The structures of the Mn-Zn ferrites synthesized under different sintering conditions by the sol-gel method were investigated by the X-ray diffraction （XRD） and the scanning electron microscopy （SEM） with focus on...The structures of the Mn-Zn ferrites synthesized under different sintering conditions by the sol-gel method were investigated by the X-ray diffraction （XRD） and the scanning electron microscopy （SEM） with focus on two factors： the pre-sintering treatment and the calcining time. The results show that the sintering conditions have significant effects on the structures and the particle size of the Mn-Zn ferrites. Compared with the products without pre-sintering, those pre-sintered at 500℃ have a single phase and no diffraction peaks of Fe2O3 that could be found. The effects of the pre-sintering temperature on the structures of the ferrites were also studied. As a result, 500℃ proves to be the favorite in the pre-sintering treatment. The XRD patterns of the ferrites calcined at 1 200℃ for 6 h will present diffraction peaks of pure crystallization of spinel phase while those for 2 h or 4 h will show peaks of Fe2O3. The SEM also bears witness to well-grown grains of pure Mn-Zn ferrites if calcined for 6 hours.展开更多
文摘The structures of the Mn-Zn ferrites synthesized under different sintering conditions by the sol-gel method were investigated by the X-ray diffraction （XRD） and the scanning electron microscopy （SEM） with focus on two factors： the pre-sintering treatment and the calcining time. The results show that the sintering conditions have significant effects on the structures and the particle size of the Mn-Zn ferrites. Compared with the products without pre-sintering, those pre-sintered at 500℃ have a single phase and no diffraction peaks of Fe2O3 that could be found. The effects of the pre-sintering temperature on the structures of the ferrites were also studied. As a result, 500℃ proves to be the favorite in the pre-sintering treatment. The XRD patterns of the ferrites calcined at 1 200℃ for 6 h will present diffraction peaks of pure crystallization of spinel phase while those for 2 h or 4 h will show peaks of Fe2O3. The SEM also bears witness to well-grown grains of pure Mn-Zn ferrites if calcined for 6 hours.