The kinetics of the chemical leaching of copper from low grade ore in ferric sulfate media was investigated using the constrained least square optimization technique. The experiments were carried out for different par...The kinetics of the chemical leaching of copper from low grade ore in ferric sulfate media was investigated using the constrained least square optimization technique. The experiments were carried out for different particle sizes in both the reactor and column at constant oxidation-reduction potential （Eh）, pH values, and temperature. The main copper mineral was chalcopyrite. About 40% of Cu recovery is obtained after 7 d of reactor leaching at 85℃ using -0.5 mm size fraction, while the same recovery is obtained at 75℃ after 24 d. Also, about 23% of Cu recovery is obtained after 60 d of column leaching for ＋4--8 mm size fraction whereas the Cu recovery is as low as about 15% for ＋8--12.7 and ＋12.7--25 mm size fractions. A 4-stage model for chalcopyrite dissolution was used to explain the observed dissolution behaviors. The results show that thick over-layers of sulphur components cause the parabolic behavior of chalcopyrite dissolution and the precipitation of Fe3＋ plays the main role in chalcopyrite passivation. In the case of coarse particles, transformation from one stage to another takes a longer time, thus only two stages including the initial reaction on fresh surfaces and S0 deposition are observed.展开更多
The decomposition of copper anode slime heated by microwave energy in a sulfuric acid medium was investigated. Leaching experiments were carried out in a multi-mode cavity with microwave assistance. The leaching proce...The decomposition of copper anode slime heated by microwave energy in a sulfuric acid medium was investigated. Leaching experiments were carried out in a multi-mode cavity with microwave assistance. The leaching process parameters were optimized using response surface methodology（RSM）. Under the optimized conditions, the leaching efficiencies of copper and tellurium were 99.56% ± 0.16% and 98.68% ± 0.12%, respectively. Meanwhile, a conventional leaching experiment was performed in order to evaluate the influence of microwave radiation. The mechanism of microwave-assisted leaching of copper anode slime was also investigated. In the results, the microwave technology is demonstrated to have a great potential to improve the leaching efficiency and reduce the leaching time. The enhanced recoveries of copper and tellurium are believed to result from the presence of a temperature gradient due to the shallow microwave penetration depth and the superheating at the solid-liquid interface.展开更多
The dissolution behavior of nickel during the oxygen chloride leaching of the copper residue was investigated.Technological variables of the leaching,including oxygen flow rate,concentrations of chloride and sulfuric...The dissolution behavior of nickel during the oxygen chloride leaching of the copper residue was investigated.Technological variables of the leaching,including oxygen flow rate,concentrations of chloride and sulfuric acid,and temperature,were discussed.展开更多
基金the support of Research & Development Division of Sarcheshmeh Copper Complex (Kerman/ Iran) and Tarbiat Modares University(Tehran/ Iran)
文摘The kinetics of the chemical leaching of copper from low grade ore in ferric sulfate media was investigated using the constrained least square optimization technique. The experiments were carried out for different particle sizes in both the reactor and column at constant oxidation-reduction potential （Eh）, pH values, and temperature. The main copper mineral was chalcopyrite. About 40% of Cu recovery is obtained after 7 d of reactor leaching at 85℃ using -0.5 mm size fraction, while the same recovery is obtained at 75℃ after 24 d. Also, about 23% of Cu recovery is obtained after 60 d of column leaching for ＋4--8 mm size fraction whereas the Cu recovery is as low as about 15% for ＋8--12.7 and ＋12.7--25 mm size fractions. A 4-stage model for chalcopyrite dissolution was used to explain the observed dissolution behaviors. The results show that thick over-layers of sulphur components cause the parabolic behavior of chalcopyrite dissolution and the precipitation of Fe3＋ plays the main role in chalcopyrite passivation. In the case of coarse particles, transformation from one stage to another takes a longer time, thus only two stages including the initial reaction on fresh surfaces and S0 deposition are observed.
基金financially supported by the National Science and Technology Support Program of China during the 12th Five-Year Plan Period (No. 2012BAE06B05)the Fundamental Research Funds for the Central Universities of China (No. N130602004)
文摘The decomposition of copper anode slime heated by microwave energy in a sulfuric acid medium was investigated. Leaching experiments were carried out in a multi-mode cavity with microwave assistance. The leaching process parameters were optimized using response surface methodology（RSM）. Under the optimized conditions, the leaching efficiencies of copper and tellurium were 99.56% ± 0.16% and 98.68% ± 0.12%, respectively. Meanwhile, a conventional leaching experiment was performed in order to evaluate the influence of microwave radiation. The mechanism of microwave-assisted leaching of copper anode slime was also investigated. In the results, the microwave technology is demonstrated to have a great potential to improve the leaching efficiency and reduce the leaching time. The enhanced recoveries of copper and tellurium are believed to result from the presence of a temperature gradient due to the shallow microwave penetration depth and the superheating at the solid-liquid interface.
文摘The dissolution behavior of nickel during the oxygen chloride leaching of the copper residue was investigated.Technological variables of the leaching,including oxygen flow rate,concentrations of chloride and sulfuric acid,and temperature,were discussed.