Experiments were carried out on carburizing and temperature rising of the semi steel melt in a plasma induction furnace.Influence of many factors, such as power supply mode,position of the plasma torch and bottom b...Experiments were carried out on carburizing and temperature rising of the semi steel melt in a plasma induction furnace.Influence of many factors, such as power supply mode,position of the plasma torch and bottom blown gas stirring,on heating efficiency and melt temperature distribution was studied. Melt temperature could be effectively controlled by plasma heating,and carbon content of semi steel melt increased from 1.92 % to 4.58 %, and the utilization rate of carbon reached up to 61.57 % during carburizing of the melt.展开更多
For describing and resolving the process of chromium ore smelting reduction in a converter preferably, the coupling dynamic model was established based on the kinetic models of chromium ore dissolution and interfacial...For describing and resolving the process of chromium ore smelting reduction in a converter preferably, the coupling dynamic model was established based on the kinetic models of chromium ore dissolution and interfacial re- ducing reaction between the slag and metal. When 150 t stainless steel crude melts with chromium of 12% are produced in a smelting reduction converter with no initial chromium in metal at 1 560℃, the results of the coupling dynamic model show that the mean reduction rate and injection rate of chromium ore are 0. 091% ·min^-1 and 467 kg · min^-1 , respectively. The foundation of the coupling dynamic model provides a reference and basis on the constitution of rational processing route for a practical stainless steelmaking.展开更多
文摘Experiments were carried out on carburizing and temperature rising of the semi steel melt in a plasma induction furnace.Influence of many factors, such as power supply mode,position of the plasma torch and bottom blown gas stirring,on heating efficiency and melt temperature distribution was studied. Melt temperature could be effectively controlled by plasma heating,and carbon content of semi steel melt increased from 1.92 % to 4.58 %, and the utilization rate of carbon reached up to 61.57 % during carburizing of the melt.
基金Sponsored by National Natural Science Foundation of China(50904017)Open Subject Fund of State Key Laboratory of Rolling and Automation of NEU of China(2009003)
文摘For describing and resolving the process of chromium ore smelting reduction in a converter preferably, the coupling dynamic model was established based on the kinetic models of chromium ore dissolution and interfacial re- ducing reaction between the slag and metal. When 150 t stainless steel crude melts with chromium of 12% are produced in a smelting reduction converter with no initial chromium in metal at 1 560℃, the results of the coupling dynamic model show that the mean reduction rate and injection rate of chromium ore are 0. 091% ·min^-1 and 467 kg · min^-1 , respectively. The foundation of the coupling dynamic model provides a reference and basis on the constitution of rational processing route for a practical stainless steelmaking.