Based on the relevant phase diagrams of ternary system in MgO - CaO - ZrO2 - SiO2 quarternary systems, the phase diagram of Fe - O system and the condensed phase stability area diagram of iron oxides, the corrosion re...Based on the relevant phase diagrams of ternary system in MgO - CaO - ZrO2 - SiO2 quarternary systems, the phase diagram of Fe - O system and the condensed phase stability area diagram of iron oxides, the corrosion resistance of MgO - CaO - ZrO2 refractories to silicate cement, and the forming conditions and prepar- ing measures of hercynite are analyzed.展开更多
Corrosion resistance and penetration resistance of MgO-CaO materials with different CaO contents （22%, 42%, 49%, 53%, in mass）to refining AOD slag or VOD slag were investigated using static crucible technique by vis...Corrosion resistance and penetration resistance of MgO-CaO materials with different CaO contents （22%, 42%, 49%, 53%, in mass）to refining AOD slag or VOD slag were investigated using static crucible technique by visual observation, SEM and XRD. The corrosion resistance and penetration resistance of speci-mens decrease with the increase of CaO content. This may be caused by the formation of C3S and C2S during the reactions between specimens and the slag. The formed C3S and C2S can restrain the further penetration to the matrix. The higher the CaO content, the more the C2S or C3S formed, the lower the porosity of the speci-mens, and the lower the penetration depth and corrosion rate. The corrosion resistance to AOD slag is better than that to VOD slag, because the reaction between AOD slag and the matrix is slighter than that between VOD slag and the matrix.展开更多
Magnesia-based refractories hold a big share in the total refractories output in China because of abundance of magnesite resource. In this paper a short review has been focused on the current and future new use of mag...Magnesia-based refractories hold a big share in the total refractories output in China because of abundance of magnesite resource. In this paper a short review has been focused on the current and future new use of magnesia in the production of magnesia-based products including low carbon MgO-C bricks, MgO- CaO bricks, MgO-based castables, MgO-CaO-Fe2O3 ramming mix and MgO-CaO-C bricks for low carbon steelmaking and clean steel making, magnesite ball for slag splashing, MgO-CaO-ZrO2 for sintering and transfering zones of cement kiln and MgAlON for special use in the steel industry.展开更多
文摘Based on the relevant phase diagrams of ternary system in MgO - CaO - ZrO2 - SiO2 quarternary systems, the phase diagram of Fe - O system and the condensed phase stability area diagram of iron oxides, the corrosion resistance of MgO - CaO - ZrO2 refractories to silicate cement, and the forming conditions and prepar- ing measures of hercynite are analyzed.
文摘Corrosion resistance and penetration resistance of MgO-CaO materials with different CaO contents （22%, 42%, 49%, 53%, in mass）to refining AOD slag or VOD slag were investigated using static crucible technique by visual observation, SEM and XRD. The corrosion resistance and penetration resistance of speci-mens decrease with the increase of CaO content. This may be caused by the formation of C3S and C2S during the reactions between specimens and the slag. The formed C3S and C2S can restrain the further penetration to the matrix. The higher the CaO content, the more the C2S or C3S formed, the lower the porosity of the speci-mens, and the lower the penetration depth and corrosion rate. The corrosion resistance to AOD slag is better than that to VOD slag, because the reaction between AOD slag and the matrix is slighter than that between VOD slag and the matrix.
文摘Magnesia-based refractories hold a big share in the total refractories output in China because of abundance of magnesite resource. In this paper a short review has been focused on the current and future new use of magnesia in the production of magnesia-based products including low carbon MgO-C bricks, MgO- CaO bricks, MgO-based castables, MgO-CaO-Fe2O3 ramming mix and MgO-CaO-C bricks for low carbon steelmaking and clean steel making, magnesite ball for slag splashing, MgO-CaO-ZrO2 for sintering and transfering zones of cement kiln and MgAlON for special use in the steel industry.