Inspired by the Chinese Knotting weave structure,an electromagnetic interference(EMI)nanofiber composite membrane with a twill surface was prepared.Poly(vinyl alcohol-co-ethylene)(Pva-co-PE)nanofibers and twill nylon ...Inspired by the Chinese Knotting weave structure,an electromagnetic interference(EMI)nanofiber composite membrane with a twill surface was prepared.Poly(vinyl alcohol-co-ethylene)(Pva-co-PE)nanofibers and twill nylon fabric were used as the matrix and filter templates,respectively.A Pva-co-PEMXene/silver nanowire(Pva-co-PE-MXene/AgNW,PM_(x)Ag)membrane was successfully prepared using a template method.When the MXene/AgNW content was only 7.4 wt%(PM_(7.4)Ag),the EMI shielding efficiency(SE)of the composite membrane with the oblique twill structure on the surface was 103.9 dB and the surface twill structure improved the EMI by 38.5%.This result was attributed to the pre-interference of the oblique twill structure in the direction of the incident EM wave,which enhanced the probability of the electromagnetic waves randomly colliding with the MXene nanosheets.Simultaneously,the internal reflection and ohmic and resonance losses were enhanced.The PM_(7.4)Ag membrane with the twill structure exhibited both an outstanding tensile strength of 22.8 MPa and EMI SE/t of 3925.2 dB cm^(-1).Moreover,the PM_(x)Ag nanocomposite membranes demonstrated an excellent thermal management performance,hydrophobicity,non-flammability,and performance stability,which was demonstrated by an EMI SE of 97.3%in a high-temperature environment of 140℃.The successful preparation of surface-twill composite membranes makes it difficult to achieve both a low filler content and a high EMI SE in electromagnetic shielding materials.This strategy provides a new approach for preparing thin membranes with excellent EMI properties.展开更多
It has been analyzed the properties such as tensile strength, tearing resistance, crease angle recovery, pilling formation, drape co-efficient, colorfastness to rubbing and colorfastness wash by testing with the help ...It has been analyzed the properties such as tensile strength, tearing resistance, crease angle recovery, pilling formation, drape co-efficient, colorfastness to rubbing and colorfastness wash by testing with the help of related instrument, The twill woven fabrics which are chosen only different to their weave structure (2/1 S twill and 3/1 S twill) whether the other specification of the fabrics like warp count, weft count, ends per inch, picks per inch, GSM of the fabrics and the fiber quality were same. From the experiment, it was found that some properties such as tensile strength, drape co-efficient and colorfastness of 2/1 twill are better than 3/1 twill on the other hand few properties such as crease angle recovery, tearing resistance and colorfastness to wash of 3/1 twill is better than 2/1 twill. Afterward while performing the job for identifying the pill formation tendency, it was observed that pill formation tendencies of the both fabrics are same.展开更多
A new arithmetic using matrix left-shift functions for the quicker generation of curved and compound twills is introduced in this paper. A matrix model for the generation of regular, curved and compound twill structur...A new arithmetic using matrix left-shift functions for the quicker generation of curved and compound twills is introduced in this paper. A matrix model for the generation of regular, curved and compound twill structures is established and its computing simulation realization are elaborated. Examples of the algorithm applying in the simulation and the automatic generation of curved and compound twills in fabric CAD are obtained.展开更多
基金supported by the National Natural Science Foundation of China(12205225,52373063,and 51873166)。
文摘Inspired by the Chinese Knotting weave structure,an electromagnetic interference(EMI)nanofiber composite membrane with a twill surface was prepared.Poly(vinyl alcohol-co-ethylene)(Pva-co-PE)nanofibers and twill nylon fabric were used as the matrix and filter templates,respectively.A Pva-co-PEMXene/silver nanowire(Pva-co-PE-MXene/AgNW,PM_(x)Ag)membrane was successfully prepared using a template method.When the MXene/AgNW content was only 7.4 wt%(PM_(7.4)Ag),the EMI shielding efficiency(SE)of the composite membrane with the oblique twill structure on the surface was 103.9 dB and the surface twill structure improved the EMI by 38.5%.This result was attributed to the pre-interference of the oblique twill structure in the direction of the incident EM wave,which enhanced the probability of the electromagnetic waves randomly colliding with the MXene nanosheets.Simultaneously,the internal reflection and ohmic and resonance losses were enhanced.The PM_(7.4)Ag membrane with the twill structure exhibited both an outstanding tensile strength of 22.8 MPa and EMI SE/t of 3925.2 dB cm^(-1).Moreover,the PM_(x)Ag nanocomposite membranes demonstrated an excellent thermal management performance,hydrophobicity,non-flammability,and performance stability,which was demonstrated by an EMI SE of 97.3%in a high-temperature environment of 140℃.The successful preparation of surface-twill composite membranes makes it difficult to achieve both a low filler content and a high EMI SE in electromagnetic shielding materials.This strategy provides a new approach for preparing thin membranes with excellent EMI properties.
文摘It has been analyzed the properties such as tensile strength, tearing resistance, crease angle recovery, pilling formation, drape co-efficient, colorfastness to rubbing and colorfastness wash by testing with the help of related instrument, The twill woven fabrics which are chosen only different to their weave structure (2/1 S twill and 3/1 S twill) whether the other specification of the fabrics like warp count, weft count, ends per inch, picks per inch, GSM of the fabrics and the fiber quality were same. From the experiment, it was found that some properties such as tensile strength, drape co-efficient and colorfastness of 2/1 twill are better than 3/1 twill on the other hand few properties such as crease angle recovery, tearing resistance and colorfastness to wash of 3/1 twill is better than 2/1 twill. Afterward while performing the job for identifying the pill formation tendency, it was observed that pill formation tendencies of the both fabrics are same.
文摘A new arithmetic using matrix left-shift functions for the quicker generation of curved and compound twills is introduced in this paper. A matrix model for the generation of regular, curved and compound twill structures is established and its computing simulation realization are elaborated. Examples of the algorithm applying in the simulation and the automatic generation of curved and compound twills in fabric CAD are obtained.