A Simple Mix Proportion Design Method Based on Frost Durability for Recycled High Performance Concrete Using Fully Coarse Recycled Aggregate

Durability design of recycled high performance concrete（RHPC） is fundamental for improving the use rate and level of concrete waste as coarse recycled aggregate（CRA）. We discussed a frostdurability-based mix proportion design method for RHPC using 100 % CRA and natural sand. Five groups of RHPC mixes with five strength grades（40, 50, 60, 70 and 80 MPa） were produced using CRA with four quality classes, and their workability, 28 d compressive strengths and frost resistances（measured by the compressive strength loss ratio and the relative dynamic modulus of elasticity） were tested. Relationships between the 28 d compressive strength, the frost resistance and the CRA quality characteristic parameter, water absorption, were then developed. The criterion of a CRA maximum water absorption limit value for RHPC was suggested, independent of its source and quality class. The results show that all RHPC mixes achieve the expected target workability, strength, and frost durability. The research results demonstrate that the application of the proposed method does not require trial testing prior to use.

Mix design optimization of seawater sea sand coral aggregate concrete

With the resource shortage in coastal areas,the construction of concrete structures using freshwater and river sand has brought great economic and environmental costs.The use of seawater,sea sand,and coral aggregates in concrete mixes has become an alternative solution for coastal and marine structures,especially for offshore structures and artificial islands.In this study,378 seawater,sea sand,and coral aggregate concrete(Coral-SWSSC)specimens were prepared,and their mechanical properties were investigated comprehensively through compressive tests to explore the optimized mix design at different grades.Results showed that the mechanical properties of Coral-SWSSC were strongly correlated with the water-to-binder ratios,coastal particle gradings,and pretreatment method of coastal particles.Based on the experimental results,mix proportion designs of CoralSWSSC were proposed for concrete from C20 to C50 grades,and the failure mechanism of Coral-SWSSC at different grades was discussed according to their respective failure modes.The findings of the current study provide knowledge on the optimized design of Coral-SWSSC,which can be used to promote the application of Coral-SWSSC in offshore,marine,and ocean engineering.