The biaxially textured ion beam-assisted deposited(IBAD)-MgO templates were successfully prepared on polycrystalline Hastelloy metal substrate with reel-to-reel system for YB2Cu3O7-d(YBCO)-coated conductors.By the sol...The biaxially textured ion beam-assisted deposited(IBAD)-MgO templates were successfully prepared on polycrystalline Hastelloy metal substrate with reel-to-reel system for YB2Cu3O7-d(YBCO)-coated conductors.By the solution deposition planarization technique,amorphous Y2O3films were coated on untreated Hastelloy substrate as the bed layer to obtain smooth,dense,and crack-free surface for subsequent IBAD-MgO deposition.The 50 m long IBAD-MgO and homo-epitaxial(epi)-MgO buffer layers deposited on Y2O3films exhibit excellent crystallographic consistency along the scope with full width half maximum(FWHM)values of(110)DU and(200)Dx in the range of 5.5°–6.0°and3.0°–3.5°,respectively.To match the lattice constant of YBCO material,LaMnO3cap layer was fabricated on IBAD-MgO templates by radio frequency(rf)magnetron sputtering with the FWHM values of in-plane and out-ofplane of 6.8°and 3.7°,respectively,indicating excellent biaxial texture.展开更多
基金supported by the Sichuan Youth Science and Technology Innovation Research Team (No. 2011JTD0006)Fundamental Research Funds for the Central Universities (Nos. ZYGX2012J039 and ZYGX2011Z002)
文摘The biaxially textured ion beam-assisted deposited(IBAD)-MgO templates were successfully prepared on polycrystalline Hastelloy metal substrate with reel-to-reel system for YB2Cu3O7-d(YBCO)-coated conductors.By the solution deposition planarization technique,amorphous Y2O3films were coated on untreated Hastelloy substrate as the bed layer to obtain smooth,dense,and crack-free surface for subsequent IBAD-MgO deposition.The 50 m long IBAD-MgO and homo-epitaxial(epi)-MgO buffer layers deposited on Y2O3films exhibit excellent crystallographic consistency along the scope with full width half maximum(FWHM)values of(110)DU and(200)Dx in the range of 5.5°–6.0°and3.0°–3.5°,respectively.To match the lattice constant of YBCO material,LaMnO3cap layer was fabricated on IBAD-MgO templates by radio frequency(rf)magnetron sputtering with the FWHM values of in-plane and out-ofplane of 6.8°and 3.7°,respectively,indicating excellent biaxial texture.
文摘为了保证定向长钻孔全区段的抽采效果,提高定向长钻孔的抽采效率,以高家庄煤矿3号煤层为研究对象,通过COMSOL Multiphysics模拟定向长钻孔孔内负压沿钻孔长度方向的衰减变化规律,进而分析钻孔抽采影响下煤层所呈现的区域性特征,为优化钻孔长度和确定合理抽采时间提供科学依据。研究表明,随着孔口负压的增加,孔内负压损失基本无太大变化,百米负压损失为0.93~1.037 k Pa;3号煤层定向抽采钻孔合理施工长度为300~400 m。抽采纯量、日累计纯量与抽采负压呈正比关系;且随着抽采时间的增加,负压损失较抽采前期大幅下降,抽采纯量和日累计纯量逐渐增加。