Previously, Polyvinyl Alcohol (PVA) and phenolic resin were used for resin impregnated bamboo fiber reinforced PP composites which was manufactures for resin impregnated bamboo fiber with polypropylene (PP). Resin imp...Previously, Polyvinyl Alcohol (PVA) and phenolic resin were used for resin impregnated bamboo fiber reinforced PP composites which was manufactures for resin impregnated bamboo fiber with polypropylene (PP). Resin impregnation method can show improvement on tensile strength of fiber. However, to reduce the contact surface area and low inter-facial shear strength (IFSS) between impregnated resin and matrix, using 40% weight fraction of bamboo fiber in PP matrix, PVA impregnated composites with mean flexural and tensile strength 10% higher than untreated composites were produced butphenolic resin impregnated fiber reinforced composition’s mechanical properties were decreased. In this study maleic anhydride grafted polypropylene (MAPP) was used to increase interfacial shear strength between resin impregnated fiber and PP. With 10% MAPP, IFSS between resin impregnated fiber and PP increased more than 100% and reinforced composites. MAPP with untreated, phenolic resin and PVA impregnated cases showed similar mechanical properties. Yet in water absorption test, the PVA treatment with bamboo/PP composites increased water absorption ratio. But with 10% MAPP, matrix PP water absorption ratio decreased like phenolic resin impregnated fiber reinforced composites. 10% MAPP with resin impregnated bamboo fiber reinforced PP composites can improve IFSS, mechanical properties of composite and can decrease water absorption PVA resin impregnated bamboo fiber reinforced composites.展开更多
To study the effect of some parameters, such as, length and fraction of glass fiber (GF), and the fraction of maleic anhydride grafted polypropylene (PP-g-MAH), on the mechanical properties of glass fiber reinforced p...To study the effect of some parameters, such as, length and fraction of glass fiber (GF), and the fraction of maleic anhydride grafted polypropylene (PP-g-MAH), on the mechanical properties of glass fiber reinforced polypropylene (GF/PP) composites, tensile tests, bending tests and impact tests were conducted. Scanning electron microscope (SEM) was used to characterize the fracture mechanisms of the composites. The results show that, compared with 3 mm GF, 9 mm GF can significantly improve the strength of the composite better. Addition of PP-g-MAH, a kind of grafting agent, into the PP-30% LGF composite can result in a better mechanical properties because of the strengthening of the bonding interface between the matrix and the fiber. When the mass fraction of GF is 30% and the PP-g-MAH fraction is 6%, the mechanical properties of the composite are the best.展开更多
The mechanical, morphological and thermo-oxidative aging properties of the glass fiber reinforced polypropylene (RGF-PP) were studied based on four different maleic anhydride grafted polypropylene (PP-g-MAH) compatibi...The mechanical, morphological and thermo-oxidative aging properties of the glass fiber reinforced polypropylene (RGF-PP) were studied based on four different maleic anhydride grafted polypropylene (PP-g-MAH) compatibilizers with different content of residual maleic anhydride (MAH). It was shown that PP-g-MAH compatibilizer could significantly improve the mechanical properties of RGF-PP, while from thermal and morphological analysis results, the content of residual MAH had negative influence on long term thermo- oxidative aging properties of RGF-PP with adding PP-g-MAH compatibilizer;the lower the residual content of MAH is, the better the thermo stability of the PP-g-MAH is, and also the better the thermo-oxidative aging properties was obtained.展开更多
The effect of R-styrene-maleic anhydride copolymer （R- SMA） compatibilzation on Nylon 6 （ PA6 ）/polypropylene （ PP ） blends has been investigated experimentally through Molan test, microscopic morphology, and ch...The effect of R-styrene-maleic anhydride copolymer （R- SMA） compatibilzation on Nylon 6 （ PA6 ）/polypropylene （ PP ） blends has been investigated experimentally through Molan test, microscopic morphology, and chemical structure. Results show that the moderate R-SMA addition can promote reaction between anhydride in R-SMA and amino in PA6, and lead to a new PA6-g- R-SMA copolymer in the blends. Such PA6-g-R-SMA eopolymer in the blends can effectively reduce the interfaeial tension and PP particle size, and improve the compatibility of two immiscible phases in the blends. The crystallinity of PA6 in PA6/PP blends has greatly decreased by PP blends. The blends have the best comprehensive mechanical and thermal properties when the mass ratio of PA6/PP/ R-SMA is 90：10：2 to 90：10：4. The impact strength of the PA6/PP blends with the eompatibilizer is increased by more than 150 %.展开更多
文摘Previously, Polyvinyl Alcohol (PVA) and phenolic resin were used for resin impregnated bamboo fiber reinforced PP composites which was manufactures for resin impregnated bamboo fiber with polypropylene (PP). Resin impregnation method can show improvement on tensile strength of fiber. However, to reduce the contact surface area and low inter-facial shear strength (IFSS) between impregnated resin and matrix, using 40% weight fraction of bamboo fiber in PP matrix, PVA impregnated composites with mean flexural and tensile strength 10% higher than untreated composites were produced butphenolic resin impregnated fiber reinforced composition’s mechanical properties were decreased. In this study maleic anhydride grafted polypropylene (MAPP) was used to increase interfacial shear strength between resin impregnated fiber and PP. With 10% MAPP, IFSS between resin impregnated fiber and PP increased more than 100% and reinforced composites. MAPP with untreated, phenolic resin and PVA impregnated cases showed similar mechanical properties. Yet in water absorption test, the PVA treatment with bamboo/PP composites increased water absorption ratio. But with 10% MAPP, matrix PP water absorption ratio decreased like phenolic resin impregnated fiber reinforced composites. 10% MAPP with resin impregnated bamboo fiber reinforced PP composites can improve IFSS, mechanical properties of composite and can decrease water absorption PVA resin impregnated bamboo fiber reinforced composites.
基金Funded by National Natural Science Foundation of China(Nos.51705295,51778351)the Science and Technology Project for the Universities of Shandong Province (No.J16LA58)Shandong University of Science and Technology Research Fund (No.2018 TDJH101)
文摘To study the effect of some parameters, such as, length and fraction of glass fiber (GF), and the fraction of maleic anhydride grafted polypropylene (PP-g-MAH), on the mechanical properties of glass fiber reinforced polypropylene (GF/PP) composites, tensile tests, bending tests and impact tests were conducted. Scanning electron microscope (SEM) was used to characterize the fracture mechanisms of the composites. The results show that, compared with 3 mm GF, 9 mm GF can significantly improve the strength of the composite better. Addition of PP-g-MAH, a kind of grafting agent, into the PP-30% LGF composite can result in a better mechanical properties because of the strengthening of the bonding interface between the matrix and the fiber. When the mass fraction of GF is 30% and the PP-g-MAH fraction is 6%, the mechanical properties of the composite are the best.
文摘The mechanical, morphological and thermo-oxidative aging properties of the glass fiber reinforced polypropylene (RGF-PP) were studied based on four different maleic anhydride grafted polypropylene (PP-g-MAH) compatibilizers with different content of residual maleic anhydride (MAH). It was shown that PP-g-MAH compatibilizer could significantly improve the mechanical properties of RGF-PP, while from thermal and morphological analysis results, the content of residual MAH had negative influence on long term thermo- oxidative aging properties of RGF-PP with adding PP-g-MAH compatibilizer;the lower the residual content of MAH is, the better the thermo stability of the PP-g-MAH is, and also the better the thermo-oxidative aging properties was obtained.
基金Science and Technology Program from Jiangxi Provincial Department of Education,China (No. CJJ10377)
文摘The effect of R-styrene-maleic anhydride copolymer （R- SMA） compatibilzation on Nylon 6 （ PA6 ）/polypropylene （ PP ） blends has been investigated experimentally through Molan test, microscopic morphology, and chemical structure. Results show that the moderate R-SMA addition can promote reaction between anhydride in R-SMA and amino in PA6, and lead to a new PA6-g- R-SMA copolymer in the blends. Such PA6-g-R-SMA eopolymer in the blends can effectively reduce the interfaeial tension and PP particle size, and improve the compatibility of two immiscible phases in the blends. The crystallinity of PA6 in PA6/PP blends has greatly decreased by PP blends. The blends have the best comprehensive mechanical and thermal properties when the mass ratio of PA6/PP/ R-SMA is 90：10：2 to 90：10：4. The impact strength of the PA6/PP blends with the eompatibilizer is increased by more than 150 %.