A new alkaline pressure oxidative leaching process(with NaNO3 as the oxidant and NaOH as the alkaline reagent)is proposed herein to remove arsenic,antimony,and lead from bismuth-rich and arsenic-rich lead anode slime ...A new alkaline pressure oxidative leaching process(with NaNO3 as the oxidant and NaOH as the alkaline reagent)is proposed herein to remove arsenic,antimony,and lead from bismuth-rich and arsenic-rich lead anode slime for bismuth,gold,and silver enrichment.The effects of the temperature,liquid-to-solid ratio,leaching time,and reagent concentration on the leaching ratios of arsenic,antimony,and lead were investigated to identify the optimum leaching conditions.The experimental results under optimized conditions indicate that the average leaching ratios of arsenic,antimony and lead are 95.36%,79.98%,63.08%,respectively.X-ray diffraction analysis indicated that the leaching residue is composed of Bi,Bi2O3,Pb2Sb2O7,and trace amounts of NaSb(OH)6.Arsenic,antimony,and lead are thus separated from lead anode slime as Na3AsO4·10H2O and Pb2Sb2O7.Scanning electron microscopy and energy-dispersive spectrometry imaging revealed that the samples undergo appreciable changes in their surface morphology during leaching and that the majority of arsenic,lead,and antimony is removed.X-ray photoelectron spectroscopy was used to demonstrate the variation in the valence states of the arsenic,lead,and antimony.The Pb(IV)and Sb(V)content was found to increase substantially with the addition of NaNO3.展开更多
A novel treatment process of lead anode slime bearing high antimony and low silver was developed by a potential-controlled chloridization leaching and continuous distillation.The experimental results show a high Sb 3+...A novel treatment process of lead anode slime bearing high antimony and low silver was developed by a potential-controlled chloridization leaching and continuous distillation.The experimental results show a high Sb 3+ concentration,489.2 g/L,in the leaching solution for two-stage countercurrent leaching process,and the leaching rates of Sb,Cu,Bi more than 99% when the potential is controlled at 450 mV.When the leaching solution is distillated and concentrated at 120°C,almost all the silicon compound is evaporated into the concentration distillate and exists as amorphous hydrated silica.By the continuous distillation,high pure SbCl3 could be prepared,and AsCl3 is enriched in the distillate while metals Bi,Cu are enriched in the continuous distillation residue.As a result,the recovery rate of Sb is more than 95%.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51564031)Independent Research Project of the State Key Laboratory of Complex Nonferrous Metal Resources Clean Utilization(No.CNMRCUTS1707)the Cooperation project between School and Enterprise of China(No.0201352042)
文摘A new alkaline pressure oxidative leaching process(with NaNO3 as the oxidant and NaOH as the alkaline reagent)is proposed herein to remove arsenic,antimony,and lead from bismuth-rich and arsenic-rich lead anode slime for bismuth,gold,and silver enrichment.The effects of the temperature,liquid-to-solid ratio,leaching time,and reagent concentration on the leaching ratios of arsenic,antimony,and lead were investigated to identify the optimum leaching conditions.The experimental results under optimized conditions indicate that the average leaching ratios of arsenic,antimony and lead are 95.36%,79.98%,63.08%,respectively.X-ray diffraction analysis indicated that the leaching residue is composed of Bi,Bi2O3,Pb2Sb2O7,and trace amounts of NaSb(OH)6.Arsenic,antimony,and lead are thus separated from lead anode slime as Na3AsO4·10H2O and Pb2Sb2O7.Scanning electron microscopy and energy-dispersive spectrometry imaging revealed that the samples undergo appreciable changes in their surface morphology during leaching and that the majority of arsenic,lead,and antimony is removed.X-ray photoelectron spectroscopy was used to demonstrate the variation in the valence states of the arsenic,lead,and antimony.The Pb(IV)and Sb(V)content was found to increase substantially with the addition of NaNO3.
基金Project(2006BAB02B04-4-1)supported by the National Science and Technology Pillar Program during the 11th Five-Year Plan Period,China
文摘A novel treatment process of lead anode slime bearing high antimony and low silver was developed by a potential-controlled chloridization leaching and continuous distillation.The experimental results show a high Sb 3+ concentration,489.2 g/L,in the leaching solution for two-stage countercurrent leaching process,and the leaching rates of Sb,Cu,Bi more than 99% when the potential is controlled at 450 mV.When the leaching solution is distillated and concentrated at 120°C,almost all the silicon compound is evaporated into the concentration distillate and exists as amorphous hydrated silica.By the continuous distillation,high pure SbCl3 could be prepared,and AsCl3 is enriched in the distillate while metals Bi,Cu are enriched in the continuous distillation residue.As a result,the recovery rate of Sb is more than 95%.