Stable CuO/La_(2)Sn_(2)O_(7) catalysts for soot combustion:Study on the monolayer dispersion behavior of CuO over a La_(2)Sn_(2)O_(7) pyrochlore support

To understand the dispersion behavior of metal oxides on composite oxide supports and with the expectation of developing more feasible catalysts for soot oxidation,CuO/La_(2)Sn_(2)O_(7)samples containing varied CuO loadings were fabricated and characterized by different techniques and density functional theory calculations.In these catalysts,a spontaneous dispersion of CuO on the La_(2)Sn_(2)O_(7)pyrochlore support formed,having a monolayer dispersion capacity of 1.90 mmol CuO/100 m^(2) La_(2)Sn_(2)O_(7)surface.When loaded below this capacity,CuO exists in a sub-monolayer or monolayer state.X-ray photoelectron spectroscopy(XPS),Raman spectroscopy,and Bader charge and density of states analyses indicate that there are strong interactions between the sub-monolayer/monolayer CuO and the La_(2)Sn_(2)O_(7)support,mainly through the donation of electrons from Cu to Sn at the B-sites of the structure.In contrast,Cu has negligible interactions with La at the A-sites.This suggests that,in composite oxide supports containing multiple metals,the supported metal oxide interacts preferentially with one kind of metal cation in the support.The Raman,in situ diffuse reflectance infrared Fourier transform spectroscopy,and XPS results confirmed the formation of both O2^(-)and O2^(2-)as the active sites on the surfaces of the CuO/La_(2)Sn_(2)O_(7)catalysts,and the concentration of these active species determines the soot combustion activity.The number of active oxygen anions increased with increase in CuO loading until the monolayer dispersion capacity was reached.Above the monolayer dispersion capacity,microsized CuO crystallites formed,and these had a negative effect on the generation of active surface oxygen sites.In summary,a highly active catalyst can be prepared by covering the surface of the La_(2)Sn_(2)O_(7)support with a CuO monolayer.

Tuning SnO_2 surface with CuO for soot particulate combustion: The effect of monolayer dispersion capacity on reaction performance

With the objective to investigate the structure-reactivity relationship of CuO/SnO2 and eventually design more applicable catalysts for soot combustion,catalysts with different CuO loadings have been prepared by impregnation method.By using X-ray diffraction and X-ray photoelectron spectroscopy extrapolation methods,it is disclosed that CuO disperses finely on the SnO2 support to form a monolayer with a capacity of 2.09 mmol 100 m^-2,which equals 4.8 wt%CuO loading.When the CuO loading is below the capacity,it is in a sub-monolayer state.However,when the loading is above the capacity,CuO micro-crystallites will be formed that coexist with the CuO monolayer.The soot combustion activity of the catalyst increases with the CuO loading until it reaches the monolayer dispersion capacity.A further increase in the CuO loading has no evident influence on the activity.Raman results have testified that with the addition of CuO onto the SnO2 support,a surface-active oxygen species can be formed,the amount of which also increases significantly with the increase in the CuO loading until it reaches the monolayer dispersion capacity.Increasing the CuO loading further has no evident impact on the amount of surface oxygen.Therefore,an apparent monolayer dispersion threshold effect is observed for soot combustion over CuO/SnO2 catalysts.It is concluded that the amount of surface-active oxygen sites is the major factor determining the activity of the catalyst.

On the monolayer dispersion behavior of Co_(3)O_(4)on HZSM-5 support:designing applicable catalysts for selective catalytic reduction of nitrogen oxides by ammonia

Based on monolayer dispersion theory,Co_(3)O_(4)/ZSM-5 catalysts with different loadings have been prepared for selective catalytic reduction of nitrogen oxides by ammonia.Co_(3)O_(4)can spontaneously disperse on HZSM-5 support with a monolayer dispersion threshold of 0.061 mmol 100 m^(-2),equaling to a weight percentage around 4.5%.It has been revealed that the quantities of surface active oxygen(O_(2)^(-))and acid sites are crucial for the reaction,which can adsorb and activate NO_(x)and NH_(3)reactants effectively.Below the monolayer dispersion threshold,Co_(3)O_(4)is finely dispersed as sub-monolayers or monolayers and in an amorphous state,which is favorable to generate the two kinds of active sites,hence promoting the performance of ammonia selective catalytic reduction of nitrogen oxide.However,the formation of crystalline Co_(3)O_(4)above the capacity is harmful to the reaction performance.4%Co_(3)O_(4)/ZSM-5,the catalyst close to the monolayer dispersion capacity,possesses the most abundant active O_(2)^(-)species and acidic sites,thereby demonstrating the best reaction performance in all the samples.It is proposed the optimal Co_(3)O_(4)/ZSM-5 catalyst can be prepared by loading the capacity amount of Co_(3)O_(4)onto HZSM-5 support.

Phonon Confinement Effect in Two-dimensional Nanocrystallites of Monolayer MoS_2 to Probe Phonon Dispersion Trends Away from Brillouin-Zone Center

The fundamental momentum conservation requirement q - 0 for the Raman process is relaxed in the nanocrystal- lites （NCs）, and phonons away from the Brillouin-zone center will be involved in the Raman scattering, which is well-known as the phonon confinement effect in NCs. This usually gives a downshift and asymmetric broadening of the Raman peak in various NCs. Recently, the A1 mode of 1L MoS2 NCs is found to exhibit a blue shift and asymmetric broadening toward the high-frequency side [Chem. Soc. Rev. 44 （2015） 2757 and Phys. Rev. B 91 （2015） 195411]. In this work, we carefully check this issue by studying Raman spectra of lL MoS2 NCs prepared by the ion implantation technique in a wide range of ion-implanted dosage. The same confinement coefficient is used for both E＇ and A＇1 modes in 1L MoS2 NCs since the phonon uncertainty in an NC is mainly determined by its domain size. The asymmetrical broadening near the A＇1 and E＇ modes is attributed to the appearance of defect-activated phonons at the zone edge and the intrinsic asymmetrical broadening of the two modes, where the anisotropy of phonon dispersion curves along Г-K and Г- M is also considered. The photoluminescence spectra confirm the formation of small domain size of 1L MoS2 nanocrystallites in the ion-implanted 1L MoS2. This study provides not only an approach to quickly probe phonon dispersion trends of 2D materials away from Г by the Raman scattering of the corresponding NCs, but also a reference to completely understand the confinement effect of different modes in various nanomaterials.