iron in laterite nickel ore by deep reduction and magnetic separation

The process of deep reduction and magnetic separation was proposed to enrich nickel and iron from laterite nickel ores.Results show that nickel-iron concentrates with nickel grade of 6.96%,nickel recovery of 94.06%,iron grade of 34.74%,and iron recovery of 80.44% could be obtained after magnetic separation under the conditions of reduction temperature of 1275℃,reduction time of 50 min,slag basicity of 1.0,carbon-containing coefficient of 2.5,and magnetic field strength of 72 kA/m.Reduction temperature and time affected the possibility of deep reduction and reaction progress.Slag basicity affected the composition of slag in burden and the spilling and enriching rate of nickel-iron from a matrix to form nickel-iron particles.Nickel-iron particles were generated,aggregated,and grew gradually in the reduction process.Nickel-iron particles can be effectively separated from gangue minerals by magnetic separation.

Transformation and leaching kinetics of silicon from low-grade nickel laterite ore by pre-roasting and alkaline leaching process

The mineralogical phase transformation of a low-grade nickel laterite ore during pre-roasting process and the extraction of silicon during alkaline leaching process were investigated.The results indicate that the reaction activity of nickel ores is effectively improved by pre-roasting at650°C for2h,because of the transformation of lizardite into magnesium olivine and protoenstatite.When finely ground ore samples(44-61μm)pre-roasted firstly react with sodium hydroxide solution(60g/L)with a solid/liquid ratio of1:5at140°C for120min,the extraction of silicon can reach89.89%,and the other valuable elements of magnesium,iron and nickel are accumulated in the solid residues.The leaching kinetics of nickel laterite ore can be described successfully by the diffusion through the product layer control model.The activation energy is calculated to be11.63kJ/mol and the kinetics equation can be expressed as1-3(1-x)2/3+2(1-x)=13.53×10-2exp[-11.63/(RT)]t.

Extraction of valuable metals from low-grade nickeliferous laterite ore by reduction roasting-ammonia leaching method

Nickel and cobalt were extracted from low-grade nickeliferous laterite ore using a reduction roasting-ammonia leaching method.The reduction roasting-ammonia leaching experimental tests were chiefly introduced,by which fine coal was used as a reductant.The results show that the optimum process conditions are confirmed as follows:in reduction roasting process,the mass fraction of reductant in the ore is 10%,roasting time is 120 min,roasting temperature is 1 023-1 073 K;in ammonia leaching process,the liquid-to-solid ratio is 4:1(mL/g),leaching temperature is 313 K,leaching time is 120 min,and concentration ratio of NH3 to CO2 is 90 g/L:60 g/L.Under the optimum conditions,leaching efficiencies of nickel and cobalt are 86.25% and 60.84%,respectively.Therefore,nickel and cobalt can be effectively reclaimed,and the leaching agent can be also recycled at room temperature and normal pressure.

Nitric acid pressure leaching of limonitic laterite ores:Regeneration of HNO3 and simultaneous synthesis of fibrous CaSO4·2H2O by-products

An innovative technology,nitric acid pressure leaching of limonitic laterite ores,was proposed by our research team.The HNO3 regeneration is considerable significance for the improvement of the proposed technology and its commercial application,but it has not been systematically investigated.Herein,regenerating HNO3 from Ca(NO3)2 solution with low-cost H2SO4,and simultaneous synthesis of fibrous CaSO4·2H2O by-products were studied.As a theoretical basis,the solubility of CaSO4·2H2O in HNO3 medium is studied.It is concluded that the solubility of CaSO4·2H2O increases with increasing temperature or increasing HNO3 concentration,which has considerable guiding significance for the subsequent experimental research and analysis.Then,the effects of various factors on the residual Ca^2+ concentration of filtrate,the regenerated HNO3 concentration and the morphology of synthesized products are investigated using ICP-AES and SEM.And the effect mechanism is also analyzed.The results indicate the regenerated HNO3 concentration reaches 116 g/L with the residual Ca^2+ concentration being 9.7 g/L at the optimum conditions.Moreover,fibrous CaSO4·2H2O by-products with high aspect ratios(length,406.32μm;diameter,14.71μm;aspect ratio,27.62)can be simultaneously synthesized.

Desiliconization kinetics of nickeliferous laterite ores in molten sodium hydroxide system

A novel process was proposed for treating nickeliferous laterite ores with molten sodium hydroxide.The effect on silicon extraction caused by the factors,such as stirring speed,reaction temperature,particle size and NaOH-to-ore mass ratio,was investigated.The results show that increasing stirring speed,reaction temperature and NaOH-to-ore mass ratio while decreasing particle size increases silicon extraction rate.The desiliconization kinetics of nickeliferous laterite ores in molten sodium hydroxide system was described successfully by chemical reaction control model.The activation energy of the desiliconization process was found to be 44.01 kJ/mol,and the reaction rate based on a chemical reaction-controlled process can be expressed as:1-(1-α) 1/3 = 27.67exp[-44 010/(RT)]t.

Activation pretreatment of limonitic laterite ores by alkali-roasting using NaOH

Activation pretreatment of Cr-containing limonitic laterite ores by NaOH roasting to remove Cr, Al, and Si, as well as its effect on Ni and Co extraction in the subsequent pressure acid leaching process was investigated. Characterization results of X-ray diffraction （XRD） and scanning electron microscopy/X-ray energy dispersive spectroscopy （SEM/XEDS） show that goethite is the major Ni-bearing mineral, and chromite is the minor one. Experimental results show that the leaching rates of Cr, Al, and Si are 95.6wt%, 83.8wt%, and 40.1wt%, respectively, under the optimal alkali-roasting conditions. Compared with the direct pressure acid leaching of laterite ores, the leaching rates of Ni and Co increase from 80.1wt% to 96.9wt% and 70.2wt% to 95.1wt% after pretreatment, respectively. Meanwhile, the grade of acid leaching iron residues increases from 54.4wt% to 62.5wt%, and these residues with low Cr content are more suitable raw materials for iron making.

Relationship between process mineralogical characterization and beneficiability of low-grade laterite nickel ore

Process mineralogy of low-grade laterite nickel ore in Indonesia was systematically characterized and the beneficiation process of mineral components such as limonite,serpentine and chromite was studied on the basis of process mineralogy.The results show that the low-grade laterite nickel ore is a typical weathering sedimentary metamorphic oxidized ore,with the main valuable elements of Ni,Co and Cr and the main mineral components of limonite,serpentine,chromite,etc.There is no independent carrier mineral of Ni and Co in the raw ore,and the occurrence states of Ni and Co are relatively dispersed.For the limonite in laterite nickel mine,the nickel bearing magnetite concentrate with nickel grade of 1.98%and recovery rate of 88.42%can be obtained by reduction roasting magnetic separation process.For the serpentine in laterite nickel mine,the cobalt bearing concentrate with Co grade of 0.17%and recovery rate of 23.17%can be obtained by positive and reverse flotation process.A chromium concentrate containing 35.17%Cr_(2)O_(3) and a recovery of 33.42%can be obtained by using the combined process of coarse and fine classification and gravity and magnetic.

Microwave assisted atmospheric acid leaching of nickel from laterite ore

The recovery of nickel from laterite ore with sulphuric acid under the effect of microwave irradiation was studied.The experimental results indicated that the extraction rate of nickel was influenced by reaction time,sulphuric acid concentration,and temperature,especially by microwave power.The results obtained from the experiments of orthogonal arrays showed that the optimum conditions of sulphuric acid concentration,reaction time,microwave power,and temperature were 25 vol.%,1.5 h,600 W,and 90°C,respectively.Under the optimal conditions,the nickel recovery could reach approximately 90.8%,which was higher than that obtained by conventional water bath heating.Kinetic experiments showed that the leaching of nickel in a sulphuric acid medium was controlled by chemical reaction occurring on the surface of laterite ore.The apparent activation energy was 38.9 kJ/mol.Microwave heating technology is efficient,clean,and easy to control and facilitate continuous processing of materials.

Effects of Na_2SO_4 on iron and nickel reduction in a high-iron and low-nickel laterite ore

This study investigates the reactions of Na2SO4 and its effects on iron and nickel reduction in the roasting of a high-iron and low-nickel laterite ore through gas composition, X-ray diffraction, and scanning electron microscope analyses. Results showed that a reduction reaction of Na2SO4 to SO2 was performed with roasting up to 600℃. However, no clear influence on iron and nickel reductions appeared, because only a small amount of Na2SO4 reacted to produce SO2. Na2SO4 reacted completely at 1000℃, mainly producing troilite and nepheline, which remarkably improves selective reduction of nickel. Furthermore, the production of low-melting-point minerals, including troilite and nepheline, accelerated nickel reduction and delayed iron reduction, which is attributed to the concurrent production of magnesium magnetite, whose structure is more stable than the structure of magnetite. Reduction reactions of Na2SO4 resulted in weakening of the reduction atmosphere, and the main product of Na2SO4 changed and delayed the reduction of iron. Eventually, iron metallization was effectively controlled during laterite ore reduction roasting, leading to iron mainly being found in wustite and high iron-containing olivine.

Generation process of FeS and its inhibition mechanism on iron mineral reduction in selective direct reduction of laterite nickel ore

Numerous studies have demonstrated that Na2SO4 can significantly inhibit the reduction of iron oxide in the selective reduction process of laterite nickel ore. FeS generated in the process plays an important role in selective reduction, but the generation process of FeS and its inhibition mechanism on iron reduction are not clear. To figure this out, X-ray diffraction and scanning electron microscopy analyses were conducted to study the roasted ore. The results show that when Na2SO4 is added in the roasting, the FeO content in the roasted ore increases accompanied by the emergence of FeS phase. Further analysis indicates that NaeS formed by the reaction of Na2SO4 with CO reacts with SiO2 at the FeO surface to generate FeS and Na2Si2Os. As a result, a thin film forms on the surface of FeO, hindering the contact between reducing gas and FeO. Therefore, the reduction of iron is depressed, and the FeO content in the roasted ore increases.

A green process for recovering nickel from nickeliferous laterite ores

A novel process was proposed for recovering nickel from nickeliferous laterite ores.First of all,silicon and magnesium were removed from lateritic ore by high concentration sodium hydroxide leaching and carbonation respectively,so as to enrich nickel. Then the method of ammonia carbonate leaching was adopted to recover nickel from the carbonized slag,and the remaining residue was used as a raw material for recovering iron.The effects of temperature,ammonia carbonate concentration,liquid/solid ratio and stirring speed on the recovery of nickel were examined.When the leached residue reacted with ammonia carbonate(6 mol·L- 1)in a ratio of liquid-to-solid of 5-1 at 60℃for 150 min at the stirring speed of 300 r·min- 1,approximate more than 95%nickel was recovered.During the whole process,there was no contamination produced and the chemical raw materials were recycled,thus the process was a green technology that having good social benefit.

Feasibility of co-reduction roasting of a saprolitic laterite ore and waste red mud

Large scale utilization is still an urgent problem for waste red mud with a high content of alkaline metal component in the future.Laterite ores especially the saprolitic laterite ore are one refractory nickel resource,the nickel and iron of which can be effectively recovered by direct reduction and magnetic separation.Alkaline metal salts were usually added to enhance reduction of laterite ores.The feasibility of co-reduction roasting of a saprolitic laterite ore and red mud was investigated.Results show that the red mud addition promoted the reduction of the saprolitic laterite ore and the iron ores in the red mud were co-reduced and recovered.By adding 35wt%red mud,the nickel grade and recovery were 4.90wt%and 95.25wt%,and the corresponding iron grade and total recovery were 71.00wt%and 93.77wt%,respectively.The X-ray diffraction（XRD）,scanning electron microscopy,and energy dispersive spectroscopy（SEM-EDS）analysis results revealed that red mud addition was helpful to increase the liquid phase and ferronickel grain growth.The chemical compositions＂Ca O and Na_2O＂in the red mud replaced Fe O to react with Si O_2 and Mg Si O_3 to form augite.

Evolution of ferronickel particles during the reduction of low-grade saprolitic laterite nickel ore by coal in the temperature range of 900–1250℃with the addition of CaO–CaF_(2)–H_(3)BO_(3)

The method of producing ferronickel at low temperature(1250–1400℃)has been applied since the 1950s at Nippon Yakin Kogyo,Oheyama Works,Japan.Limestone was used as an additive to adjust the slag composition for lowering the slag melting point.The ferronickel product was recovered by means of a magnetic separator from semi-molten slag and metal after water quenching.To increase the efficiency of magnetic separation,a large particle size of ferronickel is desired.Therefore,in this study,the influences of CaO,CaF_(2),and H_(3)BO_(3) additives on the evolution of ferronickel particle at≤1250℃were investigated.The experiments were conducted at 900–1250℃with the addition of CaO,CaF_(2),and H_(3)BO_(3).The reduction processes were carried out in a horizontal tube furnace for 2 h under argon atmosphere.At 1250℃,with the CaO addition of 10 wt%of the ore weight,ferronickel particles with size of 20μm were obtained.The ferronickel particle size increased to 165μm by adding 10 wt%CaO and 10 wt%CaF_(2).The addition of boric acid further increased the ferronickel particle size to 376μm,as shown by the experiments with the addition of 10 wt%CaO,10 wt%CaF_(2),and 10 wt%H_(3)BO_(3).

Two-stage reduction for the preparation of ferronickel alloy from nickel laterite ore with low Co and high MgO contents

The preparation of ferronickel alloy from the nickel laterite ore with low Co and high MgO contents was studied by using a pre-reduction-smelting method. The effects of reduction time, calcination temperature, quantity of reductant and calcium oxide (CaO), and pellet diameter on the reduction ratio of Fe and on the pellet strength were investigated. The results show that, for a roasting temperature > 800 A degrees C, a roasting time > 30 min, 1.5wt% added anthracite coal, 5wt% added CaO, and a pellet size of similar to 10 mm, the reduction ratio of Fe exceeds 70% and the compressive strength of the pellets exceeds 10 kg per pellet. Reduction smelting experiments were performed by varying the smelting time, temperature, quantity of reductant and CaO, and reduction ratio of Fe in the pellets. Optimal conditions for the reduction smelting process are as follows: smelting time, 30-45 min; smelting temperature, 1550A degrees C; quantity of reductant, 4wt%-5wt%; and quantity of CaO, 5wt%; leading to an Fe reduction ratio of 75% in the pellets. In addition, the mineral composition of the raw ore and that during the reduction process were investigated by process mineralogy.

Leaching of magnesium from desiliconization slag of nickel laterite ores by carbonation process

The leaching of magnesium from desiliconization slag of nickel laterite ores by carbonation process was studied.The influence of various parameters was investigated to optimize the conditions and determine the kinetics of the reaction.The results show that with increasing stirring speed,liquid-to-solid ratio and reaction time,and decreasing temperature,the leaching rate of magnesium enhances.The leaching process of the desiliconization slag in the range of 288-298 K is controlled by the surface chemical reaction model.The apparent activation energy is-20.45 kJ/mol,and the kinetics model is obtained.