The technical parameters and the structural factors of melt-blown nonwovens used as filteringmedium are analysed,the orientation of particles filtered in a filter is described,and the optimalparameters for air filtrat...The technical parameters and the structural factors of melt-blown nonwovens used as filteringmedium are analysed,the orientation of particles filtered in a filter is described,and the optimalparameters for air filtration are obtained.The results are shown as follows:the ratio of tenacity oflongitudinal to cross direction has a close agreement with the random coefficient of fiber arrange-ment in practice;large particles are most likely trapped on the surface of a filter,and smaller parti-cles are filtered throughout the depth of a filter,and the deeper,the smaller;moreover,higher fil-tering efficiency and lower pressure drop can be effected through the optimization of parameters.展开更多
Biodegradable polylactic acid(PLA)melt-blown nonwovens are attractive candidates to replace nondegradable polypropylene melt-blown nonwovens.However,it is still an extremely challenging task to prepare PLA melt-blown ...Biodegradable polylactic acid(PLA)melt-blown nonwovens are attractive candidates to replace nondegradable polypropylene melt-blown nonwovens.However,it is still an extremely challenging task to prepare PLA melt-blown nonwovens with sufficient mechanical properties for practical application.Herein,we report a simple strategy for the large-scale preparation of biodegradable PLA/poly(3-hydroxybutyrate-co-3-hydroxyvalerate)(PHBV)melt-blown nonwovens with high strength and excellent toughness.In this process,a small amount of PHBV is added to PLA to improve the latter’s crystallization rate and crystallinity.In addition,when the PHBV content increases from 0 to 7.5 wt%,the diameters of the PLA/PHBV melt-blown fibers decrease significantly(with the proportion of nanofibers increasing from 7.7%to 42.9%).The resultant PLA/PHBV(5 wt%PHBV)melt-blown nonwovens exhibit the highest mechanical properties.The tensile stress,elongation,and toughness of PLA/PHBV(5 wt%PHBV)melt-blown nonwovens reach 2.5 MPa,45%,and 1.0 MJm3,respectively.More importantly,PLA/PHBV melt-blown nonwovens can be completely degraded into carbon dioxide and water after four months in the soil,making them environmentally friendly.A general tensile-failure model of melt-blown nonwovens is proposed in this study,which may shed light on mechanical performance enhancement for nonwovens.展开更多
In this study,to efficiently remove Pb(Ⅱ) from aqueous environments,a novel L-serine-modified polyethylene/polypropylene nonwoven fabric sorbent(NWF-serine)was fabricated through the radiation grafting of glycidyl me...In this study,to efficiently remove Pb(Ⅱ) from aqueous environments,a novel L-serine-modified polyethylene/polypropylene nonwoven fabric sorbent(NWF-serine)was fabricated through the radiation grafting of glycidyl methacrylate and subsequent L-serine modification.The effect of the absorbed dose was investigated in the range of 5–50 kGy.NWF-serine was characterized by Fourier transform infrared spectroscopy,thermogravimetric analysis,and scanning electron microscopy.Batch adsorption tests were conducted to investigate the influences of pH,adsorption time,temperature,initial concentration,and sorbent dosage on the Pb(Ⅱ) adsorption performance of NWF-serine.The results indicated that Pb(Ⅱ) adsorption onto NWF-serine was an endothermic process,following the pseudo-second-order kinetic model and Langmuir isotherm model.The saturated adsorption capacity was 198.1 mg/g.NWF-serine exhibited Pb(Ⅱ) removal rates of 99.8% for aqueous solutions with initial concentrations of 100 mg/L and 82.1% for landfill leachate containing competitive metal ions such as Cd,Cu,Ni,Mn,and Zn.Furthermore,NWF-serine maintained 86% of its Pb(Ⅱ) uptake after five use cycles.The coordination of the carboxyl and amino groups with Pb(Ⅱ) was confirmed using X-ray photoelectron spectroscopy and extended X-ray absorption fine structure analysis.展开更多
Nonwoven fabrics have become indispensable materials across various industries due to their versatility,durability,and cost-effectiveness.These fabrics are manufactured by bonding or interlocking fibers using mechanic...Nonwoven fabrics have become indispensable materials across various industries due to their versatility,durability,and cost-effectiveness.These fabrics are manufactured by bonding or interlocking fibers using mechanical,thermal,or chemical processes,instead of weaving or knitting.The nonwoven fabric market has witnessed significant growth in recent years,driven by technological advancements,increasing demand from various enduse industries,and shifting consumer preferences towards sustainable and eco-friendly materials.This article delves into the innovations and demand surge propelling the growth of the nonwoven fabric market.展开更多
Phase change materials have a key role for wearable thermal management,but suffer from poor water vapor permeability,low enthalpy value and weak shape stability caused by liquid phase leakage and intrinsic rigidity of...Phase change materials have a key role for wearable thermal management,but suffer from poor water vapor permeability,low enthalpy value and weak shape stability caused by liquid phase leakage and intrinsic rigidity of solid–liquid phase change materials.Herein,we report for the first time a versatile strategy for designed assembly of high-enthalpy flexible phase change nonwovens(GB-PCN)by wet-spinning hybrid grapheneboron nitride(GB)fiber and subsequent impregnating paraffins(e.g.,eicosane,octadecane).As a result,our GB-PCN exhibited an unprecedented enthalpy value of 206.0 J g^(−1),excellent thermal reliability and anti-leakage capacity,superb thermal cycling ability of 97.6%after 1000 cycles,and ultrahigh water vapor permeability(close to the cotton),outperforming the reported PCM films and fibers to date.Notably,the wearable thermal management systems based on GB-PCN for both clothing and face mask were demonstrated,which can maintain the human body at a comfortable temperature range for a significantly long time.Therefore,our results demonstrate huge potential of GB-PCN for human-wearable passive thermal management in real scenarios.展开更多
The preparation process parameters of intercalated meltblown nonwoven materials are complicated, and the relationship between process parameters, structural variables, and product performance needs to be investigated ...The preparation process parameters of intercalated meltblown nonwoven materials are complicated, and the relationship between process parameters, structural variables, and product performance needs to be investigated to establish a good mechanism for product performance regulation. In this study, we first used Wilcoxon test and Pearson correlation analysis to investigate the effect of intercalation rate on structural variables and product performance. Then, regression models were constructed to predict the values of each structural variable under different combinations of process parameters. Finally, we constructed a multi-objective constrained optimization problem based on the stepwise regression model and the product variable conditions. The problem was solved using the NSGA-II algorithm. The optimal was achieved when the acceptance distance was 2.892 cm and the hot air speed was 2000 r/min.展开更多
文摘The technical parameters and the structural factors of melt-blown nonwovens used as filteringmedium are analysed,the orientation of particles filtered in a filter is described,and the optimalparameters for air filtration are obtained.The results are shown as follows:the ratio of tenacity oflongitudinal to cross direction has a close agreement with the random coefficient of fiber arrange-ment in practice;large particles are most likely trapped on the surface of a filter,and smaller parti-cles are filtered throughout the depth of a filter,and the deeper,the smaller;moreover,higher fil-tering efficiency and lower pressure drop can be effected through the optimization of parameters.
基金supported by the National Key Research and Development Program of China(2022YFB3804903 and 2022YFB3804900)the National Natural Science Foundation of China(52273052)+1 种基金the Program of Shanghai Academic/Technology Research Leader(21XD1420100)the International Cooperation Fund of Science and Technology Commission of Shanghai Municipality(21130750100).
文摘Biodegradable polylactic acid(PLA)melt-blown nonwovens are attractive candidates to replace nondegradable polypropylene melt-blown nonwovens.However,it is still an extremely challenging task to prepare PLA melt-blown nonwovens with sufficient mechanical properties for practical application.Herein,we report a simple strategy for the large-scale preparation of biodegradable PLA/poly(3-hydroxybutyrate-co-3-hydroxyvalerate)(PHBV)melt-blown nonwovens with high strength and excellent toughness.In this process,a small amount of PHBV is added to PLA to improve the latter’s crystallization rate and crystallinity.In addition,when the PHBV content increases from 0 to 7.5 wt%,the diameters of the PLA/PHBV melt-blown fibers decrease significantly(with the proportion of nanofibers increasing from 7.7%to 42.9%).The resultant PLA/PHBV(5 wt%PHBV)melt-blown nonwovens exhibit the highest mechanical properties.The tensile stress,elongation,and toughness of PLA/PHBV(5 wt%PHBV)melt-blown nonwovens reach 2.5 MPa,45%,and 1.0 MJm3,respectively.More importantly,PLA/PHBV melt-blown nonwovens can be completely degraded into carbon dioxide and water after four months in the soil,making them environmentally friendly.A general tensile-failure model of melt-blown nonwovens is proposed in this study,which may shed light on mechanical performance enhancement for nonwovens.
基金supported by the National Natural Science Foundation of China(Nos.11605275 and 11675247)。
文摘In this study,to efficiently remove Pb(Ⅱ) from aqueous environments,a novel L-serine-modified polyethylene/polypropylene nonwoven fabric sorbent(NWF-serine)was fabricated through the radiation grafting of glycidyl methacrylate and subsequent L-serine modification.The effect of the absorbed dose was investigated in the range of 5–50 kGy.NWF-serine was characterized by Fourier transform infrared spectroscopy,thermogravimetric analysis,and scanning electron microscopy.Batch adsorption tests were conducted to investigate the influences of pH,adsorption time,temperature,initial concentration,and sorbent dosage on the Pb(Ⅱ) adsorption performance of NWF-serine.The results indicated that Pb(Ⅱ) adsorption onto NWF-serine was an endothermic process,following the pseudo-second-order kinetic model and Langmuir isotherm model.The saturated adsorption capacity was 198.1 mg/g.NWF-serine exhibited Pb(Ⅱ) removal rates of 99.8% for aqueous solutions with initial concentrations of 100 mg/L and 82.1% for landfill leachate containing competitive metal ions such as Cd,Cu,Ni,Mn,and Zn.Furthermore,NWF-serine maintained 86% of its Pb(Ⅱ) uptake after five use cycles.The coordination of the carboxyl and amino groups with Pb(Ⅱ) was confirmed using X-ray photoelectron spectroscopy and extended X-ray absorption fine structure analysis.
文摘Nonwoven fabrics have become indispensable materials across various industries due to their versatility,durability,and cost-effectiveness.These fabrics are manufactured by bonding or interlocking fibers using mechanical,thermal,or chemical processes,instead of weaving or knitting.The nonwoven fabric market has witnessed significant growth in recent years,driven by technological advancements,increasing demand from various enduse industries,and shifting consumer preferences towards sustainable and eco-friendly materials.This article delves into the innovations and demand surge propelling the growth of the nonwoven fabric market.
基金supported by the National Natural Science Foundation of China(Nos.21903082,22003065,22125903,51872283,22075279,21805273,22273100)Dalian Innovation Support Plan for High Level Talents(2019RT09)+3 种基金Dalian National Laboratory For Clean Energy(DNL),CAS,DNL Cooperation Fund,CAS(DNL201912,DNL201915,DNL202016,DNL202019)DICP(DICP I2020032,DICP I202036,I202218)The Joint Fund of the Yulin University and the Dalian National Laboratory for Clean Energy(YLU-DNL Fund 2021002,YLU-DNL 2021007,YLU-DNL 2021009)Q.Shi would like to thank Dalian Outstanding Young Scientific Talent Program(Grant 2019RJ10).
文摘Phase change materials have a key role for wearable thermal management,but suffer from poor water vapor permeability,low enthalpy value and weak shape stability caused by liquid phase leakage and intrinsic rigidity of solid–liquid phase change materials.Herein,we report for the first time a versatile strategy for designed assembly of high-enthalpy flexible phase change nonwovens(GB-PCN)by wet-spinning hybrid grapheneboron nitride(GB)fiber and subsequent impregnating paraffins(e.g.,eicosane,octadecane).As a result,our GB-PCN exhibited an unprecedented enthalpy value of 206.0 J g^(−1),excellent thermal reliability and anti-leakage capacity,superb thermal cycling ability of 97.6%after 1000 cycles,and ultrahigh water vapor permeability(close to the cotton),outperforming the reported PCM films and fibers to date.Notably,the wearable thermal management systems based on GB-PCN for both clothing and face mask were demonstrated,which can maintain the human body at a comfortable temperature range for a significantly long time.Therefore,our results demonstrate huge potential of GB-PCN for human-wearable passive thermal management in real scenarios.
文摘The preparation process parameters of intercalated meltblown nonwoven materials are complicated, and the relationship between process parameters, structural variables, and product performance needs to be investigated to establish a good mechanism for product performance regulation. In this study, we first used Wilcoxon test and Pearson correlation analysis to investigate the effect of intercalation rate on structural variables and product performance. Then, regression models were constructed to predict the values of each structural variable under different combinations of process parameters. Finally, we constructed a multi-objective constrained optimization problem based on the stepwise regression model and the product variable conditions. The problem was solved using the NSGA-II algorithm. The optimal was achieved when the acceptance distance was 2.892 cm and the hot air speed was 2000 r/min.