Preventing Occurrence of Transverse Corner Cracks on Nb, V and Ti Microalloying Steel CC Slabs

Based on their hot ductilities, Nb, V and Ti microalloying steels can be classified into two groups. The first group includes steels with lower carbon content (≤0.10%). Ductilities of steels of this group recover and rise with decreasing temperature when temperature lowers to below 825℃. Another group includes steels which contain more carbon (>0.12%) or contain more Nb and V. The low ductility temperature Region Ⅲ for steels of mis group extends to temperature as low as 725℃. The occurrence of the transverse corner cracks of the Nb, V and Ti microalloying steel CC slabs has be considerably decreased by stabilizing casting speed, increasing mold steel level automatic control ratio,enhancing caster segment radial alignment and adopting proper secondary cooling patterns to make slab corner temperature at straightening out off the low ductility temperature region.

Effects of Cr, Ni and Cu on the Corrosion Behavior of Low Carbon Microalloying Steel in a Cl^- Containing Environment

The effects of Cr, Ni and Cu on the corrosion behavior of low carbon microalloying steel in a CI- containing environment were investigated. The results revealed that the corrosion process could be divided into the initial stage in which the corrosion rate increased with accumulation of corrosion products and the later stage in which homogeneous and compact inner rust layers started to protect steel substrate out of corrosion mediums. The results of X-ray diffraction （XRD） indicated that the rust layers of the three-group steels （Cr, Cr-Ni and Cr-Ni-Cu steels） were composed of α-FeOOH, β-FeOOH, γ-FeOOH, Fe3O4 and large amounts of amorphous compounds. The content of amorphous compounds of Cr-Ni-Cu steel was about 2%-3% more than that of Cr-Ni steel. The results of electron probe microanalysis （EPMA） showed that Cr concentrated mainly in the inner region of the rust of Cr-Ni-Cu steel, inner/outer interface especially, whereas Ni was uniformly distributed all over the rust and Cu was noticed rarely after 73 wet/dry cycles. The addition of Cr and Ni was beneficial to the formation of dense and compact inner rust layer, which was the most important reason for the improvement of corrosion resistance of experimental steel.

Effect of V and V-N Microalloying on Deformation-Induced Ferrite Transformation in Low Carbon Steels

Deformation-induced ferrite transformation （DIFT） has been proved to be an effective approach to refine ferrite grains. This paper shows that the ferrite grains can further be refined through combination of DIFT and V or V-N microalloying. Vanadium dissolved in γ matrix restrains DIFT. During deformation, vanadium carbonitrides rapidly precipitate due to strain-induced precipitation, which causes decrease in vanadium dissolved in matrix and indirectly accelerates DIFT. Under heavy deformation, deformation induced ferrite （DIF） grains in V microalloyed steel were finer than those in V free steel. The more V added to steel, the finer DIF grains obtained. Moreover, the addition of N to V microalloyed steels can remarkably accelerate precipitation of V, and then promote DIFT. However, DIF grains in V-N microalloyed steel easily coarsen.

Kinetics of austenite growth and bainite transformation during reheating and cooling treatments of high strength microalloyed steel produced by sub-rapid solidification

First,strip cast samples of high strength microalloyed steel with sub-rapid solidification characteristics were prepared by simulated strip casting technique.Next,the isothermal growth of austenite grain during the reheating treatment of strip casts was observed in situ through confocal laser scanning microscope(CLSM).The results indicated that the time exponent of grains growth suddenly rise when the isothermal temperature higher than 1000℃.And the activation energy for austenite grain growth were calculated to be 538.0 kJ/mol in the high temperature region(above 1000℃)and 693.2 kJ/mol in the low temperature region(below 1000℃),respectively.Then,the kinetics model of austenite isothermal growth was established,which can predict the austenite grain size during isothermal hold very well.Besides,high density of second phase particles with small size was found during the isothermal hold at the low temperature region,leading to the refinement of austenite grain.After isothermal hold at different temperature for 1800 s,the bainite transformation in microalloyed steel strip was also observed in situ during the continuous cooling process.And growth rates of bainite plates with different nucleation positions and different prior austenite grain size(PAGS)were calculated.It was indicated that the growth rate of the bainite plate is not only related to the nucleation position but also to the PAGS.

Friction and wear behavior and mechanism of low carbon microalloyed steel containing Nb

Dry sliding friction and wear test of Nb containing low carbon microalloyed steel was carried out at room temperature,and the effect of Nb on the wear behavior of the steel,as welll as the mechanism was studied.Scanning electron microscopy(SEM) and energy dispersive spectrometry(EDS) were employed to analyze the morphology and composition of the worn surface,and the structure evolution of the plastic deformation layer.The carbide content and type in the steel were analyzed by the electrolytic extraction device and X-ray diffraction(XRD).The experimental results demonstrate that the addition of 0.2% Nb can refine the grain and generate Nb C to improve the wear resistance of the steel.By enhancing the load and speed of wear experiment,the wear mechanism of the test steel with 0.2% Nb changes from slight oxidation wear to severe adhesion wear and oxidation wear.Compared with the load,the increase in the rotation speed exerts a greater influence on the wear of the test steel.

MICROSTRUCTURE AND INCLUSION CHARACTERIZATION IN THE SIMULATED COARSE-GRAIN HEAT AFFECTED ZONE WITH LARGE HEAT INPUT OF A Ti-Zr-MICROALLOYED HSLA STEEL

The microstructure and the characteristics of the inclusions embedded in ferrite matrix in simulated coarse-grain heat affected zone (CGHAZ) of a Ti-Zr-treated high strength low alloy (HSLA) steel have been investigated. The microstructure of the simulated CGHAZ dominantly consisted of intragranular acicular ferrite (IAF) combining with a small amount of polygonal ferrite (PF), widmanst tten ferrite (WF), bainite ferrite (BF), pearlite and martensite-austenite (M-A) islands. The PF, WF and BF were generally observed at the prior austenite grain boundaries and the interlocking acicular ferrite was usually found intragranularly. It was found that the inclusions were composed of Ti2O3, ZrO2, Al2O3 locating at the center of the particles and MnS lying on the surface layer of the inclusions. The intragranular complex inclusions promoted the acicular ferrite formation and the refinement of microstructure whilst those at prior austenite grain boundaries caused PF formation on the inclusions. The simulated CGHAZ consisting of such complicated microstructure exhibited desired mechanical properties.

Grain refinement in the coarse-grained region of the heat-affected zone in low-carbon high-strength microalloyed steels

The microstructural features and grain refinement in the coarse-grained region of the heat-affected zone in low-carbon high-strength microalloyed steels were investigated using optical microscopy, scanning electron microscopy, and electron backscattering dif- fraction. The coarse-grained region of the heat-affected zone consists of predominantly bainite and a small proportion of acicular ferrite. Bainite packets are separated by high angle boundaries. Acicular ferrite laths or plates in the coarse-grained region of the heat-affected zone formed prior to bainite packets partition austenite grains into many smaller and separate areas, resulting in fine-grained mixed microstruc- tures. Electron backscattefing diffraction analysis indicates that the average crystallographic grain size of the coarse-grained region of the heat-affected zone reaches 6-9 μm, much smaller than that of anstanite grains.

MODELING OF MICROSTRUCTURAL EVOLUTION IN MICROALLOYED STEEL DURING HOT FORGING PROCESS

The microstractural evolution of microalloyed steel during hot forging process was investigated using physical simulation experiments. The dynamic recrystallized fraction was described by modifying Avrami＇s equation, the parameters of which were determined by single hit compression tests. Double hit compression tests were performed to model the equation describing the static recrystallized fraction, and the obtained predicted values were in good agreement with the measured values. Austenitic grain growth was modeled as： Dinc^5 = D0^5 ＋ 1.6 × 10^32t·exp （ -716870/RT ） using isothermal tests. Furthermore, an equation describing the dynamic recrystallized grain size was given as Ddyn=3771·Z^-0.2. The models of microstructural evolution could be applied to the numerical simulation of hot forging.

Mechanical Properties of V-,Nb-,and Ti-bearing As-cast Microalloyed Steels

The influence of microalloying additions on the mechanical properties of a low-carbon cast steel containing combinations of V, Nb, and Ti in the as-cast condition was evaluated. Tensile and hardness test results indicated that good combinations of strength and ductility could be achieved by V and Nb additions. While the yield strength and UTS （ultimate tensile strength） increased up to the range of 378-435 MPa and 579- 590 MPa, respectively in the microalloyed heats, their total elongation ranged from 18% to 23%. The presence of Ti, however, led to some reduction in the strength. Microstructural studies including scanning electron microscopy （SEM） and optical microscopy revealed that coarse TiN particles were responsible for this behavior. The Charpy impact values of all compositions indicated that microalloying additions significantly decreased the impact energy and led to the dominance of cleavage facets on the fracture surfaces. It seems that the increase in the hardness of coarse ferrite grains due to the precipitation hardening is the main reason for brittle fracture.

Precipitation characteristic of high strength steels microalloyed with titanium produced by compact strip production

Transmission electron microscopy （TEM） and physics-chemical phase analysis were employed to investigate the precipitates in high strength steels microalloyed with Ti produced by compact strip production （CSP）. It was seen that precipitates in Ti microalloyed steels mainly included TiN, Ti4C2S2, and TiC. The size of TiN particles varied from 50 to 500 nm, and they could precipitate during or before soaking. The Ti4C2S2 with the size of 40-100 nm might precipitate before rolling, and the TiC particles with the size of 5-50 nm precipitated heterogeneously. High Ti content would lead to the presence of bigger TiC particles that precipitated in austenite, and by contrast, TiC particles that precipitated in ferrite and the transformation of austenite to ferrite was smaller. They were less than 30 nm and mainly responsible for precipitate strengthening. It should be noted that the TiC particles in higher Ti content were generally smaller than those in the steel with a lower Ti content.

Properties and homogeneity of 550-MPa grade TMCP steel for ship hull

Ultra low carbon steels by the thermal mechanical control process（TMCP） with less Ni,Cr,and Mo contents have been developed for 550 MPa grade heavy gauge ship hulls and offshore structures.The relationships among microstructures,process,and properties of the studied steel have been investigated.A series of accurate control technologies have been developed for this kind of steel.Cu microalloying and TMCP＋relaxation precipitation control（RPC）＋accelerated cooling process were employed to optimize the mechanical properties and ensure the homogeneity of the 80-mm thick plate.The microstructures of thin plates slightly changed from surface to center,but the micro-structures of the heavy gauge plate（80 mm） changed notably.Adopting the simple composition,it can meet the requirement of thin plates by adopting a few microalloys.As for thick plates（80 mm）,a little higher Cu and Ni contents should be adopted.These steels can meet the needs without tempering.By these ways,the properties of the steels can be optimized,and the cost can be decreased notably.

Effect of Strain Rate on the Ferrite Grain Refinement in a Low Carbon Nb-Ti Microalloyed Steel during Low Temperature Deformation

Grain refinement is one of the effective methods to develop new generation low carbon microalloyed steels possessing excellent combination of mechanical properties. The microstructural evolution and ferrite grain refinement at the deformation temperature of 865℃, above Ar3, with different strain rates were investigated using single pass isothermal hot compression experiments for a low carbon Nb-Ti microalloyed steel. The physical processes that occurred during deformation were discussed by observing the optical microstructure and analyzing the true stress-true strain responses. At strain rates of 0.001 and 0.01s^-1, there is no evidence of work hardening behavior during hot deformation and strain-induced transformation （SIT） leads to dynamic flow softening in flow curves. Optical microscopy observation shows that ultrafine and equiaxed ferrite with grain sizes of 2μm can be obtained by applying deformation with strain rate of 0.1 s^-1 due to SIT just after deformation. Furthermore, increasing the strain rate from 0.001 to 0.1 s^-1 reduces both the grain size of the equiaxed ferrite and the amount of deformed ferrite.

Effects of Rare Earth on Behavior of Precipitation and Properties in Microalloyed Steels

The influence of rare earths on the behavior of precipitation of 14MnNb,X60 and 10MnV steels was studied by STEM, XRD, ICP and thermal simulation method. The main carbonitride precipitates are Nb(C, N),(Nb, Ti)(C, N)and V(C, N). In austenite RE delays the beginning of precipitation, and decreases the rate of precipitation. In ferrite RE promotes precipitation and increases the amount of equilibrium carbonitride precipitation. RE can make precipitates fine, globular and dispersed in the microalloyed steels. With the increase of the amount of RE in steel, the amount of precipitation increases. The promotion effect is weakened with excessive RE. RE has only little influence on the strength of microalloyed steel, but it can improve impact toughness effectively.

Thermodynamic Research on Precipitates in Low Carbon Nb-Microalloyed Steels Produced by Compact Strip Production

Microalloying element Nb in low carbon steels produced by compact strip production （CSP） process plays an important role in inhibiting recrystallization, decreasing the transformation temperature and grain refinement.With decreasing the rolling temperature, dislocations can be pinned by carbonitrides and the strength is increased. Based on the two sublattice model, with metal atom sublattice and interstitial atom sublattice,a thermodynamic model for carbonitride was established to calculate the equilibrium between matrix and carbonitride. In the steel produced by CSP, the calculation results showed that the starting temperature of precipitation of Ti and Nb are 1340℃ and 1040℃, respectively. In the range of 890-950℃, Nb rapidly precipitated. And the maximum of the atomic fraction of Nb in carbonitride was about 0.68. The morphologies and energy spectrum of the precipitates showed that （NbTi） （CN） precipitated near the dislocations. The experiment results show that Nb rapidly precipitated when the temperature was lower than 970℃, and the atomic fraction of Nb in carbonitride was about 60%-80%. The calculation results are in agreement with the experiment data. Therefore the thermodynamic model can be a useful assistant tool in the research on the precipitates in the low carbon steels produced by CSP.

Dynamic Recrystallization Behaviour of Nb-Ti Microalloyed Steels

The dynamic recrystallization （DRX） behavior of Nb-Ti microalloyed steels was investigated by isothermal single compression tests in the temperature range of 900-1 150 ℃ at constant strain rates of 0.1-5 s^-1. DRX was retarded effectively at low temperature due to the onset of dynamic precipitation of Nb and Ti carbonitrides, resulting in higher values of the peak strain. An expression was developed for the activation energy of deformation as a function of the contents of Nb and Ti in solution as well as other alloying elements. A new value of corrective factor was determined and applied to quantify the retardation produced by increase in the amount of Nb and Ti dissolved at the reheating temperature. The ratio of critical strain to peak strain decreases with increasing equivalent Nb content. In addition, the effects of Ti content and deformation conditions on DRX kinetics and steady state grain size were determined. Finally, the kinetics of dynamic precipitation was determined and effect of dynamic precipitation on the onset of DRX was clarified based on the comparison between precipitate pinning force and recrystallization driving force.

Isothermal Growth Kinetics of Ultra-fine Austenite Grains in a Nb-V-Ti Microalloyed Steel

Ultra-fine austenite grains with size of i-3 μm were prepared in a Nb-V-Ti steel through repetitive treatment of rapid heating and quenching. A model for the growth kinetics of these ultra-fine austenite grains was successfully created through successive 2 processes, and the activation energy Q for growth was estimated to be about 693.2 kJ/mol, which directly shows the inhibition effect of microalloy elements on the growth of ultra-fine austenite grains.

Effect of acicular ferrite on banded structures in low-carbon microalloyed steel

The effect of acicular ferrite （AF） on banded structures in low-carbon microalloyed steel with Mn segregation during both iso- thermal transformation and continuous cooling processes was studied by dilatometry and microscopic observation. With respect to the iso- thermal transformation process, the specimen isothermed at 550℃ consisted of AF in Mn-poor bands and martensite in Mn-rich bands, whereas the specimen isothermed at 450℃ exhibited two different morphologies of AF that appeared as bands. At a continuous cooling rate in the range of 4 to 50℃/s, a mixture of AF and martensite formed in both segregated bands, and the volume fraction of martensite in Mn-rich bands was always higher than that in Mn-poor bands. An increased cooling rate resulted in a decrease in the difference of martensite volume fraction between Mn-rich and Mn-poor bands and thereby leaded to less distinct microstrucmral banding. The results show that Mn segregation and cooling rate strongly affect the formation of AF-containing banded structures. The formation mechanism of microstructural banding was also discussed.

Growth behavior of ultrafine austenite grains in microalloyed steel

Ultrafine austenite gains （UFAGs） with size of 1-5 μm were prepared through repetitive treatment, four times, of rapid heating and quenching, and the growth behaviors of these UFACs during both the reheating and cooling stages were investigated. The results indicated that UFAGs without pinning particles appeared with significant coarsening when the reheating temperature reached 1000 ℃. Although coarsening still occurred in the cooling stage, the growth was obscured during the isothermal holding process at temperatures between 900 ℃ and At3.

GRAIN REFINEMENT OF MICROALLYED STEEL THROUGH HEAVY HOT DEFORMATION AND CONTROLLED COOLING

Heavy deformation and controlled cooling is one of the most effective effective ways for grain refinement in HSIA steels. In this paper, experimental specimens are prepared with a commercial linepipe steel grade X65, and the chemical compositions are (wt% ): Fe-0.094C-1.42Mn-0. 29Si-0. 045Nb-0. 008Ti. After heavy deformation with 80% reduction in non-recrystallization range of austenite, and at controlled cooling rates from 2K/s to 64K/s, the grain sizes vary from 9.55μm to 1.06μm.It is shown by the results that a linear relationship still remains between the yield strength and reciprocal of square root of ferrite grain size as grain size is refined to 1m.The ultra-fine grains might be dynam- ically formed through the deformation-induced transformation when reduction is large enough.The grain sizes decrease when the cooling rates increase.When the cooling rates increase over 10K/s, the grain sizes are rarely changed. The particles distribute on grain boundaries, sub-grain boundaries, deformed bands and within the ferrite grains.

GRAIN COARSENING BEHAVIOR OF V-Ti-N MICROALLOYED STEELS

The effects of chemical composition and cooling rate after solidication on the grain coarsening temperature,T_(GC),of the V-Ti-N microalloyed steels have been investigated.It is shown that the T_(GC) may be obviously raised by adding even a little Ti to the base steel so as to pre- cipitate a great deal of fine Ti-bearing particles of about 10 nm.The T_(GC) does not increase with the cooling rate,as it is over a certain critical value.The T_(GC) is insensitive to any varia- tion of N content at simulated cooling condition of 150 mm continuous cast slab.The T_(GC) may be dropped down about 100℃ by adding 0.33 wt-%Mo to the steels.The sensitivi- ty of T_(GC) to cooling condition relates to the Ti and V contents.