By means of Miedema formation enthalpy model with Toop model, the excess free-energy, enthalpies of formation, excess entropies and activity values of all components of Mg-A1-Y ternary alloy were calculated with compu...By means of Miedema formation enthalpy model with Toop model, the excess free-energy, enthalpies of formation, excess entropies and activity values of all components of Mg-A1-Y ternary alloy were calculated with computer programming. The experimental results show that enthalpies of formation, excess free- energy and excess entropies of the ternary alloy are negative in the whole content range, the minimum values at 1 123 K are all obtained at x_Al=55%, x_y=45%, X_Mg=0%, which are -37.969, -30.961 kJ/mol and -6.24 J/（mol-k） respectively. Activity curves show that the activity values of A1 and Y in Mg-A1-Y ternary alloy rapidly decrease with the decrease of molar fraction, the values of which are very small when the molar fraction decreases to 0.4. It means that there is a strong interaction between A1 and Y and stable compounds can be form in the Mg-A1-Y ternary alloy system.展开更多
基金Funded by the National Natural Science Foundation of China(Nos.51165032 and 51364035)the Innovative Group of Science and Technology of College of Jiangxi Province(No.00008713)+2 种基金the Jiangxi Province Education Commission Foundation(GJJ13203)the Production and Teaching and Research Cooperation Plan of Nanchang Non-party Experts and Doctor(No.2012-CYH-DW-XCL-002)the Special Funds for Postgraduate Innovation of Jiangxi Province
文摘By means of Miedema formation enthalpy model with Toop model, the excess free-energy, enthalpies of formation, excess entropies and activity values of all components of Mg-A1-Y ternary alloy were calculated with computer programming. The experimental results show that enthalpies of formation, excess free- energy and excess entropies of the ternary alloy are negative in the whole content range, the minimum values at 1 123 K are all obtained at x_Al=55%, x_y=45%, X_Mg=0%, which are -37.969, -30.961 kJ/mol and -6.24 J/（mol-k） respectively. Activity curves show that the activity values of A1 and Y in Mg-A1-Y ternary alloy rapidly decrease with the decrease of molar fraction, the values of which are very small when the molar fraction decreases to 0.4. It means that there is a strong interaction between A1 and Y and stable compounds can be form in the Mg-A1-Y ternary alloy system.