The surface tension of molten tin was determined by a set of self-developed digital equipment with sessile drop method at oxygen partial pressure of 1.0×10 -6MPa under different temperatures, and the dependence...The surface tension of molten tin was determined by a set of self-developed digital equipment with sessile drop method at oxygen partial pressure of 1.0×10 -6MPa under different temperatures, and the dependence of surface tension of molten tin on temperature was also discussed. The emphasis was placed on the comparison of surface tension of the same molten tin sample measured by using different equipments with sessile drop method. Results of the comparison indicate that the measurement results with sessile drop method under the approximate experimental conditions are coincident, and the self-developed digital equipment for surface tension measurement has higher stability and accuracy. The relationships of surface tension of molten tin and its temperature coefficient with temperature and oxygen partial pressure were also elucidated from the thermodynamic equilibrium analysis.展开更多
The components of the equipment for processing the Al melts into the molded parts can be markedly corroded by the molten Al. In this study, a 4 μm CrN coating or CrN/TiN multilayer coating for providing the physical ...The components of the equipment for processing the Al melts into the molded parts can be markedly corroded by the molten Al. In this study, a 4 μm CrN coating or CrN/TiN multilayer coating for providing the physical and chemical barriers between the molten reactive Al and the steel substrate were deposited by Cathodic Arc Evaporation onto 10 mm-thick heat-resistant steel plates. The dipping tests were conducted in a 700℃ A356 melt for 1 to 21 h at intervals of 3 h. The damage of the coated steel was eva...展开更多
Tin-doped multiwall carbon nanotubes (CNTs) were prepared by electrolysis in molten salt of LiCl (62%)-NaCl(37%)-SnCl2(1%) in mass fraction with a graphite rod as a cathode. TEM and XRD investigations show that struct...Tin-doped multiwall carbon nanotubes (CNTs) were prepared by electrolysis in molten salt of LiCl (62%)-NaCl(37%)-SnCl2(1%) in mass fraction with a graphite rod as a cathode. TEM and XRD investigations show that structure characteristic of tin-doped CNTs is webs of well-graphitized hollow tubes with outer diameters between 10 and 20 nm with presence of Sn and SnO2. The EDS elementary analysis confirms the content of tin in the products was 9%. Electrochemical Li insertion into the doped CNTs was investigated in a nonaqueous medium. Galvanostatic discharge-charge measurement revealed that their specific capacities of insertion and extraction lithium were 1762mAh/g and 1295mAh/g, respectively, in the first cycle with almost coulomb efficiency of 73%. The coulomb efficiency increased to more than 90% after the ninth cycle, and the reversible capacity was about 210 mAh/g.展开更多
The ionic species in SnCl\-2-1-butylpytidinium chloride (BPC) ambient temperature molten salt electrolytes were investigated by using the computer simulation method. It was found that the Sn electrode potential was ch...The ionic species in SnCl\-2-1-butylpytidinium chloride (BPC) ambient temperature molten salt electrolytes were investigated by using the computer simulation method. It was found that the Sn electrode potential was changed suddenly at 50.0% mole fraction SnCl\-2. The major ionic specie in the 33.3%SnCl\-2 melt is SnCl\+-\-3 and that in the 66.6% SnCl\-2 melt is Sn\-2Cl\+-\-5. Both SnCl\+-\-3 and Sn\-2Cl\+-\-5 existed in the 50.0%SnCl\-2 melt.展开更多
文摘The surface tension of molten tin was determined by a set of self-developed digital equipment with sessile drop method at oxygen partial pressure of 1.0×10 -6MPa under different temperatures, and the dependence of surface tension of molten tin on temperature was also discussed. The emphasis was placed on the comparison of surface tension of the same molten tin sample measured by using different equipments with sessile drop method. Results of the comparison indicate that the measurement results with sessile drop method under the approximate experimental conditions are coincident, and the self-developed digital equipment for surface tension measurement has higher stability and accuracy. The relationships of surface tension of molten tin and its temperature coefficient with temperature and oxygen partial pressure were also elucidated from the thermodynamic equilibrium analysis.
文摘The components of the equipment for processing the Al melts into the molded parts can be markedly corroded by the molten Al. In this study, a 4 μm CrN coating or CrN/TiN multilayer coating for providing the physical and chemical barriers between the molten reactive Al and the steel substrate were deposited by Cathodic Arc Evaporation onto 10 mm-thick heat-resistant steel plates. The dipping tests were conducted in a 700℃ A356 melt for 1 to 21 h at intervals of 3 h. The damage of the coated steel was eva...
文摘Tin-doped multiwall carbon nanotubes (CNTs) were prepared by electrolysis in molten salt of LiCl (62%)-NaCl(37%)-SnCl2(1%) in mass fraction with a graphite rod as a cathode. TEM and XRD investigations show that structure characteristic of tin-doped CNTs is webs of well-graphitized hollow tubes with outer diameters between 10 and 20 nm with presence of Sn and SnO2. The EDS elementary analysis confirms the content of tin in the products was 9%. Electrochemical Li insertion into the doped CNTs was investigated in a nonaqueous medium. Galvanostatic discharge-charge measurement revealed that their specific capacities of insertion and extraction lithium were 1762mAh/g and 1295mAh/g, respectively, in the first cycle with almost coulomb efficiency of 73%. The coulomb efficiency increased to more than 90% after the ninth cycle, and the reversible capacity was about 210 mAh/g.
文摘The ionic species in SnCl\-2-1-butylpytidinium chloride (BPC) ambient temperature molten salt electrolytes were investigated by using the computer simulation method. It was found that the Sn electrode potential was changed suddenly at 50.0% mole fraction SnCl\-2. The major ionic specie in the 33.3%SnCl\-2 melt is SnCl\+-\-3 and that in the 66.6% SnCl\-2 melt is Sn\-2Cl\+-\-5. Both SnCl\+-\-3 and Sn\-2Cl\+-\-5 existed in the 50.0%SnCl\-2 melt.