Layered double hydroxides （LDHs）/styrene-butadiene-styrene （SBS） eopolymer modified bitumen was prepared by melt blending. The effect of LDHs on the ultraviolet （UV） aging behavior of SBS modified bitumen was in...Layered double hydroxides （LDHs）/styrene-butadiene-styrene （SBS） eopolymer modified bitumen was prepared by melt blending. The effect of LDHs on the ultraviolet （UV） aging behavior of SBS modified bitumen was investigated. The changes of chemical structures of modified bitumen before and after UV aging were characterized by Fourier transform infrared spectroscopy （FTIR）. The results show that LDHs obviously reduce the variation of softening point and low temperature flexibility of SBS modified bitumen under different UV radiation intensities, which indicates that the UV aging resistance performance of SBS modified bitumen is improved effectively by LDHs. Compared with SBS modified bitumen, the changes of carbonyl, sulfoxide and butadienyl of LDHs/SBS modified bitumen decrease significantly after UV aging according to FTIR analysis, demonstrating that the oxidation and degradation reactions of SBS modified bitumen were restrained effectively by adding LDHs.展开更多
The glassy carbon (GC) electrode modified with a monolayer nickel hydroxide (GC/Ni(OH) 2) was prepared by immersion of GC substrate in 1.0×10 -3 mol/L NiSO 4 solution, and then cyclic voltammetric scannin...The glassy carbon (GC) electrode modified with a monolayer nickel hydroxide (GC/Ni(OH) 2) was prepared by immersion of GC substrate in 1.0×10 -3 mol/L NiSO 4 solution, and then cyclic voltammetric scanning in 0.20 mol/L KOH. Similarly, GC/Co(OH) 2 electrode was prepared too. The experiments showed that the voltammetric behavior of GC/Ni(OH) 2 electrode in 0.20 mol/L KOH is more stable than that of GC/ Co(OH) 2. It was found that the GC/Ni(OH) 2 electrode acts as an effective electrocatalysis for the oxidation of hydrazine.展开更多
The influence of the precipitating reagents and dispersants on the formation of nano-aluminum hydroxide from sodium aluminate solution by chemical precipitation was investigated. The influence of the dispersed seeds o...The influence of the precipitating reagents and dispersants on the formation of nano-aluminum hydroxide from sodium aluminate solution by chemical precipitation was investigated. The influence of the dispersed seeds on the decomposi-tion process was investigated too. The alkaline aluminate solutions were used as original solutions with a concentration of Al2O3 having 14.78 g/dm3, αk—1.6 and127 g/dm3, αk—1.6. For the precipitation processes there were used follow-ing precipitating reagents—solutions HCl, NaHCO3 and NH4HCO3 with a concentration of 80 g/dm3, dispersants—PEG 6000, (NaPO3)6 and Tween 20. For the decomposition process the dispersed seeds and factories seeds were used. Structural studies of the aluminum hydroxide particles were carried out by means of the electron-probe microanalysis and scanning electron microscopy, and phase composition of products was determined by means of X-ray diffraction analysis. Ammonium bicarbonate and Tween 20 were determined as the optimal precipitating reagent and dispersant, correspondingly, resulting in dispersed aluminum hydroxide, which is used as a seed in the decomposition process. It was established that this product in form of dispersed seed considerably reduces the duration of the decomposition process;the maximal decomposition of solution (73.9%) was observed after injection of dispersеd aluminum hydroxide into solution. The final aluminum hydroxide having 90% of particles less than 100 nanometers was obtained within 7 hours of steady decreasing temperature from 70°C to 48°C.展开更多
基金Funded by the National Basic Research Program of China(973 Program)(No.2014CB932104)
文摘Layered double hydroxides （LDHs）/styrene-butadiene-styrene （SBS） eopolymer modified bitumen was prepared by melt blending. The effect of LDHs on the ultraviolet （UV） aging behavior of SBS modified bitumen was investigated. The changes of chemical structures of modified bitumen before and after UV aging were characterized by Fourier transform infrared spectroscopy （FTIR）. The results show that LDHs obviously reduce the variation of softening point and low temperature flexibility of SBS modified bitumen under different UV radiation intensities, which indicates that the UV aging resistance performance of SBS modified bitumen is improved effectively by LDHs. Compared with SBS modified bitumen, the changes of carbonyl, sulfoxide and butadienyl of LDHs/SBS modified bitumen decrease significantly after UV aging according to FTIR analysis, demonstrating that the oxidation and degradation reactions of SBS modified bitumen were restrained effectively by adding LDHs.
文摘The glassy carbon (GC) electrode modified with a monolayer nickel hydroxide (GC/Ni(OH) 2) was prepared by immersion of GC substrate in 1.0×10 -3 mol/L NiSO 4 solution, and then cyclic voltammetric scanning in 0.20 mol/L KOH. Similarly, GC/Co(OH) 2 electrode was prepared too. The experiments showed that the voltammetric behavior of GC/Ni(OH) 2 electrode in 0.20 mol/L KOH is more stable than that of GC/ Co(OH) 2. It was found that the GC/Ni(OH) 2 electrode acts as an effective electrocatalysis for the oxidation of hydrazine.
文摘The influence of the precipitating reagents and dispersants on the formation of nano-aluminum hydroxide from sodium aluminate solution by chemical precipitation was investigated. The influence of the dispersed seeds on the decomposi-tion process was investigated too. The alkaline aluminate solutions were used as original solutions with a concentration of Al2O3 having 14.78 g/dm3, αk—1.6 and127 g/dm3, αk—1.6. For the precipitation processes there were used follow-ing precipitating reagents—solutions HCl, NaHCO3 and NH4HCO3 with a concentration of 80 g/dm3, dispersants—PEG 6000, (NaPO3)6 and Tween 20. For the decomposition process the dispersed seeds and factories seeds were used. Structural studies of the aluminum hydroxide particles were carried out by means of the electron-probe microanalysis and scanning electron microscopy, and phase composition of products was determined by means of X-ray diffraction analysis. Ammonium bicarbonate and Tween 20 were determined as the optimal precipitating reagent and dispersant, correspondingly, resulting in dispersed aluminum hydroxide, which is used as a seed in the decomposition process. It was established that this product in form of dispersed seed considerably reduces the duration of the decomposition process;the maximal decomposition of solution (73.9%) was observed after injection of dispersеd aluminum hydroxide into solution. The final aluminum hydroxide having 90% of particles less than 100 nanometers was obtained within 7 hours of steady decreasing temperature from 70°C to 48°C.