More and more light-weighted fabrics are being required by the market, especially for the worsted manufacture.In the past, such fabrics are produced mainly through changing the structure of woven goods or by using fin...More and more light-weighted fabrics are being required by the market, especially for the worsted manufacture.In the past, such fabrics are produced mainly through changing the structure of woven goods or by using finer yarns. But these possibilities are very limited. In this paper, new devices are discussed: (1) on the yarn level- to use single yarns instead of conventional doubled ones, to decrease number of fibers in yarn cross sections beth during spinning and after finishing; (2) on the fiber level - to use finer fibers in blends with wool and modification of the wool fibers; (3) on the macromolecule level - to stretch the macromolecules in alpha keratin, to get super fine wool fibers.展开更多
The colloidal crystal template or opal with a closed-packed face centered cubic (fcc) lattice, was prepared from monodisperse polystyrene (PS) spheres by gravity sedimentation. The template was used for the generatio...The colloidal crystal template or opal with a closed-packed face centered cubic (fcc) lattice, was prepared from monodisperse polystyrene (PS) spheres by gravity sedimentation. The template was used for the generation of photonic crystal. The template provided void space for infiltration of liquid precursor composed of titanium butyloxide, barium acetate, ethanol, and acetic acid. The opal composite was hydrolyzed, dried, sintered by heating for completely removing PS spheres to form BaTiO3 photonic crystals with inverse opal structure. The PS spheres were replaced by air spheres, which interconnected each other through the windows on the BaTiO3 wall. So both the BaTiO3 wall and air void constitute continuous phases.展开更多
The colloidal crystal template or opal with a closed-packed face-centered cubic （fcc） lattice was prepared from monodisperse polystyrene （PS） spheres by vertical sedimentation. The template provided void space for...The colloidal crystal template or opal with a closed-packed face-centered cubic （fcc） lattice was prepared from monodisperse polystyrene （PS） spheres by vertical sedimentation. The template provided void space for infiltration of monomer precursor composed of acrylate acid, acrylamide and ammonium-persulfate, as well as microgel from the subsequent copolymerization. The sample was immersed in dimethylbenzene for completely removing PS spheres to form PAM inverse opal hydrogels （IOHPAM） or PAM/PAA inverse opal hydrogels （IOHPAM/PAA） photonic crystals. The PS spheres were replaced by air spheres, which interconnected each other through the windows. The study of responses to pH show that there are two peaks for both IOHPAM and IOHPAM/PAA films, but the IOHPAM/PAA peaks shift to higher pH, and the peaks are independent with the AA content.展开更多
Owing to its photonic band gap(PBG)and slow light effects,aniline black(AB)-poly(vinylidene fluoride)(PVDF)inverse opal(IO)photonic crystal(PC)was constructed to promote the utility of light and realize photothermal s...Owing to its photonic band gap(PBG)and slow light effects,aniline black(AB)-poly(vinylidene fluoride)(PVDF)inverse opal(IO)photonic crystal(PC)was constructed to promote the utility of light and realize photothermal synergetic catalysis.As a highly efficient reaction platform with the capability of restricting heat,a microreactor was introduced to further amplify the photothermal effects of near infrared(NIR)radiation.The photocatalytic efficiency of ZnO/0.5AB-PVDF IO(Z0.5A)increases 1.63-fold compared to that of pure ZnO film under a full solar spectrum,indicating the effectiveness of synergetic promotion by slow light and photothermal effects.Moreover,a 5.85-fold increase is achieved by combining Z0.5A with a microreactor compared to the film in a beaker.The photon localization effect of PVDF IO was further exemplified by finite-difference time-domain(FDTD)calculations.In conclusion,photonic crystal-microreactor enhanced photothermal catalysis has immense potential for alleviating the deteriorating water environment.展开更多
We present the details of the sol-gel processing used to realize inverse silica opal,where the silica was activated with 0.3 mol% of Er3+ ions. The template(direct opal) was obtained assembling polystyrene spheres of ...We present the details of the sol-gel processing used to realize inverse silica opal,where the silica was activated with 0.3 mol% of Er3+ ions. The template(direct opal) was obtained assembling polystyrene spheres of the dimensions of 260 nm by means of a vertical deposition technique. The Er3+-activated silica inverse opal was obtained infiltrating,into the void of the template,the silica sol doped with Er3+ ions and subsequently removing the polystyrene spheres by means of calcinations. Scanning electron microscope showed that the inverse opals possess a fcc structure with a air hollows of about 210 nm and a photonic band gap,in the visible range,was observed from reflectance measurements. Spectroscopic properties of Er3+-activated silica inverse opal were investigated by luminescence spectroscopy,where,upon excitation at 514.5 nm,an emission of 4I13/2 → 4I15/2 of Er3+ ions transition with a 21 nm bandwidth was observed. Moreover the 4I13/2 level decay curve presents a single-exponential profile,with a measured lifetime of 18 ms,corresponding a high quantum efficiency of the system.展开更多
High entropy alloys(HEAs)possess good mechanical properties and a wide range of industrial applications.In this paper,phase formation prediction theory,microstructure,properties and preparation methods of light-weight...High entropy alloys(HEAs)possess good mechanical properties and a wide range of industrial applications.In this paper,phase formation prediction theory,microstructure,properties and preparation methods of light-weight HEAs(LWHEAs)were reviewed.The problems and challenges faced by LWHEAs development were analyzed.The results showed that many aspects are still weak and require investigation for future advanced alloys,such as clarification of the role of entropy in phase formation and properties of HEAs,improved definition and different generations division of HEAs,close-packed hexagonal(HCP)phase structure prediction and corresponding alloy design and fabrication.Finally,some suggestions were presented in this paper including in-depth research on formation mechanism of multi-component alloy phase and strengthening of large-scale HEA preparation methods via technology compounding and 3D printing technology.Also,there is a need for more research on the in-situ preparation of HEA coatings and films,as well as developing LWHEAs with superior strength and elevated temperature resistance or ultra-low temperature resistance to meet the requirements of future engineering applications.展开更多
Thermodynamic stability, microvoid distribution and phases transformation of natural pozzolana opal shale（POS） were studied systematically in this work. XRD analysis showed that opal-CT, including microcrystal crist...Thermodynamic stability, microvoid distribution and phases transformation of natural pozzolana opal shale（POS） were studied systematically in this work. XRD analysis showed that opal-CT, including microcrystal cristobalite and tridymite, is a major component of POS. DTA and FT-IR indicated that there were many hydroxyl groups and acid sites on the surface of amorphous SiO2 materials. FE-SEM analysis exhibited amorphous SiO2 particles（opal-A） covering over stacking sequences microcrystal cristobalite and tridymite. Meanwhile, MIP analysis demonstrated that porosity and pore size distribution of POS remained uniform below 600 ℃. Because stable porous microstructure is a key factor in improving photocatalyst activity, POS is suited to preparing highly active supported.展开更多
Light-weight magnesium -aluminate spinel materi- als were prepared by foaming-gel process with polyalumi- nium chloride （PAC） as gel. Effect of solid loading in initial slurry on microstructure, porosity, pore size ...Light-weight magnesium -aluminate spinel materi- als were prepared by foaming-gel process with polyalumi- nium chloride （PAC） as gel. Effect of solid loading in initial slurry on microstructure, porosity, pore size distri- bution, thermal conductivity and mechanical properties was investigated. The results show that the bulk density of the light-weight magnesium -aluminate spinel mate- rials is in the range of O. 7 1.2 g cm-3 ; pore size distribution curves show single-peak characteristics and the mean pore size is in the range of 30. 83 - 61.37 μm ; with the increase of solid loading, the linear shrinkage of the green body during firing and the permanent change in dimensions on heating at l 600 ℃ for 3 h de- crease, but the bulk density increases, the mechanical properties increase obviously; the maximum compressive strength and bending strength reach 35. 25 MPa and 9. 92 MPa, respectively, while the bulk density is 1. 16 g · cm ; and the thermal conductivity at 1 000 ℃ tea- ches 0. 371 W · m-1 . K-1 while the bulk density is O. 7 -3 g · cm展开更多
文摘More and more light-weighted fabrics are being required by the market, especially for the worsted manufacture.In the past, such fabrics are produced mainly through changing the structure of woven goods or by using finer yarns. But these possibilities are very limited. In this paper, new devices are discussed: (1) on the yarn level- to use single yarns instead of conventional doubled ones, to decrease number of fibers in yarn cross sections beth during spinning and after finishing; (2) on the fiber level - to use finer fibers in blends with wool and modification of the wool fibers; (3) on the macromolecule level - to stretch the macromolecules in alpha keratin, to get super fine wool fibers.
文摘The colloidal crystal template or opal with a closed-packed face centered cubic (fcc) lattice, was prepared from monodisperse polystyrene (PS) spheres by gravity sedimentation. The template was used for the generation of photonic crystal. The template provided void space for infiltration of liquid precursor composed of titanium butyloxide, barium acetate, ethanol, and acetic acid. The opal composite was hydrolyzed, dried, sintered by heating for completely removing PS spheres to form BaTiO3 photonic crystals with inverse opal structure. The PS spheres were replaced by air spheres, which interconnected each other through the windows on the BaTiO3 wall. So both the BaTiO3 wall and air void constitute continuous phases.
基金supported by the National Natural Science Foundation of China(No.50473044).
文摘The colloidal crystal template or opal with a closed-packed face-centered cubic （fcc） lattice was prepared from monodisperse polystyrene （PS） spheres by vertical sedimentation. The template provided void space for infiltration of monomer precursor composed of acrylate acid, acrylamide and ammonium-persulfate, as well as microgel from the subsequent copolymerization. The sample was immersed in dimethylbenzene for completely removing PS spheres to form PAM inverse opal hydrogels （IOHPAM） or PAM/PAA inverse opal hydrogels （IOHPAM/PAA） photonic crystals. The PS spheres were replaced by air spheres, which interconnected each other through the windows. The study of responses to pH show that there are two peaks for both IOHPAM and IOHPAM/PAA films, but the IOHPAM/PAA peaks shift to higher pH, and the peaks are independent with the AA content.
文摘Owing to its photonic band gap(PBG)and slow light effects,aniline black(AB)-poly(vinylidene fluoride)(PVDF)inverse opal(IO)photonic crystal(PC)was constructed to promote the utility of light and realize photothermal synergetic catalysis.As a highly efficient reaction platform with the capability of restricting heat,a microreactor was introduced to further amplify the photothermal effects of near infrared(NIR)radiation.The photocatalytic efficiency of ZnO/0.5AB-PVDF IO(Z0.5A)increases 1.63-fold compared to that of pure ZnO film under a full solar spectrum,indicating the effectiveness of synergetic promotion by slow light and photothermal effects.Moreover,a 5.85-fold increase is achieved by combining Z0.5A with a microreactor compared to the film in a beaker.The photon localization effect of PVDF IO was further exemplified by finite-difference time-domain(FDTD)calculations.In conclusion,photonic crystal-microreactor enhanced photothermal catalysis has immense potential for alleviating the deteriorating water environment.
基金The work has been supported by the MIUR-FIRB RBNE012N3X,MIUR PRIN, PAT FAPVU 2004-2006,GRICES-CNR.
文摘We present the details of the sol-gel processing used to realize inverse silica opal,where the silica was activated with 0.3 mol% of Er3+ ions. The template(direct opal) was obtained assembling polystyrene spheres of the dimensions of 260 nm by means of a vertical deposition technique. The Er3+-activated silica inverse opal was obtained infiltrating,into the void of the template,the silica sol doped with Er3+ ions and subsequently removing the polystyrene spheres by means of calcinations. Scanning electron microscope showed that the inverse opals possess a fcc structure with a air hollows of about 210 nm and a photonic band gap,in the visible range,was observed from reflectance measurements. Spectroscopic properties of Er3+-activated silica inverse opal were investigated by luminescence spectroscopy,where,upon excitation at 514.5 nm,an emission of 4I13/2 → 4I15/2 of Er3+ ions transition with a 21 nm bandwidth was observed. Moreover the 4I13/2 level decay curve presents a single-exponential profile,with a measured lifetime of 18 ms,corresponding a high quantum efficiency of the system.
基金Funded by the National Natural Science Foundation of China(No.51405510)。
文摘High entropy alloys(HEAs)possess good mechanical properties and a wide range of industrial applications.In this paper,phase formation prediction theory,microstructure,properties and preparation methods of light-weight HEAs(LWHEAs)were reviewed.The problems and challenges faced by LWHEAs development were analyzed.The results showed that many aspects are still weak and require investigation for future advanced alloys,such as clarification of the role of entropy in phase formation and properties of HEAs,improved definition and different generations division of HEAs,close-packed hexagonal(HCP)phase structure prediction and corresponding alloy design and fabrication.Finally,some suggestions were presented in this paper including in-depth research on formation mechanism of multi-component alloy phase and strengthening of large-scale HEA preparation methods via technology compounding and 3D printing technology.Also,there is a need for more research on the in-situ preparation of HEA coatings and films,as well as developing LWHEAs with superior strength and elevated temperature resistance or ultra-low temperature resistance to meet the requirements of future engineering applications.
基金Funded by the National Natural Science Foundation of China(Nos.51278086,51578108)Special Fund for Scientific Research in the Public Interest by Ministry of Water Resource of the People’s Republic of China(No.201501003)
文摘Thermodynamic stability, microvoid distribution and phases transformation of natural pozzolana opal shale（POS） were studied systematically in this work. XRD analysis showed that opal-CT, including microcrystal cristobalite and tridymite, is a major component of POS. DTA and FT-IR indicated that there were many hydroxyl groups and acid sites on the surface of amorphous SiO2 materials. FE-SEM analysis exhibited amorphous SiO2 particles（opal-A） covering over stacking sequences microcrystal cristobalite and tridymite. Meanwhile, MIP analysis demonstrated that porosity and pore size distribution of POS remained uniform below 600 ℃. Because stable porous microstructure is a key factor in improving photocatalyst activity, POS is suited to preparing highly active supported.
基金supported by the National Basic Research Program of China(973 Program,No.2010CB735810)
文摘Light-weight magnesium -aluminate spinel materi- als were prepared by foaming-gel process with polyalumi- nium chloride （PAC） as gel. Effect of solid loading in initial slurry on microstructure, porosity, pore size distri- bution, thermal conductivity and mechanical properties was investigated. The results show that the bulk density of the light-weight magnesium -aluminate spinel mate- rials is in the range of O. 7 1.2 g cm-3 ; pore size distribution curves show single-peak characteristics and the mean pore size is in the range of 30. 83 - 61.37 μm ; with the increase of solid loading, the linear shrinkage of the green body during firing and the permanent change in dimensions on heating at l 600 ℃ for 3 h de- crease, but the bulk density increases, the mechanical properties increase obviously; the maximum compressive strength and bending strength reach 35. 25 MPa and 9. 92 MPa, respectively, while the bulk density is 1. 16 g · cm ; and the thermal conductivity at 1 000 ℃ tea- ches 0. 371 W · m-1 . K-1 while the bulk density is O. 7 -3 g · cm