Based on the production practice of medium carbon thin slabs in the CSP plant,the reasons and influencing factors for the formation of longitudinal cracks were investigated,and some industrial measures were taken to e...Based on the production practice of medium carbon thin slabs in the CSP plant,the reasons and influencing factors for the formation of longitudinal cracks were investigated,and some industrial measures were taken to eliminate the cracks.The results show that the efficient solutions to reduce longitudinal cracks are improving the performance of the mold powder,stabilizing the mold heat flux,and maintaining a proper taper of the mold during casting.Proper pouring temperature and secondary cooling also play important roles in preventing longitudinal surface cracks.展开更多
The flow field of molten steel and the interfacial behaviour between molten steel and liquid slag layer in medium-thin slab continuous casting mold with argon gas injection were studied by numerical simulation, in whi...The flow field of molten steel and the interfacial behaviour between molten steel and liquid slag layer in medium-thin slab continuous casting mold with argon gas injection were studied by numerical simulation, in which the effects of nozzle submergence depth and port angle, casting speed, and argon gas flow rate on the flow and the level fluctuation of molten steel were considered. The results show that the molten steel is jetted from the submerged en- try nozzle （SEN） with three ports into the mold and forms three recirculation zones including one upper recireulation zone and two lower recirculation zones. Argon gas injection results in a secondary vortex flow in the upper zone near the nozzle. For a given casting speed and argon gas flow rate, increasing the side port angle and submergence depth of nozzle can effectively restrain the steel/slag interracial fluctuation. Increasing the casting speed would prick up the level fluctuation. For a fixed casting speed, argon gas flow rate has a critical value, the interracial fluctuation with argon gas injection are stronger than the case without argon gas injection when the argon gas flow rate is less than the critical value, but when the argon gas flow rate exceeds the critical value, the level fluctuation is calmer than that without argon gas injection.展开更多
利用VOF(volume of fluid)方法和Lagrangian离散模型模拟了厚度为135 mm中薄板坯连铸结晶器内的钢液流动及钢/渣界面波动行为,分析了结晶器宽度、水口浸入深度、水口侧孔倾角、拉速和吹氩对结晶器内钢液流动和液面波动的影响规律.结果表...利用VOF(volume of fluid)方法和Lagrangian离散模型模拟了厚度为135 mm中薄板坯连铸结晶器内的钢液流动及钢/渣界面波动行为,分析了结晶器宽度、水口浸入深度、水口侧孔倾角、拉速和吹氩对结晶器内钢液流动和液面波动的影响规律.结果表明:钢液从三孔浸入式水口流入结晶器后形成上、下三个回流区;吹氩使结晶器上回流区靠近水口附近形成二次涡流;在一定拉速下,增加水口侧孔倾角和浸入深度均能有效抑制钢/渣界面波动;增加拉速和在一定拉速下增加结晶器宽度均将加剧液面波动.展开更多
文摘Based on the production practice of medium carbon thin slabs in the CSP plant,the reasons and influencing factors for the formation of longitudinal cracks were investigated,and some industrial measures were taken to eliminate the cracks.The results show that the efficient solutions to reduce longitudinal cracks are improving the performance of the mold powder,stabilizing the mold heat flux,and maintaining a proper taper of the mold during casting.Proper pouring temperature and secondary cooling also play important roles in preventing longitudinal surface cracks.
基金Item Sponsored by National Natural Science Foundation of China and Baosteel Co(50674020)
文摘The flow field of molten steel and the interfacial behaviour between molten steel and liquid slag layer in medium-thin slab continuous casting mold with argon gas injection were studied by numerical simulation, in which the effects of nozzle submergence depth and port angle, casting speed, and argon gas flow rate on the flow and the level fluctuation of molten steel were considered. The results show that the molten steel is jetted from the submerged en- try nozzle （SEN） with three ports into the mold and forms three recirculation zones including one upper recireulation zone and two lower recirculation zones. Argon gas injection results in a secondary vortex flow in the upper zone near the nozzle. For a given casting speed and argon gas flow rate, increasing the side port angle and submergence depth of nozzle can effectively restrain the steel/slag interracial fluctuation. Increasing the casting speed would prick up the level fluctuation. For a fixed casting speed, argon gas flow rate has a critical value, the interracial fluctuation with argon gas injection are stronger than the case without argon gas injection when the argon gas flow rate is less than the critical value, but when the argon gas flow rate exceeds the critical value, the level fluctuation is calmer than that without argon gas injection.
文摘利用VOF(volume of fluid)方法和Lagrangian离散模型模拟了厚度为135 mm中薄板坯连铸结晶器内的钢液流动及钢/渣界面波动行为,分析了结晶器宽度、水口浸入深度、水口侧孔倾角、拉速和吹氩对结晶器内钢液流动和液面波动的影响规律.结果表明:钢液从三孔浸入式水口流入结晶器后形成上、下三个回流区;吹氩使结晶器上回流区靠近水口附近形成二次涡流;在一定拉速下,增加水口侧孔倾角和浸入深度均能有效抑制钢/渣界面波动;增加拉速和在一定拉速下增加结晶器宽度均将加剧液面波动.