Optimization of iron ore blending based on replacing Australian low alumina limonite

Mauritanian iron ore powder(OM)has advantages of high iron grade,low aluminum content,and low loss on ignition,which can be used as a new mineral to replace low alumina limonite that has been exhausted in Australia.However,it will have a certain negative impact on sintering because of its high SiO_(2) content.The mechanism of SiO_(2) content affecting the sintering behavior was first studied through FactSage 7.2.Then,the liquid fluidity,penetration,and high-temperature performance of different iron ore powders were compared.Finally,the optimization of ore blending structure was studied by the micro-sintering method and the sinter pot test.The results show that the increase in SiO_(2) content can reduce the assimilation temperature.The low penetration of OM can lead to an increase in the amount of liquid,and the high SiO_(2) content of OM increases the viscosity of the liquid phase.What is more,the increase in SiO_(2) also increases the formation of silicate and fayalite phase and inhibits the formation of silico-ferrite of calcium and aluminum(SFCA).To optimize ore blending structure,OM and the low SiO_(2) powder OD from Australia were used together,which improves the content of SFCA by 2.04%and decreases the contents of calcium silicate and fayalite by 0.63%and 4.99%,respectively.The results of the sinter pot test indicated that the properties of sinter have been improved.

Determination method of high-temperature characteristics of iron-ore sintering based on n(Fe2O3)/n(CaO)

The high-temperature characteristics of iron ores play important roles in optimizing ore proportion of sintering,which are tested by using iron-ore fines and analytical reagent CaO as raw materials.Two calculation methods of CaO addition amount based on binary basicity(basicity method)and n(Fe2O3)/n(CaO)(mole ratio method),respectively,were employed to evaluate the liquid phase fluidity(LPF)and the capability of calcium ferrite formation(CCFF)of iron ores.The results show that the rule of LPF of iron ores under the mole ratio method is different from that with basicity method.The LPF measured by basicity method has a linear positive correlation with the SiO2 content,and there is no linear relationship between LPF and Al2O3 content or mass loss on ignition,which are inconsistent with the results of the previous study.And the results of CCFF with low SiO2 content(<3 wt.%)or high SiO2 content(>7 wt.%)based on basicity method cannot reflect the true CCFF.The mole ratio method could successfully solve this problem by reducing the effect of CaO addition amount changes caused by SiO2 content of iron ores.