The effects of moisture content （8%, 10%and 12%）, variety （Tarom and Fajr） and parboiling on milling quality of rice as a function of milling recovery （MR）, head rice yield （HRY）, degree of milling （DOM） and...The effects of moisture content （8%, 10%and 12%）, variety （Tarom and Fajr） and parboiling on milling quality of rice as a function of milling recovery （MR）, head rice yield （HRY）, degree of milling （DOM） and whiteness were investigated. The parboiled grains was prepared with three soaking temperatures of 25 oC, 50 oC and 75 oC and three steaming times of 10, 15 and 20 min. As a result of parboiling, the increasing rates of MR and HRY values were 7.8%and 14.3%for Tarom and 9.8%and 10.0%for Fajr, respectively, and the decreasing rates for DOM and whiteness were 6.6%and 10.8%for Tarom and 6.8% and 10.5% for Fajr, respectively. Moreover, decreasing moisture content to 8%maximized MR （75.8% for Tarom and 74.3% for Fajr） and HRY （65.8% for Tarom and 57.0% for Fajr） while increasing that to 12%revealed maximum values of DOM （6.1%for Tarom and 6.2%for Fajr） and whiteness （24.8%for Tarom and 28.2%for Fajr）.展开更多
High pressure roll grinding（HPRG）and ball milling were compared to investigate the influence of mechanical activation on the acid leaching dephosphorization of a high-phosphorus iron ore concentrate,which was manufa...High pressure roll grinding（HPRG）and ball milling were compared to investigate the influence of mechanical activation on the acid leaching dephosphorization of a high-phosphorus iron ore concentrate,which was manufactured through magnetizing roasting-magnetic separation of high-phosphorus oolitic iron ores.The results indicated that when high-phosphorus iron ore concentrates containing 54.92 mass% iron and 0.76 mass% phosphorus were directly processed through acid leaching,iron ore concentrates containing 55.74mass%iron and 0.33mass%phosphorus with an iron recovery of 84.64%and dephosphorization of 63.79% were obtained.When high-phosphorus iron ore concentrates activated by ball milling were processed by acid leaching,iron ore concentrates containing56.03mass%iron and 0.21mass% phosphorus with an iron recovery of 85.65% and dephosphorization of 77.49%were obtained.Meanwhile,when high-phosphorus iron ore concentrates activated by HPRG were processed by acid leaching,iron ore concentrates containing 58.02mass%iron and 0.10mass% phosphorus were obtained,with the iron recovery reaching 88.42% and the dephosphorization rate reaching 88.99%.Mechanistic studies demonstrated that ball milling can reduce the particle size,demonstrating aprominent reunion phenomenon.In contrast,HPRG pretreatment contributes to the formation of more cracks within the particles and selective dissociation of iron and P bearing minerals,which can provide the favorable kinetic conditions to accelerate the solid-liquid reaction rate.As such,the crystal structure is destroyed and the surface energy of mineral particles is strengthened by mechanical activation,further strengthening the dephosphorization.展开更多
基金Ferdowsi Universityof Mashhad,Iran for providing the laboratory facilitiesand financial support(Grant No.15226)
文摘The effects of moisture content （8%, 10%and 12%）, variety （Tarom and Fajr） and parboiling on milling quality of rice as a function of milling recovery （MR）, head rice yield （HRY）, degree of milling （DOM） and whiteness were investigated. The parboiled grains was prepared with three soaking temperatures of 25 oC, 50 oC and 75 oC and three steaming times of 10, 15 and 20 min. As a result of parboiling, the increasing rates of MR and HRY values were 7.8%and 14.3%for Tarom and 9.8%and 10.0%for Fajr, respectively, and the decreasing rates for DOM and whiteness were 6.6%and 10.8%for Tarom and 6.8% and 10.5% for Fajr, respectively. Moreover, decreasing moisture content to 8%maximized MR （75.8% for Tarom and 74.3% for Fajr） and HRY （65.8% for Tarom and 57.0% for Fajr） while increasing that to 12%revealed maximum values of DOM （6.1%for Tarom and 6.2%for Fajr） and whiteness （24.8%for Tarom and 28.2%for Fajr）.
基金Item Sponsored by National Torch Program Project of China(2011GH561685)
文摘High pressure roll grinding（HPRG）and ball milling were compared to investigate the influence of mechanical activation on the acid leaching dephosphorization of a high-phosphorus iron ore concentrate,which was manufactured through magnetizing roasting-magnetic separation of high-phosphorus oolitic iron ores.The results indicated that when high-phosphorus iron ore concentrates containing 54.92 mass% iron and 0.76 mass% phosphorus were directly processed through acid leaching,iron ore concentrates containing 55.74mass%iron and 0.33mass%phosphorus with an iron recovery of 84.64%and dephosphorization of 63.79% were obtained.When high-phosphorus iron ore concentrates activated by ball milling were processed by acid leaching,iron ore concentrates containing56.03mass%iron and 0.21mass% phosphorus with an iron recovery of 85.65% and dephosphorization of 77.49%were obtained.Meanwhile,when high-phosphorus iron ore concentrates activated by HPRG were processed by acid leaching,iron ore concentrates containing 58.02mass%iron and 0.10mass% phosphorus were obtained,with the iron recovery reaching 88.42% and the dephosphorization rate reaching 88.99%.Mechanistic studies demonstrated that ball milling can reduce the particle size,demonstrating aprominent reunion phenomenon.In contrast,HPRG pretreatment contributes to the formation of more cracks within the particles and selective dissociation of iron and P bearing minerals,which can provide the favorable kinetic conditions to accelerate the solid-liquid reaction rate.As such,the crystal structure is destroyed and the surface energy of mineral particles is strengthened by mechanical activation,further strengthening the dephosphorization.