Ice melting performance of deicers and their effect on stripping resistance of asphalt mixture

The ice melting performance of three types of deicers, including sodium chloride, calcium chloride and sodium acetate, were tested in laboratory under different temperature conditions, and their effects on asphalt mixture were evaluated from the point of the stripping resistance of asphalt mixture. Unsaturated Marshall samples were exposed to freeze-thaw cycling while immersed in the deicer solutions of different concentrations. After the freeze-thaw cycles, Cantabro tests were performed, and Cantabro loss was adopted to characterize the stripping resistance of asphalt mixture. The test results show that calcium chloride has the best comprehensive ice melting performance, and all deicers have detrimental effect on the stripping resistance of asphalt mixture at different degrees. The damage degree depends on deicer types and their concentration in the solution. Deicer solutions with about 2% concentration cause the greatest loss of stripping resistance due to serious freeze-thaw damage. Sodium acetate causes greater loss of stripping resistance than sodium chloride and calcium chloride at the same concentration.

Highly Improved Electrochemical Performances of the Nanocrystalline and Amorphous Mg_2Ni-type Alloys by Substituting Ni with M (M=Cu,Co,Mn)

The element Ni in the Mg2Ni alloy is partially substituted by M（M = Cu, Co, Mn） in order to ameliorate the electrochemical hydrogen storage performances of Mg2Ni-type electrode alloys. The nanocrystalline and amorphous Mg20Ni10-xMx（M = None, Cu, Co, Mn; x = 0-4） alloys were prepared by melt spinning. The effects of the M（M = Cu, Co, Mn） content on the structures and electrochemical hydrogen storage characteristics of the as-cast and spun alloys were comparatively studied. The analyses by XRD, SEM and HRTEM reveal that all the as-cast alloys have a major phase of Mg2Ni but the M（M = Co, Mn） substitution brings on the formation of some secondary phases, MgCo2 and Mg for the（M = Co） alloy, and Mn Ni and Mg for the（M = Mn） alloy. Besides, the as-spun（M = None, Cu） alloys display an entirely nanocrystalline structure, whereas the as-spun（M = Co, Mn） alloys hold a nanocrystalline/amorphous structure, suggesting that the substitution of M（M = Co, Mn） for Ni facilitates the glass formation in the Mg2Ni-type alloys. The electrochemical measurements indicate that the variation of M（M = Cu, Co, Mn） content engenders an obvious effect on the electrochemical performances of the as-cast and spun alloys. To be specific, the cyclic stabilities of the alloys augment monotonously with increasing M（M = Cu, Co, Mn） content, and the capacity retaining rate（S20） is in an order of（M = Cu） 〉（M = Co） 〉（M = Mn） 〉（M = None） for x≤1 but changes to（M = Co） 〉（M = Mn） 〉（M = Cu） 〉（M = None） for x≥2. The discharge capacities of the as-cast and spun alloys always grow with the rising of M（M = Co, Mn） content but first mount up and then go down with increasing M（M = Cu） content. Whatever the M content is, the discharge capacities are in sequence：（M = Co） 〉（M = Mn） 〉（M = Cu） 〉（M = None）. The high rate discharge abilities（HRDs） of all the alloys grow clearly with rising M（M = Cu, Co） content except for（M = Mn） alloy, whose HRD has a maximum value with varying M（M = Mn） content. Furthermore, for the as-cast alloys, the HRD is in order of（M = Co） 〉（M = Mn） 〉（M = Cu） 〉（M = None）, while for the as-spun（20 m·s^-1） alloys, it changes from（M = Co） 〉（M = Mn） 〉（M = Cu） 〉（M = None） for x = 1 to（M = Cu） 〉（M = Co） 〉（M = None） 〉（M = Mn） for x = 4.

Electrochemical Performance of Nanocrystalline and Amorphous Mg–Nd–Ni–Cu-Based Mg_2Ni-type Alloy Electrodes Used in Ni-MH Batteries

Nanocrystalline and amorphous Mg2Ni-type（Mg24Ni10Cu2）100–xNdx（x = 0, 5, 10, 15, 20） alloys were prepared by melt-spinning technology. The structures of as-cast and spun alloys were characterised by X-ray diffraction,scanning electron microscopy and transmission electron microscopy. Electrochemical performance of the alloy electrodes was measured using an automatic galvanostatic system. The electrochemical impedance spectra and Tafel polarisation curves of the alloy electrodes were plotted using an electrochemical work station. The hydrogen diffusion coefficients were calculated using the potential step method. Results indicate that all the as-cast alloys present a multiphase structure with Mg2 Ni type as the major phase with Mg6 Ni, Nd5Mg41 and Nd Ni as secondary phases. The secondary phases increased with the increasing Nd content. The as-spun Nd-free alloy exhibited nanocrystalline structure, whereas the as-spun Nd-doped alloys exhibited nanocrystalline and amorphous structures. These results suggest that adding Nd facilitates glass formation of Mg2Ni-type alloys. Melt spinning and Nd addition improved alloy electrochemical performance, which includes discharge potential characteristics, discharge capacity, electrochemical cycle stability and high-rate discharge ability.