Crystallographic plasticity was applied to study the initiation of micro cracks on the smooth surface of polycrystalline under uniform applied stress. Even under the uniform external stress, due to the different cryst...Crystallographic plasticity was applied to study the initiation of micro cracks on the smooth surface of polycrystalline under uniform applied stress. Even under the uniform external stress, due to the different crystallographic orientations of the grains in the polycrystalline, there is un-uniform stress distribution and the deformation is also not uniform. Under the fatigue loading, the roughness increases with the number of fatigue, and deformation will localize in some places, where micro cracks form.展开更多
The micro crack of aluminum sheet during cold rolling lubricated with emulsions is investigated. Experi-ments show that micro cracks occur after cold rolling process and this is attributed to various parameters, for i...The micro crack of aluminum sheet during cold rolling lubricated with emulsions is investigated. Experi-ments show that micro cracks occur after cold rolling process and this is attributed to various parameters, for instance, the thin oxide film formed at the sheet surface. The micro crack spacing thus becomes an important parameter which deserves more concerns. The aspect ratio of these micro cracks is then analyzed theoreti-cally, which takes into consideration of the oxide fracture process. The good agreement between the obser-vations and the theoretical predictions validates the analysis. The approach can shed some new lights on the mechanical process of aluminium sheet during cold rolling.展开更多
The internal micro cracks with the critical length about 30?μm and thickness less than 1?μm were introduced into the pure titanium samples by uniaxial tension compression low cycle fatigue method. The experimental r...The internal micro cracks with the critical length about 30?μm and thickness less than 1?μm were introduced into the pure titanium samples by uniaxial tension compression low cycle fatigue method. The experimental results indicate that the internal fatigue micro crack clearly evolves from the original penny shaped crack into a string of spherical voids in the longitudinal section plane of the fatigue sample after the vacuum diffusive healing at the high temperature. The quantitative relationship between the radius and the spacing of spherical voids depends on the crack position (within grains, on grain boundaries or transgranular sites) and its orientations within the grain. The diffusive healing, the related thermodynamics and mechanism, and the effect of the surface tension anisotropy on the relationship between void diameter and void spacing are also discussed.展开更多
The paper presents a principal formulation of statistical evolution of microcracks, occurring insolids, subjected to external loading. In particular, the concept of ideal microcracks is elaborated, in orderto describe...The paper presents a principal formulation of statistical evolution of microcracks, occurring insolids, subjected to external loading. In particular, the concept of ideal microcracks is elaborated, in orderto describe the fundamental features of damage resulting from nucleation and extension of microcracks.Relevant average damage functions are also discussed.展开更多
We propose a nonlinear ultrasonic technique by using the mixed-frequency signals excited Lamb waves to conduct micro-crack detection in thin plate structures.Simulation models of three-dimensional(3D)aluminum plates a...We propose a nonlinear ultrasonic technique by using the mixed-frequency signals excited Lamb waves to conduct micro-crack detection in thin plate structures.Simulation models of three-dimensional(3D)aluminum plates and composite laminates are established by ABAQUS software,where the aluminum plate contains buried crack and composite laminates comprises cohesive element whose thickness is zero to simulate delamination damage.The interactions between the S0 mode Lamb wave and the buried micro-cracks of various dimensions are simulated by using the finite element method.Fourier frequency spectrum analysis is applied to the received time domain signal and fundamental frequency amplitudes,and sum and difference frequencies are extracted and simulated.Simulation results indicate that nonlinear Lamb waves have different sensitivities to various crack sizes.There is a positive correlation among crack length,height,and sum and difference frequency amplitudes for an aluminum plate,with both amplitudes decreasing as crack thickness increased,i.e.,nonlinear effect weakens as the micro-crack becomes thicker.The amplitudes of sum and difference frequency are positively correlated with the length and width of the zero-thickness cohesive element in the composite laminates.Furthermore,amplitude ratio change is investigated and it can be used as an effective tool to detect inner defects in thin 3D plates.展开更多
Standards of highway conservation and maintenance are improved gradually following the improvement of requirements of road service. Before obvious damage such as obvious cracking (block,transverse, longitudinal ) and ...Standards of highway conservation and maintenance are improved gradually following the improvement of requirements of road service. Before obvious damage such as obvious cracking (block,transverse, longitudinal ) and rutting emerge, inconspicuous distress (micro-cracks, polishing, pockmarked) is generated previously. These inconspicuous distresses may provide basis and criteria for pavement preventive maintenance. Currently most of preventive conservation measures are determined by experienced experts in maintenance and repair of road after site visits. Thus method is difficult in operation, and has a certain amount of instability as it is based on experience and personal knowledge. In this paper, camera and laser were used for automated high-speed acquisition images. Methods to preprocess pavement image are compared. The pretreatment method suitable for analyze micro-cracks picture is elected, an effective way to remove shadow is also proposed.展开更多
This paper develops the non-equilibrium statistical fatigue damage theory to study the statistical behaviour of micro-crack for metals in magnetic field. The one-dimensional homogeneous crack system is chosen for stud...This paper develops the non-equilibrium statistical fatigue damage theory to study the statistical behaviour of micro-crack for metals in magnetic field. The one-dimensional homogeneous crack system is chosen for study. To investigate the effect caused by magnetic field on the statistical distribution of micro-crack in the system, the theoretical analysis on microcrack evolution equation, the average length of micro-crack, density distribution function of micro-crack and fatigue fracture probability have been performed. The derived results relate the changes of some quantities, such as average length, density distribution function and fatigue fracture probability, to the applied magnetic field, the magnetic and mechanical properties of metals. It gives a theoretical explanation on the change of fatigue damage due to magnetic fields observed by experiments, and presents an analytic approach on studying the fatigue damage of metal in magnetic field.展开更多
The main results obtained from the experimental and engineering investigation on the heat evolution and cracking risk of a furnace concrete block were presented. The heat evolution of experimental mortars containing m...The main results obtained from the experimental and engineering investigation on the heat evolution and cracking risk of a furnace concrete block were presented. The heat evolution of experimental mortars containing micro-slag under different environmental temperatures was instrumented in order to investigate the self-catalyzed effect, which was discovered in engineering. Moreover, the thermal stress of the furnace concrete due to heat temperature rise was calculated to evaluate the cracking risk of mass concrete containing micro-slag due to self-catalyzed effect. The experimental results illustrate that with the development of hydration and initial temperature of mixture, the hydration can be also accelerated and temperature of concrete will be continued to rise, which was the self-catalyzed effect. And the thermal stress due to self-catalyzed effect could not result in the cracking of furnace concrete.展开更多
论文建立了基于比例边界有限元法(scaled boundary finite element methods,SBFEM)框架的非局部宏微观损伤模型,考虑材料细观物理参数的空间变异性,探讨了材料参数的空间变异性对结构开裂过程的影响。结果表明:考虑材料参数空间变异性后...论文建立了基于比例边界有限元法(scaled boundary finite element methods,SBFEM)框架的非局部宏微观损伤模型,考虑材料细观物理参数的空间变异性,探讨了材料参数的空间变异性对结构开裂过程的影响。结果表明:考虑材料参数空间变异性后,裂纹扩展路径具有不确定性,建议的模型能够很好地反应材料内在的随机性;随着结构受力情况的复杂化和结构本体缺陷的增多,裂纹开裂模式的变异性也会增大。自相关长度和参数变异系数对结构开裂分析结果有重要影响。展开更多
文摘Crystallographic plasticity was applied to study the initiation of micro cracks on the smooth surface of polycrystalline under uniform applied stress. Even under the uniform external stress, due to the different crystallographic orientations of the grains in the polycrystalline, there is un-uniform stress distribution and the deformation is also not uniform. Under the fatigue loading, the roughness increases with the number of fatigue, and deformation will localize in some places, where micro cracks form.
文摘The micro crack of aluminum sheet during cold rolling lubricated with emulsions is investigated. Experi-ments show that micro cracks occur after cold rolling process and this is attributed to various parameters, for instance, the thin oxide film formed at the sheet surface. The micro crack spacing thus becomes an important parameter which deserves more concerns. The aspect ratio of these micro cracks is then analyzed theoreti-cally, which takes into consideration of the oxide fracture process. The good agreement between the obser-vations and the theoretical predictions validates the analysis. The approach can shed some new lights on the mechanical process of aluminium sheet during cold rolling.
文摘The internal micro cracks with the critical length about 30?μm and thickness less than 1?μm were introduced into the pure titanium samples by uniaxial tension compression low cycle fatigue method. The experimental results indicate that the internal fatigue micro crack clearly evolves from the original penny shaped crack into a string of spherical voids in the longitudinal section plane of the fatigue sample after the vacuum diffusive healing at the high temperature. The quantitative relationship between the radius and the spacing of spherical voids depends on the crack position (within grains, on grain boundaries or transgranular sites) and its orientations within the grain. The diffusive healing, the related thermodynamics and mechanism, and the effect of the surface tension anisotropy on the relationship between void diameter and void spacing are also discussed.
基金The project partially supported by National Natural Science Foundation of China.
文摘The paper presents a principal formulation of statistical evolution of microcracks, occurring insolids, subjected to external loading. In particular, the concept of ideal microcracks is elaborated, in orderto describe the fundamental features of damage resulting from nucleation and extension of microcracks.Relevant average damage functions are also discussed.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.61571222,61602235,and 11474160)the Six Talent Peaks Project of Jiangsu Province,China
文摘We propose a nonlinear ultrasonic technique by using the mixed-frequency signals excited Lamb waves to conduct micro-crack detection in thin plate structures.Simulation models of three-dimensional(3D)aluminum plates and composite laminates are established by ABAQUS software,where the aluminum plate contains buried crack and composite laminates comprises cohesive element whose thickness is zero to simulate delamination damage.The interactions between the S0 mode Lamb wave and the buried micro-cracks of various dimensions are simulated by using the finite element method.Fourier frequency spectrum analysis is applied to the received time domain signal and fundamental frequency amplitudes,and sum and difference frequencies are extracted and simulated.Simulation results indicate that nonlinear Lamb waves have different sensitivities to various crack sizes.There is a positive correlation among crack length,height,and sum and difference frequency amplitudes for an aluminum plate,with both amplitudes decreasing as crack thickness increased,i.e.,nonlinear effect weakens as the micro-crack becomes thicker.The amplitudes of sum and difference frequency are positively correlated with the length and width of the zero-thickness cohesive element in the composite laminates.Furthermore,amplitude ratio change is investigated and it can be used as an effective tool to detect inner defects in thin 3D plates.
文摘Standards of highway conservation and maintenance are improved gradually following the improvement of requirements of road service. Before obvious damage such as obvious cracking (block,transverse, longitudinal ) and rutting emerge, inconspicuous distress (micro-cracks, polishing, pockmarked) is generated previously. These inconspicuous distresses may provide basis and criteria for pavement preventive maintenance. Currently most of preventive conservation measures are determined by experienced experts in maintenance and repair of road after site visits. Thus method is difficult in operation, and has a certain amount of instability as it is based on experience and personal knowledge. In this paper, camera and laser were used for automated high-speed acquisition images. Methods to preprocess pavement image are compared. The pretreatment method suitable for analyze micro-cracks picture is elected, an effective way to remove shadow is also proposed.
文摘This paper develops the non-equilibrium statistical fatigue damage theory to study the statistical behaviour of micro-crack for metals in magnetic field. The one-dimensional homogeneous crack system is chosen for study. To investigate the effect caused by magnetic field on the statistical distribution of micro-crack in the system, the theoretical analysis on microcrack evolution equation, the average length of micro-crack, density distribution function of micro-crack and fatigue fracture probability have been performed. The derived results relate the changes of some quantities, such as average length, density distribution function and fatigue fracture probability, to the applied magnetic field, the magnetic and mechanical properties of metals. It gives a theoretical explanation on the change of fatigue damage due to magnetic fields observed by experiments, and presents an analytic approach on studying the fatigue damage of metal in magnetic field.
基金Funded by the Key Technologies R&D Program from Department of Science and Technology Hubei Province(200410G0121) "973" Pro-gram(001CB610704-3) from Ministry of Science and Technology of China
文摘The main results obtained from the experimental and engineering investigation on the heat evolution and cracking risk of a furnace concrete block were presented. The heat evolution of experimental mortars containing micro-slag under different environmental temperatures was instrumented in order to investigate the self-catalyzed effect, which was discovered in engineering. Moreover, the thermal stress of the furnace concrete due to heat temperature rise was calculated to evaluate the cracking risk of mass concrete containing micro-slag due to self-catalyzed effect. The experimental results illustrate that with the development of hydration and initial temperature of mixture, the hydration can be also accelerated and temperature of concrete will be continued to rise, which was the self-catalyzed effect. And the thermal stress due to self-catalyzed effect could not result in the cracking of furnace concrete.
文摘论文建立了基于比例边界有限元法(scaled boundary finite element methods,SBFEM)框架的非局部宏微观损伤模型,考虑材料细观物理参数的空间变异性,探讨了材料参数的空间变异性对结构开裂过程的影响。结果表明:考虑材料参数空间变异性后,裂纹扩展路径具有不确定性,建议的模型能够很好地反应材料内在的随机性;随着结构受力情况的复杂化和结构本体缺陷的增多,裂纹开裂模式的变异性也会增大。自相关长度和参数变异系数对结构开裂分析结果有重要影响。