Carbonated recycled powder as cementitious auxiliary material can reduce carbon emissions and realize high-quality recycling of recycled concrete.In this paper,microscopic property of recycled powder with three carbon...Carbonated recycled powder as cementitious auxiliary material can reduce carbon emissions and realize high-quality recycling of recycled concrete.In this paper,microscopic property of recycled powder with three carbonation methods was tested through XRD and SEM,the mechanical property and microstructure of recycled powder mortar with three replacement rates were studied by ISO method and SEM,and the strengthening mechanism was analyzed.The results showed that the mechanical property of recycled powder mortar decreased with the increasing of replacement rate.It is suggested that the replacement rate of recycled powder should not exceed 20%.The strength index and activity index of carbonated recycled powder mortar were improved,in which the flexural strength was increased by 27.85%and compressive strength was increased by 20%at the maximum.Recycled powder can be quickly and completely carbonated,and the improvement effect of CH pre-soaking carbonation was the best.The activity index of carbonated recycled powder can meet the requirements of Grade II technical standard for recycled powder.Microscopic results revealed the activation mechanism of carbonated recycled powder such as surplus calcium source effect,alkaline polycondensation effect and carbonation enhancement effect.展开更多
Face-centered cubic (f.c.c.) high entropy alloys (HEAs) are attracting more and more attention owing to their excellent strength and ductility synergy, irradiation resistance, etc. However, the yield strength of f.c.c...Face-centered cubic (f.c.c.) high entropy alloys (HEAs) are attracting more and more attention owing to their excellent strength and ductility synergy, irradiation resistance, etc. However, the yield strength of f.c.c. HEAs is generally low, significantly limiting their practical applications. Recently, the alloying of W has been evidenced to be able to remarkably improve the mechanical properties of f.c.c. HEAs and is becoming a hot topic in the community of HEAs. To date, when W is introduced, multiple strengthening mechanisms, including solid-solution strengthening, precipitation strengthening (μphase,σphase, and b.c.c. phase), and grain-refinement strengthening, have been discovered to be activated or enhanced. Apart from mechanical properties, the addition of W improves corrosion resistance as W helps to form a dense WO_(3) film on the alloy surface. Until now, despite the extensive studies in the literature, there is no available review paper focusing on the W doping of the f.c.c. HEAs. In that context, the effects of W doping on f.c.c. HEAs were reviewed in this work from three aspects, i.e., microstructure,mechanical property, and corrosion resistance. We expect this work can advance the application of the W alloying strategy in the f.c.c. HEAs.展开更多
In this study,HEA/AI composite interlayer was used to fabricate Ti/Mg bimetal composites by solidliquid compound casting process.The Al layer was prepared on the surface of TC4 alloy by hot dipping,and the FeCoNiCr HE...In this study,HEA/AI composite interlayer was used to fabricate Ti/Mg bimetal composites by solidliquid compound casting process.The Al layer was prepared on the surface of TC4 alloy by hot dipping,and the FeCoNiCr HEA layer was prepared by magnetron sputtering onto the Al layer.The influence of the HEA layer thickness and pouring temperature on interface evolution was investigated based on SEM observation and thermodynamic analysis.Results indicate that the sluggish diffusion effect of HEA can effectively inhibit the interfacial diffusion between Al and Mg,which is conducive to the formation of solid solution,especially when the thickness of HEA is 800 nm.With the increase of casting temperature from 720 ℃ to 730 ℃,740℃,and 750 ℃,α-Al(Mg),α-Al(Mg)+Al3Mg2,Al3Mg2+Al12Mg17,and Al12Mg17+δ-Mg are formed at the interface of Ti/Mg bimetal,respectively.When the thickness of the HEA layer is 800 nm and the pouring temperature is 720 ℃,the bonding strength of the Ti/Mg bimetal can reach the maximum of 93.6 MPa.展开更多
To study the water absorption of hollow glass microspheres(HGMs)composite epoxy resin solid buoyancy materials in the marine environment and its effect on the mechanical properties,the water absorption was measured by...To study the water absorption of hollow glass microspheres(HGMs)composite epoxy resin solid buoyancy materials in the marine environment and its effect on the mechanical properties,the water absorption was measured by immersing the material in distilled water for 36 days at ambient temperature and fitted to Fick’s second law.The strength of materials before and after water absorption were tested by uniaxial experiments,and the effects of the filling ratio and water absorption on the mechanical properties of the materials were analyzed and explained.Finally,the failure modes and mechanism of the hollow glass microspheres composite material were explicated from the microscopic level by scanning electron microscope(SEM).This research will help solve the problems of solid buoyancy materials in ocean engineering applications.展开更多
The main objective of this work was to study and develop composite materials by experiments with mixtures of synthetic(glass fiber, carbon fiber) and natural fiber(durian skin fiber) reinforcements on a polylactic aci...The main objective of this work was to study and develop composite materials by experiments with mixtures of synthetic(glass fiber, carbon fiber) and natural fiber(durian skin fiber) reinforcements on a polylactic acid(PLA) matrix composite, because of its excellent mechanical properties. Durian skin fiber(DSF) is a natural waste throughout Thailand, and an alternative to recycling is to realize its potential as a new reinforcement through mixing and the injection molding processes. The flexural strength(σ_(F)) and flexural modulus(E_(F)) of the composites from specimens showed a maximum value by content of durian skin fiber at 10 wt%, for good performance relative to particle dispersion between the matrix and the fiber, and showed a minimum value by content of durian skin fiber at 20 wt%, because the reinforcement material affects the mechanical properties in the experiments.展开更多
The cold radial forging process usually introduces some changes of the material, such as the increased strength, the decreased plasticity and the introduction of anisotropic mechanical prop- erty. To obtain the change...The cold radial forging process usually introduces some changes of the material, such as the increased strength, the decreased plasticity and the introduction of anisotropic mechanical prop- erty. To obtain the changes of mechanical property of barrel processed by cold radial forging, the tangential mechanical properties of the barrel blank and the forged barrel are measured with a de- signed test based on the plastic deformation analysis for a barrel and by applying internal pressure, and their axial mechanical properties are measured by the tensile test. The changes of mechanical property of barrel processed by cold radial forging are obtained by comparing the mechanical proper- ties of the barrel blank and the forged barrel. The tangential and axial flow stresses of the barrel blank and the forged barrel are also presented.展开更多
In this paper, melt blends of poly(propylene carbonate) (PPC) with poly(butylene succinate) (PBS) were characterized by dynamic mechanical analysis (DMA), differential scanning calorimetry (DSC), tensile t...In this paper, melt blends of poly(propylene carbonate) (PPC) with poly(butylene succinate) (PBS) were characterized by dynamic mechanical analysis (DMA), differential scanning calorimetry (DSC), tensile testing, wide-angle X-ray diffraction (WAXD), polarized optical microscopy and thermogravimetric analysis (TGA). The results indicated that the glass transition temperature of PPC in the 90/10 PPC/PBS blend was decreased by about 11 K comparing with that of pure PPC. The presence of 10% PBS was partially miscible with PPC. The 90/10 PPC/PBS blend had better impact and tensile strength than those of the other PPC/PBS blends. The glass transition temperature of PPC in the 80/20, 70/30, and 60/40 PPC/PBS blends was improved by about 4.9 K, 4.2 K, and 13 K comparing with that of pure PPC, respectively; which indicated the immiscibility between PPC and PBS. The DSC results indicated that the crystallization of PBS became more difficult when the PPC content increased. The matrix of PPC hindered the crystallization process of PBS. While the content of PBS was above 20%, significant crystallization-induced phase separation was observed by polarized optical microscopy. It was found from the WAXD analysis that the crystal structure of PBS did not change, and the degree of crystallinity increased with increasing PBS content in the PPC/PBS blends.展开更多
The effects of addition of La on the microstructure of as-cast ADC12 A1-Alloy were investigated by using optical microscope (OM), X-ray diffraction (XRD), scanning electron microscope (SEM), and energy disperse ...The effects of addition of La on the microstructure of as-cast ADC12 A1-Alloy were investigated by using optical microscope (OM), X-ray diffraction (XRD), scanning electron microscope (SEM), and energy disperse spectroscopy (EDS). The experimental results showed that the a-A1 and eutectic Si crystals were modified with the addition of 0.3 wt% La. The eutectic Si crystals showed a granular distribution. At the same time, the alloy possessed the best mechanical property. When more than 0.3 wt% La was added to ADC12 aluminum alloy, the microstructure of as-cast alloy was coarsening gradually with the increase of the content of La and the mechanical property decreased. The effect of rare earth La which was added in ADC 12 A1-Alloy for up to 0.9 wt% had been investigated in this study. The dendrites ofADC12 Al-alloy was refined obviously and the morphology of Si crystals showed a particle structure when the addition of La reached 0,3 wt%. Besides, the acicular La-rich intermetallics in the alloy deteriorated the mechanical property of alloy: To avoid this unwanted phase, the amount of added rare earth La must be less than 0.6 wt%.展开更多
Based on domestic-developed triaxial servo-controlled seepage equipment for thermal-hydrologicalmechanical coupling of coal containing methane,an experimental study was carried out to investigate mechanical property a...Based on domestic-developed triaxial servo-controlled seepage equipment for thermal-hydrologicalmechanical coupling of coal containing methane,an experimental study was carried out to investigate mechanical property and gas permeability of raw coal,under the situation of conventional triaxial compression and unloading confining pressure tests in different gas pressure conditions.Triaxial unloading confining pressure process was reducing confining pressure while increasing axial pressure.The research results show that,compared with the peak intensity of conventional triaxial loading,the ultimate strength of coal samples of triaxial unloading confining pressure was lower,deformation under loading was far less than unloading,dilation caused by unloading was more obvious than loading.The change trend of volumetric strain would embody change of gas permeability of coal,the permeability first reduced along with volumetric strain increase,and then raised with volume strain decrease,furthermore,the change trends of permeability of coal before and after destruction were different in the stage of decreasing volume strain due to the effect of gas pressure.When gas pressure was greater,the effective confining pressure was smaller,and the radial deformation produced by unloading was greater.When the unloading failed confining pressure difference was smaller,coal would be easier to get unstable failure.展开更多
The effects of adding poly (ethylene glycol) (PEG) into polylactic acid/thermoplastic starch blends (PLA/TPS) on the properties were investigated by DSC, SEM and mechanical property-testing. The blends of PLA/TP...The effects of adding poly (ethylene glycol) (PEG) into polylactic acid/thermoplastic starch blends (PLA/TPS) on the properties were investigated by DSC, SEM and mechanical property-testing. The blends of PLA/TPS blended with increasing content PEG exhibited lower temperature of glass transition (T) and lower temperature of melting (T) as well as higher melt flow index (MFI), which indicates the plasticization and proeessability of the composites were dramatically improved. The tensile strength, flexural strength and izod impact strength of PLA/TPS (80/20) increased at first and then decreased with increasing content of PEG due to stronger interfacial adhesion. The optimized mechanical property can be obtained for the blend with 3 wt % PEG. The samples containing PEG after soil burial for 5 months showed quicker degradation being accompanied with large weight loss and mechanical properties loss.展开更多
The solid sintering behavior and mechanical properties of Fe Ni powders prepared by mechanical alloying of elemental powders and hot pressing sintering in vacuum atmospheres were investigated. It was observed that th...The solid sintering behavior and mechanical properties of Fe Ni powders prepared by mechanical alloying of elemental powders and hot pressing sintering in vacuum atmospheres were investigated. It was observed that the microstructure of the powder particles evolves in three stages. The alloy powder with average grain size of 20-30 nm was obtained. The sinter densification depends crucially on the particle rearrangement and the large amount of internal strain introduced during milling. The theoretical density of over 95 % was obtained after hot pressing sintering at 800 ℃ for 30 min with pressure of 50 MPa. No significant grain growth was observed during sintering. And also relatively high hardness was obtained.展开更多
The microstructure formation and mechanical property involving icosahedral quasicrystal (I-phase) in the Y-rich Mg-Zn-Y alloy have been studied. The equilibrium formation of I-phase from the Y-rich Mg-Zn-Y melt is ...The microstructure formation and mechanical property involving icosahedral quasicrystal (I-phase) in the Y-rich Mg-Zn-Y alloy have been studied. The equilibrium formation of I-phase from the Y-rich Mg-Zn-Y melt is through a peritectic reaction between the Y-rich melt and the primary W-phase, which is discussed in detail. The independent nucleation and coupling growth mechanism between the W-phase and the I-phase, from the melt, are revealed, which is significant for understanding the peritectic reaction process involving icosahedral quasicrystal in the Mg-Zn-Y alloy. The mechanism of the quasicrystal phase strengthened magnesium alloys is also discussed here.展开更多
The microstructure, texture and mechanical property evolution of the extruded Mg-x Y(x = 1, 5 wt.%) alloys during equal channel angular pressing(ECAP) were systematically investigated using an optical microscope, elec...The microstructure, texture and mechanical property evolution of the extruded Mg-x Y(x = 1, 5 wt.%) alloys during equal channel angular pressing(ECAP) were systematically investigated using an optical microscope, electron backscatter diffraction(EBSD) and uniaxial tensile test. The Mg-Y alloys exhibited a weakened basal texture before the ECAP, and the texture was further weakened with the max basal poles dispersed along ~45° between the extrusion direction and the transverse direction after the ECAP. The Mg-5 Y alloys always exhibited a finer grain size comparing to that of Mg-1 Y for the same ECAP process. With a proper ECAP process, both the strength and elongation of Mg-5 Y alloy could be improved simultaneously after the ECAP, i.e., the yield strength(273.9 ± 1.2 MPa), ultimate strength(306.4 ± 3.0 MPa),and elongation(23.9 ± 1.0%) were increased by 10%, 6%, and 72%, respectively, comparing to that before the ECAP. This was considered to be arose from the combined effects of grain refinement, significant improved microstructure homogeneity and solid solution hardening.In addition, it was found that Mg-Y alloy with better comprehensive properties could be obtained by the decreasing-temperature ECAP processes. The yield strength-grain size relationship could be well described by the Hall-Petch relation for all the ECAPed Mg-Y alloys,which was consistent with that the texture changes did not significantly affect the average Schmid factors of basal, prismatic and pyramidal slips for both Mg-Y alloys.展开更多
An experiment was carried out on the friction stir welding of MB3 magnesium alloy to determine welding parameters for obtaining an excellent weld appearance without void, cracking, or distortion. Frictional heat and p...An experiment was carried out on the friction stir welding of MB3 magnesium alloy to determine welding parameters for obtaining an excellent weld appearance without void, cracking, or distortion. Frictional heat and plastic flow created fine and equiaxed grains in the weld nugget, and the elongated and recovered grains in the thermomechanically affected zone (TMAZ). The grains in the heat affected zone (HAZ) grow slightly. The me- chanical property results show that maximum joint tensile strength can reach 97. 2% of the parent material, which is stronger than that of fusion joints; and the failure almost occurs in the heat affected zone.展开更多
The simulated heat affected zone (HAZ) of the high strength low alloy (HSLA) steels containing 0%, 0.047%, 0.097% and 0.151% vanadium, respectively, were studied with Gleeble-2000 thermomechanical simulator to det...The simulated heat affected zone (HAZ) of the high strength low alloy (HSLA) steels containing 0%, 0.047%, 0.097% and 0.151% vanadium, respectively, were studied with Gleeble-2000 thermomechanical simulator to determine the influence of vanadium addition on the mechanical properties of the HAZ. The HAZ simulation involved reheating the samples to 1350℃, and then cooling to ambient temperature at a cooling rate of 5℃/s ranging from 800 to 500℃ (△8/5=60s). The mechanical properties including tensile strength and -20℃ impact toughness were conducted. The microstructures of the base steel and the simulated HAZs were investigated using optical microscope, scanning electron microscope ( SEM ) and transmission electron microscope (TEM). Based on the systemutic examination, the present work confirmed that about 0.05% vanadium addition to low carbon low alloy steels resulted in expected balance of strength and toughness of the HAZ. And more than 0.10% levels addition led to detrimental toughness of the HAZ SEM study showed that the simulated 0.097% and 0.151%V HAZs consisted of more coarse ferrite plates with greater and more M-A constituents along austenite grain and ferrite plate bound- aries. The impact fracture surfaces of the simulated 0.097% and 0.151%V HAZs showed typically brittle mode with predominant cleavages. The size of the facet in the fracture surface increased with increasing vanadium level from 0.097% to 0.151%.As a result, the simulated 0.151% V HAZ has the lowest impact toughness of the four specimens.展开更多
The corrosion behavior and mechanical property of Mg-7Y-x Nd(x=0.5,1.0,1.5 wt%)alloys were investigated.The microstructure and precipitations of Mg-7Y-x Nd alloys were studied by scanning electron microscopy,energy-di...The corrosion behavior and mechanical property of Mg-7Y-x Nd(x=0.5,1.0,1.5 wt%)alloys were investigated.The microstructure and precipitations of Mg-7Y-x Nd alloys were studied by scanning electron microscopy,energy-dispersive spectrometry and X-ray Diffraction.The quantities of the Mg_(12)(Y,Nd)phase increased,whereas that of the Mg_(24)(Y,Nd)_(5)phase decreased with increasing Nd-content.The weight loss rate decreased from 17.5020 mg cm^(-2)·d^(-1)(36.7542 mm y^(-1))to 9.3744 mg cm^(-2)·d^(-1)(19.6862 mm y^(-1)).The electrochemical measurement also demonstrated the similar tendency.The loss in mechanical properties after corrosion reaction followed the order Mg-7Y-0.5Nd>Mg-7Y-1.0Nd>Mg-7Y-1.5Nd.The precipitations played dual roles in the corrosion resistance that depended on type and distribution.展开更多
Dissimilar material joining of 6008 aluminum alloy to H220 YD galvanized high strength steel was performed by resistance spot welding with especial electrodes that were a flat tip electrode against the steel surface a...Dissimilar material joining of 6008 aluminum alloy to H220 YD galvanized high strength steel was performed by resistance spot welding with especial electrodes that were a flat tip electrode against the steel surface and a domed tip electrode upon the aluminum alloy surface. An intermetallic compound layer composed of Fe2Al5 and FeAl3 was formed at the steel/ aluminum interface in the welded joint. The thickness of the intermetallic compound layer increased with increasing welding current and welding time, and the maximum thickness being 7. 0 μm was obtained at 25 kA and 300 ms. The weld nugget diameter and tensile shear load of the welded joint had increased tendencies first with increasing welding current ( 18 -22 kA) and welding time ( 50 - 300 ms), then changed little with further increasing welding current ( 22 - 25 kA) and welding time (300 -400 ms). The maximum tensile shear load reached 5.4 kN at 22 kA and 300 ms. The welded joint fractured through brittle intermetallic compound layer and aluminum alloy nugget.展开更多
A large amount of cutting heat is produced during the heavy cutting process,and insert life is restricted by the effect of thermal load. The thermal load experiment of cemented carbide SCS,WF and YT15 is carried out,a...A large amount of cutting heat is produced during the heavy cutting process,and insert life is restricted by the effect of thermal load. The thermal load experiment of cemented carbide SCS,WF and YT15 is carried out,and the results show that the bending strength and fracture toughness of cemented carbide material decrease obviously under cyclic thermal load,while in the cooling process,the material mechanical property changes worse suddenly. The high-temperature mechanical property of SCS is the most stable,and that of YT15is the worst. Further,a relation model among cutting temperature,cutting parameters and insert life is established. Finally,the measures to improve heavy cemented carbide inserts life are summarized from the aspects of cutting parameters selection,insert optimization design and TiCN,A12O3,TiN complex insert coating. The research results are expected to provide support and reference for heavy cutting technology and insert technology.展开更多
The mechanical property and deformation mechanism of twinned gold nanowire with non-uniform distribution of twinned boundaries(TBs)are studied by the molecular dynamics(MD)method.It is found that the twin boundary spa...The mechanical property and deformation mechanism of twinned gold nanowire with non-uniform distribution of twinned boundaries(TBs)are studied by the molecular dynamics(MD)method.It is found that the twin boundary spacing(TBS)has a great effect on the strength and plasticity of the nanowires with uniform distribution of TBs.And the strength enhances with the decrease of TBS,while its plasticity declines.For the nanowires with non-uniform distribution of TBs,the differences in distribution among different TBSs have little effect on the Young's modulus or strength,and the compromise in strength appears.But the differences have a remarkable effect on the plasticity of twinned gold nanowire.The twinned gold nanowire with higher local symmetry ratio has better plasticity.The initial dislocations always form in the largest TBS and the fracture always appears at or near the twin boundaries adjacent to the smallest TBS.Some simulation results are consistent with the experimental results.展开更多
In order to investigate the effects of Ce on mechanical anisotorpy of Al-Li alloys, the texture of 2090 AlLi alloy with different Ce content was determined using orientation distribution function technique, in which ...In order to investigate the effects of Ce on mechanical anisotorpy of Al-Li alloys, the texture of 2090 AlLi alloy with different Ce content was determined using orientation distribution function technique, in which the mechanical properties with different angles to rolling direction were measured. The effects of Ce on texture and mechanical properties of 2090 alloys were discussed. The results show that the type of main texture of 2090 alloys is {225} <554>. Ce will not change the type of main texture of the alloy, but make the distributiodn of main texture scattered. Ce can change the volume fractions of ideal texture components and will decrease the anisotropy of yield strength, hence the content of the texture components that enhance the anisotropy of yield strength can be reduced.展开更多
基金Funded by Joint Funds of the National Natural Science Foundation of China(No.U1904188)Jiangxi Provincial Department of Education Science and Technology Project(Nos.GJJ171079,GJJ181023 and GJJ181022)。
文摘Carbonated recycled powder as cementitious auxiliary material can reduce carbon emissions and realize high-quality recycling of recycled concrete.In this paper,microscopic property of recycled powder with three carbonation methods was tested through XRD and SEM,the mechanical property and microstructure of recycled powder mortar with three replacement rates were studied by ISO method and SEM,and the strengthening mechanism was analyzed.The results showed that the mechanical property of recycled powder mortar decreased with the increasing of replacement rate.It is suggested that the replacement rate of recycled powder should not exceed 20%.The strength index and activity index of carbonated recycled powder mortar were improved,in which the flexural strength was increased by 27.85%and compressive strength was increased by 20%at the maximum.Recycled powder can be quickly and completely carbonated,and the improvement effect of CH pre-soaking carbonation was the best.The activity index of carbonated recycled powder can meet the requirements of Grade II technical standard for recycled powder.Microscopic results revealed the activation mechanism of carbonated recycled powder such as surplus calcium source effect,alkaline polycondensation effect and carbonation enhancement effect.
基金financially supported by the National Key R&D Program of China (No.2021YFA1200203)the National Natural Science Foundation of China (Nos.51922026 and 51975111)+1 种基金the Fundamental Research Funds for the Central Universities (No.N2202015,N2002005,and N2105001)the 111 Project of China (No.BP0719037 and B20029)。
文摘Face-centered cubic (f.c.c.) high entropy alloys (HEAs) are attracting more and more attention owing to their excellent strength and ductility synergy, irradiation resistance, etc. However, the yield strength of f.c.c. HEAs is generally low, significantly limiting their practical applications. Recently, the alloying of W has been evidenced to be able to remarkably improve the mechanical properties of f.c.c. HEAs and is becoming a hot topic in the community of HEAs. To date, when W is introduced, multiple strengthening mechanisms, including solid-solution strengthening, precipitation strengthening (μphase,σphase, and b.c.c. phase), and grain-refinement strengthening, have been discovered to be activated or enhanced. Apart from mechanical properties, the addition of W improves corrosion resistance as W helps to form a dense WO_(3) film on the alloy surface. Until now, despite the extensive studies in the literature, there is no available review paper focusing on the W doping of the f.c.c. HEAs. In that context, the effects of W doping on f.c.c. HEAs were reviewed in this work from three aspects, i.e., microstructure,mechanical property, and corrosion resistance. We expect this work can advance the application of the W alloying strategy in the f.c.c. HEAs.
基金financial supports from the National Natural Science Foundation of China (No. 51875062)China Postdoctoral Science Foundation (No. 2021M700567)。
文摘In this study,HEA/AI composite interlayer was used to fabricate Ti/Mg bimetal composites by solidliquid compound casting process.The Al layer was prepared on the surface of TC4 alloy by hot dipping,and the FeCoNiCr HEA layer was prepared by magnetron sputtering onto the Al layer.The influence of the HEA layer thickness and pouring temperature on interface evolution was investigated based on SEM observation and thermodynamic analysis.Results indicate that the sluggish diffusion effect of HEA can effectively inhibit the interfacial diffusion between Al and Mg,which is conducive to the formation of solid solution,especially when the thickness of HEA is 800 nm.With the increase of casting temperature from 720 ℃ to 730 ℃,740℃,and 750 ℃,α-Al(Mg),α-Al(Mg)+Al3Mg2,Al3Mg2+Al12Mg17,and Al12Mg17+δ-Mg are formed at the interface of Ti/Mg bimetal,respectively.When the thickness of the HEA layer is 800 nm and the pouring temperature is 720 ℃,the bonding strength of the Ti/Mg bimetal can reach the maximum of 93.6 MPa.
基金financially supported by the Natural Science Foundation of Liaoning Province(Grant No.2021-MS-109)。
文摘To study the water absorption of hollow glass microspheres(HGMs)composite epoxy resin solid buoyancy materials in the marine environment and its effect on the mechanical properties,the water absorption was measured by immersing the material in distilled water for 36 days at ambient temperature and fitted to Fick’s second law.The strength of materials before and after water absorption were tested by uniaxial experiments,and the effects of the filling ratio and water absorption on the mechanical properties of the materials were analyzed and explained.Finally,the failure modes and mechanism of the hollow glass microspheres composite material were explicated from the microscopic level by scanning electron microscope(SEM).This research will help solve the problems of solid buoyancy materials in ocean engineering applications.
文摘The main objective of this work was to study and develop composite materials by experiments with mixtures of synthetic(glass fiber, carbon fiber) and natural fiber(durian skin fiber) reinforcements on a polylactic acid(PLA) matrix composite, because of its excellent mechanical properties. Durian skin fiber(DSF) is a natural waste throughout Thailand, and an alternative to recycling is to realize its potential as a new reinforcement through mixing and the injection molding processes. The flexural strength(σ_(F)) and flexural modulus(E_(F)) of the composites from specimens showed a maximum value by content of durian skin fiber at 10 wt%, for good performance relative to particle dispersion between the matrix and the fiber, and showed a minimum value by content of durian skin fiber at 20 wt%, because the reinforcement material affects the mechanical properties in the experiments.
文摘The cold radial forging process usually introduces some changes of the material, such as the increased strength, the decreased plasticity and the introduction of anisotropic mechanical prop- erty. To obtain the changes of mechanical property of barrel processed by cold radial forging, the tangential mechanical properties of the barrel blank and the forged barrel are measured with a de- signed test based on the plastic deformation analysis for a barrel and by applying internal pressure, and their axial mechanical properties are measured by the tensile test. The changes of mechanical property of barrel processed by cold radial forging are obtained by comparing the mechanical proper- ties of the barrel blank and the forged barrel. The tangential and axial flow stresses of the barrel blank and the forged barrel are also presented.
基金This work was supported by the National Natural Science Foundation of China(Nos.270274049 and 220374051).
文摘In this paper, melt blends of poly(propylene carbonate) (PPC) with poly(butylene succinate) (PBS) were characterized by dynamic mechanical analysis (DMA), differential scanning calorimetry (DSC), tensile testing, wide-angle X-ray diffraction (WAXD), polarized optical microscopy and thermogravimetric analysis (TGA). The results indicated that the glass transition temperature of PPC in the 90/10 PPC/PBS blend was decreased by about 11 K comparing with that of pure PPC. The presence of 10% PBS was partially miscible with PPC. The 90/10 PPC/PBS blend had better impact and tensile strength than those of the other PPC/PBS blends. The glass transition temperature of PPC in the 80/20, 70/30, and 60/40 PPC/PBS blends was improved by about 4.9 K, 4.2 K, and 13 K comparing with that of pure PPC, respectively; which indicated the immiscibility between PPC and PBS. The DSC results indicated that the crystallization of PBS became more difficult when the PPC content increased. The matrix of PPC hindered the crystallization process of PBS. While the content of PBS was above 20%, significant crystallization-induced phase separation was observed by polarized optical microscopy. It was found from the WAXD analysis that the crystal structure of PBS did not change, and the degree of crystallinity increased with increasing PBS content in the PPC/PBS blends.
基金Supported by the National Natural Science Foundation of China(No.51165032)the Innovative Group of Science and Technology of College of Jiangxi Province(No.00008713)
文摘The effects of addition of La on the microstructure of as-cast ADC12 A1-Alloy were investigated by using optical microscope (OM), X-ray diffraction (XRD), scanning electron microscope (SEM), and energy disperse spectroscopy (EDS). The experimental results showed that the a-A1 and eutectic Si crystals were modified with the addition of 0.3 wt% La. The eutectic Si crystals showed a granular distribution. At the same time, the alloy possessed the best mechanical property. When more than 0.3 wt% La was added to ADC12 aluminum alloy, the microstructure of as-cast alloy was coarsening gradually with the increase of the content of La and the mechanical property decreased. The effect of rare earth La which was added in ADC 12 A1-Alloy for up to 0.9 wt% had been investigated in this study. The dendrites ofADC12 Al-alloy was refined obviously and the morphology of Si crystals showed a particle structure when the addition of La reached 0,3 wt%. Besides, the acicular La-rich intermetallics in the alloy deteriorated the mechanical property of alloy: To avoid this unwanted phase, the amount of added rare earth La must be less than 0.6 wt%.
基金financially supported by the National Basic Research Program of China(No.2011CB201203)the National Natural Science Foundation of China(Nos.51204217 and 51374256)+1 种基金the National Major Science and Technology Projects of China(Nos.2011ZX05034-004 and 2011ZX05040-001-005)the Scientific Research Foundation of State Key Laboratory of Coal Mine Disaster Dynamics and Control(No.2011DA105287-MS201212)
文摘Based on domestic-developed triaxial servo-controlled seepage equipment for thermal-hydrologicalmechanical coupling of coal containing methane,an experimental study was carried out to investigate mechanical property and gas permeability of raw coal,under the situation of conventional triaxial compression and unloading confining pressure tests in different gas pressure conditions.Triaxial unloading confining pressure process was reducing confining pressure while increasing axial pressure.The research results show that,compared with the peak intensity of conventional triaxial loading,the ultimate strength of coal samples of triaxial unloading confining pressure was lower,deformation under loading was far less than unloading,dilation caused by unloading was more obvious than loading.The change trend of volumetric strain would embody change of gas permeability of coal,the permeability first reduced along with volumetric strain increase,and then raised with volume strain decrease,furthermore,the change trends of permeability of coal before and after destruction were different in the stage of decreasing volume strain due to the effect of gas pressure.When gas pressure was greater,the effective confining pressure was smaller,and the radial deformation produced by unloading was greater.When the unloading failed confining pressure difference was smaller,coal would be easier to get unstable failure.
文摘The effects of adding poly (ethylene glycol) (PEG) into polylactic acid/thermoplastic starch blends (PLA/TPS) on the properties were investigated by DSC, SEM and mechanical property-testing. The blends of PLA/TPS blended with increasing content PEG exhibited lower temperature of glass transition (T) and lower temperature of melting (T) as well as higher melt flow index (MFI), which indicates the plasticization and proeessability of the composites were dramatically improved. The tensile strength, flexural strength and izod impact strength of PLA/TPS (80/20) increased at first and then decreased with increasing content of PEG due to stronger interfacial adhesion. The optimized mechanical property can be obtained for the blend with 3 wt % PEG. The samples containing PEG after soil burial for 5 months showed quicker degradation being accompanied with large weight loss and mechanical properties loss.
文摘The solid sintering behavior and mechanical properties of Fe Ni powders prepared by mechanical alloying of elemental powders and hot pressing sintering in vacuum atmospheres were investigated. It was observed that the microstructure of the powder particles evolves in three stages. The alloy powder with average grain size of 20-30 nm was obtained. The sinter densification depends crucially on the particle rearrangement and the large amount of internal strain introduced during milling. The theoretical density of over 95 % was obtained after hot pressing sintering at 800 ℃ for 30 min with pressure of 50 MPa. No significant grain growth was observed during sintering. And also relatively high hardness was obtained.
基金the National Natural Science Foundation of China(Nos.50571081,50671083)Aeronautical Foundation of China(No.04G53042).
文摘The microstructure formation and mechanical property involving icosahedral quasicrystal (I-phase) in the Y-rich Mg-Zn-Y alloy have been studied. The equilibrium formation of I-phase from the Y-rich Mg-Zn-Y melt is through a peritectic reaction between the Y-rich melt and the primary W-phase, which is discussed in detail. The independent nucleation and coupling growth mechanism between the W-phase and the I-phase, from the melt, are revealed, which is significant for understanding the peritectic reaction process involving icosahedral quasicrystal in the Mg-Zn-Y alloy. The mechanism of the quasicrystal phase strengthened magnesium alloys is also discussed here.
基金supported by the National Natural Science Foundation of China(Nos.51401172 and 51601003)Sichuan Science and Technology Program(2019YJ0238)+1 种基金Fundamental Research Funds for the Central Universities(2682020ZT114)open funding of International Joint Laboratory for Light Alloys(MOE),Chongqing University。
文摘The microstructure, texture and mechanical property evolution of the extruded Mg-x Y(x = 1, 5 wt.%) alloys during equal channel angular pressing(ECAP) were systematically investigated using an optical microscope, electron backscatter diffraction(EBSD) and uniaxial tensile test. The Mg-Y alloys exhibited a weakened basal texture before the ECAP, and the texture was further weakened with the max basal poles dispersed along ~45° between the extrusion direction and the transverse direction after the ECAP. The Mg-5 Y alloys always exhibited a finer grain size comparing to that of Mg-1 Y for the same ECAP process. With a proper ECAP process, both the strength and elongation of Mg-5 Y alloy could be improved simultaneously after the ECAP, i.e., the yield strength(273.9 ± 1.2 MPa), ultimate strength(306.4 ± 3.0 MPa),and elongation(23.9 ± 1.0%) were increased by 10%, 6%, and 72%, respectively, comparing to that before the ECAP. This was considered to be arose from the combined effects of grain refinement, significant improved microstructure homogeneity and solid solution hardening.In addition, it was found that Mg-Y alloy with better comprehensive properties could be obtained by the decreasing-temperature ECAP processes. The yield strength-grain size relationship could be well described by the Hall-Petch relation for all the ECAPed Mg-Y alloys,which was consistent with that the texture changes did not significantly affect the average Schmid factors of basal, prismatic and pyramidal slips for both Mg-Y alloys.
文摘An experiment was carried out on the friction stir welding of MB3 magnesium alloy to determine welding parameters for obtaining an excellent weld appearance without void, cracking, or distortion. Frictional heat and plastic flow created fine and equiaxed grains in the weld nugget, and the elongated and recovered grains in the thermomechanically affected zone (TMAZ). The grains in the heat affected zone (HAZ) grow slightly. The me- chanical property results show that maximum joint tensile strength can reach 97. 2% of the parent material, which is stronger than that of fusion joints; and the failure almost occurs in the heat affected zone.
文摘The simulated heat affected zone (HAZ) of the high strength low alloy (HSLA) steels containing 0%, 0.047%, 0.097% and 0.151% vanadium, respectively, were studied with Gleeble-2000 thermomechanical simulator to determine the influence of vanadium addition on the mechanical properties of the HAZ. The HAZ simulation involved reheating the samples to 1350℃, and then cooling to ambient temperature at a cooling rate of 5℃/s ranging from 800 to 500℃ (△8/5=60s). The mechanical properties including tensile strength and -20℃ impact toughness were conducted. The microstructures of the base steel and the simulated HAZs were investigated using optical microscope, scanning electron microscope ( SEM ) and transmission electron microscope (TEM). Based on the systemutic examination, the present work confirmed that about 0.05% vanadium addition to low carbon low alloy steels resulted in expected balance of strength and toughness of the HAZ. And more than 0.10% levels addition led to detrimental toughness of the HAZ SEM study showed that the simulated 0.097% and 0.151%V HAZs consisted of more coarse ferrite plates with greater and more M-A constituents along austenite grain and ferrite plate bound- aries. The impact fracture surfaces of the simulated 0.097% and 0.151%V HAZs showed typically brittle mode with predominant cleavages. The size of the facet in the fracture surface increased with increasing vanadium level from 0.097% to 0.151%.As a result, the simulated 0.151% V HAZ has the lowest impact toughness of the four specimens.
基金The authors gratefully acknowledge the National Natural Science Foundation of China(Grant No.51501181)the Fun-damental Research Project of Technology Program of Qing-dao(17-1-1-76-JCH)the Key Research and Development Program of Shandong Province(2017GGX20139)for provid-ing support for this work.
文摘The corrosion behavior and mechanical property of Mg-7Y-x Nd(x=0.5,1.0,1.5 wt%)alloys were investigated.The microstructure and precipitations of Mg-7Y-x Nd alloys were studied by scanning electron microscopy,energy-dispersive spectrometry and X-ray Diffraction.The quantities of the Mg_(12)(Y,Nd)phase increased,whereas that of the Mg_(24)(Y,Nd)_(5)phase decreased with increasing Nd-content.The weight loss rate decreased from 17.5020 mg cm^(-2)·d^(-1)(36.7542 mm y^(-1))to 9.3744 mg cm^(-2)·d^(-1)(19.6862 mm y^(-1)).The electrochemical measurement also demonstrated the similar tendency.The loss in mechanical properties after corrosion reaction followed the order Mg-7Y-0.5Nd>Mg-7Y-1.0Nd>Mg-7Y-1.5Nd.The precipitations played dual roles in the corrosion resistance that depended on type and distribution.
文摘Dissimilar material joining of 6008 aluminum alloy to H220 YD galvanized high strength steel was performed by resistance spot welding with especial electrodes that were a flat tip electrode against the steel surface and a domed tip electrode upon the aluminum alloy surface. An intermetallic compound layer composed of Fe2Al5 and FeAl3 was formed at the steel/ aluminum interface in the welded joint. The thickness of the intermetallic compound layer increased with increasing welding current and welding time, and the maximum thickness being 7. 0 μm was obtained at 25 kA and 300 ms. The weld nugget diameter and tensile shear load of the welded joint had increased tendencies first with increasing welding current ( 18 -22 kA) and welding time ( 50 - 300 ms), then changed little with further increasing welding current ( 22 - 25 kA) and welding time (300 -400 ms). The maximum tensile shear load reached 5.4 kN at 22 kA and 300 ms. The welded joint fractured through brittle intermetallic compound layer and aluminum alloy nugget.
基金Sponsored by the National Natural Science Foundation of China(Grant No.51205095)Support Program for Key Youth(Grant No.1154G39)
文摘A large amount of cutting heat is produced during the heavy cutting process,and insert life is restricted by the effect of thermal load. The thermal load experiment of cemented carbide SCS,WF and YT15 is carried out,and the results show that the bending strength and fracture toughness of cemented carbide material decrease obviously under cyclic thermal load,while in the cooling process,the material mechanical property changes worse suddenly. The high-temperature mechanical property of SCS is the most stable,and that of YT15is the worst. Further,a relation model among cutting temperature,cutting parameters and insert life is established. Finally,the measures to improve heavy cemented carbide inserts life are summarized from the aspects of cutting parameters selection,insert optimization design and TiCN,A12O3,TiN complex insert coating. The research results are expected to provide support and reference for heavy cutting technology and insert technology.
基金the National Natural Science Foundation of China(Grant No.51771033).
文摘The mechanical property and deformation mechanism of twinned gold nanowire with non-uniform distribution of twinned boundaries(TBs)are studied by the molecular dynamics(MD)method.It is found that the twin boundary spacing(TBS)has a great effect on the strength and plasticity of the nanowires with uniform distribution of TBs.And the strength enhances with the decrease of TBS,while its plasticity declines.For the nanowires with non-uniform distribution of TBs,the differences in distribution among different TBSs have little effect on the Young's modulus or strength,and the compromise in strength appears.But the differences have a remarkable effect on the plasticity of twinned gold nanowire.The twinned gold nanowire with higher local symmetry ratio has better plasticity.The initial dislocations always form in the largest TBS and the fracture always appears at or near the twin boundaries adjacent to the smallest TBS.Some simulation results are consistent with the experimental results.
基金the National Natural Science Foundation of China!58971071
文摘In order to investigate the effects of Ce on mechanical anisotorpy of Al-Li alloys, the texture of 2090 AlLi alloy with different Ce content was determined using orientation distribution function technique, in which the mechanical properties with different angles to rolling direction were measured. The effects of Ce on texture and mechanical properties of 2090 alloys were discussed. The results show that the type of main texture of 2090 alloys is {225} <554>. Ce will not change the type of main texture of the alloy, but make the distributiodn of main texture scattered. Ce can change the volume fractions of ideal texture components and will decrease the anisotropy of yield strength, hence the content of the texture components that enhance the anisotropy of yield strength can be reduced.