Effects of quenching temperature and cooling conditions(water cooling and 10%NaCl cooling)on microstructure and mechanical properties of a 0.2%Ti low alloy martensitic wear-resistant steel used for die casting ejector...Effects of quenching temperature and cooling conditions(water cooling and 10%NaCl cooling)on microstructure and mechanical properties of a 0.2%Ti low alloy martensitic wear-resistant steel used for die casting ejector plate were investigated.The results show that lath martensite can be obtained after austenitizing in the range of 860-980℃and then water cooling.With an increase in austenitizing temperature,the precipitate content gradually decreases.The precipitates are mainly composed of TiC and Ti4C2S2,and their total content is between 1.15wt.%and 1.64wt.%.The precipitate phase concentration by water-cooling is higher than that by10%NaCl cooling due to the lower cooling rate of water cooling.As the austeniting temperature increases,the hardness and tensile strength of both water cooled and 10%NaCl cooled steels firstly increase and then decrease.The experimental steel exhibits the best comprehensive mechanical properties after being austenitized at 900℃,cooled by 10%NaCl,and then tempered at 200℃.Its hardness,ultimate tensile strength,and wear rate reach551.4 HBW,1,438.2 MPa,and 0.48×10^(-2)mg·m^(-1),respectively.展开更多
Electrochemical impedance spectroscopy, cyclic potentiodynamic polarization measurements, and scanning electron microscopy in conjunction with energy-dispersive X-ray spectroscopy were used to investigate the influenc...Electrochemical impedance spectroscopy, cyclic potentiodynamic polarization measurements, and scanning electron microscopy in conjunction with energy-dispersive X-ray spectroscopy were used to investigate the influence of mill scale and rust layer on the passivation capability and chloride-induced corrosion behaviors of conventional low-carbon(LC) steel and low-alloy(LA) steel in simulated concrete pore solution. The results show that mill scale exerts different influences on the corrosion resistance of both steels at various electrochemical stages. We propose that the high long-term corrosion resistance of LA steel is mainly achieved through the synergistic effect of a gradually formed compact, adherent and well-distributed Cr-enriched inner rust layer and the physical barrier protection effect of mill scale.展开更多
During the past thirty years, two generations of low alloy steels(ferrite/pearlite followed by bainite/martensite) have been developed and widely used in structural applications. The third-generation of low alloy stee...During the past thirty years, two generations of low alloy steels(ferrite/pearlite followed by bainite/martensite) have been developed and widely used in structural applications. The third-generation of low alloy steels is expected to achieve high strength and improved ductility and toughness, while satisfying the new demands for weight reduction, greenness, and safety. This paper reviews recent progress in the development of third-generation low alloy steels with an M^3 microstructure, namely, microstructures with multi-phase, meta-stable austenite, and multi-scale precipitates. The review summarizes the alloy designs and processing routes of microstructure control, and the mechanical properties of the alloys.The stabilization of retained austenite in low alloy steels is especially emphasized. Multi-scale nano-precipitates, including carbides of microalloying elements and Cu-rich precipitates obtained in third-generation low alloy steels, are then introduced. The structure–property relationships of third-generation alloys are also discussed. Finally, the promises and challenges to future applications are explored.展开更多
In this work, a parametric approach is presented and utilized to determine the creep properties of weldments; then the model of creep strain for cross weld specimen is given. On the basis of the experimental results, ...In this work, a parametric approach is presented and utilized to determine the creep properties of weldments; then the model of creep strain for cross weld specimen is given. On the basis of the experimental results, attempt has been made to establish equations of the isochronous stress-strain for weld joint that can predict the function of loading and service time in use of the creep data of base metal and weld metal.展开更多
A novel diffusion couple method was used to investigate the interface diffusion of arsenic into a Nb-Ti microalloyed low carbon steel and its effects on phase transformation at the interface. It is discovered that the...A novel diffusion couple method was used to investigate the interface diffusion of arsenic into a Nb-Ti microalloyed low carbon steel and its effects on phase transformation at the interface. It is discovered that the content of arsenic has great effect on grain growth and phase transformation at high temperature. When the arsenic content is no more than lwt%, there is no obvious grain growth and no obvious ferrite transitional region formed at the diffusion interface. However, when the arsenic content is no less than 5wt%, the grain grows very rapidly. In addition, the arsenic-enriched ferrite transitional layer forms at the diffusion interface in the hot-rolling process, which results from a slower diffusion rate of arsenic atoms than that of carbon in ferrite.展开更多
Machine-learning and big data are among the latest approaches in corrosion research.The biggest challenge in corrosion research is to accurately predict how materials will degrade in a given environment.Corrosion big ...Machine-learning and big data are among the latest approaches in corrosion research.The biggest challenge in corrosion research is to accurately predict how materials will degrade in a given environment.Corrosion big data is the application of mathematical methods to huge amounts of data to find correlations and infer probabilities.It is possible to use corrosion big data method to distinguish the influence of the minimal changes of alloying elements and small differences in microstructure on corrosion resistance of low alloy steels.In this research,corrosion big data evaluation methods and machine learning were used to study the effect of Sb and Sn,as well as environmental factors on the corrosion behavior of low alloy steels.Results depict corrosion big data method can accurately identify the influence of various factors on corrosion resistance of low alloy and is an effective and promising way in corrosion research.展开更多
A high-building multi-directional pipe joint(HBMDPJ)was fabricated by wire and arc additive manufacturing using high-strength low-alloy(HSLA)steel.The microstructure characteristics and transformation were observed an...A high-building multi-directional pipe joint(HBMDPJ)was fabricated by wire and arc additive manufacturing using high-strength low-alloy(HSLA)steel.The microstructure characteristics and transformation were observed and analyzed.The results show that the forming part includes four regions.The solidification zone solidifies as typical columnar crystals from a molten pool.The complete austenitizing zone forms from the solidification zone heated to a temperature greater than 1100℃,and the typical columnar crystals in this zone are difficult to observe.The partial austenitizing zone forms from the completely austenite zone heated between Ac1(austenite transition temperature)and1100℃,which is mainly equiaxed grains.After several thermal cycles,the partial austenitizing zone transforms to the tempering zone,which consistes of fully equiaxed grains.From the solidification zone to the tempering zone,the average grain size decreases from 75 to20μm.The mechanical properties of HBMDPJ satisfies the requirement for the intended application.展开更多
A newly developed low-alloy weathering steel has been exposed in two coastal sites (Qingdao in the north, Wanning in the south) in China for one year. The samples in Wanning corroded far more seriously than those in...A newly developed low-alloy weathering steel has been exposed in two coastal sites (Qingdao in the north, Wanning in the south) in China for one year. The samples in Wanning corroded far more seriously than those in Qingdao. The rust layer formed on the steel was analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), N2 adsorption approach, polarization curves, and electrochemical impedance spectroscopy (EIS). The rust formed in Qingdao contains more X-ray amorphous compounds and is more compact than that formed in Wanning. Cr and Cu are enriched in the rust layer near the steel matrix, and the phenomenon is more obvious in Qingdao than in Wanning. The rust layer formed in Qingdao suppresses the anodic and cathodic reaction more remarkably than that formed in Wanning does. The rust layer formed in Qingdao possesses a higher ability to block the permeation of chloride ions than that formed in Wanning does.展开更多
Four low-alloy hull steels with different alloy elements were selected. Theirsusceptibility to pitting corrosion was compared by means of electrochemical polarization test. Theinclusions in the steels and their pittin...Four low-alloy hull steels with different alloy elements were selected. Theirsusceptibility to pitting corrosion was compared by means of electrochemical polarization test. Theinclusions in the steels and their pitting corrosion characteristics were studied by an electronprobe micro-analyzer (EPMA). The results indicate that some inclusions are the main sources ofpitting corrosion. The susceptibility of nickel-chromium steel to pit initiation is less than thatof manganese steel. Under the same conditions, nickel-chromium steel is easier to passivate thanmanganese steel, and the passive films on nickel-chromium steel surface are more stable than that onmanganese steel. In low-alloy steels, the higher the contents of nickel and chromium, the lower thecritical passive pH value. In the same kind of steel, multi-phase inclusions containing sulfide areeasier to initiate pitting corrosion than other inclusions.展开更多
Dual phase heat treatment is an economical and effective way for improving the properties of low carbon steels and low-alloy steel materials. In this paper, the microstructures and mechanical properties of 20MnSi stee...Dual phase heat treatment is an economical and effective way for improving the properties of low carbon steels and low-alloy steel materials. In this paper, the microstructures and mechanical properties of 20MnSi steel treated by different dual phase heat treatment have been studied. The results show that dual phase heat treatment with pre-quenching technique and then heating from room temperature to the critical zone can achieve finer and more homogeneous microstructure than that with pre-normalizing technique and then cooling from austenite zone to the critical zone. Among all factors affecting dual phase heat treatment, quenching temperature at the critical zone and tempering temperature play an important part in mechanical properties. Using proper dual phase heat treatment technique with computer optimized parameters, the yield strength, the elongation and impact toughness of 20MnSi can reach 860 MPa, 16% and 207 MPa respectively.展开更多
The influence of soaking time in deep cryogenic treatment on the tensile and impact properties of low-alloy medium-carbon HY-TUF steel was investigated in this study. Microstructural studies based on phase distributio...The influence of soaking time in deep cryogenic treatment on the tensile and impact properties of low-alloy medium-carbon HY-TUF steel was investigated in this study. Microstructural studies based on phase distribution mapping by electron backscatter diffraction show that the deep cryogenic process causes a decrease in the content of retained austenite and an increase in the volume fraction of η-carbide with increasing soaking time up to 48 h. The decrease in the content of retained austenite from ~1.23vol% to 0.48vol% suggests an isothermal martensitic transformation at 77 K. The η-type precipitates formed in deep cryogenic-treated martensite over 48 h have the Hirotsu and Nagakura orientation relation with the martensitic matrix. Furthermore, a high coherency between η-carbide and the martensitic matrix is observed by high-resolution transmission electron microscopy. The variations in macrohardness, yield strength, ultimate tensile strength, and ductility with soaking time in the deep cryogenic process show a peak/plateau trend.展开更多
Based on the steady-state strain measured by single-pass hot compression tests,the method by a double-pass hot compression testing was developed to measure the metadynamic-recrystallization kinetics.The metadynamic re...Based on the steady-state strain measured by single-pass hot compression tests,the method by a double-pass hot compression testing was developed to measure the metadynamic-recrystallization kinetics.The metadynamic recrystallization behavior of low-alloy steel Q345B during hot compression deformation was investigated in the temperature range of 1 000-1 100℃,the strain rate range of 0.01-0.10 s -1 and the interpass time range of 0.5-50 s on a Gleeble-3500 thermo-simulation machine.The results show that metadynamic recrystallization during the interpass time can be observed.As the deformation temperature and strain rate increase,softening caused by metadynamic recrystallization is obvious.According to the data of thermo-simulation,the metadynamic recrystallization activation energy is obtained to be Qmd=100.674 kJ/mol and metadynamic recrystallization kinetics model is set up.Finally,the error analysis of metadynamic recrystallization kinetics model proves that the model has high accuracy(correlation coefficient R=0.988 6).展开更多
In order to investigate the regularity of metal magnetic signals of ferromagnetic materials under the effect of applied load, the static tensile test of Q235 steel and 18CrNiWA steel plate specimens were conducted and...In order to investigate the regularity of metal magnetic signals of ferromagnetic materials under the effect of applied load, the static tensile test of Q235 steel and 18CrNiWA steel plate specimens were conducted and metal magnetic memory signals of specimens were measured during the test process. The influencing factors of metal magnetic memory signals and the relationship between axial applied load and signals were analyzed. The fracture and microstructure of the specimens were observed. The results show that the magnetic signals corresponding to the measured points change linearly approximately with increasing axial load. The microstructure of Q235 steel is ferrite and perlite, whereas that of 18CrNiWA steel is bainite and low-carbon martensite. The fracture of these two kinds of specimens is ductile rupture; carbon content of specimen materials and dislocation glide give much contribution to the characteristics of magnetic curves.展开更多
The effect of microstructure variation on the corrosion behavior of high-strength low-alloy(HSLA) steel was investigated. The protective property of the corrosion product layer was also explored. Experimental result...The effect of microstructure variation on the corrosion behavior of high-strength low-alloy(HSLA) steel was investigated. The protective property of the corrosion product layer was also explored. Experimental results reveal that the type of microstructure has significant effect on the corrosion resistance of HSLA steel. The measurement results of weight loss, potentiodynamic polarization curves, and electrochemical impedance spectroscopy indicate that the steel with acicular ferrite microstructure exhibits the lowest corrosion rate. Martensite exhibits a reduced corrosion resistance compared with polygonal ferrite. It is found that the surface of the acicular ferrite specimen uniformly covered by corrosion products is seemingly denser and more compact than those of the other two microstructures, and can provide some amount of protection to the steel; thus, the charge transfer resistance and modulus values of the acicular ferrite specimen are the largest. However, corrosion products on martensite and polygonal ferrite are generally loose, porous, and defective, and can provide minor protectiveness; thus, the charge transfer resistance values for polygonal ferrite and martensite are lower.展开更多
Embrittlement of a Cr-Mo2.25CrlMo steel stemming from neutron irradiation at 270℃ is studied by virtue of small punch testing in conjunction with scanning electron microscopy. The ductile-brittle transition temperatu...Embrittlement of a Cr-Mo2.25CrlMo steel stemming from neutron irradiation at 270℃ is studied by virtue of small punch testing in conjunction with scanning electron microscopy. The ductile-brittle transition temperature determined by the small punch test is much lower than that determined by the standard Charpy test. There is some irradiation-induced embrittlement effect after the steel is irradiated for 46 days with a neutron dose rate of 1.05×10^18dpa/s (displacement per atom per second).展开更多
A method of fuzzy identification based on T-S fuzzy model was proposed for predicting temperature Ms from chemical composition, austenitizing temperature and time for low alloy steel. The degree of membership of each ...A method of fuzzy identification based on T-S fuzzy model was proposed for predicting temperature Ms from chemical composition, austenitizing temperature and time for low alloy steel. The degree of membership of each sample was calculated with fuzzy clustering algorithm. Kalman filtering was used to identify the consequent parameters. Compared with the results obtained by empirical models based on the same data, the results by the fuzzy method showed good precision. The accuracy of the fuzzy model is almost 6 times higher than that of the best empirical model. The influence of alloying elements, austenitizing temperature and time on Ms was analyzed quantitatively by using the fuzzy model. It is shown that there exists a nonlinear relationship between the contents of alloying elements in steels and their Ms, and the effects of austenitizing temperature and time on Ms temperature cannot be neglected.展开更多
The size of austenite grain has significant effects on components and proportions ofvarious ferrites in low-alloy steel weld metal. Therefore, it is important to determinethe size of austenite grain in the weld metal....The size of austenite grain has significant effects on components and proportions ofvarious ferrites in low-alloy steel weld metal. Therefore, it is important to determinethe size of austenite grain in the weld metal. In this paper, a model based upon thecarbon diffusion rate is developed for computing austenite grain size in low-alloy steelweld metal during continuous cooling. The model takes into account the effects of theweld thermal cycles, inclusion particles and various alloy elements on the austenitegrain growth. The calculating results agree reasonably with those reported experimentalobservations. The model demonstrates a significant promise to understand the weldmicrostructure and properties based on the welding science.展开更多
For some casting low-alloy steels,traditional quenching and tempering heat treatments can improve the strength;however,sometimes the ductility is not satisf ied.Therefore,some kind of effective heat treatment method s...For some casting low-alloy steels,traditional quenching and tempering heat treatments can improve the strength;however,sometimes the ductility is not satisf ied.Therefore,some kind of effective heat treatment method seems necessary;one which could improve the ductility,but not seriously affect the strength.In this paper,the effect of inter-critical quenching(IQ)on the mechanical properties of casting low-alloy steel was studied.IQ was added between quenching and tempering heat treatment;and the microstructure and mechanical properties were compared to the same steel with the traditional quenching and tempering treatments.The experimental results show that the microstructure comprises small-size ferrite and martensite when the IQ is adopted;and that different temperatures can control the ferrite quantity and distribution,and,as a result,infl uence the mechanical properties.In the case of IQ,the tensile strength decreases just a little,but the ductility increases a lot;and the strength-ductility product(its value is the arithmetic product of elongation and tensile strength)increases by between 6%and 10%,which means the IQ heat treatment can improve comprehensive mechanical properties.展开更多
文摘Effects of quenching temperature and cooling conditions(water cooling and 10%NaCl cooling)on microstructure and mechanical properties of a 0.2%Ti low alloy martensitic wear-resistant steel used for die casting ejector plate were investigated.The results show that lath martensite can be obtained after austenitizing in the range of 860-980℃and then water cooling.With an increase in austenitizing temperature,the precipitate content gradually decreases.The precipitates are mainly composed of TiC and Ti4C2S2,and their total content is between 1.15wt.%and 1.64wt.%.The precipitate phase concentration by water-cooling is higher than that by10%NaCl cooling due to the lower cooling rate of water cooling.As the austeniting temperature increases,the hardness and tensile strength of both water cooled and 10%NaCl cooled steels firstly increase and then decrease.The experimental steel exhibits the best comprehensive mechanical properties after being austenitized at 900℃,cooled by 10%NaCl,and then tempered at 200℃.Its hardness,ultimate tensile strength,and wear rate reach551.4 HBW,1,438.2 MPa,and 0.48×10^(-2)mg·m^(-1),respectively.
基金the support by the National Natural Science Foundation of China(Nos.51208098 and 51678144)the National Basic Research Program of China(No.2015CB655100)+1 种基金the Natural Science Foundation of Jiangsu Province(No.BK20161420)Industry-University Research Cooperative Innovation Fund of Jiangsu Province(No.BY2013091)
文摘Electrochemical impedance spectroscopy, cyclic potentiodynamic polarization measurements, and scanning electron microscopy in conjunction with energy-dispersive X-ray spectroscopy were used to investigate the influence of mill scale and rust layer on the passivation capability and chloride-induced corrosion behaviors of conventional low-carbon(LC) steel and low-alloy(LA) steel in simulated concrete pore solution. The results show that mill scale exerts different influences on the corrosion resistance of both steels at various electrochemical stages. We propose that the high long-term corrosion resistance of LA steel is mainly achieved through the synergistic effect of a gradually formed compact, adherent and well-distributed Cr-enriched inner rust layer and the physical barrier protection effect of mill scale.
基金financially supported by the National Natural Science Foundation of China (No. 51701012)the National Basic Research Program of China (973 Program: No. 2010CB630801)the Fundamental Research Funds for the Central Universities (No. FRF-TP-17-004A1)
文摘During the past thirty years, two generations of low alloy steels(ferrite/pearlite followed by bainite/martensite) have been developed and widely used in structural applications. The third-generation of low alloy steels is expected to achieve high strength and improved ductility and toughness, while satisfying the new demands for weight reduction, greenness, and safety. This paper reviews recent progress in the development of third-generation low alloy steels with an M^3 microstructure, namely, microstructures with multi-phase, meta-stable austenite, and multi-scale precipitates. The review summarizes the alloy designs and processing routes of microstructure control, and the mechanical properties of the alloys.The stabilization of retained austenite in low alloy steels is especially emphasized. Multi-scale nano-precipitates, including carbides of microalloying elements and Cu-rich precipitates obtained in third-generation low alloy steels, are then introduced. The structure–property relationships of third-generation alloys are also discussed. Finally, the promises and challenges to future applications are explored.
基金supports provided by Natural Science Foundation of Shanghai(contract No.03ZR14022)the“Tenth Five”National Key Technological Research and Development Program(contract No.2001BA803B03)National Natural Science Foundation of China(contract No.50225517)are gratefully acknowledged.
文摘In this work, a parametric approach is presented and utilized to determine the creep properties of weldments; then the model of creep strain for cross weld specimen is given. On the basis of the experimental results, attempt has been made to establish equations of the isochronous stress-strain for weld joint that can predict the function of loading and service time in use of the creep data of base metal and weld metal.
基金supported by the National Natural Science Foundation of China (No.50874083)the China Postdoctoral Science Foundation (No.201104493)the China International Scientific and Technological Cooperation Projects (No.2010DFA52130)
文摘A novel diffusion couple method was used to investigate the interface diffusion of arsenic into a Nb-Ti microalloyed low carbon steel and its effects on phase transformation at the interface. It is discovered that the content of arsenic has great effect on grain growth and phase transformation at high temperature. When the arsenic content is no more than lwt%, there is no obvious grain growth and no obvious ferrite transitional region formed at the diffusion interface. However, when the arsenic content is no less than 5wt%, the grain grows very rapidly. In addition, the arsenic-enriched ferrite transitional layer forms at the diffusion interface in the hot-rolling process, which results from a slower diffusion rate of arsenic atoms than that of carbon in ferrite.
基金financially supported by the Postdoctor Research Foundation of Shunde Graduate School of University of Science and Technology Beijing(No.2022 B H003)。
文摘Machine-learning and big data are among the latest approaches in corrosion research.The biggest challenge in corrosion research is to accurately predict how materials will degrade in a given environment.Corrosion big data is the application of mathematical methods to huge amounts of data to find correlations and infer probabilities.It is possible to use corrosion big data method to distinguish the influence of the minimal changes of alloying elements and small differences in microstructure on corrosion resistance of low alloy steels.In this research,corrosion big data evaluation methods and machine learning were used to study the effect of Sb and Sn,as well as environmental factors on the corrosion behavior of low alloy steels.Results depict corrosion big data method can accurately identify the influence of various factors on corrosion resistance of low alloy and is an effective and promising way in corrosion research.
基金financially supported by the National Key R&D Program of China(No.2017YFB1103200)the Independent Innovation Research Fund Project of Huazhong University of Science and Technology(No.2018KFYXMPT002)。
文摘A high-building multi-directional pipe joint(HBMDPJ)was fabricated by wire and arc additive manufacturing using high-strength low-alloy(HSLA)steel.The microstructure characteristics and transformation were observed and analyzed.The results show that the forming part includes four regions.The solidification zone solidifies as typical columnar crystals from a molten pool.The complete austenitizing zone forms from the solidification zone heated to a temperature greater than 1100℃,and the typical columnar crystals in this zone are difficult to observe.The partial austenitizing zone forms from the completely austenite zone heated between Ac1(austenite transition temperature)and1100℃,which is mainly equiaxed grains.After several thermal cycles,the partial austenitizing zone transforms to the tempering zone,which consistes of fully equiaxed grains.From the solidification zone to the tempering zone,the average grain size decreases from 75 to20μm.The mechanical properties of HBMDPJ satisfies the requirement for the intended application.
基金supported by the National Key Basic Research and Development Program of China (No.2004CB619102) and New Century Excellent Talents in China.
文摘A newly developed low-alloy weathering steel has been exposed in two coastal sites (Qingdao in the north, Wanning in the south) in China for one year. The samples in Wanning corroded far more seriously than those in Qingdao. The rust layer formed on the steel was analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), N2 adsorption approach, polarization curves, and electrochemical impedance spectroscopy (EIS). The rust formed in Qingdao contains more X-ray amorphous compounds and is more compact than that formed in Wanning. Cr and Cu are enriched in the rust layer near the steel matrix, and the phenomenon is more obvious in Qingdao than in Wanning. The rust layer formed in Qingdao suppresses the anodic and cathodic reaction more remarkably than that formed in Wanning does. The rust layer formed in Qingdao possesses a higher ability to block the permeation of chloride ions than that formed in Wanning does.
文摘Four low-alloy hull steels with different alloy elements were selected. Theirsusceptibility to pitting corrosion was compared by means of electrochemical polarization test. Theinclusions in the steels and their pitting corrosion characteristics were studied by an electronprobe micro-analyzer (EPMA). The results indicate that some inclusions are the main sources ofpitting corrosion. The susceptibility of nickel-chromium steel to pit initiation is less than thatof manganese steel. Under the same conditions, nickel-chromium steel is easier to passivate thanmanganese steel, and the passive films on nickel-chromium steel surface are more stable than that onmanganese steel. In low-alloy steels, the higher the contents of nickel and chromium, the lower thecritical passive pH value. In the same kind of steel, multi-phase inclusions containing sulfide areeasier to initiate pitting corrosion than other inclusions.
文摘Dual phase heat treatment is an economical and effective way for improving the properties of low carbon steels and low-alloy steel materials. In this paper, the microstructures and mechanical properties of 20MnSi steel treated by different dual phase heat treatment have been studied. The results show that dual phase heat treatment with pre-quenching technique and then heating from room temperature to the critical zone can achieve finer and more homogeneous microstructure than that with pre-normalizing technique and then cooling from austenite zone to the critical zone. Among all factors affecting dual phase heat treatment, quenching temperature at the critical zone and tempering temperature play an important part in mechanical properties. Using proper dual phase heat treatment technique with computer optimized parameters, the yield strength, the elongation and impact toughness of 20MnSi can reach 860 MPa, 16% and 207 MPa respectively.
文摘The influence of soaking time in deep cryogenic treatment on the tensile and impact properties of low-alloy medium-carbon HY-TUF steel was investigated in this study. Microstructural studies based on phase distribution mapping by electron backscatter diffraction show that the deep cryogenic process causes a decrease in the content of retained austenite and an increase in the volume fraction of η-carbide with increasing soaking time up to 48 h. The decrease in the content of retained austenite from ~1.23vol% to 0.48vol% suggests an isothermal martensitic transformation at 77 K. The η-type precipitates formed in deep cryogenic-treated martensite over 48 h have the Hirotsu and Nagakura orientation relation with the martensitic matrix. Furthermore, a high coherency between η-carbide and the martensitic matrix is observed by high-resolution transmission electron microscopy. The variations in macrohardness, yield strength, ultimate tensile strength, and ductility with soaking time in the deep cryogenic process show a peak/plateau trend.
基金Project(101048) supported by Fok Ying Tung Education FoundationProject(E2008000835) supported by the Natural Science Foundation of Hebei Province,China
文摘Based on the steady-state strain measured by single-pass hot compression tests,the method by a double-pass hot compression testing was developed to measure the metadynamic-recrystallization kinetics.The metadynamic recrystallization behavior of low-alloy steel Q345B during hot compression deformation was investigated in the temperature range of 1 000-1 100℃,the strain rate range of 0.01-0.10 s -1 and the interpass time range of 0.5-50 s on a Gleeble-3500 thermo-simulation machine.The results show that metadynamic recrystallization during the interpass time can be observed.As the deformation temperature and strain rate increase,softening caused by metadynamic recrystallization is obvious.According to the data of thermo-simulation,the metadynamic recrystallization activation energy is obtained to be Qmd=100.674 kJ/mol and metadynamic recrystallization kinetics model is set up.Finally,the error analysis of metadynamic recrystallization kinetics model proves that the model has high accuracy(correlation coefficient R=0.988 6).
基金Projects(50235030, 50505052) supported by the National Natural Science Foundation of China
文摘In order to investigate the regularity of metal magnetic signals of ferromagnetic materials under the effect of applied load, the static tensile test of Q235 steel and 18CrNiWA steel plate specimens were conducted and metal magnetic memory signals of specimens were measured during the test process. The influencing factors of metal magnetic memory signals and the relationship between axial applied load and signals were analyzed. The fracture and microstructure of the specimens were observed. The results show that the magnetic signals corresponding to the measured points change linearly approximately with increasing axial load. The microstructure of Q235 steel is ferrite and perlite, whereas that of 18CrNiWA steel is bainite and low-carbon martensite. The fracture of these two kinds of specimens is ductile rupture; carbon content of specimen materials and dislocation glide give much contribution to the characteristics of magnetic curves.
基金financially supported by the National Science Fund for Distinguished Young Scholars (No. 51325401)the International Thermonuclear Experimental Reactor (ITER) Program Special Project (No. 2014GB125006)+1 种基金the Major State Basic Research Development Program of China (No. 2014CB046805)the National Natural Science Foundation of China (No. 51474156)
文摘The effect of microstructure variation on the corrosion behavior of high-strength low-alloy(HSLA) steel was investigated. The protective property of the corrosion product layer was also explored. Experimental results reveal that the type of microstructure has significant effect on the corrosion resistance of HSLA steel. The measurement results of weight loss, potentiodynamic polarization curves, and electrochemical impedance spectroscopy indicate that the steel with acicular ferrite microstructure exhibits the lowest corrosion rate. Martensite exhibits a reduced corrosion resistance compared with polygonal ferrite. It is found that the surface of the acicular ferrite specimen uniformly covered by corrosion products is seemingly denser and more compact than those of the other two microstructures, and can provide some amount of protection to the steel; thus, the charge transfer resistance and modulus values of the acicular ferrite specimen are the largest. However, corrosion products on martensite and polygonal ferrite are generally loose, porous, and defective, and can provide minor protectiveness; thus, the charge transfer resistance values for polygonal ferrite and martensite are lower.
文摘Embrittlement of a Cr-Mo2.25CrlMo steel stemming from neutron irradiation at 270℃ is studied by virtue of small punch testing in conjunction with scanning electron microscopy. The ductile-brittle transition temperature determined by the small punch test is much lower than that determined by the standard Charpy test. There is some irradiation-induced embrittlement effect after the steel is irradiated for 46 days with a neutron dose rate of 1.05×10^18dpa/s (displacement per atom per second).
文摘A method of fuzzy identification based on T-S fuzzy model was proposed for predicting temperature Ms from chemical composition, austenitizing temperature and time for low alloy steel. The degree of membership of each sample was calculated with fuzzy clustering algorithm. Kalman filtering was used to identify the consequent parameters. Compared with the results obtained by empirical models based on the same data, the results by the fuzzy method showed good precision. The accuracy of the fuzzy model is almost 6 times higher than that of the best empirical model. The influence of alloying elements, austenitizing temperature and time on Ms was analyzed quantitatively by using the fuzzy model. It is shown that there exists a nonlinear relationship between the contents of alloying elements in steels and their Ms, and the effects of austenitizing temperature and time on Ms temperature cannot be neglected.
文摘The size of austenite grain has significant effects on components and proportions ofvarious ferrites in low-alloy steel weld metal. Therefore, it is important to determinethe size of austenite grain in the weld metal. In this paper, a model based upon thecarbon diffusion rate is developed for computing austenite grain size in low-alloy steelweld metal during continuous cooling. The model takes into account the effects of theweld thermal cycles, inclusion particles and various alloy elements on the austenitegrain growth. The calculating results agree reasonably with those reported experimentalobservations. The model demonstrates a significant promise to understand the weldmicrostructure and properties based on the welding science.
文摘For some casting low-alloy steels,traditional quenching and tempering heat treatments can improve the strength;however,sometimes the ductility is not satisf ied.Therefore,some kind of effective heat treatment method seems necessary;one which could improve the ductility,but not seriously affect the strength.In this paper,the effect of inter-critical quenching(IQ)on the mechanical properties of casting low-alloy steel was studied.IQ was added between quenching and tempering heat treatment;and the microstructure and mechanical properties were compared to the same steel with the traditional quenching and tempering treatments.The experimental results show that the microstructure comprises small-size ferrite and martensite when the IQ is adopted;and that different temperatures can control the ferrite quantity and distribution,and,as a result,infl uence the mechanical properties.In the case of IQ,the tensile strength decreases just a little,but the ductility increases a lot;and the strength-ductility product(its value is the arithmetic product of elongation and tensile strength)increases by between 6%and 10%,which means the IQ heat treatment can improve comprehensive mechanical properties.