The effect of limestone powder and fly ash on magnesium sulfate resistance of mortar was studied by testing on the strength, expansion and hydration products of the specimens stored in MgSO4 solution at certain period...The effect of limestone powder and fly ash on magnesium sulfate resistance of mortar was studied by testing on the strength, expansion and hydration products of the specimens stored in MgSO4 solution at certain periods. The experimental results show that the strength of mortar stored in MgSO4 solution increases a little before 28 d, but decreases fast subsequently. The more the contents of limestone powder and fly ash, the less the strength losses. Mortar swells in the MgSO4 solution with the soaking time. And the more the contents of limestone powder and fly ash, the less the expansion rate is. The expansion or strength loss of mortars results from the expansion of gypsum, as well as the loss of Ca（OH）2 and other hydration products of cement. The magnesium sulfate resistance of the mortars containing limestone powder and fly ash is high.展开更多
To decrease the cement and SF content of RPC by using ultra-fine fly ash （UFFA） and steel slag powder （SS）, the effect of these mineral admixtures on compressive strength of RPC were investigated. The experimental...To decrease the cement and SF content of RPC by using ultra-fine fly ash （UFFA） and steel slag powder （SS）, the effect of these mineral admixtures on compressive strength of RPC were investigated. The experimental results indicate that the utilization of UFFA and SS in RPC is feasible and has prominent mechanical performance. The microstructure analysis （SEM and TG-DTG-DSC） demonstrated that the excellent mechanical properties of RPC containing SS and UFFA were mainly attributed to the sequential hydration filling effect of the compound system.展开更多
The potential for using fly ash as a supplementary cementing material in concrete has been known almost since the beginning of the previous century. Fly ash was used as a supplementary cementing material (SCM) in the ...The potential for using fly ash as a supplementary cementing material in concrete has been known almost since the beginning of the previous century. Fly ash was used as a supplementary cementing material (SCM) in the production of Portland cement concrete. A supplementary cementing material, when used in conjunction with Portland cement, contributes to the properties of the hardened concrete through hydraulic or pozzolanic activity, or both. In this study, the fly ash and waste glass powder were used in concrete blocks to study the improvement of concrete in terms of workability and strength. Therefore, an experimental study will be conducted to measure the engineering properties of cured concrete. In this research, local raw material from Jaresh area was used.展开更多
The curing sensitivity of concrete with cement Types 1, 3, and 5 as well as multiple powders consisting of cement, fly ash, and limestone powder was studied. Bottom ash was also used in the study as an internal curing...The curing sensitivity of concrete with cement Types 1, 3, and 5 as well as multiple powders consisting of cement, fly ash, and limestone powder was studied. Bottom ash was also used in the study as an internal curing agent and a partial substi- tution of fine aggregate. The curing sensitivity index was calculated by considering the performances of compressive strength and carbonation depth. Specimens were subjected to two curing conditions： continuously water-cured and continuously air-cured. The results show that cement Type 3 has a lower curing sensitivity, while cement Type 5 increases the curing sensitivity. For the mixes without bottom ash, the use of fly ash increases the curing sensitivity, while limestone powder reduces the curing sen- sRivity of concrete. The use of bottom ash in concrete reduces the curing sensitivity, especially at a lower mass ratio of water to binder. Concrete with limestone powder, together with bottom ash, is least sensitive to curing. The curing sensitivity calculated from carbonation depth also has a similar tendency as that derived by considering compressive strength. From the test results of compressive strength and curing sensitivity, bottom ash has been proven to be an effective internal curing agent.展开更多
The effects of glass powder on the strength development, chloride permeability and potential alkali-aggregate reaction expansion of lightweight aggregate concrete were investigated. Ground blast furnace slag, coal fly...The effects of glass powder on the strength development, chloride permeability and potential alkali-aggregate reaction expansion of lightweight aggregate concrete were investigated. Ground blast furnace slag, coal fly ash and silica fume were used as reference materials. The re- placement of cement with 25% glass powder slightly decreases the strengthes at ？ and 28 d, but shows no effect on 90 d＇s. Silica fume is very effective in improving both the strength and chloride penetration resistance, while ground glass powder is much more effective than blast furnace slag and fly ash in improving chloride penetration resistance of the concrete. When expanded shale or clay is used as coarse aggregate, the concrete containing glass powder does not exhibit deleterious expansion even if alkali-reactive sand is used as fine aggregate of the concrete.展开更多
基金Funded by the Specialized Research Fund for the Doctoral Program of Higher Education of China (No.200804861060)
文摘The effect of limestone powder and fly ash on magnesium sulfate resistance of mortar was studied by testing on the strength, expansion and hydration products of the specimens stored in MgSO4 solution at certain periods. The experimental results show that the strength of mortar stored in MgSO4 solution increases a little before 28 d, but decreases fast subsequently. The more the contents of limestone powder and fly ash, the less the strength losses. Mortar swells in the MgSO4 solution with the soaking time. And the more the contents of limestone powder and fly ash, the less the expansion rate is. The expansion or strength loss of mortars results from the expansion of gypsum, as well as the loss of Ca（OH）2 and other hydration products of cement. The magnesium sulfate resistance of the mortars containing limestone powder and fly ash is high.
基金Funded by the Guide Project in National Science & Technology Pillar Program during the 10th Five-Year Plan Period (2003BA652C)
文摘To decrease the cement and SF content of RPC by using ultra-fine fly ash （UFFA） and steel slag powder （SS）, the effect of these mineral admixtures on compressive strength of RPC were investigated. The experimental results indicate that the utilization of UFFA and SS in RPC is feasible and has prominent mechanical performance. The microstructure analysis （SEM and TG-DTG-DSC） demonstrated that the excellent mechanical properties of RPC containing SS and UFFA were mainly attributed to the sequential hydration filling effect of the compound system.
文摘The potential for using fly ash as a supplementary cementing material in concrete has been known almost since the beginning of the previous century. Fly ash was used as a supplementary cementing material (SCM) in the production of Portland cement concrete. A supplementary cementing material, when used in conjunction with Portland cement, contributes to the properties of the hardened concrete through hydraulic or pozzolanic activity, or both. In this study, the fly ash and waste glass powder were used in concrete blocks to study the improvement of concrete in terms of workability and strength. Therefore, an experimental study will be conducted to measure the engineering properties of cured concrete. In this research, local raw material from Jaresh area was used.
基金supported by the Higher Education Research Promotion and National Research University Project of Thailand, Office of the Higher Education Commissionsupported by the National Metal and Materials Technology Center, National Science and Technology Development Agency, Ministry of Science and Technology, Thailand
文摘The curing sensitivity of concrete with cement Types 1, 3, and 5 as well as multiple powders consisting of cement, fly ash, and limestone powder was studied. Bottom ash was also used in the study as an internal curing agent and a partial substi- tution of fine aggregate. The curing sensitivity index was calculated by considering the performances of compressive strength and carbonation depth. Specimens were subjected to two curing conditions： continuously water-cured and continuously air-cured. The results show that cement Type 3 has a lower curing sensitivity, while cement Type 5 increases the curing sensitivity. For the mixes without bottom ash, the use of fly ash increases the curing sensitivity, while limestone powder reduces the curing sen- sRivity of concrete. The use of bottom ash in concrete reduces the curing sensitivity, especially at a lower mass ratio of water to binder. Concrete with limestone powder, together with bottom ash, is least sensitive to curing. The curing sensitivity calculated from carbonation depth also has a similar tendency as that derived by considering compressive strength. From the test results of compressive strength and curing sensitivity, bottom ash has been proven to be an effective internal curing agent.
文摘The effects of glass powder on the strength development, chloride permeability and potential alkali-aggregate reaction expansion of lightweight aggregate concrete were investigated. Ground blast furnace slag, coal fly ash and silica fume were used as reference materials. The re- placement of cement with 25% glass powder slightly decreases the strengthes at ？ and 28 d, but shows no effect on 90 d＇s. Silica fume is very effective in improving both the strength and chloride penetration resistance, while ground glass powder is much more effective than blast furnace slag and fly ash in improving chloride penetration resistance of the concrete. When expanded shale or clay is used as coarse aggregate, the concrete containing glass powder does not exhibit deleterious expansion even if alkali-reactive sand is used as fine aggregate of the concrete.