The effects of ultrafine WC(WC_(UF),0.5μm) or W(1μm) and C(0.3μm)(W+C)_(UF) additives on the densification,microstructure and mechanical properties of coarse-grained cemented carbides were compared systematically.O...The effects of ultrafine WC(WC_(UF),0.5μm) or W(1μm) and C(0.3μm)(W+C)_(UF) additives on the densification,microstructure and mechanical properties of coarse-grained cemented carbides were compared systematically.Overall,the cemented carbides with WC_(UF)/(W+C)_(UF) additives are almost fully densification to be higher than 99%,and the average grain size is kept above 2.8μm.The WC_(UF) additive assists grains to(truncated)trigonal prism shape by two dimensional(2D) growth,whereas the(W+C)_(UF) additive assists grains to rounded shape by three dimensional(3D) growth,lowers WC contiguity and increases face-centered-cubic Co.The hardness and bending strength of(75WC_(C)-15WC_(UF))-10Co are 86.6 HRA and 2 272 MPa,respectively,both higher than those of(75WC_(C)-15(W+C)_(UF))-10Co,which could be ascribed to the enhanced densification and unblemished grains.However,the fracture toughness of the(75WC_(C)-15(W+C)_(UF))-10Co is 23.5 MPa·m^(1/2),higher than that of the(75WC_(C)-15WC_(UF))-10Co due to the uniform WC-Co structure and flexible binder phase.展开更多
In this paper, we get W 1,p(Rn)-boundedness for tangential maximal func- tion and nontangential maximal function , which improves J.Kinnunen, P.Lindqvist and Tananka’s results.
Given a positive Radon measure μ on R^d satisfying the linear growth condition μ(B(x,r))≤C0r^n,x∈R^d,r〉0,(1) where n is a fixed number and O〈n≤d. When d-1〈n,it is proved that if Tt,N1=0,then the correspo...Given a positive Radon measure μ on R^d satisfying the linear growth condition μ(B(x,r))≤C0r^n,x∈R^d,r〉0,(1) where n is a fixed number and O〈n≤d. When d-1〈n,it is proved that if Tt,N1=0,then the corresponding maximal Calderon-Zygmund singular integral is bounded from RBMO to itself only except that it is infinite μ-a. e. on R^d.展开更多
基金Funded by the Technology Innovation Leading Program of Shaanxi(No.2022QFY08-02)。
文摘The effects of ultrafine WC(WC_(UF),0.5μm) or W(1μm) and C(0.3μm)(W+C)_(UF) additives on the densification,microstructure and mechanical properties of coarse-grained cemented carbides were compared systematically.Overall,the cemented carbides with WC_(UF)/(W+C)_(UF) additives are almost fully densification to be higher than 99%,and the average grain size is kept above 2.8μm.The WC_(UF) additive assists grains to(truncated)trigonal prism shape by two dimensional(2D) growth,whereas the(W+C)_(UF) additive assists grains to rounded shape by three dimensional(3D) growth,lowers WC contiguity and increases face-centered-cubic Co.The hardness and bending strength of(75WC_(C)-15WC_(UF))-10Co are 86.6 HRA and 2 272 MPa,respectively,both higher than those of(75WC_(C)-15(W+C)_(UF))-10Co,which could be ascribed to the enhanced densification and unblemished grains.However,the fracture toughness of the(75WC_(C)-15(W+C)_(UF))-10Co is 23.5 MPa·m^(1/2),higher than that of the(75WC_(C)-15WC_(UF))-10Co due to the uniform WC-Co structure and flexible binder phase.
基金Supported by the key Academic Discipline of Zhejiang Province of China under Grant No.2005the Zhejiang Provincial Natural Science Foundation of China
文摘In this paper, we get W 1,p(Rn)-boundedness for tangential maximal func- tion and nontangential maximal function , which improves J.Kinnunen, P.Lindqvist and Tananka’s results.
文摘Given a positive Radon measure μ on R^d satisfying the linear growth condition μ(B(x,r))≤C0r^n,x∈R^d,r〉0,(1) where n is a fixed number and O〈n≤d. When d-1〈n,it is proved that if Tt,N1=0,then the corresponding maximal Calderon-Zygmund singular integral is bounded from RBMO to itself only except that it is infinite μ-a. e. on R^d.