Lath-shaped and highly crystalline trioctahedral smectites were synthesized under hydrothermal conditions. The quenched glasses with stoichiometrically dehydrated Na-smectite compositions were treated at （a） 500℃ a...Lath-shaped and highly crystalline trioctahedral smectites were synthesized under hydrothermal conditions. The quenched glasses with stoichiometrically dehydrated Na-smectite compositions were treated at （a） 500℃ and 100 MPa for 1 and 11 days; and （b） 300℃ and 100 MPa for 7 days. The crystallinity and particle size of products were dependent on the chemical composition of the starting glass, synthetic temperature and duration of hydrothermal treatment. The high structural ordering and large dimensions of the products were confirmed from the sharpness of XRD peaks; and hydration behavior under controlled relative humidity. Transmission electron microscopy was also performed for the characterization of the particle size of product. Particle sizes vary from ca. 10 nm to a few pm by changing the chemical compositions of the starting materials. The product with the highest structural ordering and largest dimension was obtained from Nao.33（Mg1.83Al0.67）Si4O11 glass treated at 500℃ and 100 MPa for 1 day. The obtained results also confirmed the metastability and compositional dependency in the formation of highly crystalline trioctahedral smectite at hydrothermal conditions.展开更多
There are few relevant researches on coils by tempering,and the variations of microstructure and properties of steel coil during the tempering process also remain unclear.By using thermo-mechanical control process（T...There are few relevant researches on coils by tempering,and the variations of microstructure and properties of steel coil during the tempering process also remain unclear.By using thermo-mechanical control process（TMCP）technology,Mn-Ti typical HSLA steel coils with yield strength of 920 MPa are produced on the 2250 hot rolling production line.Then,the samples are taken from the coils and tempered at the temperatures of 220℃,350℃,and 620℃respectively.After tempering the strength,ductility and toughness of samples are tested,and meanwhile microstructures are investigated.Precipitates initially emerge inside the ferrite laths and the density of the dislocation drops.Then,the lath-shaped ferrites begin to gather,and the retained austenite films start to decompose.Finally,the retained austenite films are completely decomposed into coarse and short rod-shape precipitates composed of C and Ti compounds.The yield strength increases with increasing tempering temperature due to the pinning effect of the precipitates,and the dislocation density decreases.The yield strength is highest when the steel is tempered at 220℃because of pinning of the precipitates to dislocations.The total elongation increases in all samples because of the development of ferrites during tempering.The tensile strength and impact absorbed energy decline because the effect of impeding crack propagation weakens as the retained austenite films completely decompose and the precipitates coarsen.This paper clarifies the influence of different tempering temperatures on phase transformation characteristics and process of Mn-Ti typical multiphase steels,as well as its resulting performance variation rules.展开更多
文摘Lath-shaped and highly crystalline trioctahedral smectites were synthesized under hydrothermal conditions. The quenched glasses with stoichiometrically dehydrated Na-smectite compositions were treated at （a） 500℃ and 100 MPa for 1 and 11 days; and （b） 300℃ and 100 MPa for 7 days. The crystallinity and particle size of products were dependent on the chemical composition of the starting glass, synthetic temperature and duration of hydrothermal treatment. The high structural ordering and large dimensions of the products were confirmed from the sharpness of XRD peaks; and hydration behavior under controlled relative humidity. Transmission electron microscopy was also performed for the characterization of the particle size of product. Particle sizes vary from ca. 10 nm to a few pm by changing the chemical compositions of the starting materials. The product with the highest structural ordering and largest dimension was obtained from Nao.33（Mg1.83Al0.67）Si4O11 glass treated at 500℃ and 100 MPa for 1 day. The obtained results also confirmed the metastability and compositional dependency in the formation of highly crystalline trioctahedral smectite at hydrothermal conditions.
基金Supported by National Natural Science Foundation of China(Grant No.51201154)
文摘There are few relevant researches on coils by tempering,and the variations of microstructure and properties of steel coil during the tempering process also remain unclear.By using thermo-mechanical control process（TMCP）technology,Mn-Ti typical HSLA steel coils with yield strength of 920 MPa are produced on the 2250 hot rolling production line.Then,the samples are taken from the coils and tempered at the temperatures of 220℃,350℃,and 620℃respectively.After tempering the strength,ductility and toughness of samples are tested,and meanwhile microstructures are investigated.Precipitates initially emerge inside the ferrite laths and the density of the dislocation drops.Then,the lath-shaped ferrites begin to gather,and the retained austenite films start to decompose.Finally,the retained austenite films are completely decomposed into coarse and short rod-shape precipitates composed of C and Ti compounds.The yield strength increases with increasing tempering temperature due to the pinning effect of the precipitates,and the dislocation density decreases.The yield strength is highest when the steel is tempered at 220℃because of pinning of the precipitates to dislocations.The total elongation increases in all samples because of the development of ferrites during tempering.The tensile strength and impact absorbed energy decline because the effect of impeding crack propagation weakens as the retained austenite films completely decompose and the precipitates coarsen.This paper clarifies the influence of different tempering temperatures on phase transformation characteristics and process of Mn-Ti typical multiphase steels,as well as its resulting performance variation rules.