To improve the performance, the surface of 12Mn2O4 was coated with very fine MgO , Al2O3 and ZnO by solgel method, respectively. The structure and morphology of the coated materials were investigated by X-ray diffract...To improve the performance, the surface of 12Mn2O4 was coated with very fine MgO , Al2O3 and ZnO by solgel method, respectively. The structure and morphology of the coated materials were investigated by X-ray diffraction （ XRD ）, X-ray photoelectron spectroscopy （ XPS ） and scanning electron microscopy （SEM）. The charge and discharge performance of uncoated and surfnce modified 12Mn2O4 spinel at 25℃ and 55 ℃ were tested, using a voltage window of 3.0-4.35 V and a current deasity of 0. 1 C rate. There is a slight decrease in the initial discharge capacity relative to that of uncoated UMn2 O4, bat the cycle ability of 12 12Mn2O4 coated by metal-oxide has remarkably been improved. The EIS measuremeuts of uncoated and Al2O3 -coated 12Mn2O4 were carried out by a model 273 A potentiostatl galvanistat controUed by a computer using M270 software, and using a freqnency response analyzer （ Zsimpwin ） combined with a potentiostate （ PAR 273）. Coaseqnently, the reason for the improved cycle properties is that the surface modification reduces the dissolution of Mn , which results from the suppression of the electrolyte decomposition, and suppresses the formation of passivation film that acts as an electronic insulating layer. In conclusion, the use of surface modification is an effective way to improve the electrochemical performance of 12Mn2O4 cathode material for lithium batteries.展开更多
The Li Ni1/3Co1/3Mn1/3O2 is first obtained by the controlled crystallization method and then coated with Ni3(PO4)2particles. The effects of the coating on rate capability and cycle life at high cut-off voltage are inv...The Li Ni1/3Co1/3Mn1/3O2 is first obtained by the controlled crystallization method and then coated with Ni3(PO4)2particles. The effects of the coating on rate capability and cycle life at high cut-off voltage are investigated by electrochemical impedance spectroscopy and galvanostatic measurements. The element ratio of Ni:Mn:Co is tested by inductively-coupled plasma spectrometer(ICP) analysis and it testified to be 1:1:1. It is indicated that Ni3(PO4)2-coated Li Ni1/3Co1/3Mn1/3O2 has an outstanding capacity retention, where 99% capacity retention is maintained after 10 cycles at 5C discharge rate between 2.7 V and 4.6 V. The electrochemical impedance spectroscopy(EIS) results show that the current exchange density i0 of the coated sample is higher than that of Li Ni1/3Co1/3Mn1/3O2, which is beneficial to its electrochemical performances. All the conclusions show that the Ni3(PO4)2coating can prominently enhance the high rate performance of the Li Ni1/3Co1/3Mn1/3O2, especially at high cut-off voltage.展开更多
基金Funded by Guangdong Provincial Natural Science Foundation ofChina(No.06300397) and Director Foundation of South China Ag-ricultural University (No.K06143)
文摘To improve the performance, the surface of 12Mn2O4 was coated with very fine MgO , Al2O3 and ZnO by solgel method, respectively. The structure and morphology of the coated materials were investigated by X-ray diffraction （ XRD ）, X-ray photoelectron spectroscopy （ XPS ） and scanning electron microscopy （SEM）. The charge and discharge performance of uncoated and surfnce modified 12Mn2O4 spinel at 25℃ and 55 ℃ were tested, using a voltage window of 3.0-4.35 V and a current deasity of 0. 1 C rate. There is a slight decrease in the initial discharge capacity relative to that of uncoated UMn2 O4, bat the cycle ability of 12 12Mn2O4 coated by metal-oxide has remarkably been improved. The EIS measuremeuts of uncoated and Al2O3 -coated 12Mn2O4 were carried out by a model 273 A potentiostatl galvanistat controUed by a computer using M270 software, and using a freqnency response analyzer （ Zsimpwin ） combined with a potentiostate （ PAR 273）. Coaseqnently, the reason for the improved cycle properties is that the surface modification reduces the dissolution of Mn , which results from the suppression of the electrolyte decomposition, and suppresses the formation of passivation film that acts as an electronic insulating layer. In conclusion, the use of surface modification is an effective way to improve the electrochemical performance of 12Mn2O4 cathode material for lithium batteries.
基金Supported by the National Natural Science Foundation of China(51074096)
文摘The Li Ni1/3Co1/3Mn1/3O2 is first obtained by the controlled crystallization method and then coated with Ni3(PO4)2particles. The effects of the coating on rate capability and cycle life at high cut-off voltage are investigated by electrochemical impedance spectroscopy and galvanostatic measurements. The element ratio of Ni:Mn:Co is tested by inductively-coupled plasma spectrometer(ICP) analysis and it testified to be 1:1:1. It is indicated that Ni3(PO4)2-coated Li Ni1/3Co1/3Mn1/3O2 has an outstanding capacity retention, where 99% capacity retention is maintained after 10 cycles at 5C discharge rate between 2.7 V and 4.6 V. The electrochemical impedance spectroscopy(EIS) results show that the current exchange density i0 of the coated sample is higher than that of Li Ni1/3Co1/3Mn1/3O2, which is beneficial to its electrochemical performances. All the conclusions show that the Ni3(PO4)2coating can prominently enhance the high rate performance of the Li Ni1/3Co1/3Mn1/3O2, especially at high cut-off voltage.