Effects of quenching temperature and cooling conditions(water cooling and 10%NaCl cooling)on microstructure and mechanical properties of a 0.2%Ti low alloy martensitic wear-resistant steel used for die casting ejector...Effects of quenching temperature and cooling conditions(water cooling and 10%NaCl cooling)on microstructure and mechanical properties of a 0.2%Ti low alloy martensitic wear-resistant steel used for die casting ejector plate were investigated.The results show that lath martensite can be obtained after austenitizing in the range of 860-980℃and then water cooling.With an increase in austenitizing temperature,the precipitate content gradually decreases.The precipitates are mainly composed of TiC and Ti4C2S2,and their total content is between 1.15wt.%and 1.64wt.%.The precipitate phase concentration by water-cooling is higher than that by10%NaCl cooling due to the lower cooling rate of water cooling.As the austeniting temperature increases,the hardness and tensile strength of both water cooled and 10%NaCl cooled steels firstly increase and then decrease.The experimental steel exhibits the best comprehensive mechanical properties after being austenitized at 900℃,cooled by 10%NaCl,and then tempered at 200℃.Its hardness,ultimate tensile strength,and wear rate reach551.4 HBW,1,438.2 MPa,and 0.48×10^(-2)mg·m^(-1),respectively.展开更多
The effects of Si content on combinations of important properties such as hardness, hardenability, and weldability in addition to strength increment were systematically investigated to develop a Mo and V free low allo...The effects of Si content on combinations of important properties such as hardness, hardenability, and weldability in addition to strength increment were systematically investigated to develop a Mo and V free low alloy cast steel for automobile cold pressing die insert. For the evaluation of the applicability as the die insert, the mechanical properties were measured after spheroidization annealing （SA）, quenching and tempering （Q/T）, and flame hardening （FH） treatments, respectively. The developed 0.8%-1.6%Si containing Mo and V free alloy cast steels showed excellent matrix strengthening effect, hardenability, and weldability, fulfilling the industrial criterion of the mechanical properties for the die insert.展开更多
Corrosion behaviour of cast iron and low alloy steel in cocoa liquor and well water was investigated. The average weight losses of the specimens were measured using digital weighing balance. The results showed that th...Corrosion behaviour of cast iron and low alloy steel in cocoa liquor and well water was investigated. The average weight losses of the specimens were measured using digital weighing balance. The results showed that the weight losses of both cast iron and low alloy steel in both media increases with time. Corrosion rate of cast iron in cocoa liquor increases rapidly with time for up to 336 hours (1000 μm/yr), but in well water the rapid rate of corrosion only lasted up to 187 hours (1160 μm/yr) thereafter it continuously dropping until 264 hours (667 μm/yr) after which it remains constant. Low alloy steel corroded faster in cocoa liquor up to 264 hours (200 μm/yr), whereas the initial rapid corrosion rate only lasted up to 168 hours (180 μm/yr) in well water environment. The results revealed that low alloy steel exhibited better corrosion resistance in both media, with cocoa liquor been more aggressive. Thus, low alloy steel will be a better material for piping and pumping system in cocoa processing industries.展开更多
The fracture modes of low alloy steels and cast irons under tensile and fatigue conditions were identified by electron back-scattered diffraction（EBSD） misorientation analysis in this research. The curves of grain r...The fracture modes of low alloy steels and cast irons under tensile and fatigue conditions were identified by electron back-scattered diffraction（EBSD） misorientation analysis in this research. The curves of grain reference orientation deviation（GROD） distribution perpendicular to the fracture surface were obtained by EBSD observation, and the characteristics of each fracture mode were identified. The GROD value of the specimen fractured in tension decreases to a constant related to the elongation of corresponding specimen in the far field（farther than 5 mm away from the fracture surface）. The peak exhibits in GROD curves of two smooth specimens and a notched specimen near the fracture surface（within 5 mm away from the fracture surface）, and the formation mechanisms were discussed in detail based on the influences of specimen geometries（smooth or notched） and material toughness. The GROD value of fatigue fractured specimen is close to that at undeformed condition in the whole field, except the small area near the crack path. The loading conditions（constant stress amplitude loading or constant stress intensity factor range K loading） and the EBSD striation formation during fatigue crack propagation were also studied by EBSD observation parallel to the crack path.展开更多
文摘Effects of quenching temperature and cooling conditions(water cooling and 10%NaCl cooling)on microstructure and mechanical properties of a 0.2%Ti low alloy martensitic wear-resistant steel used for die casting ejector plate were investigated.The results show that lath martensite can be obtained after austenitizing in the range of 860-980℃and then water cooling.With an increase in austenitizing temperature,the precipitate content gradually decreases.The precipitates are mainly composed of TiC and Ti4C2S2,and their total content is between 1.15wt.%and 1.64wt.%.The precipitate phase concentration by water-cooling is higher than that by10%NaCl cooling due to the lower cooling rate of water cooling.As the austeniting temperature increases,the hardness and tensile strength of both water cooled and 10%NaCl cooled steels firstly increase and then decrease.The experimental steel exhibits the best comprehensive mechanical properties after being austenitized at 900℃,cooled by 10%NaCl,and then tempered at 200℃.Its hardness,ultimate tensile strength,and wear rate reach551.4 HBW,1,438.2 MPa,and 0.48×10^(-2)mg·m^(-1),respectively.
文摘The effects of Si content on combinations of important properties such as hardness, hardenability, and weldability in addition to strength increment were systematically investigated to develop a Mo and V free low alloy cast steel for automobile cold pressing die insert. For the evaluation of the applicability as the die insert, the mechanical properties were measured after spheroidization annealing （SA）, quenching and tempering （Q/T）, and flame hardening （FH） treatments, respectively. The developed 0.8%-1.6%Si containing Mo and V free alloy cast steels showed excellent matrix strengthening effect, hardenability, and weldability, fulfilling the industrial criterion of the mechanical properties for the die insert.
文摘Corrosion behaviour of cast iron and low alloy steel in cocoa liquor and well water was investigated. The average weight losses of the specimens were measured using digital weighing balance. The results showed that the weight losses of both cast iron and low alloy steel in both media increases with time. Corrosion rate of cast iron in cocoa liquor increases rapidly with time for up to 336 hours (1000 μm/yr), but in well water the rapid rate of corrosion only lasted up to 187 hours (1160 μm/yr) thereafter it continuously dropping until 264 hours (667 μm/yr) after which it remains constant. Low alloy steel corroded faster in cocoa liquor up to 264 hours (200 μm/yr), whereas the initial rapid corrosion rate only lasted up to 168 hours (180 μm/yr) in well water environment. The results revealed that low alloy steel exhibited better corrosion resistance in both media, with cocoa liquor been more aggressive. Thus, low alloy steel will be a better material for piping and pumping system in cocoa processing industries.
基金financially supported by Mitsubishi Heavy Industries,Ltd.,Japanthe National Natural Science Foundation of China(Nos.11572171,11632010 and U1533134)the opening project(No.KFJJ15-12M)of State Key Laboratory of Explosion Science and Technology(Beijing Institute of Technology)
文摘The fracture modes of low alloy steels and cast irons under tensile and fatigue conditions were identified by electron back-scattered diffraction（EBSD） misorientation analysis in this research. The curves of grain reference orientation deviation（GROD） distribution perpendicular to the fracture surface were obtained by EBSD observation, and the characteristics of each fracture mode were identified. The GROD value of the specimen fractured in tension decreases to a constant related to the elongation of corresponding specimen in the far field（farther than 5 mm away from the fracture surface）. The peak exhibits in GROD curves of two smooth specimens and a notched specimen near the fracture surface（within 5 mm away from the fracture surface）, and the formation mechanisms were discussed in detail based on the influences of specimen geometries（smooth or notched） and material toughness. The GROD value of fatigue fractured specimen is close to that at undeformed condition in the whole field, except the small area near the crack path. The loading conditions（constant stress amplitude loading or constant stress intensity factor range K loading） and the EBSD striation formation during fatigue crack propagation were also studied by EBSD observation parallel to the crack path.