Nanometer SnO2 particles were synthesized by sol-gel dialytic processes and used as a support to prepare CuO supported catalysts via a deposition-precipitation method. The samples were characterized by means of TG-DTA...Nanometer SnO2 particles were synthesized by sol-gel dialytic processes and used as a support to prepare CuO supported catalysts via a deposition-precipitation method. The samples were characterized by means of TG-DTA, XRD, H2-TPR and XPS. The catalytic activity of the CuO/TiO2-SnO2 catalysts was markedly depended on the loading of CuO, and the optimum CuO loading was 8 wt.% (Tloo = 80 ℃). The CuO/TiO2-SnO2 catalysts exhibited much higher catalytic activity than the CuO/TiO2 and CuO/SnO2 catalysts. H2-TPR result indicated that a large amount of CuO formed the active site for CO oxidation in 8 wt.% CuO/TiO2-SnO2 catalyst.展开更多
High active and stable gold catalysts supported on crystalline Fe203 and CeO2/Fe2O3 were prepared via the deposition-precipitation method. The catalyst with a Au load of 1.0% calcined at 180 ℃ showed a CO conversion ...High active and stable gold catalysts supported on crystalline Fe203 and CeO2/Fe2O3 were prepared via the deposition-precipitation method. The catalyst with a Au load of 1.0% calcined at 180 ℃ showed a CO conversion of 100% at -8.9℃, while Au/CeO2/Fe2O3 converted CO completely at -16.1 ℃. Even having been calcined at 500 ℃, Au/Fe2O3 still exhibited significant catalytic activity, achieving full conversion of CO at 61.6℃. The catalyst with a low Au load of 0.5% could convert CO completely at room temperature and kept the activity unchanged for at least 150 h. N2 adsorption-desorption measurements show that the crystalline supports possessed a high specific surface area of about 200 m2/g. Characterizations of X-ray diffraction and transmission electron microscopy indicate that gold species were highly dispersed as nano or sub-nano particles on the supports. Even after the catalyst was calcined at 500 ℃, the Au particles remained in a nano-size of about 6--10 nm. X-ray photoelectron spectra reveal that the supported Au existed in metallic state Au0. The modification of Au/Fe2O3 by CeO2 proved to be beneficial to the inhibition of crystallization of Fe2O3 and the stabilization of gold particles in dispersed state, consequently promoting catalytic activity.展开更多
Mixed iron-cobalt oxide (Co/Fe molar ratio = 1/5) are prepared using a simple co-precipitation procedure and studied for the catalytic oxidation of carbon monoxide. In particular, the effects of a range of preparati...Mixed iron-cobalt oxide (Co/Fe molar ratio = 1/5) are prepared using a simple co-precipitation procedure and studied for the catalytic oxidation of carbon monoxide. In particular, the effects of a range of preparation variables such as pH value when precipitation, aging temperature, precipitation agent type and aging time are investigated on the catalytic performance of synthesized Fe-Co oxides in CO oxidation reaction. In addition, the preparation factors were optimized by Taguchi design method. The optimized sample was characterized by XRD, N2 adsortion/desorption, TEM and TGA/DTA techniques. The results reveal that the optimized sample shows a mesoporous structure with a narrow pore size distribution centered in the range of 2-7 nm. The sample prepared under optimized conditions has high activity and stability toward removal of carbon monoxide at lower temperatures. It is shown that different preparation variables influence the catalytic performance of Fe-Co oxide in CO oxidation reaction.展开更多
CeO2 was synthesized via sol-gel process and used as supporter to prepare CuO/CeO2, Cu/CeO2 catalysts by impregnation method. The catalytic properties and characterization of CeO2, CuO/CeO2 and Cu/CeO2 catalysts were ...CeO2 was synthesized via sol-gel process and used as supporter to prepare CuO/CeO2, Cu/CeO2 catalysts by impregnation method. The catalytic properties and characterization of CeO2, CuO/CeO2 and Cu/CeO2 catalysts were examined by means of a microreactor-GC system, HRTEM, XRD, TPR and XPS techniques. The results show that CuO has not catalytic activity and the activity of CeO2 is quite low for CO oxidation. However, the catalytic activity of CuO/CeO2 and Cu/ CeO2 catalysts increases significantly. Furthermore, the activity of CuO/CeO2 is higher than that of Cu/CeO2 catalysts.展开更多
The effects of CeO2 contents and silica carrier porosity with their pore diameters ranging from 5.2 nm to 12.5 nm of CuO-CeO2/SiO2 cata-lysts in CO oxidation were investigated.The catalysts were characterized by N2 ad...The effects of CeO2 contents and silica carrier porosity with their pore diameters ranging from 5.2 nm to 12.5 nm of CuO-CeO2/SiO2 cata-lysts in CO oxidation were investigated.The catalysts were characterized by N2 adsorption/desorption at low temperature,X-ray diffraction (XRD),temperature-programmed reduction by H2 (H2-TPR),oxygen temperature programmed desorption (O2-TPD) and X-ray photoelectron spectroscopy (XPS).The results suggested that,the ceria content and the porosity of SiO2 carrier possessed great impacts on the structures and catalytic performances of CuO-CeO2/SiO2 catalysts.When appropriate content of CeO2 (Ce content 8 wt%) was added,the catalytic activity was greatly enhanced.In the catalyst supported on silica carrier with larger pore diameter,higher dispersion of CuO was observed,better agglomeration-resistant capacity was displayed and more lattice oxygen could be found,thus the CuO-CeO2 supported on Si-1 showed higher catalytic activity for low-temperature CO oxidation.展开更多
Cold plasma generated by dielectric barrier discharge (DBD) at atmospheric pressure was adopted for preparation of commercial TiO2 Degussa P25 supported Au catalysts (Au/P25- P) with the assistance of the depositi...Cold plasma generated by dielectric barrier discharge (DBD) at atmospheric pressure was adopted for preparation of commercial TiO2 Degussa P25 supported Au catalysts (Au/P25- P) with the assistance of the deposition-precipitation procedure. The influences of the plasma reduction time and calcination on the performance of the Au/P25-P catalysts were investigated. CO oxidation was performed to investigate the catalytic activity of the Au/P25 catalysts. The results show that DBD cold plasma for the fabrication of Au/P25-P catalysts is a fast process, and Au/P25-P (4 min) exhibited the highest CO oxidation activity due to the complete reduction of Au compounds and less consumption of oxygen vacancies. In order to form more oxygen vacancies active species, Au/P25-P was calcined to obtain Au/P25-PC catalysts. Interestingly, Au/P25- PC exhibited the highest activity for CO oxidation among the Au/P25 samples. The results of transmission electron microscopy (TEM) indicated that the smaller size and high distribution of Au nanoparticles are the mean reasons for a high performance of Au/P25-PC. Atmospheric- pressure DBD cold plasma was proved to be of great efficiency in preparing high performance supported Au catalysts.展开更多
In this work, we have reported the influence of the addition of base (KOH) on the physicochemical property of ceria synthesized by alcohothermal process, and the alcohothermal mechanism was also put forward. Further...In this work, we have reported the influence of the addition of base (KOH) on the physicochemical property of ceria synthesized by alcohothermal process, and the alcohothermal mechanism was also put forward. Furthermore, the prepared CeO2 was used as the support to prepare CuO/CeO2 catalysts via the wet impregnation method. The samples were characterized by N2 adsorption-desorption, X-ray powder diffraction (XRD), high resolution transmission electron microscopy (HRTEM), and temperatureprogrammed reduction by H2 (H2-TPR). The catalytic properties of the CuO/CeO2 catalysts for lowtemperature CO oxidation were studied using a microreactor-GC system. The crystal size of CeO2-A was much smaller than that of CeO2-B, and the corresponding copper oxide catalysts exhibited higher catalytic activity than that of the CeO2-B-supported catalysts under the same reaction conditions. The alcohothermal mechanism indicated that KOH plays a key role in determining the physicochemical and catalytic properties of ceria-based materials.展开更多
Supported Au catalysts for low-temperature CO oxidation were prepared by solvated metal atom impregnation (SMAI) and conventional impregnation (Cl). X-ray photoelectron spectroscopy (XPS) investigations indicated that...Supported Au catalysts for low-temperature CO oxidation were prepared by solvated metal atom impregnation (SMAI) and conventional impregnation (Cl). X-ray photoelectron spectroscopy (XPS) investigations indicated that the elemental gold in all the samples was in the metallic state, XRD measurements showed that the mean diameters of Au particles prepared by SMAI were smaller than those prepared by Cl with the same gold content. Catalytic tests showed that the SMAI catalyst had higher CO oxidation activity than the CI catalyst with the same compositions. Both SMAI and Cl catalysts exhibited high activity in low temperature CO oxidation. Full CO conversion was obtained at 323-383K.展开更多
Au/Al2O3 catalyst was prepared by a modified anion impregnation method and investigated with respect to its initial activity and stability for low-temperature CO oxidation.The activity changes of the catalyst were exa...Au/Al2O3 catalyst was prepared by a modified anion impregnation method and investigated with respect to its initial activity and stability for low-temperature CO oxidation.The activity changes of the catalyst were examined after separate treatment in CO+O2 or CO2 +O2 .Furthermore,in situ FT-IR studies were performed to investigate the species on the surface when CO or CO+O2 or CO2 +O2 was selected separately as adsorption gas.The results showed that Au/Al2O3 catalyst exhibited very high initial activity,but the catalytic activity was found to decrease gradually during CO oxidation with time on stream.And also,the activity of the catalyst declined after treatment in CO+O2 or CO2 +O2 .The formation and accumulation of carbonate-like species during CO oxidation or treatment in CO+O2 or CO2 +O2 might be mainly responsible for the activity decrease,which was reversible.展开更多
Developing efficient and stable cathodes for low-temperature solid oxide fuel cells(LT-SOFCs) is of great importance for the practical commercialization.Herein,we propose a series of Sm-modified Bi_(0.7-x)Sm_xSr_(0.3)...Developing efficient and stable cathodes for low-temperature solid oxide fuel cells(LT-SOFCs) is of great importance for the practical commercialization.Herein,we propose a series of Sm-modified Bi_(0.7-x)Sm_xSr_(0.3)FeO_(3-δ) perovskites as highly-active catalysts for LT-SOFCs.Sm doping can significantly enhance the electrocata lytic activity and chemical stability of cathode.At 600℃,Bi_(0.675)Sm_(0.025)Sr_(0.3)FeO_(3-δ)(BSSF25) cathode has been found to be the optimum composition with a polarization resistance of 0.098 Ω cm^2,which is only around 22.8% of Bi_(0.7)Sr_(0.3)FeO_(3-δ)(BSF).A full cell utilizing BSSF25 displays an exceptional output density of 790 mW cm^(-2),which can operate continuously over100 h without obvious degradation.The remarkable electrochemical performance observed can be attributed to the improved O_(2) transport kinetics,superior surface oxygen adsorption capacity,as well as O_(2)p band centers in close proximity to the Fermi level.Moreover,larger average bonding energy(ABE) and the presence of highly acidic Bi,Sm,and Fe ions restrict the adsorption of CO_(2) on the cathode surface,resulting in excellent CO_(2) resistivity.This work provides valuable guidance for systematic design of efficient and durable catalysts for LT-SOFCs.展开更多
It is urgent to develop catalysts with application potential for oxidative coupling of methane(OCM)at relatively lower temperature.Herein,three-dimensional ordered macro porous(3 DOM)La_(2-x)Sr_(x)Ce_(2-y)CayO_(7-δ)(...It is urgent to develop catalysts with application potential for oxidative coupling of methane(OCM)at relatively lower temperature.Herein,three-dimensional ordered macro porous(3 DOM)La_(2-x)Sr_(x)Ce_(2-y)CayO_(7-δ)(A_(2)B_(2)O_(7)-type)catalysts with disordered defective cubic fluorite phased structure were successfully prepared by a colloidal crystal template method.3DOM structure promotes the accessibility of the gaseous reactants(O2and CH4)to the active sites.The co-doping of Ca and Sr ions in La_(2-x)Sr_(x)Ce_(2-y)CayO_(7-δ)catalysts improved the formation of oxygen vacancies,thereby leading to increased density of surface-active oxygen species(O_(2)^(-))for the activation of CH4and the formation of C2products(C2H6and C2H4).3DOM La_(2-x)Sr_(x)Ce_(2-y)CayO_(7-δ)catalysts exhibit high catalytic activity for OCM at low temperature.3DOM La1.7Sr0.3Ce1.7Ca0.3O7-δcatalyst with the highest density of O_(2)^(-)species exhibited the highest catalytic activity for low-temperature OCM,i.e.,its CH4conversion,selectivity and yield of C2products at 650℃are 32.2%,66.1%and 21.3%,respectively.The mechanism was proposed that the increase in surface oxygen vacancies induced by the co-doping of Ca and Sr ions boosts the key step of C-H bond breaking and C-C bond coupling in catalyzing low-temperature OCM.It is meaningful for the development of the low-temperature and high-efficient catalysts for OCM reaction in practical application.展开更多
CsPbX_(3)-based(X=I,Br,Cl)inorganic perovskite solar cells(PSCs)prepared by low-temperature process have attracted much attention because of their low cost and excellent thermal stability.However,the high trap state d...CsPbX_(3)-based(X=I,Br,Cl)inorganic perovskite solar cells(PSCs)prepared by low-temperature process have attracted much attention because of their low cost and excellent thermal stability.However,the high trap state density and serious charge recombination between low-temperature processed TiO_(2)film and inorganic perovskite layer interface seriously restrict the performance of all-inorganic PSCs.Here a thin polyethylene oxide(PEO)layer is employed to modify TiO_(2)film to passivate traps and promote carrier collection.The impacts of PEO layer on microstructure and photoelectric characteristics of TiO_(2)film and related devices are systematically studied.Characterization results suggest that PEO modification can reduce the surface roughness of TiO_(2)film,decrease its average surface potential,and passivate trap states.At optimal conditions,the champion efficiency of CsPbI_(2)Br PSCs with PEO-modified TiO_(2)(PEO-PSCs)has been improved to 11.24%from 9.03%of reference PSCs.Moreover,the hysteresis behavior and charge recombination have been suppressed in PEO-PSCs.展开更多
Low-temperature oxidation(LTO)is the main reaction that affects fuel formation in the in-situ combustion process,which has important significance for the subsequent combustion propulsion and the successful extraction ...Low-temperature oxidation(LTO)is the main reaction that affects fuel formation in the in-situ combustion process,which has important significance for the subsequent combustion propulsion and the successful extraction of crude oil.In this study,heavy oil was subjected to LTO reactions at different temperatures.Three types of reaction products with varying oxidation depths were characterized in terms of the number of oxygen atoms and the polarity of the molecule to reveal the low-temperature oxidation process of the heavy oil.Ketone compounds and acid polyoxides in the oil phase and deep oxidation products with a higher number of oxygen atoms in the coke were identified with increasing oxidation depth.The experimental results showed that the oxidation reaction of the heavy oil changed from kinetic-controlled to diffusion-controlled in the open oxidation system of the heavy oil as the oxidation depth increased.The oxidation reaction of the oil phase reached a maximum and stable value in oxygen content.The molecular compositions of the ketone compound and acid polyoxide did not change significantly with further increase in reaction temperature.The molecular compositions of the deep oxidation products with a higher number of oxygen atoms in the coke phase changed significantly.The coke precursor molecules with a lower oxygen content and condensation degree participated in the coke formation,and the oxidation reaction pathway and the complexity of the oxidation product component also increased.展开更多
Magnetization roasting is one of the most effective way of utilizing low-grade refractory iron ore.However,the reduction roasting of siderite(FeCO3)generates weakly magnetic wüstite,thus reducing iron recovery vi...Magnetization roasting is one of the most effective way of utilizing low-grade refractory iron ore.However,the reduction roasting of siderite(FeCO3)generates weakly magnetic wüstite,thus reducing iron recovery via weak magnetic separation.We systematically studied and proposed the fluidized preoxidation-low-temperature reduction magnetization roasting process for siderite.We found that the maghemite generated during the air oxidation roasting of siderite would be further reduced into wüstite at 500 and 550℃due to the unstable intermediate product magnetite(Fe_(3)O_(4)).Stable magnetite can be obtained through maghemite reduction only at low temperature.The optimal fluidized magnetization roasting parameters included preoxidation at 610℃for 2.5 min,followed by reduction at 450℃for 5 min.For roasted ore,weak magnetic separation yielded an iron ore concentrate grade of 62.0wt%and an iron recovery rate of 88.36%.Compared with that of conventional direct reduction magnetization roasting,the iron recovery rate of weak magnetic separation had greatly improved by 34.33%.The proposed fluidized preoxidation-low-temperature reduction magnetization roasting process can realize the efficient magnetization roasting utilization of low-grade refractory siderite-containing iron ore without wüstite generation and is unlimited by the proportion of siderite and hematite in iron ore.展开更多
A high thrust-to-weight ratio poses challenges to the high-temperature performance of Ni-based superalloys. The oxidation behavior of GH4738 at extreme temperatures has been investigated by isothermal and non-isotherm...A high thrust-to-weight ratio poses challenges to the high-temperature performance of Ni-based superalloys. The oxidation behavior of GH4738 at extreme temperatures has been investigated by isothermal and non-isothermal experiments. As a result of the competitive diffusion of alloying elements, the oxide scale included an outermost porous oxide layer (OOL), an inner relatively dense oxide layer (IOL), and an internal oxide zone (IOZ), depending on the temperature and time. A high temperature led to the formation of large voids at the IOL/IOZ interface. At 1200℃, the continuity of the Cr-rich oxide layer in the IOL was destroyed, and thus, spallation occurred. Extension of oxidation time contributed to the size of Al-rich oxide particles with the increase in the IOZ. Based on this finding,the oxidation kinetics of GH4738 was discussed, and the corresponding oxidation behavior at 900-1100℃ was predicted.展开更多
Globally,the efficient utilization of polymer wastes is one of the most important issues for current sustainable development topics.Herein,a green and efficient low-temperature combustion approach is proposed to deal ...Globally,the efficient utilization of polymer wastes is one of the most important issues for current sustainable development topics.Herein,a green and efficient low-temperature combustion approach is proposed to deal with polymer wastes and recover heat energy,simultaneously alleviating the environment and energy crisis.Non-noble metal oxides(Al_(2)O_(3),Fe_(2)O_(3),NiO_(2),ZrO_(2),La_(2)O_(3)and CeO_(2)) were prepared,characterized and screened to boost the low-temperature combustion of polyethylene waste at 300℃ in air.The mass change,heat release and CO_(x) formation were studied in details and employed to evaluate the combustion rate and efficiency.It was found that CeO_(2)significantly enhanced the combustion rate and efficiency,which was respectively 2 and 7 times that of non-catalytic case.An interesting phenomenon was observed that the catalytic performance of CeO_(2) in polyethylene low-temperature combustion was significantly improved by the 7-day storage in the room environment or water treatment.XPS analysis confirmed the co-existence of Ce^(3+) and Ce^(4+) in CeO_(2),and the 7-day storage and water treatment promoted the amount of Ce^(3+),which facilitated the formation of the oxygen vacancies.That may be the reason why CeO_(2) exhibited excellent catalytic performance in polyethylene low-temperature combustion.展开更多
Vegetable oils are a source of energy, essential fatty acids, antioxidants and fat-soluble vitamins useful for human health care and development. These oils also contribute to organoleptic quality of their products’ ...Vegetable oils are a source of energy, essential fatty acids, antioxidants and fat-soluble vitamins useful for human health care and development. These oils also contribute to organoleptic quality of their products’ derivatives. However, their chemical and physical properties can be modified by the mode of their extraction, storage and distribution. These modifications might negatively affect the nutritional quality of the oils. The goals of this study were to: sample different vegetable oils for cosmetic or dietary use marketed in Cameroon, and verify purity and oxidation states of each kind of oil through determination of its acidity, iodine, peroxide, saponification, refractive indexes and the conformity of the labeling. The carotene content, the level of polar components and specific absorbance were also determined. As the result, six oils namely palm, palm kernel, coconut, black cumin, peanut and shea butter were collected. Apart from labeling, chemicals and physicals parameters analyzed were generally in accordance with the Cameroonian and Codex Alimentarius standard. This study suggests that vegetable oils sampled in the Cameroonian market may not expose consumers to lipid oxidation products generating pathological oxidative stress and inflammation. However, efforts in application of existing standard need to be done as far as labeling are concerned.展开更多
The severe degradation of electrochemical performance for lithium-ion batteries(LIBs)at low temperatures poses a significant challenge to their practical applications.Consequently,extensive efforts have been contribut...The severe degradation of electrochemical performance for lithium-ion batteries(LIBs)at low temperatures poses a significant challenge to their practical applications.Consequently,extensive efforts have been contributed to explore novel anode materials with high electronic conductivity and rapid Li^(+)diffusion kinetics for achieving favorable low-temperature performance of LIBs.Herein,we try to review the recent reports on the synthesis and characterizations of low-temperature anode materials.First,we summarize the underlying mechanisms responsible for the performance degradation of anode materials at subzero temperatures.Second,detailed discussions concerning the key pathways(boosting electronic conductivity,enhancing Li^(+)diffusion kinetics,and inhibiting lithium dendrite)for improving the low-temperature performance of anode materials are presented.Third,several commonly used low-temperature anode materials are briefly introduced.Fourth,recent progress in the engineering of these low-temperature anode materials is summarized in terms of structural design,morphology control,surface&interface modifications,and multiphase materials.Finally,the challenges that remain to be solved in the field of low-temperature anode materials are discussed.This review was organized to offer valuable insights and guidance for next-generation LIBs with excellent low-temperature electrochemical performance.展开更多
The trade-off between efficiency and stability has limited the application of TiO_(2)as a catalyst due to its poor surface reactivity.Here,we present a modification of a TiO_(2)layer with highly stable Sub-5 nm Fe_(2)...The trade-off between efficiency and stability has limited the application of TiO_(2)as a catalyst due to its poor surface reactivity.Here,we present a modification of a TiO_(2)layer with highly stable Sub-5 nm Fe_(2)O_(3)nanoparticles(NP)by modulating its structure-surface reactivity relationship to attain efficiency-stability balance via a voltage-assisted oxidation approach.In situ simultaneous oxidation of the Ti substrate and Fe precursor using high-energy plasma driven by high voltage resulted in uniform distribution of Fe_(2)O_(3)NP embedded within porous TiO_(2)layer.Comprehensive surface characterizations with density functional theory demonstrated an improved electronic transition in TiO_(2)due to the presence of surface defects from reactive oxygen species and possible charge transfer from Ti to Fe;it also unexpectedly increased the active site in the TiO_(2)layer due to uncoordinated electrons in Sub-5 nm Fe_(2)O_(3)NP/TiO_(2)catalyst,thereby enhancing the adsorption of chemical functional groups on the catalyst.This unique embedded structure exhibited remarkable improvement in reducing 4-nitrophenol to 4-aminophenol,achieving approximately 99%efficiency in 20 min without stability decay after 20 consecutive cycles,outperforming previously reported TiO_(2)-based catalysts.This finding proposes a modified-electrochemical strategy enabling facile construction of TiO_(2)with nanoscale oxides extandable to other metal oxide systems.展开更多
With the continuing boost in the demand for energy storage,there is an increasing requirement for batteries to be capable of operation in extreme environmental conditions.Sodium-ion batteries(SIBs) have emerged as a h...With the continuing boost in the demand for energy storage,there is an increasing requirement for batteries to be capable of operation in extreme environmental conditions.Sodium-ion batteries(SIBs) have emerged as a highly promising energy storage solution due to their promising performance over a wide range of temperatures and the abundance of sodium resources in the earth's crust.Compared to lithiumion batteries(LIBs),although sodium ions possess a larger ionic radius,they are more easily desolvated than lithium ions.Fu rthermore,SIBs have a smaller Stokes radius than lithium ions,resulting in improved sodium-ion mobility in the electrolyte.Nevertheless,SIBs demonstrate a significant decrease in performance at low temperatures(LT),which constrains their operation in harsh weather conditions.Despite the increasing interest in SIBs,there is a notable scarcity of research focusing specifically on their mechanism under LT conditions.This review explores recent research that considers the thermal tolerance of SIBs from an inner chemistry process perspective,spanning a wide temperature spectrum(-70 to100℃),particularly at LT conditions.In addition,the enhancement of electrochemical performance in LT SIBs is based on improvements in reaction kinetics and cycling stability achieved through the utilization of effective electrode materials and electrolyte components.Furthermore,the safety concerns associated with SIBs are addressed and effective strategies are proposed for mitigating these issues.Finally,prospects conducted to extend the environmental frontiers of commercial SIBs are discussed mainly from three viewpoints including innovations in materials,development and research of relevant theoretical mechanisms,and intelligent safety management system establishment for larger-scale energy storage SIBs.展开更多
基金supported by the National Natural Science Foundation of China (20771061 and 20871071)the 973 Program (2005CB623607)Science and Technology Commission Foundation of Tianjin (08JCYBJC00100 and 09JCYBJC03600)
文摘Nanometer SnO2 particles were synthesized by sol-gel dialytic processes and used as a support to prepare CuO supported catalysts via a deposition-precipitation method. The samples were characterized by means of TG-DTA, XRD, H2-TPR and XPS. The catalytic activity of the CuO/TiO2-SnO2 catalysts was markedly depended on the loading of CuO, and the optimum CuO loading was 8 wt.% (Tloo = 80 ℃). The CuO/TiO2-SnO2 catalysts exhibited much higher catalytic activity than the CuO/TiO2 and CuO/SnO2 catalysts. H2-TPR result indicated that a large amount of CuO formed the active site for CO oxidation in 8 wt.% CuO/TiO2-SnO2 catalyst.
基金Supported by the Henkel Professorship of Tongji University,China
文摘High active and stable gold catalysts supported on crystalline Fe203 and CeO2/Fe2O3 were prepared via the deposition-precipitation method. The catalyst with a Au load of 1.0% calcined at 180 ℃ showed a CO conversion of 100% at -8.9℃, while Au/CeO2/Fe2O3 converted CO completely at -16.1 ℃. Even having been calcined at 500 ℃, Au/Fe2O3 still exhibited significant catalytic activity, achieving full conversion of CO at 61.6℃. The catalyst with a low Au load of 0.5% could convert CO completely at room temperature and kept the activity unchanged for at least 150 h. N2 adsorption-desorption measurements show that the crystalline supports possessed a high specific surface area of about 200 m2/g. Characterizations of X-ray diffraction and transmission electron microscopy indicate that gold species were highly dispersed as nano or sub-nano particles on the supports. Even after the catalyst was calcined at 500 ℃, the Au particles remained in a nano-size of about 6--10 nm. X-ray photoelectron spectra reveal that the supported Au existed in metallic state Au0. The modification of Au/Fe2O3 by CeO2 proved to be beneficial to the inhibition of crystallization of Fe2O3 and the stabilization of gold particles in dispersed state, consequently promoting catalytic activity.
基金supported by the University of Kashan (Grant No.158426/3)
文摘Mixed iron-cobalt oxide (Co/Fe molar ratio = 1/5) are prepared using a simple co-precipitation procedure and studied for the catalytic oxidation of carbon monoxide. In particular, the effects of a range of preparation variables such as pH value when precipitation, aging temperature, precipitation agent type and aging time are investigated on the catalytic performance of synthesized Fe-Co oxides in CO oxidation reaction. In addition, the preparation factors were optimized by Taguchi design method. The optimized sample was characterized by XRD, N2 adsortion/desorption, TEM and TGA/DTA techniques. The results reveal that the optimized sample shows a mesoporous structure with a narrow pore size distribution centered in the range of 2-7 nm. The sample prepared under optimized conditions has high activity and stability toward removal of carbon monoxide at lower temperatures. It is shown that different preparation variables influence the catalytic performance of Fe-Co oxide in CO oxidation reaction.
基金Projected supported by the National Natural Science Foundation of China (20271028) and Tianjin Natural Science Foundation(033602511)
文摘CeO2 was synthesized via sol-gel process and used as supporter to prepare CuO/CeO2, Cu/CeO2 catalysts by impregnation method. The catalytic properties and characterization of CeO2, CuO/CeO2 and Cu/CeO2 catalysts were examined by means of a microreactor-GC system, HRTEM, XRD, TPR and XPS techniques. The results show that CuO has not catalytic activity and the activity of CeO2 is quite low for CO oxidation. However, the catalytic activity of CuO/CeO2 and Cu/ CeO2 catalysts increases significantly. Furthermore, the activity of CuO/CeO2 is higher than that of Cu/CeO2 catalysts.
基金supported by the National Natural Science Foundation of China(20590360)New Century Excellent Talent Project of China(NCET-05-0783)
文摘The effects of CeO2 contents and silica carrier porosity with their pore diameters ranging from 5.2 nm to 12.5 nm of CuO-CeO2/SiO2 cata-lysts in CO oxidation were investigated.The catalysts were characterized by N2 adsorption/desorption at low temperature,X-ray diffraction (XRD),temperature-programmed reduction by H2 (H2-TPR),oxygen temperature programmed desorption (O2-TPD) and X-ray photoelectron spectroscopy (XPS).The results suggested that,the ceria content and the porosity of SiO2 carrier possessed great impacts on the structures and catalytic performances of CuO-CeO2/SiO2 catalysts.When appropriate content of CeO2 (Ce content 8 wt%) was added,the catalytic activity was greatly enhanced.In the catalyst supported on silica carrier with larger pore diameter,higher dispersion of CuO was observed,better agglomeration-resistant capacity was displayed and more lattice oxygen could be found,thus the CuO-CeO2 supported on Si-1 showed higher catalytic activity for low-temperature CO oxidation.
基金supported by National Natural Science Foundation of China(Nos.11505019,21173028)the Science and Technology Research Project of Liaoning Provincial Education Department(No.L2013464)+1 种基金the Scientific Research Foundation for the Doctor of Liaoning Province(No.20131004)the Dalian Jinzhou New District Science and Technology Plan Project(No.KJCX-ZTPY-2014-0001)
文摘Cold plasma generated by dielectric barrier discharge (DBD) at atmospheric pressure was adopted for preparation of commercial TiO2 Degussa P25 supported Au catalysts (Au/P25- P) with the assistance of the deposition-precipitation procedure. The influences of the plasma reduction time and calcination on the performance of the Au/P25-P catalysts were investigated. CO oxidation was performed to investigate the catalytic activity of the Au/P25 catalysts. The results show that DBD cold plasma for the fabrication of Au/P25-P catalysts is a fast process, and Au/P25-P (4 min) exhibited the highest CO oxidation activity due to the complete reduction of Au compounds and less consumption of oxygen vacancies. In order to form more oxygen vacancies active species, Au/P25-P was calcined to obtain Au/P25-PC catalysts. Interestingly, Au/P25- PC exhibited the highest activity for CO oxidation among the Au/P25 samples. The results of transmission electron microscopy (TEM) indicated that the smaller size and high distribution of Au nanoparticles are the mean reasons for a high performance of Au/P25-PC. Atmospheric- pressure DBD cold plasma was proved to be of great efficiency in preparing high performance supported Au catalysts.
文摘In this work, we have reported the influence of the addition of base (KOH) on the physicochemical property of ceria synthesized by alcohothermal process, and the alcohothermal mechanism was also put forward. Furthermore, the prepared CeO2 was used as the support to prepare CuO/CeO2 catalysts via the wet impregnation method. The samples were characterized by N2 adsorption-desorption, X-ray powder diffraction (XRD), high resolution transmission electron microscopy (HRTEM), and temperatureprogrammed reduction by H2 (H2-TPR). The catalytic properties of the CuO/CeO2 catalysts for lowtemperature CO oxidation were studied using a microreactor-GC system. The crystal size of CeO2-A was much smaller than that of CeO2-B, and the corresponding copper oxide catalysts exhibited higher catalytic activity than that of the CeO2-B-supported catalysts under the same reaction conditions. The alcohothermal mechanism indicated that KOH plays a key role in determining the physicochemical and catalytic properties of ceria-based materials.
基金This project is supported by the Natural Science Foundation of Tianjin (No. 983603611)
文摘Supported Au catalysts for low-temperature CO oxidation were prepared by solvated metal atom impregnation (SMAI) and conventional impregnation (Cl). X-ray photoelectron spectroscopy (XPS) investigations indicated that the elemental gold in all the samples was in the metallic state, XRD measurements showed that the mean diameters of Au particles prepared by SMAI were smaller than those prepared by Cl with the same gold content. Catalytic tests showed that the SMAI catalyst had higher CO oxidation activity than the CI catalyst with the same compositions. Both SMAI and Cl catalysts exhibited high activity in low temperature CO oxidation. Full CO conversion was obtained at 323-383K.
基金supported by the Science and Research Reward Fund Program of Shandong Excellent Young Scientist of China (2007BS04033)
文摘Au/Al2O3 catalyst was prepared by a modified anion impregnation method and investigated with respect to its initial activity and stability for low-temperature CO oxidation.The activity changes of the catalyst were examined after separate treatment in CO+O2 or CO2 +O2 .Furthermore,in situ FT-IR studies were performed to investigate the species on the surface when CO or CO+O2 or CO2 +O2 was selected separately as adsorption gas.The results showed that Au/Al2O3 catalyst exhibited very high initial activity,but the catalytic activity was found to decrease gradually during CO oxidation with time on stream.And also,the activity of the catalyst declined after treatment in CO+O2 or CO2 +O2 .The formation and accumulation of carbonate-like species during CO oxidation or treatment in CO+O2 or CO2 +O2 might be mainly responsible for the activity decrease,which was reversible.
基金supported by the National Natural Science Foundation of China(22279025,21773048)the Natural Science Foundation of Heilongjiang Province(LH2021A013)+1 种基金the Sichuan Science and Technology Program(2021YFSY0022)the Fundamental Research Funds for the Central Universities(2023FRFK06005,HIT.NSRIF202204)。
文摘Developing efficient and stable cathodes for low-temperature solid oxide fuel cells(LT-SOFCs) is of great importance for the practical commercialization.Herein,we propose a series of Sm-modified Bi_(0.7-x)Sm_xSr_(0.3)FeO_(3-δ) perovskites as highly-active catalysts for LT-SOFCs.Sm doping can significantly enhance the electrocata lytic activity and chemical stability of cathode.At 600℃,Bi_(0.675)Sm_(0.025)Sr_(0.3)FeO_(3-δ)(BSSF25) cathode has been found to be the optimum composition with a polarization resistance of 0.098 Ω cm^2,which is only around 22.8% of Bi_(0.7)Sr_(0.3)FeO_(3-δ)(BSF).A full cell utilizing BSSF25 displays an exceptional output density of 790 mW cm^(-2),which can operate continuously over100 h without obvious degradation.The remarkable electrochemical performance observed can be attributed to the improved O_(2) transport kinetics,superior surface oxygen adsorption capacity,as well as O_(2)p band centers in close proximity to the Fermi level.Moreover,larger average bonding energy(ABE) and the presence of highly acidic Bi,Sm,and Fe ions restrict the adsorption of CO_(2) on the cathode surface,resulting in excellent CO_(2) resistivity.This work provides valuable guidance for systematic design of efficient and durable catalysts for LT-SOFCs.
基金supported by the National Key Research and Development Program of China(Nos.2022YFB3504100,2022YFB3506200)the National Natural Science Foundation of China(Nos.22208373,22376217)+1 种基金the Beijing Nova Program(No.20220484215)the Science Foundation of China University of Petroleum,Beijing(No.2462023YJRC030)。
文摘It is urgent to develop catalysts with application potential for oxidative coupling of methane(OCM)at relatively lower temperature.Herein,three-dimensional ordered macro porous(3 DOM)La_(2-x)Sr_(x)Ce_(2-y)CayO_(7-δ)(A_(2)B_(2)O_(7)-type)catalysts with disordered defective cubic fluorite phased structure were successfully prepared by a colloidal crystal template method.3DOM structure promotes the accessibility of the gaseous reactants(O2and CH4)to the active sites.The co-doping of Ca and Sr ions in La_(2-x)Sr_(x)Ce_(2-y)CayO_(7-δ)catalysts improved the formation of oxygen vacancies,thereby leading to increased density of surface-active oxygen species(O_(2)^(-))for the activation of CH4and the formation of C2products(C2H6and C2H4).3DOM La_(2-x)Sr_(x)Ce_(2-y)CayO_(7-δ)catalysts exhibit high catalytic activity for OCM at low temperature.3DOM La1.7Sr0.3Ce1.7Ca0.3O7-δcatalyst with the highest density of O_(2)^(-)species exhibited the highest catalytic activity for low-temperature OCM,i.e.,its CH4conversion,selectivity and yield of C2products at 650℃are 32.2%,66.1%and 21.3%,respectively.The mechanism was proposed that the increase in surface oxygen vacancies induced by the co-doping of Ca and Sr ions boosts the key step of C-H bond breaking and C-C bond coupling in catalyzing low-temperature OCM.It is meaningful for the development of the low-temperature and high-efficient catalysts for OCM reaction in practical application.
基金financially supported by the Guangzhou Basic and Applied Basic Research Foundation,China(No.303523)。
文摘CsPbX_(3)-based(X=I,Br,Cl)inorganic perovskite solar cells(PSCs)prepared by low-temperature process have attracted much attention because of their low cost and excellent thermal stability.However,the high trap state density and serious charge recombination between low-temperature processed TiO_(2)film and inorganic perovskite layer interface seriously restrict the performance of all-inorganic PSCs.Here a thin polyethylene oxide(PEO)layer is employed to modify TiO_(2)film to passivate traps and promote carrier collection.The impacts of PEO layer on microstructure and photoelectric characteristics of TiO_(2)film and related devices are systematically studied.Characterization results suggest that PEO modification can reduce the surface roughness of TiO_(2)film,decrease its average surface potential,and passivate trap states.At optimal conditions,the champion efficiency of CsPbI_(2)Br PSCs with PEO-modified TiO_(2)(PEO-PSCs)has been improved to 11.24%from 9.03%of reference PSCs.Moreover,the hysteresis behavior and charge recombination have been suppressed in PEO-PSCs.
基金supported by the National Key R&D Program of China(2018YFA0702400)the PetroChina Exploration&Production Company(KS2020-01-05).
文摘Low-temperature oxidation(LTO)is the main reaction that affects fuel formation in the in-situ combustion process,which has important significance for the subsequent combustion propulsion and the successful extraction of crude oil.In this study,heavy oil was subjected to LTO reactions at different temperatures.Three types of reaction products with varying oxidation depths were characterized in terms of the number of oxygen atoms and the polarity of the molecule to reveal the low-temperature oxidation process of the heavy oil.Ketone compounds and acid polyoxides in the oil phase and deep oxidation products with a higher number of oxygen atoms in the coke were identified with increasing oxidation depth.The experimental results showed that the oxidation reaction of the heavy oil changed from kinetic-controlled to diffusion-controlled in the open oxidation system of the heavy oil as the oxidation depth increased.The oxidation reaction of the oil phase reached a maximum and stable value in oxygen content.The molecular compositions of the ketone compound and acid polyoxide did not change significantly with further increase in reaction temperature.The molecular compositions of the deep oxidation products with a higher number of oxygen atoms in the coke phase changed significantly.The coke precursor molecules with a lower oxygen content and condensation degree participated in the coke formation,and the oxidation reaction pathway and the complexity of the oxidation product component also increased.
基金the National Natural Science Foundation of China(Nos.51974287 and 21736010)Innovation Academy for Green Manufacture,Chinese Academy of Sciences(No.IAGM-2019-A11).
文摘Magnetization roasting is one of the most effective way of utilizing low-grade refractory iron ore.However,the reduction roasting of siderite(FeCO3)generates weakly magnetic wüstite,thus reducing iron recovery via weak magnetic separation.We systematically studied and proposed the fluidized preoxidation-low-temperature reduction magnetization roasting process for siderite.We found that the maghemite generated during the air oxidation roasting of siderite would be further reduced into wüstite at 500 and 550℃due to the unstable intermediate product magnetite(Fe_(3)O_(4)).Stable magnetite can be obtained through maghemite reduction only at low temperature.The optimal fluidized magnetization roasting parameters included preoxidation at 610℃for 2.5 min,followed by reduction at 450℃for 5 min.For roasted ore,weak magnetic separation yielded an iron ore concentrate grade of 62.0wt%and an iron recovery rate of 88.36%.Compared with that of conventional direct reduction magnetization roasting,the iron recovery rate of weak magnetic separation had greatly improved by 34.33%.The proposed fluidized preoxidation-low-temperature reduction magnetization roasting process can realize the efficient magnetization roasting utilization of low-grade refractory siderite-containing iron ore without wüstite generation and is unlimited by the proportion of siderite and hematite in iron ore.
基金financially supported by the National Key R&D Program of China (No.2021YFB3700400)the National Natural Science Foundation of China (Nos.52074030,51904021,and 52174294)。
文摘A high thrust-to-weight ratio poses challenges to the high-temperature performance of Ni-based superalloys. The oxidation behavior of GH4738 at extreme temperatures has been investigated by isothermal and non-isothermal experiments. As a result of the competitive diffusion of alloying elements, the oxide scale included an outermost porous oxide layer (OOL), an inner relatively dense oxide layer (IOL), and an internal oxide zone (IOZ), depending on the temperature and time. A high temperature led to the formation of large voids at the IOL/IOZ interface. At 1200℃, the continuity of the Cr-rich oxide layer in the IOL was destroyed, and thus, spallation occurred. Extension of oxidation time contributed to the size of Al-rich oxide particles with the increase in the IOZ. Based on this finding,the oxidation kinetics of GH4738 was discussed, and the corresponding oxidation behavior at 900-1100℃ was predicted.
基金the financial support from the National Natural Science Foundation of China(21908010)Jilin Provincial Department of Science and Technology(20220101089JC)the Education Department of Jilin Province(JJKH20220694KJ)。
文摘Globally,the efficient utilization of polymer wastes is one of the most important issues for current sustainable development topics.Herein,a green and efficient low-temperature combustion approach is proposed to deal with polymer wastes and recover heat energy,simultaneously alleviating the environment and energy crisis.Non-noble metal oxides(Al_(2)O_(3),Fe_(2)O_(3),NiO_(2),ZrO_(2),La_(2)O_(3)and CeO_(2)) were prepared,characterized and screened to boost the low-temperature combustion of polyethylene waste at 300℃ in air.The mass change,heat release and CO_(x) formation were studied in details and employed to evaluate the combustion rate and efficiency.It was found that CeO_(2)significantly enhanced the combustion rate and efficiency,which was respectively 2 and 7 times that of non-catalytic case.An interesting phenomenon was observed that the catalytic performance of CeO_(2) in polyethylene low-temperature combustion was significantly improved by the 7-day storage in the room environment or water treatment.XPS analysis confirmed the co-existence of Ce^(3+) and Ce^(4+) in CeO_(2),and the 7-day storage and water treatment promoted the amount of Ce^(3+),which facilitated the formation of the oxygen vacancies.That may be the reason why CeO_(2) exhibited excellent catalytic performance in polyethylene low-temperature combustion.
文摘Vegetable oils are a source of energy, essential fatty acids, antioxidants and fat-soluble vitamins useful for human health care and development. These oils also contribute to organoleptic quality of their products’ derivatives. However, their chemical and physical properties can be modified by the mode of their extraction, storage and distribution. These modifications might negatively affect the nutritional quality of the oils. The goals of this study were to: sample different vegetable oils for cosmetic or dietary use marketed in Cameroon, and verify purity and oxidation states of each kind of oil through determination of its acidity, iodine, peroxide, saponification, refractive indexes and the conformity of the labeling. The carotene content, the level of polar components and specific absorbance were also determined. As the result, six oils namely palm, palm kernel, coconut, black cumin, peanut and shea butter were collected. Apart from labeling, chemicals and physicals parameters analyzed were generally in accordance with the Cameroonian and Codex Alimentarius standard. This study suggests that vegetable oils sampled in the Cameroonian market may not expose consumers to lipid oxidation products generating pathological oxidative stress and inflammation. However, efforts in application of existing standard need to be done as far as labeling are concerned.
基金supported by the National Key Research and Development Program of China(No.2019YFA0705601)the National Natural Science Foundation of China(No.U23A20122,52101267)the Key Science and Technology Special Project of Henan Province(No.201111311400).
文摘The severe degradation of electrochemical performance for lithium-ion batteries(LIBs)at low temperatures poses a significant challenge to their practical applications.Consequently,extensive efforts have been contributed to explore novel anode materials with high electronic conductivity and rapid Li^(+)diffusion kinetics for achieving favorable low-temperature performance of LIBs.Herein,we try to review the recent reports on the synthesis and characterizations of low-temperature anode materials.First,we summarize the underlying mechanisms responsible for the performance degradation of anode materials at subzero temperatures.Second,detailed discussions concerning the key pathways(boosting electronic conductivity,enhancing Li^(+)diffusion kinetics,and inhibiting lithium dendrite)for improving the low-temperature performance of anode materials are presented.Third,several commonly used low-temperature anode materials are briefly introduced.Fourth,recent progress in the engineering of these low-temperature anode materials is summarized in terms of structural design,morphology control,surface&interface modifications,and multiphase materials.Finally,the challenges that remain to be solved in the field of low-temperature anode materials are discussed.This review was organized to offer valuable insights and guidance for next-generation LIBs with excellent low-temperature electrochemical performance.
基金supported by the National Projects of the National Research Foundation(NRF)funded by Republic of Korea(#2022R1F1A1072739 and#2022R1A2C1004392)Prof.Nashrah is also grateful for financial supports by the YU Infra-Project in conjunction with BK21 FOUR National Program(#222A251009)by the Nano-Fab-NRF grant funded by Republic of Korea(#2009-0082580).
文摘The trade-off between efficiency and stability has limited the application of TiO_(2)as a catalyst due to its poor surface reactivity.Here,we present a modification of a TiO_(2)layer with highly stable Sub-5 nm Fe_(2)O_(3)nanoparticles(NP)by modulating its structure-surface reactivity relationship to attain efficiency-stability balance via a voltage-assisted oxidation approach.In situ simultaneous oxidation of the Ti substrate and Fe precursor using high-energy plasma driven by high voltage resulted in uniform distribution of Fe_(2)O_(3)NP embedded within porous TiO_(2)layer.Comprehensive surface characterizations with density functional theory demonstrated an improved electronic transition in TiO_(2)due to the presence of surface defects from reactive oxygen species and possible charge transfer from Ti to Fe;it also unexpectedly increased the active site in the TiO_(2)layer due to uncoordinated electrons in Sub-5 nm Fe_(2)O_(3)NP/TiO_(2)catalyst,thereby enhancing the adsorption of chemical functional groups on the catalyst.This unique embedded structure exhibited remarkable improvement in reducing 4-nitrophenol to 4-aminophenol,achieving approximately 99%efficiency in 20 min without stability decay after 20 consecutive cycles,outperforming previously reported TiO_(2)-based catalysts.This finding proposes a modified-electrochemical strategy enabling facile construction of TiO_(2)with nanoscale oxides extandable to other metal oxide systems.
基金supported by the Natural Science Foundation of Jiangsu Province(No.BK20220618)the National Natural Science Foundation of China(Nos.22078028 and 21978026)。
文摘With the continuing boost in the demand for energy storage,there is an increasing requirement for batteries to be capable of operation in extreme environmental conditions.Sodium-ion batteries(SIBs) have emerged as a highly promising energy storage solution due to their promising performance over a wide range of temperatures and the abundance of sodium resources in the earth's crust.Compared to lithiumion batteries(LIBs),although sodium ions possess a larger ionic radius,they are more easily desolvated than lithium ions.Fu rthermore,SIBs have a smaller Stokes radius than lithium ions,resulting in improved sodium-ion mobility in the electrolyte.Nevertheless,SIBs demonstrate a significant decrease in performance at low temperatures(LT),which constrains their operation in harsh weather conditions.Despite the increasing interest in SIBs,there is a notable scarcity of research focusing specifically on their mechanism under LT conditions.This review explores recent research that considers the thermal tolerance of SIBs from an inner chemistry process perspective,spanning a wide temperature spectrum(-70 to100℃),particularly at LT conditions.In addition,the enhancement of electrochemical performance in LT SIBs is based on improvements in reaction kinetics and cycling stability achieved through the utilization of effective electrode materials and electrolyte components.Furthermore,the safety concerns associated with SIBs are addressed and effective strategies are proposed for mitigating these issues.Finally,prospects conducted to extend the environmental frontiers of commercial SIBs are discussed mainly from three viewpoints including innovations in materials,development and research of relevant theoretical mechanisms,and intelligent safety management system establishment for larger-scale energy storage SIBs.