The influence of dissolved oxygen content on the oxidative stability of a linked polymer solution (LPS) was studied by micro-filtration, dynamic light scattering and viscosity measurements. The results showed that at ...The influence of dissolved oxygen content on the oxidative stability of a linked polymer solution (LPS) was studied by micro-filtration, dynamic light scattering and viscosity measurements. The results showed that at the same temperature, the degree of the oxidative degradation of the LPS increased and the rapidity of the oxidative degradation was accelerated with the increase of the dissolved oxygen content. Consequently, the size of linked polymer coils (LPCs) of the LPS became small, and the plugging capability of the LPS decreased. At a fixed content of dissolved oxygen, with increasing degradation temperature, almost the same results were observed, namely, an increased degree of oxidative degradation, accelerated rapidity of the oxidative degradation and decreased plugging capacity, with decreased oxidative stability of LPS. At 90 °C, in the presence of oxygen, LPS lost its plugging capability after having been degraded for a period of time. But at 40 °C, LPS with low dissolved oxygen content could be stable for a long time. The decreased plugging ability of LPS after oxidative degradation is mainly caused by the decreased size and number of the LPCs due to the breaking of hydrolyzed polyacrylamide (HPAM) molecule segments and the structural changing of HPAM molecules.展开更多
Performance characteristics of partially hydrolyzed polyacrylamide （HPAM） and cross- linked polymer （CLP, Cr^3＋ as the cross linker） solutions have been investigated. A Brookfield viscometer, rheometer, dynamic l...Performance characteristics of partially hydrolyzed polyacrylamide （HPAM） and cross- linked polymer （CLP, Cr^3＋ as the cross linker） solutions have been investigated. A Brookfield viscometer, rheometer, dynamic light scattering system, and core flow device have been used to measure the viscosity, viscoelasticity, polymer coil dimensions, molecular configuration, flow characteristics, and profile modification. The results show that, under conditions of high salinity and low HPAM and Cr^3＋ concentrations, cross-linking mainly occurred between different chains of the same HPAM molecule in the presence of Cr^3＋, and a cross-linked polymer （CLP） system with a local network structure was formed. Compared with an HPAM solution of the same concentration, the apparent viscosity of the CLP solution increased slightly or remained almost unchanged, but its viscoelasticity （namely storage modulus, loss modulus, and first normal stress difference） increased, and the resistance coefficient and residual resistance coefficient increased significantly. This indicates that the CLP solution exhibits a strong capability to divert the sequentially injected polymer flood from high-permeability zones to low- permeability zones in a reservoir. Under the same HPAM concentration conditions, the dimensions of polymer coils in the CLP solution increased slightly compared with the dimensions of polymer coils in HPAM solution, which were smaller than the rock pores, indicating that the cross-linked polymer solution was well adapted to reservoir rocks. Core flood experiments show that at the same cost of reagent, the oil recovery by CLP injection （HPAM-1, Cr^3＋ as the cross linker） is 3.1% to 5.2% higher than that by HPAM- 2 injection.展开更多
Linked polymer solution (LPS) is defined as the solution of linked polymer coils (LPCs) dispersed in water, composed of low concentration partially hydrolyzed polyacrylamide (HPAM) and aluminum citrate (crosslinker). ...Linked polymer solution (LPS) is defined as the solution of linked polymer coils (LPCs) dispersed in water, composed of low concentration partially hydrolyzed polyacrylamide (HPAM) and aluminum citrate (crosslinker). In the work, the conformational changes of LPCs under different conditions were investigated by the methods of membrane filtering under low pressure, dynamic light scattering and core flooding experiments. The results showed that in some conditions the LPCs could be compressed mechanically to 1/158.5 of their original volume because of relatively lower HPAM cross-linking. The hydration property of LPCs was similar to that of normal polymer coils. The deformation of LPCs was more restricted than that of ordinary polymer coils under the flow shear stress or the shift of hydration equilibrium caused in the variation of the electrolyte concentration which is responsible for the effective plugging in the throats of porous media when LPCs are used for deep diverting.展开更多
A simple and effective photochemical method was developed for cross-linking of polymer gate dielectrics. Laborious synthetic processes for functionalizing polymer dielectrics with photo-cross-linkable groups were avoi...A simple and effective photochemical method was developed for cross-linking of polymer gate dielectrics. Laborious synthetic processes for functionalizing polymer dielectrics with photo-cross-linkable groups were avoided. The photo-cross-linker, BBP-4, was added into host polymers by simple solution blending process, which was capable of abstracting hydrogen atoms from polymers containing active C--H groups upon exposure to ultraviolet （UV） radiation. The cross-linking can be completed with a relatively long wavelength UV light （365 nm）. The approach has been applied to methacrylate and styrenic polymers such as commercial poly（methylmethacrylate） （PMMA）, poly（iso-butylmethacrylate） （PiBMA） and poly（4-methylstyrene） （PMS）. The cross-linked networks enhanced dielectric properties and solvent resistance of the thin films. The bottom-gate organic field-effect transistors （OFETs） through all solution processes on plastic substrate were fabricated. The OFET devices showed low voltage operation and steep subthreshold swing at relatively small gate dielectric capacitance.展开更多
文摘The influence of dissolved oxygen content on the oxidative stability of a linked polymer solution (LPS) was studied by micro-filtration, dynamic light scattering and viscosity measurements. The results showed that at the same temperature, the degree of the oxidative degradation of the LPS increased and the rapidity of the oxidative degradation was accelerated with the increase of the dissolved oxygen content. Consequently, the size of linked polymer coils (LPCs) of the LPS became small, and the plugging capability of the LPS decreased. At a fixed content of dissolved oxygen, with increasing degradation temperature, almost the same results were observed, namely, an increased degree of oxidative degradation, accelerated rapidity of the oxidative degradation and decreased plugging capacity, with decreased oxidative stability of LPS. At 90 °C, in the presence of oxygen, LPS lost its plugging capability after having been degraded for a period of time. But at 40 °C, LPS with low dissolved oxygen content could be stable for a long time. The decreased plugging ability of LPS after oxidative degradation is mainly caused by the decreased size and number of the LPCs due to the breaking of hydrolyzed polyacrylamide (HPAM) molecule segments and the structural changing of HPAM molecules.
基金financial support from the National Key Technology R&D Program in the 12th Five Year Plan of PetroChina (No: 2011ZX05010-003-02)the National Key Technology R&D Program in the 12th Five Year Plan of CNOOC (No: 2011ZX05024-04-05-03)
文摘Performance characteristics of partially hydrolyzed polyacrylamide （HPAM） and cross- linked polymer （CLP, Cr^3＋ as the cross linker） solutions have been investigated. A Brookfield viscometer, rheometer, dynamic light scattering system, and core flow device have been used to measure the viscosity, viscoelasticity, polymer coil dimensions, molecular configuration, flow characteristics, and profile modification. The results show that, under conditions of high salinity and low HPAM and Cr^3＋ concentrations, cross-linking mainly occurred between different chains of the same HPAM molecule in the presence of Cr^3＋, and a cross-linked polymer （CLP） system with a local network structure was formed. Compared with an HPAM solution of the same concentration, the apparent viscosity of the CLP solution increased slightly or remained almost unchanged, but its viscoelasticity （namely storage modulus, loss modulus, and first normal stress difference） increased, and the resistance coefficient and residual resistance coefficient increased significantly. This indicates that the CLP solution exhibits a strong capability to divert the sequentially injected polymer flood from high-permeability zones to low- permeability zones in a reservoir. Under the same HPAM concentration conditions, the dimensions of polymer coils in the CLP solution increased slightly compared with the dimensions of polymer coils in HPAM solution, which were smaller than the rock pores, indicating that the cross-linked polymer solution was well adapted to reservoir rocks. Core flood experiments show that at the same cost of reagent, the oil recovery by CLP injection （HPAM-1, Cr^3＋ as the cross linker） is 3.1% to 5.2% higher than that by HPAM- 2 injection.
基金Supported by Open Foundation of State Key Laboratoy of Heavy Oil Processing(No. 200013)
文摘Linked polymer solution (LPS) is defined as the solution of linked polymer coils (LPCs) dispersed in water, composed of low concentration partially hydrolyzed polyacrylamide (HPAM) and aluminum citrate (crosslinker). In the work, the conformational changes of LPCs under different conditions were investigated by the methods of membrane filtering under low pressure, dynamic light scattering and core flooding experiments. The results showed that in some conditions the LPCs could be compressed mechanically to 1/158.5 of their original volume because of relatively lower HPAM cross-linking. The hydration property of LPCs was similar to that of normal polymer coils. The deformation of LPCs was more restricted than that of ordinary polymer coils under the flow shear stress or the shift of hydration equilibrium caused in the variation of the electrolyte concentration which is responsible for the effective plugging in the throats of porous media when LPCs are used for deep diverting.
基金financially supported by the National Natural Science Foundation of China (Nos.21674060,21274087,61674102,and 61334008)National Key R&D Program (No.2016YFB0401100)
文摘A simple and effective photochemical method was developed for cross-linking of polymer gate dielectrics. Laborious synthetic processes for functionalizing polymer dielectrics with photo-cross-linkable groups were avoided. The photo-cross-linker, BBP-4, was added into host polymers by simple solution blending process, which was capable of abstracting hydrogen atoms from polymers containing active C--H groups upon exposure to ultraviolet （UV） radiation. The cross-linking can be completed with a relatively long wavelength UV light （365 nm）. The approach has been applied to methacrylate and styrenic polymers such as commercial poly（methylmethacrylate） （PMMA）, poly（iso-butylmethacrylate） （PiBMA） and poly（4-methylstyrene） （PMS）. The cross-linked networks enhanced dielectric properties and solvent resistance of the thin films. The bottom-gate organic field-effect transistors （OFETs） through all solution processes on plastic substrate were fabricated. The OFET devices showed low voltage operation and steep subthreshold swing at relatively small gate dielectric capacitance.