Controlled Rolling and Cooling Process for Low Carbon Cold Forging Steel

Effect of controlled rolling and cooling process on the mechanical properties of low carbon cold forging steel was investigated for different processing parameters of a laboratory hot rolling mill. The results show that the specimens with fast cooling after hot rolling exhibit very good mechanical properties, and the improvement of the mechanical properties can be attributed mainly to the ferrite-grain refinement. The mechanical properties increase with decreasing final cooling temperature within the range from 670 ℃ to 570 ℃ due to the finer interlamellar spacing of pearlite colony. The specimen with fast cooling after low temperature rolling shows the highest values of the mechanical properties. The effect of the ferrite grain size on the mechanical properties was greater than that of pearlite morphology in the present study. The mechanical properties of specimens by controlled rolling and cooling process without thermal treatment were greatly superior to that of the same specimens by the conventional rolling, and their tensile strength reached 490 MPa grade even in the case of low temperature rolling without controlled rolling. It might be expected to realize the substitution medium-carbon by low-carbon for 490 MPa grade cold forging steel with controlled rolling and cooling process.

Effect of Thermomechanical Controlled Processing on Mechanical Properties of 490 MPa Grade Low Carbon Cold Heading Steel

Thermomechanical controlled processing （TMCP） of low carbon cold heading steel in different austenite conditions were conducted by a laboratory hot rolling mill. Effect of various processing parameters on the mechanical properties of the steel was investigated. The results showed that the mechanical properties of the low carbon cold heading steel could be significantly improved by TMCP without heat treatment. The improvement of mechanical properties can be attributed mainly to the ferrite grain refinement due to low temperature rolling. In the experiments the better ultimate tensile strength and ductility are obtained by lowering finishing cooling temperature within the temperature range from 650 ℃ to 550 ℃ since the interlamellar space in pearlite colonies become smaller. Good mechanical properties can be obtained in a proper austenite condition and thermomechanical processing parameter. The ferrite morphology has a more pronounced effect on the mechanical behavior than refinement of the microstructure. It is possible to realize the replacement of medium-carbon by low-carbon for 490 MPa grade cold heading steel with TMCP.