The method based on transient heat transfer model is adopted to simulate electro-slag remelting process. The calculated results of the model show that the process is in the quasi-steady state, and the shape of pool re...The method based on transient heat transfer model is adopted to simulate electro-slag remelting process. The calculated results of the model show that the process is in the quasi-steady state, and the shape of pool remains unchanged when the height of ingot is approximately 2.5-3 times the thickness of slab ingot. The change in the shape of pool is found to be strongly dependent on the pattern of melting rate, and hence, the power input; the depth of the molten pool increases with the increase in melting speed. It is concluded that a transient heat transfer model has to be used to obtain reliable input information for the entire, operatina time.展开更多
The electrode configuration determines the thermophysical field during the electroslag remelting(ESR) process and affects the final microstructure of the ingot. In this work, ingot with a diameter of 400 mm was prepar...The electrode configuration determines the thermophysical field during the electroslag remelting(ESR) process and affects the final microstructure of the ingot. In this work, ingot with a diameter of 400 mm was prepared with two electrode configuration modes of single power ESR process, namely one electrode(OE) and two series-connected electrodes(TSCE). Finite element simulation was employed to calculate the electromagnetic field, flow field and temperature field of the ESR system. The results show that the temperature of the slag pool and the metal pool of the TSCE process is lower and more uniform than that of the OE process.The calculated temperature distribution of the ingot could be indirectly verified from the shape of the metal pool by the experiment. The experimental results show that the depth of the metal pool in the OE ingot is about 160 mm, while the depth of the TSCE ingot is nearly 40 mm shallower than that of the OE ingot. Microstructural comparisons indicate that coarse eutectic carbides are formed in the center of the OE ingot, whereas more even eutectic carbides appear in the center of the TSCE ingot. In general, compared with the OE process, the TSCE process is preferred to remelt high speed steel ingots.展开更多
文摘The method based on transient heat transfer model is adopted to simulate electro-slag remelting process. The calculated results of the model show that the process is in the quasi-steady state, and the shape of pool remains unchanged when the height of ingot is approximately 2.5-3 times the thickness of slab ingot. The change in the shape of pool is found to be strongly dependent on the pattern of melting rate, and hence, the power input; the depth of the molten pool increases with the increase in melting speed. It is concluded that a transient heat transfer model has to be used to obtain reliable input information for the entire, operatina time.
基金financially surpported by the Foundation of Hebei Provincial Department of Education,China(Grant No.QN2018034 and QN2017051)
文摘The electrode configuration determines the thermophysical field during the electroslag remelting(ESR) process and affects the final microstructure of the ingot. In this work, ingot with a diameter of 400 mm was prepared with two electrode configuration modes of single power ESR process, namely one electrode(OE) and two series-connected electrodes(TSCE). Finite element simulation was employed to calculate the electromagnetic field, flow field and temperature field of the ESR system. The results show that the temperature of the slag pool and the metal pool of the TSCE process is lower and more uniform than that of the OE process.The calculated temperature distribution of the ingot could be indirectly verified from the shape of the metal pool by the experiment. The experimental results show that the depth of the metal pool in the OE ingot is about 160 mm, while the depth of the TSCE ingot is nearly 40 mm shallower than that of the OE ingot. Microstructural comparisons indicate that coarse eutectic carbides are formed in the center of the OE ingot, whereas more even eutectic carbides appear in the center of the TSCE ingot. In general, compared with the OE process, the TSCE process is preferred to remelt high speed steel ingots.