Research of Lignin Modified Phenol Formaldehyde Resin Bonded Magnesia Carbon Bricks

In order to reduce the cost and to improve the low temperature bonding strength of phenol formaldehyde resin（ PF）,the lignin modified phenol formaldehyde resin（ LPF） was synthesized using calcium lignosulfonate as a partial replacement of phenol,and sodium hydroxide as catalyzer. Then the magnesia carbon bricks were prepared using the LPF as binder. Different process conditions of LPFs such as calcium lignosulfonate additions（ 10%,20%,30%,40% and 50%,in mass,the same hereinafter）,catalyzer additions（ extra added,1%,2%,3%,4% and 5%） and reaction times（ 1,1. 5,2,2. 5 and 3 h） were investigated. Effects of prepared LPFs on properties of magnesia carbon bricks（ baked at 200 ℃ for 24 h） were researched in order to modify the synthesizing conditions of LPFs. Cold physical properties and hot modulus of rupture of magnesia carbon bricks bonded by LPF and by traditional PF after baked at 200 ℃ for 24 h and fired at 1 200 ℃ for 3 h were compared,respectively. The results show that the optimal synthesizing conditions of LPF for preparing magnesia carbon bricks are 30% calcium lignosulfonate,1% catalyzer,and 2 h reaction time. The magnesia carbon bricks bonded by the optimal LPF achieve：（ 1） the bulk densities 2. 84 g · cm- 3and 2. 82g·cm- 3,apparent porosities 9. 6% and 14. 6%,moduli of rupture 17. 8 MPa and 6. 4 MPa,crushing strengths72. 3 MPa and 48. 7 MPa,after baked at 200 ℃ and1 200 ℃,respectively;（ 2） the hot modulus of rupture7. 3 MPa after fired at 1 400 ℃. The above properties are better than those of the magnesia carbon brick bonded by PF.

Ablation Performance of a Novel Super-hybrid Composite

A novel super-hybrid composite (NSHC) was boron-modified phenolic resin (BPR) with three-dimensional reticulated SiC ceramic (3DRC) and high silica fibers. Ablation performance of the NSHC was studied. The results show that the linear ablation rate of NSHC was lower than that of pure BPR and the high silica/BPR composite. Its linear ablation rate is 1/17 of the high silica/BPR. Mass ablation rate of the NSHC is very close to that of the pure BPR and the high silica/BPR composite. Scanning electron microscope (SEM) analysis indicates that 3DRC has scarcely changed its shape at the ablation temperature. Its special reticulated structure can restrict the materials deformation and prevent high velocity heat flow from eroding the surface of the materials largely and thus increase ablation resistance of the NSHC.

Ablation Property of Ceramics/Carbon Fibers/Resin Novel Super-hybrid Composite

A novel super-hybrid composite (NSHC) is prepared with three-dimension reticulated SiC ceramic (3DRC), high performance carbon fibers and modified phenolic resin (BPR) in this paper. Ablation performance of super-hybrid composite is studied. The results show that the NSHC has less linear ablation rate compared with pure BPR and CF/BPR composite, for example, its linear ablation rate is 50% of CF/BPR at the same fiber content. Mass ablation rate of the NSHC is slightly lower than that of pure BPR and CF/BPR composite because of their difference in the density. Scanning electron microscopic analysis indicates that 3DRC can increase anti-erosion capacity of materials because its special reticulated structure can control the deformation of materials and strengthen the stability of integral structure.